CN103174100A - Elastic self-repairing anti-glare panel and manufacturing method thereof - Google Patents
Elastic self-repairing anti-glare panel and manufacturing method thereof Download PDFInfo
- Publication number
- CN103174100A CN103174100A CN 201310138421 CN201310138421A CN103174100A CN 103174100 A CN103174100 A CN 103174100A CN 201310138421 CN201310138421 CN 201310138421 CN 201310138421 A CN201310138421 A CN 201310138421A CN 103174100 A CN103174100 A CN 103174100A
- Authority
- CN
- China
- Prior art keywords
- parts
- covering layer
- rubber covering
- elasticity
- elastic rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an elastic self-repairing anti-glare panel and a manufacturing method of the elastic self-repairing anti-glare panel. A manufacturing process that a central elastic steel strap is externally wrapped by a high-elasticity rubber covering layer is adopted, and the high-elasticity rubber covering layer wrapped outside has good flexibility, so that the damage to human bodies and vehicles in collision accident is reduced; and as the elastic steel strap and the high-elasticity rubber covering layer are bonded by using a high-quality heat vulcanization type adhesive, the strength in bonding is ensured; and the combination of the elastic steel strap and the high-elasticity rubber covering layer ensures that the anti-glare panel can rapidly reset when being collided or blown by gale. An anti-aging agent, an ultraviolet-proof agent and a cold-resistant plasticizer dioctyl-phthalate are added into the high-elasticity rubber covering layer at the outer part, so that the elastic self-repairing anti-glare panel can adapt to atrocious weather environment such as low temperature, high temperature and chemical erosion, the service life is prolonged to 20 years, and no maintenance is needed within 20 years, thereby being energy-saving and environmental-friendly.
Description
Technical field
The present invention relates to the means of transportation technical field, relate in particular to a kind of elasticity selfreparing antiglare shield and preparation method thereof.
Background technology
Continuous increase along with Modern High-Speed highway quantity, the demand of antiglare shield is also more and more, in prior art, antiglare shield generally adopts PVC or glass fiber reinforced plastic to add the iron plate manufacturing, when accident, the vehicle of running at high speed is easy to clash into guardrail and then clashes into antiglare shield, the bad antiglare shield of elasticity can cause very large damage to people and vehicle, and it is short application life that PVC or glass fiber reinforced plastic add the antiglare shield that iron plate makes in addition, and the later maintenance expense is high.Wherein application number is: 201010607255.6 patent of invention discloses a kind of antiglare shield, and it utilizes the elasticity of mechanical stage clip to make the antiglare shield resilience, and this product structure is complicated, when the resilience compression spring component goes wrong, easily causes the antiglare shield resilience to lose efficacy.Therefore be necessary to provide a kind of new elasticity selfreparing antiglare shield to solve above-mentioned technical problem.
Summary of the invention
The object of the present invention is to provide a kind of elasticity selfreparing antiglare shield, it is in the situation that be subject to Vehicular impact and the larger wind not frangibility of bending of taking advantage of a situation, and can return to rapidly initial erectility, and is simple in structure, is easy to safeguard long service life.
For solving the problems of the technologies described above, the present invention adopts following technical scheme: a kind of elasticity selfreparing antiglare shield,
Comprise flexible strip and the outside high-elastic rubber covering layer at center, the bottom is provided with fixing hole, and the constitutive material weight portion of described high-elastic rubber covering layer is:
70 parts of natural gums;
5 parts of magnesium zinc;
5 parts of stearic acid;
2 parts of diboron trioxides;
3 parts of carbon blacks (N660);
3 parts of carbon blacks (N110);
2 parts of Sulfurs;
2 parts, paraffin;
3 parts of aging-proof agents (4010NA);
3 parts of accelerator (tetramethylthiuram disulfide);
2 parts of antiscorching agent (CTP)
Described flexible strip material is No. 65 manganese steel plates
Concrete preparation method of the present invention is:
1) make flexible strip: the steel band that cuts is quenched and the sandblast Passivation Treatment;
2) preparation of high-elastic rubber covering layer: take raw material natural gum, magnesium zinc, stearic acid, diboron trioxide, carbon black (N660), carbon black (N110), Sulfur, paraffin, aging-proof agent (4010NA), accelerator (tetramethylthiuram disulfide), antiscorching agent (CTP) by proportion, fully mix, be heated to the 150-180 degree, add molding pressure 20-30MPa, slaking 2-3 hour, moulding.
