CN103232675A - High toughness PC/ABS alloy material - Google Patents
High toughness PC/ABS alloy material Download PDFInfo
- Publication number
- CN103232675A CN103232675A CN 201310107752 CN201310107752A CN103232675A CN 103232675 A CN103232675 A CN 103232675A CN 201310107752 CN201310107752 CN 201310107752 CN 201310107752 A CN201310107752 A CN 201310107752A CN 103232675 A CN103232675 A CN 103232675A
- Authority
- CN
- China
- Prior art keywords
- parts
- alloy material
- abs
- stearic acid
- abs alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high toughness PC/ABS alloy material, which comprises the following materials by weight: 40-50 parts of PC, 60-80 parts of ABS, 10-20 parts of a halogen-free intumescent flame retardant, 10-15 parts of an ethylene copolymer elastomer, 10-13 parts of nano-calcium carbonate, 12-15 parts of ethylene-acrylate, 1-5 parts of trimethylsilyl dimethyl methylphosphonate, 2-8 parts of melamine cyanurate, 5-8 parts of molybdenum trioxide, 2-8 parts of ammonium polyphosphate, 1-2 parts of stearic acid, 1-5 parts of stearate, 1-3 parts of stearamide, 1 part of silicone oil, 2 parts of tourmaline mineral micro-powder, 1-2 parts of poly-4-methyl-1-pentene, 5 parts of active calcium, 6 parts of stearic acid, 2-9 parts of a processing stabilizer, and 3-5 parts of a lubricant. According to the invention, the notch impact strength of a flame retardant PC/ABS material can be effectively improved, thus obtaining the high toughness flame retardant PC/ABS alloy material, which can be more adaptable to various high-tech manufacturing industries and has considerable economic benefits.
Description
Technical field
The present invention relates to a kind of PC/ABS alloy material of high tenacity.
Background technology
PC/ABS is a kind of plastic alloy material of excellent property.It not only has favorable mechanical performance and moulding processability, and the product surface good luster, and is attractive in appearance, thereby is widely used in industries such as electronics, household electrical appliances.When PC/ABS alloy material during for the manufacture of electronics zero member, often require material to have flame retardant properties.To this, people adopt the method for adding fire retardant to improve the flame retardant properties of material usually.But the affiliation that adds of fire retardant causes the decline of gathering of PS/ABS alloy material notched Izod impact strength, need improve the toughness of material.
Summary of the invention
Technical problem to be solved by this invention provides a kind of PC/ABS alloy material of high tenacity.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of PC/ABS alloy material of high tenacity is characterized in that, comprises the material of following parts by weight: PC40-50 part, ABS60-80 part, halogen-free expansion fire retardant 10-20 part, ethylene copolymer elastomerics 10-15 part, nano-calcium carbonate 10-13 part, ethylene-propylene hydrochlorate 12-15 part, the silica-based dimethyl methyl phosphonate 1-5 of front three part, melamine cyanurate 2-8 part, molybdic oxide 5-8 part, ammonium polyphosphate 2-8 part, stearic acid 1-2 part, stearate 1-5 part, stearylamide 1-3 part, 1 part of silicone oil, 2 parts of the brilliant ore deposit of tourmalinite micro mists, poly--4-methyl-1-pentene 1-2 part, 5 parts of Calcium of intensifiens, 6 parts of stearic acid, processing stabilizers 2-9 part, lubricant 3-5 part.
The invention has the beneficial effects as follows: can effectively improve the notched Izod impact strength of fire retardation PC/ABS material, drawing high tenacity fire retardation PC/ABS alloy material, thereby make this material more be adapted to each hi-tech manufacturing, have considerable economic.
Embodiment
Embodiment 1
A kind of PC/ABS alloy material of high tenacity is characterized in that, comprises the material of following parts by weight: PC40-50 part, ABS60-80 part, halogen-free expansion fire retardant 10-20 part, ethylene copolymer elastomerics 10-15 part, nano-calcium carbonate 10-13 part, ethylene-propylene hydrochlorate 12-15 part, the silica-based dimethyl methyl phosphonate 1-5 of front three part, melamine cyanurate 2-8 part, molybdic oxide 5-8 part, ammonium polyphosphate 2-8 part, stearic acid 1-2 part, stearate 1-5 part, stearylamide 1-3 part, 1 part of silicone oil, 2 parts of the brilliant ore deposit of tourmalinite micro mists, poly--4-methyl-1-pentene 1-2 part, 5 parts of Calcium of intensifiens, 6 parts of stearic acid, processing stabilizers 2-9 part, lubricant 3-5 part.
Claims (1)
1. the PC/ABS alloy material of a high tenacity is characterized in that, comprises the material of following parts by weight: PC40-50 part, ABS60-80 part, halogen-free expansion fire retardant 10-20 part, ethylene copolymer elastomerics 10-15 part, nano-calcium carbonate 10-13 part, ethylene-propylene hydrochlorate 12-15 part, the silica-based dimethyl methyl phosphonate 1-5 of front three part, melamine cyanurate 2-8 part, molybdic oxide 5-8 part, ammonium polyphosphate 2-8 part, stearic acid 1-2 part, stearate 1-5 part, stearylamide 1-3 part, 1 part of silicone oil, 2 parts of the brilliant ore deposit of tourmalinite micro mists, poly--4-methyl-1-pentene 1-2 part, 5 parts of Calcium of intensifiens, 6 parts of stearic acid, processing stabilizers 2-9 part, lubricant 3-5 part.