CN103169183B - cloth and preparation method thereof - Google Patents
cloth and preparation method thereof Download PDFInfo
- Publication number
- CN103169183B CN103169183B CN201210395043.5A CN201210395043A CN103169183B CN 103169183 B CN103169183 B CN 103169183B CN 201210395043 A CN201210395043 A CN 201210395043A CN 103169183 B CN103169183 B CN 103169183B
- Authority
- CN
- China
- Prior art keywords
- neoprene
- cloth
- layer
- thin
- ground floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of cloth and preparation method thereof, comprise cloth main body, cloth main body comprises three-decker, and be followed successively by ground floor Neoprene, superlastic layer of cloth and second layer Neoprene, superlastic layer of cloth is fixed between ground floor Neoprene and second layer Neoprene.The present invention is by pasting Neoprene on superlastic cloth two sides, and the integral thickness making cloth shaping through multiple operation is between 0.5mm ~ 1mm, makes this cloth high resilience, can not be wrinkling; Neoprene has certain warming effect, so after gym suit made by cloth, not only thin and take into account warming effect.
Description
Technical field
The present invention relates to field of textiles, particularly a kind of cloth and preparation method thereof.
Background technology
Along with socioeconomic growing, the hobby of people to every motion is more and more higher, thus to sports products to the performance of product and the requirement of quality also more and more higher, also more and more diversified, its aquatic sports such as went swimming and diving is one of favorite motion of modern.At present, diving suit cloth uses SBRCR Neoprene (neoprene) usually, this kind of cloth has good water proofing property, sealing and warmth retention property, but due to its pliability, elasticity is not enough, affect unfolding of action, be rarely used on the gym suit of other field, and be easy to folding line after folding.
Summary of the invention
The object of the present invention is to provide a kind of novel cloth and preparation method thereof.
According to an aspect of the present invention, provide a kind of cloth, comprise cloth main body, cloth main body comprises three-decker, and be followed successively by the first diving bed of material, superlastic layer of cloth and second layer Neoprene, superlastic layer of cloth is fixed between ground floor Neoprene and second layer Neoprene.
Above-mentioned cloth preparation method for material, comprises the steps:
(1), ground floor Neoprene and second layer Neoprene being carried out first time cuts thin;
(2), by cut in step (1) thin after ground floor Neoprene one side be fixed on the one side of superlastic cloth by glue after, then the another side of described ground floor Neoprene carried out second time cut thin;
(3), by cut in step (1) thin after second layer Neoprene one side be fixed on the another side of the described superlastic cloth of step (2) by glue after, the another side of described second layer Neoprene is carried out second time and cuts thin, obtain type at the beginning of cloth;
(4), at the beginning of the gym suit of step (3) gained type cloth is ironed, just coats smooth agent mixture in type surface, obtain cloth at described gym suit.
In some embodiments, the ground floor Neoprene of step (1) and second layer Neoprene first time cut thin after thickness be 2mm ~ 3mm.
In some embodiments, the glue of step (2) is neoprene, the ground floor Neoprene of step (2) second time cut thin after thickness be 0.4mm ~ 0.6mm.
In some embodiments, the glue of step (3) is neoprene, the second layer Neoprene of step (3) second time cut thin after thickness be 0.4mm ~ 0.6mm.
In some embodiments, the ironed pressure of step (4) is 100T ~ 300T, and temperature is 25 DEG C ~ 165 DEG C, and the thickness after ironed is 0.5mm ~ 1mm.
In some embodiments, ironed temperature is 120 DEG C ~ 160 DEG C.
In some embodiments, the smooth agent mixture of step (4) comprises neoprene, smooth agent and toner, and its mass ratio is 1:3:1, and the curing dose of adding in every 15KG smooth agent mixture is 500ML.
In some embodiments, smooth agent is aqueous, environmental protective organic silicon emulsion or two amido functional group organic silicon emulsion, and curing agent is polyetheramine.
In some embodiments, ground floor Neoprene and second layer Neoprene are neoprene (SBRCR Neoprene), and superlastic cloth is spandex (OP) yarn.
Above-mentioned manufacture method is adopted to obtain cloth of the present invention, by pasting Neoprene on superlastic cloth two sides, and the integral thickness making cloth shaping through multiple operation is between 0.5mm ~ 1mm, because superlastic cloth has extraordinary elasticity and pliability, the thickness of Neoprene is compressed in the process made, make this cloth high resilience, can not be wrinkling; Neoprene has certain warming effect, so after gym suit made by cloth, not only thin and take into account warming effect.Also scribble smooth agent mixture on the surface of cloth in addition, make the not only smooth surface of cloth, comfortable and easy to wear, and the water of erasing above can be easy to, user therefore can not be allowed to feel wet.
