CN103160041A - Composite material for lining of fire-fighting hose and preparation process for same - Google Patents
Composite material for lining of fire-fighting hose and preparation process for same Download PDFInfo
- Publication number
- CN103160041A CN103160041A CN2011104084892A CN201110408489A CN103160041A CN 103160041 A CN103160041 A CN 103160041A CN 2011104084892 A CN2011104084892 A CN 2011104084892A CN 201110408489 A CN201110408489 A CN 201110408489A CN 103160041 A CN103160041 A CN 103160041A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- fire hose
- fire
- hose liner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a composite material, and particularly relates to a composite material for the lining of a fire-fighting hose and a preparation method for the same. In order to overcome the defects of no ageing resistance, no high pressure resistance and high price of the lining of the existing fire-fighting hose, the composite material for the lining of a fire-fighting hose disclosed by the invention is prepared from the raw materials in the following proportioning ratio by weight parts: 55-65 parts of polyvinyl chloride, 4-6 parts of nitrile rubber, 3-6 parts of adhesive, 2-4 parts of activator, 4-6 parts of vulcanizer, 35-45 parts of aluminium hydroxide, 18-25 parts of plasticizer, 1-3 parts of antiager, and 4-6 parts of compound stabilizer. The composite material disclosed by the invention can be used for a fire-fighting hose and used as the lining of the fire-fighting hose; and by reasonably distributing the components and adopting a proper preparation method, the fire-fighting hose with wear resistance, high pressure resistance, corrosion resistance, high temperature resistance and long service life is obtained.
Description
Technical field
The present invention relates to matrix material, be specifically related to a kind of matrix material for the fire hose liner and preparation technology thereof.
Background technology
Fire hose is a kind of flexible pipe that is used for carrying water or foam mixing liquid in fire service, the employing high strength synthetic fibre is basic unit, the inside also has one deck liner, because liner be directly with the water of use or the structural sheet that foam mixing liquid directly contacts of putting out a fire, so the material of liner directly determines the use properties of fire hose.At present, the elastomeric material of fire hose liner mainly contains three kinds, natural rubber, ethylene-propylene rubber(EPR) and urethanes, it respectively has advantage, but the liner of natural rubber not Weather-resistant, work-ing life is short, the bonding difficulty of ethylene-propylene rubber(EPR) liner and synthon and fiber basic unit, and price is more expensive, and the urethanes liner is also expensive.Therefore, a kind of corrosion-resistant, wear-resisting, high pressure resistant, ageing-resistant and cheap fire hose inner lining material of research and development is the demand in market.
Summary of the invention
The object of the present invention is to provide matrix material and preparation technology thereof for the fire hose liner, overcome the existing defective that the fire hose liner is not ageing-resistant, not high pressure resistant and price is more expensive.
Matrix material for the fire hose liner of the present invention is made by the raw material of following weight part proportioning:
Polyvinyl chloride 55-65 part, nitrile rubber 4-6 part, tackiness agent 3-6 part, activator 2-4 part, vulcanizing agent 4-6 part, aluminium hydroxide 35-45 part, softening agent 18-25 part, anti-aging agent 1-3 part, one package stabilizer 4-6 part.
Preferably, described matrix material for the fire hose liner is made by the raw material of following weight part proportioning:
60 parts of polyvinyl chloride, 5 parts of nitrile rubbers, 5 parts, tackiness agent, 3 parts, activator, 5 parts of vulcanizing agents, 40 parts, aluminium hydroxide, 22 parts, softening agent, 2 parts, anti-aging agent, 5 parts of one package stabilizers.
Described tackiness agent can be adhesive A.
Described activator can be one or more the mixture in stearic acid, zinc oxide, organic zinc, Zinic stearas.
Described softening agent can be citrate or rubber plastizing agent A.
Described one package stabilizer can be calcium-zinc composite stabilizing agent.
Described vulcanizing agent can be one or more the mixture in sulphur, dicumyl peroxide, benzoyl peroxide and TMTD.
Described anti-aging agent can be selected conventional anti-aging agent such as RD, and NBC/octamine also uses etc.
