CN103214967A - Chromium and phosphorus-free strong sealing treatment agent used universally in cold rolled coils, galvanized and aluminum-zinc coated coil steel and its preparation method - Google Patents
Chromium and phosphorus-free strong sealing treatment agent used universally in cold rolled coils, galvanized and aluminum-zinc coated coil steel and its preparation method Download PDFInfo
- Publication number
- CN103214967A CN103214967A CN2013100874010A CN201310087401A CN103214967A CN 103214967 A CN103214967 A CN 103214967A CN 2013100874010 A CN2013100874010 A CN 2013100874010A CN 201310087401 A CN201310087401 A CN 201310087401A CN 103214967 A CN103214967 A CN 103214967A
- Authority
- CN
- China
- Prior art keywords
- water
- treatment agent
- sealing treatment
- phosphorus
- aluminum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a chromium and phosphorus-free strong sealing treatment agent used universally in cold rolled coils, galvanized and aluminum-zinc coated coil steel. The strong sealing treatment agent is prepared from the following raw materials: water-based polyhydroxy fluorocarbon resin, a water-based double-claw silane coupling agent BTMSE, gamma-aminopropyl trimethoxy silane, nano-titanium oxide, a scale inhibition dispersing agent water-soluble sodium lignosulphonate, a metal chelating agent citric acid monohydrate, a corrosion inhibitor borax, an organic silicon defoamer, and deionized water with conductivity less than or equal to 10 us/cm. Being free of chromium, phosphorus and other ions harmful to the environment, the sealing treatment agent provided in the invention can generate a three-dimensional network molecular bond structure on surfaces of cold rolled, galvanized and aluminum-zinc coated coiled materials, so that the sealing membrane layer gains better corrosion resistance, weather resistance, coating performance and conductivity than sealing membrane layers containing chromate and phosphate.
Description
Technical field
The invention belongs to the surperficial encapsulant field of coil, relate in particular to the low-cost surperficial encapsulant of a kind of environmental protection and energy saving that are common to the various material coil, definite a kind of powerful sealing treatment agent that does not contain chromium, phosphorus that is common to cold rolling coil, zinc-plated, aluminum-zinc alloy coil of saying so.
Background technology
EU Committee in 2003 and European Parliament have issued the instruction (RoHS) that limits some objectionable impurities of use in (WEEE) and the electronic and electrical equipment that batch make at the electronic and electrical equipment waste, " RoHS instruction " and " WEEE instruction " clearly stipulated the use restriction of various objectionable impuritiess, wherein more clearly stipulated in all production processes and the electrical and electronic product that may contain above-mentioned six kinds of objectionable impuritiess in the starting material, mainly comprise: white household electrical appliances, as refrigerator, washing machine, microwave oven, air-conditioning, suction cleaner, water-heater etc.; Black household electrical appliances, as audio frequency, video product, DVD, CD, television set, IT product, digital product, restriction is used in the strictness of the heavy metal chromium in the communication products etc.The said products major part is the main exit electric equipment products of China.It is the erosion shield of making the said products base material of the solution of sexavalence chromic acid, chromic salts the most widely that the said products uses chromium.Because of the good solidity to corrosion and the low cost of chromic acid chromium salts solution, China most of base material factory is that coil factory adopts this kind solution, although technology may be different.
Under this background, product with organic resin, phosphoric acid salt solution substitute chromium solution has appearred on the market, this series products is introduced to the market, satisfied the products export demand fast, but in recent years along with the lake, various places exceeds standard because of the phosphorus nitrogen content, the serious eutrophy in closed system waters causes the pollution of many ground Freshwater resources, and country is limiting phosphatic use gradually.
Summary of the invention
The objective of the invention is to be to propose a kind of powerful sealing treatment agent that does not contain chromium, phosphorus that is common to cold rolling coil, zinc-plated, aluminum-zinc alloy coil.