Accompanying drawing explanation
Fig. 1 is the preparation flow schematic diagram of cloth of the present invention.
Detailed description of the invention
Embodiment 1
The preparation method of the cloth of the embodiment of the present invention 1, as shown in Figure 1, comprises the steps:
(1) slicer, provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. is carried out first time cut thin by being received SN242 neoprene that Chemical Co., Ltd. provides by upper seamount, cut thin after thickness be 2mm, and then the SOP-TH-005 bead cutter provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. to cut thin after neoprene carry out deburring;
(2), by cut in step (1) thin after the SOP-TH-003 make-up machine that provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. of ground floor neoprene one side be fixed in the one side of the spandex yarn that Dongguan City ten thousand intelligence Industrial Co., Ltd. provides, the 605 type neoprenes that the glue that make-up machine uses provides for Qi Li resin Co., Ltd, carrying out second time by bead cutter to the another side of ground floor neoprene again cuts thin, and the thickness cutting thin rear ground floor neoprene is 0.4mm;
(3), by cut in step (1) thin after the second layer neoprene one side be fixed on the another side of step (2) described spandex yarn by glue after, carrying out second time by bead cutter to the another side of second layer neoprene again cuts thin, the thickness cutting thin rear second layer neoprene is 0.4mm, obtains cloth just type;
(4), step (3) gained cloth just the vulcanizer of WZ-GC-LH-001 that provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. of type carry out ironed at the pressure of 300T and temperature are 25 DEG C, the thickness after this cloth is ironed is 0.5mm, first by neoprene in the hopper of the SOP-TH006 type film applicator then provided in Dongguan City ten thousand intelligence Industrial Co., Ltd., the 414 type aqueous, environmental protective organic silicon emulsions that Qi Li resin Co., Ltd provides and the toner of routine are that 1:3:1 is uniformly mixed with mass ratio, obtain smooth agent mixture, the ratio of the ED-2003 type polyetheramine provided with the large bright trade Co., Ltd repeatedly adding 500ML in every 15KG aqueous, environmental protective organic silicon emulsion mixture again, polyetheramine is added after material feeding box carries out uniform stirring, by the film mouth of film applicator, the mixture of gained is coated with the first type of gym suit on the surface with being evenly coated with again, cloth is obtained after cooling.
By the cloth that above-mentioned steps is obtained, comprise cloth main body, cloth main body comprises three-decker, and be followed successively by the first neoprene layer, spandex yarn layer and the second neoprene layer, spandex yarn layer is fixed between the first neoprene layer and the second neoprene layer.
The present invention adopts above-mentioned manufacture method to obtain cloth of the present invention, by pasting neoprene on spandex yarn two sides, and the integral thickness making cloth shaping through multiple operation is between 0.5mm, because spandex yarn has extraordinary elasticity and pliability, the thickness of neoprene is compressed in the process made, make this cloth high resilience, can not be wrinkling; Neoprene has certain warming effect, so after gym suit made by cloth, not only thin and take into account warming effect.Also scribble smooth agent mixture on the surface of cloth in addition, make the not only smooth surface of cloth, comfortable and easy to wear, and the water of erasing above can be easy to, user therefore can not be allowed to feel wet.
Embodiment 2
The preparation method of the cloth of the embodiment of the present invention 2, as shown in Figure 1, comprises the steps:
(1) slicer, provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. is carried out first time cut thin by being received SN242 neoprene that Chemical Co., Ltd. provides by upper seamount, cut thin after thickness be 2mm, and then the SOP-TH-005 bead cutter provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. to cut thin after neoprene carry out deburring;
(2), by cut in step (1) thin after the SOP-TH-003 make-up machine that provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. of ground floor neoprene one side be fixed in the one side of the spandex yarn that Dongguan City ten thousand intelligence Industrial Co., Ltd. provides, the 605 type neoprenes that the glue that make-up machine uses provides for Qi Li resin Co., Ltd, carrying out second time by bead cutter to the another side of ground floor neoprene again cuts thin, and the thickness cutting thin rear ground floor neoprene is 0.4mm;
(3), by cut in step (1) thin after the second layer neoprene one side be fixed on the another side of the described superlastic cloth of step (2) by glue after, carrying out second time by bead cutter to the another side of second layer neoprene again cuts thin, the thickness cutting thin rear second layer neoprene is 0.4mm, obtains cloth just type;
(4), step (3) gained cloth just the vulcanizer of WZ-GC-LH-001 that provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. of type carry out ironed at the pressure of 250T and temperature are 120 DEG C, the thickness after this cloth is ironed is 0.5mm, first by neoprene in the hopper of the SOP-TH006 type film applicator then provided in Dongguan City ten thousand intelligence Industrial Co., Ltd., the 414 type aqueous, environmental protective organic silicon emulsions that Qi Li resin Co., Ltd provides and the toner of routine are that 1:3:1 is uniformly mixed with mass ratio, obtain smooth agent mixture, the ratio of the ED-2003 type polyetheramine provided with the large bright trade Co., Ltd repeatedly adding 500ML in every 15KG aqueous, environmental protective organic silicon emulsion mixture again, polyetheramine is added after material feeding box carries out uniform stirring, by the film mouth of film applicator, the mixture of gained is coated with the first type of gym suit on the surface with being evenly coated with again, cloth is obtained after cooling.