Composite manufacture technique for the fire hose liner of the present invention, step is as follows:
First polyvinyl chloride, nitrile rubber, tackiness agent, activator, aluminium hydroxide, softening agent, anti-aging agent, one package stabilizer are mixed, drop into mixer mixing 3-4min, then drop into vulcanizing agent and continue mixing 0.5-1.5min, melting temperature is 110-120 ℃, replenish mixing 1-2 min after the banburying discharging in mill, replenish that temperature is 100-115 ℃ when mixing, then extruding and cooling after and get final product.
Matrix material of the present invention is used for fire hose as the rubber liner of fire hose, by to the properly distributed of component and adopt suitable preparation technology, has obtained fire hose wear-resisting, high pressure resistant, corrosion-resistant, high temperature resistant, long service life.
The adhesion strength of the liner that matrix material of the present invention is done and outer braid layer is high, more than reaching 42N/25mm, and unit elongation, rate of expansion≤4%, be difficult for aging delamination, heatproof 〉=130 ℃ (instantaneous 〉=600 ℃), oil resistant, strong acid-base resistance, burstpressures 〉=6Mpa, the life-span can reach more than 15 years.
The present invention has following advantage with respect to prior art:
Use matrix material provided by the invention to do that the water hose for firefighting of liner is high temperature resistant, high pressure, the adhesion strength of liner and outer braid is high, is difficult for peeling off; Ageing-resistant, long service life.
Embodiment
Below with specific embodiment, technical scheme of the present invention is described, but protection scope of the present invention is not limited to this:
Embodiment 1
The matrix material that is used for the fire hose liner is made by the raw material of following weight part proportioning:
60 parts of polyvinyl chloride, 5 parts of nitrile rubbers, 5 parts, tackiness agent, 3 parts, activator, 5 parts of vulcanizing agents, 40 parts, aluminium hydroxide, 22 parts, softening agent, 2 parts, anti-aging agent, 5 parts of one package stabilizers.
Wherein, one package stabilizer is calcium-zinc composite stabilizing agent, and activator is stearic acid, and softening agent is tributyl citrate, and vulcanizing agent is dicumyl peroxide, and described tackiness agent is adhesive A, and anti-aging agent is RD.
Preparation technology is as follows: first polyvinyl chloride, nitrile rubber, tackiness agent, activator, aluminium hydroxide, softening agent, anti-aging agent, one package stabilizer are mixed, drop into mixer mixing 3min, then drop into vulcanizing agent and continue mixing 1min, melting temperature is 115 ℃, replenish mixing 1.5 min after the banburying discharging in mill, replenish that temperature is 110 ℃ when mixing, then extruding and cooling after namely get the matrix material for fire hose of the present invention.The tackiness agent rear haulage enters in braid to vulcanize on the matrix material external parcel of tubulose, and curing temperature is 190 ℃, and the time is 4.5min, and water vapour pressure is 0.12Mpa; Obtain water hose for firefighting.The unit elongation of water band is 3.8%, rate of expansion is 3.8%, heatproof 140 ℃ of (instantaneous 650 ℃), oil resistants, strong acid-base resistance, burstpressures 7.6Mpa.
Embodiment 2
Proportioning raw materials: 55 parts of polyvinyl chloride, 4 parts of nitrile rubbers, 3 parts, tackiness agent, 2 parts, activator, 4 parts of vulcanizing agents, 35 parts, aluminium hydroxide, 18 parts, softening agent, 1 part, anti-aging agent, 4 parts of one package stabilizers.
One package stabilizer is calcium-zinc composite stabilizing agent, and activator is organic zinc, and softening agent is rubber plastizing agent A, and vulcanizing agent is TMTD, and described tackiness agent is adhesive A, and anti-aging agent is NBC/octamine and uses (mass ratio 1:1).
Preparation technology is as follows: first polyvinyl chloride, nitrile rubber, tackiness agent, activator, aluminium hydroxide, softening agent, anti-aging agent, one package stabilizer are mixed, drop into mixer mixing 4min, then drop into vulcanizing agent and continue mixing 0.5min, melting temperature is 110 ℃, replenish mixing 1 min after the banburying discharging in mill, replenish that temperature is 100 ℃ when mixing, then extruding and cooling after namely get matrix material of the present invention.The tackiness agent rear haulage enters in braid to vulcanize on the matrix material external parcel of tubulose, and curing temperature is 180 ℃, and the time is 5min, and water vapour pressure is 0.1Mpa; Obtain water hose for firefighting.The unit elongation of water band is 3.9%, rate of expansion is 3.5%, heatproof 142 ℃ of (instantaneous 620 ℃), oil resistants, strong acid-base resistance, burstpressures 7.1Mpa.