The present invention adopts following technical scheme to achieve these goals:
A kind of powerful sealing treatment agent that does not contain chromium, phosphorus that is common to cold rolling coil, zinc-plated, aluminum-zinc alloy coil is characterized in that,
It is to be made by the following weight proportion raw material for the described powerful sealing treatment agent of every 1Kg:
1. water-based poly-hydroxy fluorocarbon resin: 50-75g;
2. two pawl silane coupling agent BTMSE:4-10g of water-based;
3. γ-An Bingjisanjiayangjiguiwan: 20-50g;
4. nano titanium oxide: 100-150g;
5. the water-soluble sodium lignosulfonate of dirt dispersion agent: 10-20g;
6. metal-chelate mixture Citric acid monohydrate Food grade: 5-15g;
7. inhibiter borax: 5-10g;
8. silicone antifoam agent: 1-5g;
9. surplus is a deionized water.
Described a kind of powerful sealing treatment agent that does not contain chromium, phosphorus that is common to cold rolling coil, zinc-plated, aluminum-zinc alloy coil, it is characterized in that: described deionized water is the deionized water of specific conductivity≤10 μ S/cm
The described preparation method who is common to the powerful sealing treatment agent that does not contain chromium, phosphorus of cold rolling coil, zinc-plated, aluminum-zinc alloy coil is characterized in that:
May further comprise the steps:
(1), preparation dispersion liquid:
By weight ratio, add appropriate amount of deionized water, in the vertical response still of band high speed shear dispersion machine, open and stir, get nano titanium oxide, the water-soluble sodium lignosulfonate of dirt dispersion agent, silicone antifoam agent more by weight ratio respectively, with the 900-1100r/min rotating speed, the normal temperature state stirred 3.5-4.5 hour down, leave standstill, it is standby promptly to get dispersion liquid;
(2), prepare rare resin liquid:
Water intaking property poly-hydroxy fluorocarbon resin adds appropriate amount of deionized water by weight ratio, puts into stirrer, and with the 55-65r/min rotating speed, the normal temperature state stirs after 1-1.5 hour down, and it is standby promptly to get rare resin liquid;
(3), preparation modified resin liquid:
With the two pawl silane coupling agent BTMSE of rare resin liquid and water-based, water-based aminosilane mixing by weight ratio, under 65-75 ℃ with the 120-150r/min tachyphylaxis after 1-2 hour, cooling, it is standby promptly to get modified resin liquid;
(4), preparation hydridization liquid:
In empty reactor, add appropriate amount of deionized water, normal temperature, open to stir with the 120-150r/min rotating speed, add the made modified resin liquid of step (3), the made dispersion liquid of step (1) and all the other raw materials successively by weight ratio, mix and stir after 0.8-1.2 hour promptly.
The described preparation method who is common to the powerful sealing treatment agent that does not contain chromium, phosphorus of cold rolling coil, zinc-plated, aluminum-zinc alloy coil is characterized in that:
Contain dispersion liquid 500-600g in the described powerful sealing treatment agent of every Kg.
The described preparation method who is common to the powerful sealing treatment agent that does not contain chromium, phosphorus of cold rolling coil, zinc-plated, aluminum-zinc alloy coil is characterized in that:
Contain rare resin liquid 400-500g in the described powerful sealing treatment agent of every Kg.
The described preparation method who is common to the powerful sealing treatment agent that does not contain chromium, phosphorus of cold rolling coil, zinc-plated, aluminum-zinc alloy coil, it is characterized in that: described dispersion particle size is about 10-20nm.
Principle of the present invention is:
Described encapsulant is the organic inorganic hybridization dispersion liquid, and the invention by following record realizes:
This encapsulant membrane formation mechanism:
(1) in medicament, add normal low-temperature bake type polymer waterborne resin, behind overbaking, the water-base resin volatilization, the TiO2 that forms continuous densification in the metallic surface intercepts epithelium, and resin emulsion plays bridging action between the TiO2 particulate, and fixing TiO2 has improved the water tolerance of film.As shown in Figure 1.
The silane coupling agent that adds in medicament on the other hand has different chemical functional group, through hydrolysis, polycondensation, dehydration reaction, generate covalent linkage in one end and functional group and the macromolecule resin, an end becomes covalent linkage ≡ Si-OH+HO-Me → ≡ Si-O-Me+H with the hydroxyl reaction on inorganic metal surface
2O combines the very big material of nature difference, has improved the water tolerance and the secondary application sticking power of film.As shown in Figure 2.