By the cloth that above-mentioned steps is obtained, comprise cloth main body, cloth main body comprises three-decker, and be followed successively by the first neoprene layer, spandex yarn layer and the second neoprene layer, spandex yarn layer is fixed between the first neoprene layer and the second neoprene layer.
The present invention adopts above-mentioned manufacture method to obtain cloth of the present invention, by pasting neoprene on spandex yarn two sides, and the integral thickness making cloth shaping through multiple operation is between 0.5mm, because spandex yarn has extraordinary elasticity and pliability, the thickness of neoprene is compressed in the process made, make this cloth high resilience, can not be wrinkling; Neoprene has certain warming effect, so after gym suit made by cloth, not only thin and take into account warming effect.Also scribble smooth agent mixture on the surface of cloth in addition, make the not only smooth surface of cloth, comfortable and easy to wear, and the water of erasing above can be easy to, user therefore can not be allowed to feel wet.
Embodiment 3
The preparation method of the cloth of the embodiment of the present invention 3, as shown in Figure 1, comprises the steps:
(1) slicer, provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. is carried out first time cut thin by being received SN242 neoprene that Chemical Co., Ltd. provides by upper seamount, cut thin after thickness be 2.5mm, and then the SOP-TH-005 bead cutter provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. to cut thin after neoprene carry out deburring;
(2), by cut in step (1) thin after the SOP-TH-003 make-up machine that provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. of ground floor neoprene one side be fixed in the one side of the spandex yarn that Dongguan City ten thousand intelligence Industrial Co., Ltd. provides, the 605 type neoprenes that the glue that make-up machine uses provides for Qi Li resin Co., Ltd, carrying out second time by bead cutter to the another side of ground floor neoprene again cuts thin, and the thickness cutting thin rear ground floor neoprene is 0.5mm;
(3), by cut in step (1) thin after the second layer neoprene one side be fixed on the another side of the described superlastic cloth of step (2) by glue after, carrying out second time by bead cutter to the another side of second layer neoprene again cuts thin, the thickness cutting thin rear second layer neoprene is 0.5mm, obtains cloth just type;
(4), step (3) gained cloth just the vulcanizer of WZ-GC-LH-001 that provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. of type carry out ironed at the pressure of 200T and temperature are 135 DEG C, the thickness after this cloth is ironed is 0.7mm, first by neoprene in the hopper of the SOP-TH006 type film applicator then provided in Dongguan City ten thousand intelligence Industrial Co., Ltd., the toner of the two amido functional group organic silicon emulsion of 414 types that Qi Li resin Co., Ltd provides and routine is that 1:3:1 is uniformly mixed with mass ratio, obtain two amido functional group organic silicon emulsion mixture, the ratio of the ED-2003 type polyetheramine provided with the large bright trade Co., Ltd repeatedly adding 500ML in the two amido functional group organic silicon emulsion mixture of every 15KG again, polyetheramine is added after material feeding box carries out uniform stirring, by the film mouth of film applicator, the mixture of gained is coated with the first type of gym suit on the surface with being evenly coated with again, cloth is obtained after cooling.
By the cloth that above-mentioned steps is obtained, comprise cloth main body, cloth main body comprises three-decker, and be followed successively by the first neoprene layer, spandex yarn layer and the second neoprene layer, spandex yarn layer is fixed between the first neoprene layer and the second neoprene layer.
The present invention adopts above-mentioned manufacture method to obtain cloth of the present invention, by pasting neoprene on spandex yarn two sides, and the integral thickness making cloth shaping through multiple operation is between 0.7mm, because spandex yarn has extraordinary elasticity and pliability, the thickness of neoprene is compressed in the process made, make this cloth high resilience, can not be wrinkling; Neoprene has certain warming effect, so after gym suit made by cloth, not only thin and take into account warming effect.Also scribble smooth agent mixture on the surface of cloth in addition, make the not only smooth surface of cloth, comfortable and easy to wear, and the water of erasing above can be easy to, user therefore can not be allowed to feel wet.
