CN103199244A - Negative plate ead paste of lead-acid battery and preparation method of negative lead paste - Google Patents
Negative plate ead paste of lead-acid battery and preparation method of negative lead paste Download PDFInfo
- Publication number
- CN103199244A CN103199244A CN2013101469341A CN201310146934A CN103199244A CN 103199244 A CN103199244 A CN 103199244A CN 2013101469341 A CN2013101469341 A CN 2013101469341A CN 201310146934 A CN201310146934 A CN 201310146934A CN 103199244 A CN103199244 A CN 103199244A
- Authority
- CN
- China
- Prior art keywords
- lead
- paste
- polyaniline
- lignin
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses negative plate lead paste of a lead-acid battery. The negative plate lead paste comprises the following components in parts by weight: 9% to 11% of deionized water, 7% to 10% of sulfuric acid solution with the mass percentage concentration of 50%, 0.06% to 0.09% of fibers, 1% to 3% of barium sulfate, 0.05% to 0.3% of lignin, 0.5% to 2% of polyaniline, and the balance of lead powder. According to the invention, the novel conductive agent polyaniline is added into the lead paste so as to greatly improve the conductivity of the lead-acid battery, reduce the internal resistance of the battery, improve the utilization rate of active matters, improve the uniformity of the battery and prolong the service life of the battery pack by 15%.
Description
Technical field
The present invention relates to lead acid accumulator production field, be specifically related to a kind of lead-acid accumulator negative pole lead paste and preparation method thereof.
Background technology
Lead Acid Battery Used for Electric Vehicle is the battery that a kind of high magnification recycles at present, and designing requirement is reasonable, and process control is strict.For high-quality power type accumulator battery, require depth of discharge to want dark, cycle life will be grown, and common manufacture method is difficult to realize.Low, the problems such as negative electrode active material easily comes off, sulfation of electric vehicle power lead acid battery ubiquity active material utilization cause the consistency of motive-power battery Battery pack poor, and the life-span of battery pack is short.
Summary of the invention
The technical problem to be solved in the present invention provides a kind of lead-acid accumulator negative pole lead paste and preparation method thereof, and it is poor that this component lead plaster can effectively solve existing motive-power battery group consistency, the problem that the life-span is short.
The present invention is achieved through the following technical solutions:
A kind of lead-acid accumulator negative pole lead paste, comprise following parts by weight of component: deionized water 9~11%, mass percent concentration 50% sulfuric acid solution 7~10%, fiber 0.06~0.09%, barium sulfate 1~3%, lignin 0.05~0.3%, polyaniline 0.5~2%, all the other are lead powder.
Preferably, comprise following parts by weight of component: deionized water 9%, mass percent concentration 50% sulfuric acid solution 7%, fiber 0.06%, barium sulfate 1%, lignin 0.05%, polyaniline 0.5%, all the other are lead powder, reach most economical cathode lead plaster prescription.
Preferably, comprise following parts by weight of component: deionized water 11%, mass percent concentration 50% sulfuric acid solution 8%, fiber 0.07%, barium sulfate 2%, lignin 0.25%, polyaniline 1%, all the other are lead powder, reach the cathode lead plaster prescription of optimality price ratio.
Preferably, comprise following parts by weight of component: deionized water 10%, mass percent concentration 50% sulfuric acid solution 8%, fiber 0.05%, barium sulfate 3%, lignin 0.3%, polyaniline 2%, all the other are lead powder, reach the cathode lead plaster prescription of optimum performance.
The further improvement project of the present invention is that the oxidizability of described lead powder is 72~78%.
A kind of preparation method of lead-acid accumulator negative pole lead paste may further comprise the steps, by the described parts by weight of component of claim 1,
The first, with fiber, lignin, barium sulfate, polyaniline and lead powder, put into paste mixing machine, stirred 5 ~ 10 minutes, make it even;
The second, add deionized water, stirred 5 ~ 8 minutes;
The 3rd, add sulfuric acid, stirred 16 ~ 19 minutes, survey apparent density, control density 4.4~4.6% is made lead plaster.