(2) this encapsulant principal character: contain A, a kind of water-soluble fluorine carbon resin, B, the two pawl silane coupling agents of a kind of water-based, a kind of silane coupling agent with high reaction activity, C, a kind of water-soluble ultra-fine micropowder, D, a kind of dispersing and antisludging agent, E, a metal ion species intercalating agent, F, a kind of inhibiter, G, a kind of defoamer H, deionized water.The PH of masking liquid is 7~9.
1. above-mentioned (1) described a kind of water-soluble fluorine carbon resin, preferably water dissolubility poly-hydroxy fluorocarbon resin, reason is: the bond energy of fluorine carbon bond is maximum in the organic compound, so the corrosion prevention film based on fluorine carbon has good physical and chemical stability, have characteristics such as chemically stable that other resin can't replace, resistant, heatproof, perviousness, UV resistant.Under the effect of good penetration, become continuous dead front type coating in the coil surface adhesion, understand of the erosion of environmental corrosion media such as effective block water molecule, O2 molecule, thereby show good anticorrosion ability metal under the film.And various countries are to the increasingly stringent of VOC content restriction, and the water-based fluorocarbon resin does not contain VOC, environment friendly and pollution-free.And the contriver considers the construction and the membrane formation mechanism of whole formula system, with the molecular chain action of other organic or inorganic storerooms, poly-hydroxy water-based fluorocarbon resin can provide more hydroxyl, and form better molecule bonding force between other inorganic or organic coupling agents, can improve sticking power greatly.
2. the two pawl silane coupling agents of above-mentioned (1) described a kind of water-based, preferred BTMSE, promptly 1, the two (trimethoxies of 2-
3. a kind of high reaction activity silane, preferred water-based aminosilane, i.e. γ-An Bingjisanjiayangjiguiwan.More preferably from the A-1100 of U.S.'s union carbide corporation.
General silane has shown remarkable effect at inorganic material surfaces such as tripoli, but when at the metallized metal substrate surface, is that effect or glutinous sticking trend all reduce greatly.And two pawl silane have two hydrolysising groups, can improve greatly with inorganic metal surface hydroxyl covalent linkage and form density, improve the glutinous viscosity with inorganic materials.And the water-based aminosilane, amino organic group has high reaction activity and high, and easy and organic polymer resin forms lasting firm chemical bond fast.So add a spot of pair of pawl silane in the water-based aminosilane, the two is combined in can erect the molecule bridge of strong, durable more between organic resin and the inorganic metal base material.
4. above-mentioned (1) described a kind of ultra-fine micropowder.Preferred nano titanium oxide.Titanium dioxide has excellent chemical stability, thermostability, nontoxicity nanometer, and TiO2 has very strong " Superhydrophilic ", is difficult for forming the globule on its surface, has to intercept water tolerance preferably.
5. above-mentioned (1) described a kind of dirt dispersion agent.Preferably water dissolubility sodium lignosulfonate.Sodium lignosulfonate is a kind of natural polymers, has very strong dispersiveness, because
Molecular weightWith
Functional groupDifference and have in various degree dispersiveness, it is a kind of surfactant, can be adsorbed on the surface of various solid particles, can carry out the metal ion exchanged effect, also because have various active groups on its weave construction, thereby can produce condensation or with other compound generation hydrogen bond actions, have scale inhibition and dispersion preferably.
6. above-mentioned (1) described a kind of metal ion chelation agent.Preferred Citric acid monohydrate Food grade.Citric acid monohydrate Food grade has the ability of iron, calcium, magnesium ion in the stronger huge legendary turtle Heshui, and with low cost, environment-protecting asepsis.
7. above-mentioned (1) described a kind of inhibiter.Preferred inorganic inhibitor Sodium Tetraborate.Sodium Tetraborate has strong corrosion inhibition to carbon steel and zinc-plated material in neutrality or weakly alkaline solution system, and to human body and environmentally friendly, and with low cost.
8. above-mentioned (1) described a kind of defoamer.Preferred silicone antifoam agent.Silicone antifoam agent has under the less situation of consumption, but has outstanding antifoam performance, and heat-resisting, cold-resistant, weather-proof and ageing-resistant performance is given prominence to, and nontoxic, pollution-free, and so environmental sound is preferred.