Embodiment 4
The preparation method of the cloth of the embodiment of the present invention 4, as shown in Figure 1, comprises the steps:
(1) slicer, provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. is carried out first time cut thin by being received SN242 neoprene that Chemical Co., Ltd. provides by upper seamount, cut thin after thickness be 3mm, and then the SOP-TH-005 bead cutter provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. to cut thin after neoprene carry out deburring;
(2), by cut in step (1) thin after the SOP-TH-003 make-up machine that provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. of ground floor neoprene one side be fixed in the one side of the spandex yarn that Dongguan City ten thousand intelligence Industrial Co., Ltd. provides, the 605 type neoprenes that the glue that make-up machine uses provides for Qi Li resin Co., Ltd, carrying out second time by bead cutter to the another side of ground floor neoprene again cuts thin, and the thickness cutting thin rear ground floor neoprene is 0.6mm;
(3), by cut in step (1) thin after the second layer neoprene one side be fixed on the another side of the described superlastic cloth of step (2) by glue after, carrying out second time by bead cutter to the another side of second layer neoprene again cuts thin, the thickness cutting thin rear second layer neoprene is 0.6mm, obtains cloth just type;
(4), step (3) gained cloth just the vulcanizer of WZ-GC-LH-001 that provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. of type carry out ironed at the pressure of 150T and temperature are 150 DEG C, the thickness after this cloth is ironed is 1mm, first by neoprene in the hopper of the SOP-TH006 type film applicator then provided in Dongguan City ten thousand intelligence Industrial Co., Ltd., the 414 type aqueous, environmental protective organic silicon emulsions that Qi Li resin Co., Ltd provides and the toner of routine are that 1:3:1 is uniformly mixed with mass ratio, obtain aqueous, environmental protective organic silicon emulsion mixture, the ratio of the ED-2003 type polyetheramine provided with the large bright trade Co., Ltd repeatedly adding 500ML in every 15KG aqueous, environmental protective organic silicon emulsion mixture again, polyetheramine is added after material feeding box carries out uniform stirring, by the film mouth of film applicator, the mixture of gained is coated with the first type of gym suit on the surface with being evenly coated with again, cloth is obtained after cooling.
By the cloth that above-mentioned steps is obtained, comprise cloth main body, cloth main body comprises three-decker, and be followed successively by the first neoprene layer, spandex yarn layer and the second neoprene layer, spandex yarn layer is fixed between the first neoprene layer and the second neoprene layer.
The present invention adopts above-mentioned manufacture method to obtain cloth of the present invention, by pasting neoprene on spandex yarn two sides, and the integral thickness making cloth shaping through multiple operation is between 1mm, because spandex yarn has extraordinary elasticity and pliability, the thickness of neoprene is compressed in the process made, make this cloth high resilience, can not be wrinkling; Neoprene has certain warming effect, so after gym suit made by cloth, not only thin and take into account warming effect.Also scribble smooth agent mixture on the surface of cloth in addition, make the not only smooth surface of cloth, comfortable and easy to wear, and the water of erasing above can be easy to, user therefore can not be allowed to feel wet.
Embodiment 5
The preparation method of the cloth of the embodiment of the present invention 5, as shown in Figure 1, comprises the steps:
(1) slicer, provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. is carried out first time cut thin by being received SN242 neoprene that Chemical Co., Ltd. provides by upper seamount, cut thin after thickness be 3mm, and then the SOP-TH-005 bead cutter provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. to cut thin after neoprene carry out deburring;
(2), by cut in step (1) thin after the SOP-TH-003 make-up machine that provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. of ground floor neoprene one side be fixed in the one side of the spandex yarn that Dongguan City ten thousand intelligence Industrial Co., Ltd. provides, the 605 type neoprenes that the glue that make-up machine uses provides for Qi Li resin Co., Ltd, carrying out second time by bead cutter to the another side of ground floor neoprene again cuts thin, and the thickness cutting thin rear ground floor neoprene is 0.6mm;
(3), by cut in step (1) thin after the second layer neoprene one side be fixed on the another side of the described superlastic cloth of step (2) by glue after, carrying out second time by bead cutter to the another side of second layer neoprene again cuts thin, the thickness cutting thin rear second layer neoprene is 0.6mm, obtains cloth just type;
(4), step (3) gained cloth just the vulcanizer of WZ-GC-LH-001 that provided by Dongguan City ten thousand intelligence Industrial Co., Ltd. of type carry out ironed at the pressure of 100T and temperature are 165 DEG C, the thickness after this cloth is ironed is 1mm, first by neoprene in the hopper of the SOP-TH006 type film applicator then provided in Dongguan City ten thousand intelligence Industrial Co., Ltd., the 414 type aqueous, environmental protective organic silicon emulsions that Qi Li resin Co., Ltd provides and the toner of routine are that 1:3:1 is uniformly mixed with mass ratio, obtain aqueous, environmental protective organic silicon emulsion mixture, the ratio of the ED-2003 type polyetheramine provided with the large bright trade Co., Ltd repeatedly adding 500ML in every 15KG aqueous, environmental protective organic silicon emulsion mixture again, polyetheramine is added after material feeding box carries out uniform stirring, by the film mouth of film applicator, the mixture of gained is coated with the first type of gym suit on the surface with being evenly coated with again, cloth is obtained after cooling.