The present invention compared with prior art has following obvious advantage:
Conductive agent in present many producers cathode lead plaster prescription is acetylene black, and used the novel conductive agent polyaniline among the present invention, after adding polyaniline in the battery lead plaster, significantly improve the conductivity of battery, can reduce the internal resistance of cell, improve active material utilization, improve the consistency of battery, the life-span of battery pack prolongs 15%.
Embodiment
Embodiment one
A kind of lead-acid accumulator negative pole lead paste comprises following parts by weight of component: deionized water 9%, and mass percent concentration 50% sulfuric acid solution 7%, fiber 0.06%, barium sulfate 1%, lignin 0.05%, polyaniline 0.5%, all the other are lead powder.
Embodiment two
A kind of lead-acid accumulator negative pole lead paste comprises following parts by weight of component: deionized water 10%, and mass percent concentration 50% sulfuric acid solution 8%, fiber 0.05%, barium sulfate 3%, lignin 0.3%, polyaniline 1%, all the other are lead powder.
Embodiment three
A kind of lead-acid accumulator negative pole lead paste comprises following parts by weight of component: deionized water 11%, and mass percent concentration 50% sulfuric acid solution 8%, fiber 0.07%, barium sulfate 2%, lignin 0.25%, polyaniline 2%, all the other are lead powder.
Above-mentioned three embodiment by weight component just fiber, lignin, polyaniline and lead powder weigh, put into paste mixing machine and stir, stirred 5 ~ 10 minutes, make it even; Add the deionized water in the formula ratio again, stirred 5 ~ 8 minutes; Add sulfuric acid and barium sulfate in the formula ratio then, stirred 16 ~ 19 minutes, survey apparent density at last, control density 4.4~4.6%, lead plaster has just completed.
Claims (6)
1. lead-acid accumulator negative pole lead paste, it is characterized in that, comprise following parts by weight of component: deionized water 9~11%, mass percent concentration 50% sulfuric acid solution 7~10%, fiber 0.06~0.09%, barium sulfate 1~3%, lignin 0.05~0.3%, polyaniline 0.5~2%, all the other are lead powder.
2. a kind of lead-acid accumulator negative pole lead paste according to claim 1 is characterized in that: comprise following parts by weight of component: deionized water 9%, mass percent concentration 50% sulfuric acid solution 7%, fiber 0.06%, barium sulfate 1%, lignin 0.05%, polyaniline 0.5%, all the other are lead powder.
3. a kind of lead-acid accumulator negative pole lead paste according to claim 1 is characterized in that: comprise following parts by weight of component: deionized water 11%, mass percent concentration 50% sulfuric acid solution 8%, fiber 0.07%, barium sulfate 2%, lignin 0.25%, polyaniline 1%, all the other are lead powder.
4. a kind of lead-acid accumulator negative pole lead paste according to claim 1 is characterized in that: comprise following parts by weight of component: deionized water 10%, mass percent concentration 50% sulfuric acid solution 8%, fiber 0.05%, barium sulfate 3%, lignin 0.3%, polyaniline 2%, all the other are lead powder.
5. according to each described a kind of lead-acid accumulator negative pole lead paste of claim 1 to 4, it is characterized in that: the oxidizability of described lead powder is 72~78%.
6. the preparation method of a lead-acid accumulator negative pole lead paste is characterized in that: may further comprise the steps, and by the described parts by weight of component of claim 1,
The first, with fiber, lignin, polyaniline, barium sulfate and lead powder, put into paste mixing machine, stirred 5 ~ 10 minutes, make it even;
The second, add deionized water, stirred 5 ~ 8 minutes;
The 3rd, add sulfuric acid, stirred 16 ~ 19 minutes, survey apparent density, control density 4.4~4.6% is made lead plaster.