9. above-mentioned (1) described a kind of deionized water.Preferred deionized water specific conductivity≤10 μ S/cm.Because this encapsulant mainly designs on automatic production line and uses, the cleanliness factor of having relatively high expectations, and satisfy the requirement for anticorrosion of the coiled material of very fast streamline (100m/min), so the inventor is through experiment, find that selected encapsulant carrier institute water need select deionized water for use, and specific conductivity palpus≤10 μ S/cm.
Beneficial effect of the present invention is: though encapsulant of the present invention does not contain chromium, phosphorus etc. to the environment harmful ion, but the three-dimensional netted molecular bonding structure that can produce on coiled materials such as cold rolling, zinc-plated, aluminum-zinc alloy surface makes that sealing rete ratio contains chromic salt, phosphatic sealing rete has more solidity to corrosion, weathering resistance, coating, electroconductibility.Rare resin liquid and the two pawl silane coupling agent BTMSE of water-based, water-based aminosilane are reacted, resin have been carried out modification,
Increased the film forming properties of resin.
Description of drawings
Fig. 1 is a membrane formation mechanism synoptic diagram of the present invention;
Fig. 2 erects the synoptic diagram of molecule bridge between organic resin and inorganic substrate for silane coupling agent;
Fig. 3 is an embodiment 1-3 surface white rust area result schematic diagram behind 96 hours neutral salt spray test NSS;
Fig. 4 is anti-ethanol of substrate and MEK wiping result schematic diagram after handling through embodiment 1-3;
Fig. 5 is the substrate after handling through embodiment 1-3, appearance results synoptic diagram behind the poach;
Fig. 6 is the substrate after handling through embodiment 1-3, and through table 2 technological process, flat board is drawn hundred lattice experimental result pictures;
Fig. 7 is for the substrate after handling through embodiment 1-3, and through table 2 technological process, poach is drawn hundred lattice experimental result pictures after 1 hour;
Fig. 8, impacts the back and draws hundred lattice experimental result pictures through table 2 technological process for the substrate after handling through embodiment 1-3;
Fig. 9 through table 2 technological process, toasts 30min, appearance results synoptic diagram under the 200 degree temperature for the substrate after handling through embodiment 1-3.
Embodiment
Prepare the present invention by the method for being prepared as follows, with the deionized water preparation of specific conductivity≤10 μ S/cm, made encapsulant such as table 1 under the each component different amounts situation make embodiment 1, embodiment 2, embodiment 3: may further comprise the steps:
(1), preparation dispersion liquid:
By weight ratio, add appropriate amount of deionized water, in the vertical response still of band high speed shear dispersion machine, open and stir, get nano titanium oxide, the water-soluble sodium lignosulfonate of dirt dispersion agent, silicone antifoam agent more by weight ratio respectively, with the 1000r/min rotating speed, the normal temperature state stirred 4 hours down, leave standstill, it is standby promptly to get dispersion liquid;
(2), prepare rare resin liquid:
Water intaking property poly-hydroxy fluorocarbon resin adds appropriate amount of deionized water by weight ratio, puts into stirrer, and with the 60r/min rotating speed, the normal temperature state stirs after 1 hour down, and it is standby promptly to get rare resin liquid;
(3), preparation modified resin liquid:
With the two pawl silane coupling agent BTMSE of rare resin liquid and water-based, water-based aminosilane mixing by weight ratio, under 70 ℃ with the 150r/min tachyphylaxis after 1-2 hour, cooling, it is standby promptly to get modified resin liquid;
(4), preparation hydridization liquid:
Add appropriate amount of deionized water in empty reactor, normal temperature open to stir with the 120r/min rotating speed, adds the made modified resin liquid of step (3), the made dispersion liquid of step (1) and all the other raw materials successively by weight ratio, mixes and stirs after 1 hour promptly.
Table 1
The encapsulant that the various embodiments described above are made is coated in respectively on the substrate under shearing from cold rolling roll bending, zinc-plated roll bending, aluminum-zinc alloy roll bending by the technical process of table 2.