3) add the heat vulcanization type bonding adhesive between flexible strip and high-elastic rubber covering layer.
compared with prior art, elasticity selfreparing antiglare shield provided by the present invention, guaranteed that antiglare shield is subject to clashing into and can resets rapidly after the wind pendulum greatly, the high-elastic rubber covering layer that the outside coats has good pliability, reduced and the shock accident has occured to the injury of human body and vehicle, bonding employing high-quality heat vulcanization type bonding adhesive between flexible strip and high-elastic rubber covering layer, guaranteed bonding intensity, the high-elastic rubber covering layer of outside adds aging-proof agent, ultraviolet screener, the cold resistant plasticizer dibutyl ester, make the present invention can be at low temperature, high temperature, still keep good rebound performance in the adverse circumstances such as chemical erosion.
Description of drawings
Fig. 1 is the structural representation of a kind of elasticity selfreparing antiglare shield of the present invention.
Wherein 1 is that high-elastic rubber covering layer, 2 is that flexible strip (dotted portion in figure), 3 is fixing hole.
The specific embodiment
see also shown in Figure 1, the invention provides a kind of elasticity selfreparing antiglare shield, the flexible strip 2 and the outside high-elastic rubber covering layer 1 that comprise the center, the bottom is provided with fixing hole 3, add the heat vulcanization type bonding adhesive between flexible strip and high-elastic rubber covering layer, described high-elastic rubber covering layer is made of the raw material of following deal ratio: take the raw material natural gum by proportion, magnesium zinc, stearic acid, diboron trioxide, carbon black N660, carbon black N110, Sulfur, paraffin, aging-proof agent 4010NA, Vulcanization accelerator TMTD, tetramethylthiuram disulfide, anti-scorching agent CTP, described flexible strip material is No. 65 manganese steel plates.
The concrete making step of a kind of elasticity selfreparing of the present invention antiglare shield is:
1) utilize the concrete grammar of flared pipe of the synthetic resin manufacture of materials number of advancing as follows: to make flexible strip: the steel band that cuts is quenched and the sandblast Passivation Treatment;
2) preparation of high-elastic rubber covering layer: take raw material natural gum, magnesium zinc, stearic acid, diboron trioxide, carbon black N660, carbon black N110, Sulfur, paraffin, aging-proof agent 4010NA, Vulcanization accelerator TMTD, tetramethylthiuram disulfide, anti-scorching agent CTP by proportion, fully mix, molding pressure 20-30MPa, be heated to the 150-180 degree, slaking 2-3 hour.
3) add the heat vulcanization type bonding adhesive between flexible strip and high-elastic rubber covering layer.
The elastic caoutchouc performance indications of a kind of elasticity selfreparing of the present invention antiglare shield reach hardness 65 degree, hot strength 〉=10Mpa, elongation at break 〉=350%, compression set rate less than 18%, resilience greater than 65%, fatigue test 300,000 times, water soaking mass change 0, the high resilience energy that coordinates the inner elastomeric steel band, make antiglare shield be subject to clashing into and large wind pendulum after can reset rapidly, and reduced the injury that antiglare shield when the shock accident occurs causes human body and vehicle.
Above embodiment is only unrestricted in order to technical scheme of the present invention to be described, although with reference to preferred embodiment, the present invention is had been described in detail, those of ordinary skill in the art is to be understood that, can modify or be equal to replacement technical scheme of the present invention, and not breaking away from the spirit and scope of technical solution of the present invention, it all should be encompassed in the middle of claim scope of the present invention.
Claims (3)
1. an elasticity selfreparing antiglare shield, comprise the flexible strip at center and the high-elastic rubber covering layer of outside, and the bottom is provided with fixing hole, it is characterized in that: the constitutive material weight portion of described high-elastic rubber covering layer is:
70 parts of natural gums;
5 parts of magnesium zinc;
5 parts of stearic acid;
2 parts of diboron trioxides;
3 parts of carbon blacks (N660);
3 parts of carbon blacks (N110);
2 parts of Sulfurs;
2 parts, paraffin;
3 parts of aging-proof agents (4010NA);
3 parts of accelerator (tetramethylthiuram disulfide);
2 parts of antiscorching agent (CTP).
2. elasticity selfreparing antiglare shield as claimed in claim 1, is characterized in that, described flexible strip material is No. 65 manganese steel plates.
3. the preparation method of an elasticity selfreparing antiglare shield as claimed in claim 1, is characterized in that comprising the steps:
Make flexible strip: the steel band that cuts is quenched and the sandblast Passivation Treatment;
The preparation of high-elastic rubber covering layer: take raw material natural gum, magnesium zinc, stearic acid, diboron trioxide, carbon black (N660), carbon black (N110), Sulfur, paraffin, aging-proof agent (4010NA), accelerator (tetramethylthiuram disulfide), antiscorching agent (CTP) by proportion, fully mix, be heated to the 150-180 degree, add molding pressure 20-30MPa, slaking 2-3 hour, moulding;
Add the heat vulcanization type bonding adhesive between flexible strip and high-elastic rubber covering layer.