CN103183976B - Preparation raw material for automobile shell depression repair material and use method thereof - Google Patents
Preparation raw material for automobile shell depression repair material and use method thereof Download PDFInfo
- Publication number
- CN103183976B CN103183976B CN201310110385.2A CN201310110385A CN103183976B CN 103183976 B CN103183976 B CN 103183976B CN 201310110385 A CN201310110385 A CN 201310110385A CN 103183976 B CN103183976 B CN 103183976B
- Authority
- CN
- China
- Prior art keywords
- thin iron
- iron powder
- purpose adhesive
- raw material
- automobile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a preparation raw material for an automobile shell depression repair material and a use method thereof, which are characterized in that the raw material comprises an all-purpose adhesive fine iron powder mixture, a varnish fine iron powder mixture and repair putty; and the use method comprises the following steps: mixing an all-purpose adhesive with fine iron power, agitating into thin paste, coating at a depression with a hairbrush, mixing varnish for an automobile with fine iron power, agitating into dry paste, coating on a coating of an all-purpose adhesive and fine iron powder mixing material with the hairbrush till the depression is basically filled, and polishing and leveling with the automobile repair putty. Through the arrangement, the material has the beneficial effects that the automobile shell depression is stable to repair and is not easy to chap, an automobile shell can not be damaged during the repair, and the material is easy to take and is economic and practical.
Description
Technical field
The present invention relates to a kind of preparation raw material and using method thereof of repairing car housing depressions matrix material.
Background technology
Automobile in use, there is little collision in capital, automobile case is caused to cave in, the common method of existing repairing car shell dolly dimple is: first electricity consumption is welded in recess and burn-ons draw ring, pull draw ring with instrument, sunk part is pulled out, then draw ring is removed, after rear repairing putty of polishing is levelling, oven dry of spraying paint.When this method for repairing and mending defect is welding draw ring, easily automobile case is caused broken hole, by the antirust treatment damage layer of automobile case during polishing, mend uses for some time because of corrosion, Alligatoring, comes off.
Summary of the invention
The object of this invention is to provide preparation raw material and the using method thereof of a kind of automobile case depression patching material.
To achieve these goals, this raw material of the present invention comprises the thin iron mixture of multi-purpose adhesive, the thin iron mixture of varnish and repairing putty, the thin iron mixture of described multi-purpose adhesive is made up of multi-purpose adhesive 5-6 part and thin iron powder 4-5 part, the thin iron mixture of described varnish is by vapour automotive clear coats 6-7 part, and thin iron powder 3-4 part forms.Using method is multi-purpose adhesive 5-6 part, thin iron powder 4-5 part, be mixed into scattered paste shape, be coated in recess with hairbrush, vapour automotive clear coats 6-7 part, thin iron powder 3-4 part, be mixed into dry pasty state, be coated in hairbrush in the coating of multi-purpose adhesive and iron powder mixing material, until recess is filled and led up substantially, to be coated dry after polish, then use the polishing of car repair putty levelling.
By above setting, material of the present invention is repaired firmly automobile case depression, and not easily chap, can not cause damage during repairing to automobile case, the present invention draws materials easily, economical and practical.
Embodiment
This raw material of the present invention comprises the thin iron mixture of multi-purpose adhesive, the thin iron mixture of varnish and repairing putty, the thin iron mixture of described multi-purpose adhesive is made up of multi-purpose adhesive 5-6 part and thin iron powder 4-5 part, the thin iron mixture of described varnish is by vapour automotive clear coats 6-7 part, and thin iron powder 3-4 part forms.First with clear water, automobile case recess is cleaned, dries, free from dust impurity; Multi-purpose adhesive 5-6 part, thin iron powder 4-5 part, is mixed into scattered paste shape, is coated in recess with hairbrush, is coated with one time again after dry; Vapour automotive clear coats 6-7 part, thin iron powder 3-4 part, is mixed into dry pasty state, be coated in hairbrush in the coating of multi-purpose adhesive and iron powder mixing material, after drying, be coated with one deck again, until recess is filled and led up substantially, to be coated dry after polish, then use the polishing of car repair putty levelling; Finally carry out spraying with the automobile finish of suitable color.
Claims (2)
1. the preparation raw material of automobile case depression patching material, it is characterized in that: this raw material comprises the thin iron mixture of multi-purpose adhesive, the thin iron mixture of varnish and repairing putty, the thin iron mixture of described multi-purpose adhesive is made up of multi-purpose adhesive 5-6 part and thin iron powder 4-5 part, the thin iron mixture of described varnish is by vapour automotive clear coats 6-7 part, and thin iron powder 3-4 part forms.
2. the using method of automobile case depression patching material, it is characterized in that: multi-purpose adhesive 5-6 part, thin iron powder 4-5 part, is mixed into scattered paste shape, recess is coated in hairbrush, vapour automotive clear coats 6-7 part, thin iron powder 3-4 part, is mixed into dry pasty state, be coated in the coating of multi-purpose adhesive and iron powder mixing material with hairbrush, until recess is filled and led up substantially, to be coated dry after polish, then use the polishing of car repair putty levelling.