Table 2
Step | Process | Chemical substance | Temperature | Time | ? |
1 | Pre-degreasing is scrubbed | The green LT-901R of the company grease-removing agent of opening up | 60℃ | 1min | ? |
2 | Main degreasing is scrubbed | The green LT-901R of the company grease-removing agent of opening up | 60℃ | 1min | ? |
3 | Washing is scrubbed | Tap water | Normal temperature | 10S | ? |
4 | Pure water is scrubbed | Specific conductivity≤10 μ S/cm | Normal temperature | 10S | ? |
5 | Pure water is washed rinsing | Specific conductivity≤10 μ S/cm | Normal temperature | 10S | ? |
6 | The roller coat encapsulant | Table 1 embodiment 1-3 | Normal temperature | 10S | ? |
7 | Oven dry | ? | 120℃ | 10S | ? |
8 | Cooling | ? | Air-cooled | 10S | ? |
9 | Primary coat+curing+air-cooled | Priming paint | 200℃ | 20S | ? |
10 | Face is coated with+solidifies+and air-cooled | The polyester lacquer | 200℃ | 20S | ? |
To assessing following necessary performance through sheet material and encapsulant after table 2 flow processing:
(1) thickness
Detect the content of silicon, titanium in the rete by XRF and calculate thickness.
Standard should be: the 0.7-0.9 micron.
(2) erosion resistance
The white rust area (%) of neutral salt spray test NSS:96 hour postevaluation planar portions.
Standard should be: be no more than 5% for qualified.
(3) solvent resistance
Use ethanol (80%) and MEK to carry out 30 frictions, see and look into the epithelium appearance change, and divide 5 grade evaluations.(excellent) 5>4>3>2>1(is bad)
Standard should be: 5 for optimum, the outward appearance no change
(4) anti-blackening
Substrate after handling was boiled in boiling water 1 hour, observe the black change situation at steam position.
Standard should be: after boiling water boiled 1 hour, the surface did not have the blackout phenomenon
(5) painting adhesion
Behind the spraying polyester powder paint (about thickness 50 μ m, PMT200 ℃)
(a) sticking power detects: dull and stereotyped cross cut test, use the adhesive tape sticking surface with special, and see the paint flake situation.
Standard should be: do not have and peel off
(b) secondary sticking power detects: the substrate after the spraying boils in boiling water after 1 hour and draws lattice.
Standard should be: do not have and peel off
(c) impact+draw lattice: heavy burden 500g, diameter is the drift of 4mm, highly falls from 50cm, draws the lattice experiment in impact place.Standard should be: do not have cracking, do not have and peel off
(6) ovenable roasting property: toast 30min under the 200 degree temperature, appearance change before and after observing, and detect value of chromatism △ E.Standard should be: △ E≤2.0
(7) electroconductibility
Under certain conditions (bear a heavy burden and press: 2N/ ㎜ 2, voltage: 0.5V), with Instrument measuring strength of current I(A).By calculating interlamination resistance value R(Ω).Resistance value R(Ω)=U(voltage, 0.5V)/I(strength of current A).Standard should be: R≤1 Ω cm-2
Embodiment 1,2,3 is carried out following assessment, and the assessment content sees Table 3:
Table 3
Press as above evaluation item, the substrate assessment result after handling through embodiment 1,2,3 is as follows:
Embodiment 1-3 surface white rust area all is lower than 5% behind 96 hours neutral salt spray test NSS, as shown in Figure 3.
Through anti-ethanol of substrate and MEK wiping excellence after the embodiment 1-3 processing, vestige is not almost seen on the surface, 5 minutes.As shown in Figure 4.
Through the substrate after the embodiment 1-3 processing, outward appearance no change behind the poach, anti-blackening can be excellent.As shown in Figure 5.
Through the substrate after the embodiment 1-3 processing, through table 2 technological process, dull and stereotyped hundred lattice of drawing, nothing is peeled off, and one time sticking power is good.As shown in Figure 6.
Through the substrate after the embodiment 1-3 processing, through table 2 technological process, poach is drawn hundred lattice after 1 hour, and nothing is peeled off, and secondary sticking power is good.As shown in Figure 7.