By the cloth that above-mentioned steps is obtained, comprise cloth main body, cloth main body comprises three-decker, and be followed successively by the first neoprene layer, spandex yarn layer and the second neoprene layer, spandex yarn layer is fixed between the first neoprene layer and the second neoprene layer.
The present invention adopts above-mentioned manufacture method to obtain cloth of the present invention, by pasting neoprene on spandex yarn two sides, and the integral thickness making cloth shaping through multiple operation is between 1mm, because spandex yarn has extraordinary elasticity and pliability, the thickness of neoprene is compressed in the process made, make this cloth high resilience, can not be wrinkling; Neoprene has certain warming effect, so after gym suit made by cloth, not only thin and take into account warming effect.Also scribble smooth agent mixture on the surface of cloth in addition, make the not only smooth surface of cloth, comfortable and easy to wear, and the water of erasing above can be easy to, user therefore can not be allowed to feel wet.
The foregoing is only some embodiments of the present invention.For the person of ordinary skill of the art, without departing from the concept of the premise of the invention, some distortion can also be made and improve and all belong to protection scope of the present invention.
Claims (9)
1. cloth, wherein, comprises cloth main body, and described cloth main body comprises three-decker, is followed successively by ground floor Neoprene, superlastic layer of cloth and second layer Neoprene, and described superlastic layer of cloth is fixed between ground floor Neoprene and second layer Neoprene;
The preparation method of described cloth, comprises the steps:
(1) ground floor Neoprene and second layer Neoprene being carried out first time cuts thin;
(2) by cut in step (1) thin after ground floor Neoprene one side be fixed on the one side of superlastic cloth by glue after, then the another side of described ground floor Neoprene carried out second time cut thin;
(3) by cut in step (1) thin after second layer Neoprene one side be fixed on the another side of the described superlastic cloth of step (2) by glue after, the another side of described second layer Neoprene is carried out second time and cuts thin, obtain type at the beginning of cloth;
(4) ironed in the first type of the cloth of step (3) gained, just coat smooth agent mixture and curing agent in type surface at described cloth, after cooling, obtain cloth.
2. the preparation method of cloth according to claim 1, wherein, the ground floor Neoprene of described step (1) and the second layer Neoprene first time cut thin after thickness be 2mm ~ 3mm.
3. the preparation method of cloth according to claim 1, wherein, the glue of described step (2) is neoprene, the ground floor Neoprene of described step (2) second time cut thin after thickness be 0.4mm ~ 0.6mm.
4. the preparation method of cloth according to claim 1, wherein, the glue of described step (3) is neoprene, the second layer Neoprene of described step (3) second time cut thin after thickness be 0.4mm ~ 0.6mm.
5. the preparation method of cloth according to claim 1, wherein, the ironed pressure of described step (4) is 100T ~ 300T, and temperature is 25 DEG C ~ 165 DEG C, and the thickness after ironed is 0.5mm ~ 1mm.
6. the preparation method of cloth according to claim 5, wherein, described ironed temperature is 120 DEG C ~ 160 DEG C.
7. the preparation method of cloth according to claim 1, wherein, the smooth agent mixture of described step (4) comprises neoprene, smooth agent and toner, and its mass ratio is 1:3:1, and the curing dose of adding in every 15KG smooth agent mixture is 500ML.
8. the preparation method of cloth according to claim 7, wherein, described smooth agent is aqueous, environmental protective organic silicon emulsion or two amido functional group organic silicon emulsion, and described curing agent is polyetheramine.
9. the preparation method of the cloth according to any one of claim 1 to 8, wherein, described ground floor Neoprene and second layer Neoprene are neoprene, and described superlastic cloth is spandex yarn.