Embodiment 3
Raw material: 65 parts of polyvinyl chloride, 6 parts of nitrile rubbers, 6 parts, tackiness agent, 4 parts, activator, 6 parts of vulcanizing agents, 45 parts, aluminium hydroxide, 25 parts, softening agent, 3 parts, anti-aging agent, 6 parts of one package stabilizers.
One package stabilizer is calcium-zinc composite stabilizing agent, and activator is that zinc oxide and Zinic stearas mass ratio are the mixture of 1:1, and softening agent is ATBC, and vulcanizing agent is sulphur, and described tackiness agent is adhesive A, and anti-aging agent is BLE.
Preparation process is as follows: first polyvinyl chloride, nitrile rubber, tackiness agent, activator, aluminium hydroxide, softening agent, anti-aging agent, one package stabilizer are mixed, drop into mixer mixing 3-4min, then drop into vulcanizing agent and continue mixing 0.5-1.5min, melting temperature is 110-120 ℃, replenish mixing 1-2 min after the banburying discharging in mill, replenish that temperature is 100-115 ℃ when mixing, then extruding and cooling after namely get matrix material of the present invention.On external parcel, the tackiness agent rear haulage enters in braid to vulcanize outside the matrix material of tubulose, and curing temperature is 200 ℃, and the time is 4min, and water vapour pressure is 0.15Mpa; Obtain water hose for firefighting.The unit elongation of water band is 3.8%, rate of expansion is 3.8%, heatproof 156 ℃ of (instantaneous 651 ℃), oil resistants, strong acid-base resistance, burstpressures 7.4Mpa.
Claims (8)
1. be used for the matrix material of fire hose liner, it is characterized in that, described matrix material for the fire hose liner is made by the raw material of following weight part proportioning:
Polyvinyl chloride 55-65 part, nitrile rubber 4-6 part, tackiness agent 3-6 part, activator 2-4 part, vulcanizing agent 4-6 part, aluminium hydroxide 35-45 part, softening agent 18-25 part, anti-aging agent 1-3 part, one package stabilizer 4-6 part.
2. the matrix material for the fire hose liner according to claim 1, is characterized in that, described matrix material for the fire hose liner is made by the raw material of following weight part proportioning:
60 parts of polyvinyl chloride, 5 parts of nitrile rubbers, 5 parts, tackiness agent, 3 parts, activator, 5 parts of vulcanizing agents, 40 parts, aluminium hydroxide, 22 parts, softening agent, 2 parts, anti-aging agent, 5 parts of one package stabilizers.
3. according to claim 1 or 2 described matrix materials for the fire hose liner, it is characterized in that, described tackiness agent is adhesive A.
4. according to claim 1 or 2 described matrix materials for the fire hose liner, it is characterized in that, described activator is one or more the mixture in stearic acid, zinc oxide, organic zinc, Zinic stearas.
5. according to claim 1 or 2 described matrix materials for the fire hose liner, it is characterized in that, described softening agent is citrate or rubber plastizing agent A.
6. according to claim 1 or 2 described matrix materials for the fire hose liner, it is characterized in that, described one package stabilizer is calcium-zinc composite stabilizing agent.
7. according to claim 1 or 2 described matrix materials for the fire hose liner, it is characterized in that, described vulcanizing agent is one or more the mixture in sulphur, dicumyl peroxide, benzoyl peroxide and TMTD.
8. the described composite manufacture technique for the fire hose liner of the arbitrary claim of claim 1 to 7, is characterized in that, this step of preparation process is as follows:
First polyvinyl chloride, nitrile rubber, tackiness agent, activator, aluminium hydroxide, softening agent, anti-aging agent, one package stabilizer are mixed, drop into mixer mixing 3-4min, then drop into vulcanizing agent and continue mixing 0.5-1.5min, melting temperature is 110-120 ℃, replenish mixing 1-2 min after the banburying discharging in mill, replenish that temperature is 100-115 ℃ when mixing, then extruding and cooling after and get final product.