Through the substrate after the embodiment 1-3 processing, through table 2 technological process, to impact the back and draw hundred lattice, nothing is peeled off.As shown in Figure 8.
Through the substrate after the embodiment 1-3 processing, through table 2 technological process, toast 30min under the 200 degree temperature, outward appearance does not have any variable color, as shown in Figure 9.
As seen from the above, Chrome-free of the present invention, without phosphorus powerful encapsulant are common on cold rolling, zinc-plated, the aluminum-zinc alloy coiled material, all have good solidity to corrosion, coating, electroconductibility.
Claims (6)
1. a powerful sealing treatment agent that does not contain chromium, phosphorus that is common to cold rolling coil, zinc-plated, aluminum-zinc alloy coil is characterized in that,
It is to be made by the following weight proportion raw material for the described powerful sealing treatment agent of every 1Kg:
1. water-based poly-hydroxy fluorocarbon resin: 50-75g;
2. two pawl silane coupling agent BTMSE:4-10g of water-based;
3. γ-An Bingjisanjiayangjiguiwan: 20-50g;
4. nano titanium oxide: 100-150g;
5. the water-soluble sodium lignosulfonate of dirt dispersion agent: 10-20 g;
6. metal-chelate mixture Citric acid monohydrate Food grade: 5-15g;
7. inhibiter borax: 5-10g;
8. silicone antifoam agent: 1-5g;
9. surplus is a deionized water.
2. a kind of powerful sealing treatment agent that does not contain chromium, phosphorus that is common to cold rolling coil, zinc-plated, aluminum-zinc alloy coil according to claim 1, it is characterized in that: described deionized water is the deionized water of specific conductivity≤10 μ S/cm.
3. preparation method who is common to the powerful sealing treatment agent that does not contain chromium, phosphorus of cold rolling coil, zinc-plated, aluminum-zinc alloy coil as claimed in claim 1 is characterized in that:
May further comprise the steps:
(1), preparation dispersion liquid:
By weight ratio, add appropriate amount of deionized water, in the vertical response still of band high speed shear dispersion machine, open and stir, get nano titanium oxide, the water-soluble sodium lignosulfonate of dirt dispersion agent, silicone antifoam agent more by weight ratio respectively, with the 900-1100r/min rotating speed, the normal temperature state stirred 3.5-4.5 hour down, leave standstill, it is standby promptly to get dispersion liquid;
(2), prepare rare resin liquid:
Water intaking property poly-hydroxy fluorocarbon resin adds appropriate amount of deionized water by weight ratio, puts into stirrer, and with the 55-65r/min rotating speed, the normal temperature state stirs after 1-1.5 hour down, and it is standby promptly to get rare resin liquid;
(3), preparation modified resin liquid:
With the two pawl silane coupling agent BTMSE of rare resin liquid and water-based, water-based aminosilane mixing by weight ratio, under 65-75 ℃ with 120-150 r/min tachyphylaxises after 1-2 hour, cooling, it is standby promptly to get modified resin liquid;
(4), preparation hydridization liquid:
In empty reactor, add appropriate amount of deionized water, normal temperature, open to stir with 120-150 r/min rotating speeds, add the made modified resin liquid of step (3), the made dispersion liquid of step (1) and all the other raw materials successively by weight ratio, mix and stir after 0.8-1.2 hour promptly.
4. the preparation method who is common to the powerful sealing treatment agent that does not contain chromium, phosphorus of cold rolling coil, zinc-plated, aluminum-zinc alloy coil according to claim 3 is characterized in that:
Contain dispersion liquid 500-600g in the described powerful sealing treatment agent of every Kg.
5. the preparation method who is common to the powerful sealing treatment agent that does not contain chromium, phosphorus of cold rolling coil, zinc-plated, aluminum-zinc alloy coil according to claim 3 is characterized in that:
Contain rare resin liquid 400-500g in the described powerful sealing treatment agent of every Kg.
6. the preparation method who is common to the powerful sealing treatment agent that does not contain chromium, phosphorus of cold rolling coil, zinc-plated, aluminum-zinc alloy coil according to claim 3, it is characterized in that: described dispersion particle size is about 10-20nm.