CN103183167A - Manufacture technology of activated carbon inner container bottle - Google Patents
Manufacture technology of activated carbon inner container bottle Download PDFInfo
- Publication number
- CN103183167A CN103183167A CN2013101107904A CN201310110790A CN103183167A CN 103183167 A CN103183167 A CN 103183167A CN 2013101107904 A CN2013101107904 A CN 2013101107904A CN 201310110790 A CN201310110790 A CN 201310110790A CN 103183167 A CN103183167 A CN 103183167A
- Authority
- CN
- China
- Prior art keywords
- activated carbon
- bottle
- gas
- manufacture technology
- firing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacture technology of an activated carbon inner container bottle. The manufacture technology comprises the following steps of: forming an activated carbon material by a press machine in a pressing way, and forming a half of the bottle shape for once, i.e. a half bottle body; splicing the two half bottle bodies into a whole, and spraying or immersing ceramic slurry on the external part of the bottle body; carrying out blank repairing and glazing on the bottle body; and firing a blank of the bottle body in a heating way, and adding inert gas or reductive gas in the process of firing. According to the manufacture technology, the cost can be preferably saved, and the work efficiency can be improved; and in the process of firing, the inert gas and the reductive gas (hydrogen, helium and the like) are added, so that the characteristics of the activated carbon can be preferably protected, and a fired product is more lenitive in color and luster.
Description
Technical field
The present invention relates to vase manufacture craft in a kind of active carbon, the technical field that vase is made in belonging to.
Background technology
Market appreciiable pottery bottle all is the conventional ceramic bottle now, and method for making generally has two kinds, and a kind of is to use manual manufacture, and a kind of is to add injection forming.
Home built efficient is low, adds injection forming method cost height.
Summary of the invention
The present invention seeks to provides vase manufacture craft in a kind of active carbon at the defective that prior art exists.
The present invention adopts following technical scheme for achieving the above object:
Vase manufacture craft in a kind of active carbon of the present invention is characterized in that described technology comprises the steps:
1) utilize compression machine that absorbent charcoal material is pressed, one-shot forming is half i.e. half body of bottle type;
2) again two and half bodies are spliced into a complete body, coat ceramic size in the body outside then;
3) body is repaiied embryo, glazing;
4) blank of body is heated fire at last, in the process of firing, add body or go into reducibility gas unreactable gas.
Step 2) described coating ceramic size adopts the dip coated method.
Step 2) described gas is hydrogen or unreactable gas.
The following advantage of tool of the present invention:
1) this method is the process of making vase in the active carbon specially, does not also occur similar products up to now on the market;
2) traditional method for making before this method is abandoned just has present method to save cost more, increases work efficiency;
3) in sintering procedure, adding unreactable gas, reducing gas (hydrogen, helium etc.) help to protect the characteristic of active carbon, and can make the product color that burns out more moist.
Description of drawings
Fig. 1: flow scheme of the present invention.
The specific embodiment
As shown in Figure 1, the vase manufacture craft is as follows in a kind of active carbon of the present invention:
1) at first utilize compression machine that absorbent charcoal material is pressed, one-shot forming is half of bottle type;
2) suppress the two halves body after, again the body bottle of two halves is become a complete body, coat ceramic size/or directly body is stained with and is allowed slurry be covered with body then in ceramic size in the body outside;
3) after the body slurry is coated with completely by the time, body is repaiied embryo, glazing;
4) blank of body is heated fire at last, in the process of firing, add unreactable gas, reducing gas (hydrogen, helium etc.) prevents that active carbon from producing chemical reaction;
The above only is the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment the present invention is had been described in detail, for a person skilled in the art, it still can be made amendment to the technical scheme that aforementioned each embodiment puts down in writing, and perhaps part technical characterictic wherein is equal to replacement.Within the spirit and principles in the present invention all, any modification of doing, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. the interior vase manufacture craft of active carbon is characterized in that described technology comprises the steps:
1) utilize compression machine that absorbent charcoal material is pressed, one-shot forming is half i.e. half body of bottle type;
2) again two and half bodies are spliced into a complete body, coat ceramic size in the body outside then;
3) body is repaiied embryo, glazing;
4) blank of body is heated fire at last, in the process of firing, add unreactable gas or reducibility gas.
2. vase manufacture craft in a kind of active carbon according to claim 1 is characterized in that step 2) described coating ceramic size employing dip coated method.
3. vase manufacture craft in a kind of active carbon according to claim 1 is characterized in that step 2) described gas is hydrogen or unreactable gas.