CN103146337A - Method for preparing single-component wet cured polyurethane hot melt adhesive by utilizing spandex waste wires - Google Patents
Method for preparing single-component wet cured polyurethane hot melt adhesive by utilizing spandex waste wires Download PDFInfo
- Publication number
- CN103146337A CN103146337A CN2013100910089A CN201310091008A CN103146337A CN 103146337 A CN103146337 A CN 103146337A CN 2013100910089 A CN2013100910089 A CN 2013100910089A CN 201310091008 A CN201310091008 A CN 201310091008A CN 103146337 A CN103146337 A CN 103146337A
- Authority
- CN
- China
- Prior art keywords
- hot melt
- waste silk
- spandex waste
- der
- polyurethane hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for preparing a single-component wet cured polyurethane hot melt adhesive by utilizing spandex waste wires. The method comprises the spandex waste wire degradation process and the polyurethane hot melt adhesive synthesis process. According to the method, the defects that the conventional polyurethane hot melt adhesive is extremely high in production cost and raw material price and the spandex waste wires are not fully utilized are overcome, and by employing the method, the degradation products are not required to be separated and are directly used, the production cost of the polyurethane hot melt adhesive is greatly reduced, and lots of spandex waste wires can be recycled. According to the prepared polyurethane hot melt adhesive, high economic benefits and social benefits can be obtained.
Description
Technical field
The invention belongs to the method and technology field of spandex waste silk recycling, specifically belong to and utilize spandex waste silk to prepare the method for the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives.
Background technology
Polyurethane elastomeric fiber claims again spandex, English Polyurethane fiber(PU fiber by name), be a kind of by polyurethane ester group content greater than 85% and have an artificial man-made fiber that the segmented copolymer of linear segmented structure is formed by weaving, the hard segment that the soft chain segment that this segmented copolymer mainly is comprised of low-molecular-weight polyester or polyethers and aromatic diisocyanate form reacts synthetic under certain condition.Along with polyurethane fiber rolling up in China's production and usage quantity, inevitably can produce a large amount of polyurethane fiber waste materials, it is spandex waste silk, most of polyurethane fibers belong to thermosetting material, have insoluble not molten characteristic, this brings very large difficulty with regard to the re-using of giving polyurethane waste material.At present, the recycling approach of polyurethane waste material mainly contains: energy method, Physical and chemical method; At present main the employing burned, processed as the method for packing filler or chemical degradation, burns or low as the method resource utilization of packing filler, also brings new pollution, and chemical degradation complex process, cost be higher, be difficult to promote.Along with the raising of people's environmental consciousness, realize low making rational use of resources of polluting, continue, become the problem that people must overcome and consider in actual production.The polyurethane fiber total quantity consumed of China in 2007 accounts for 28.5% of global total quantity consumed, is only second to the North America, it is predicted that 2012 ~ 2015 years China will become the main consumption market of global polyurethane fiber.Therefore, the recycling of polyurethane fiber waste material has been to need the problem of solution emphatically.
And on the other hand, reactive polyurethane hot melt is equipped with corresponding auxiliary agent by the base polyurethane prepolymer for use as of single component, solvent-free isocyanate terminated base and is prepared from.Its main component is by the synthetic isocyanate groups terminated polyurethane prepolymers of polyester polyol, polyether glycol and vulcabond, can meet the moisture fast setting after the melting applying glue, has just glutinous intensity preferably; Moisture diffusion enters sizing agent in the after fixing process, react with the isocyanic ester of prepolymer end group and form urea, biuret and allophanate, make the low molecule of linear prepolymer form crosslinked macromolecular structure, thereby have better high temperature resistant, anti-solvent and water resistance than traditional hot melt adhesive.At present, One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is widely used in vehicle structure and component, as windshield glass sealing and lamp assembled etc.; Textile industry and shoe industry, as bonding in fabric seam and sole is bonding; The books unsewn binding; Wood working and furniture industry; Building trade.In a word, locate fast at needs, bonded part needs the occasion of anti-high humidity, comparatively high temps and higher ambient pressure all can adopt moisture-curable polyurethane hot melt adhesive.So just caused moisture-curable polyurethane hot melt adhesive to obtain more and more widely using, it is too high that preparation method's ubiquity of present moisture-curable polyurethane hot melt adhesive production cost, range of application little problem.
Summary of the invention
The invention provides a kind of method of utilizing spandex waste silk to prepare the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, comprise the degradation process of spandex waste silk and the building-up process of adhesive for polyurethane, the method has overcome present polyurethane hot melt production cost and the prices of raw and semifnished materials are high, spandex waste silk is underused defective, adopting said method, degraded product need not separate and directly use, and the production cost that greatly reduces polyurethane hot melt can also be recycled a large amount of spandex waste silks.The adhesive for polyurethane of preparation can obtain good economic benefit and social benefit.
For achieving the above object, technical scheme of the present invention is:
A kind of method of utilizing spandex waste silk to prepare the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, step is as follows:
Step 1: pretreatment stage, be about to spandex waste silk and be ground into the spandex waste silk of desired length through fiber pulverizer, the spandex waste silk of desired length is just spandex waste silk to be added like this;
step 2: DeR stage, the raw material that uses in stage in this DeR is the alcoholysis agent, DeR is with catalyzer and the spandex waste silk to be added that obtains in step 1, at first in the three-necked bottle that agitator and prolong are housed, first according to adding the alcoholysis agent in the default parts by weight ratio range dealing three-necked bottle of alcoholysis agent with spandex waste silk to be added, subsequently heat temperature raising is carried out in the alcoholysis agent in three-necked bottle, heat temperature raising is until temperature is 180-200 ℃, then 1/10 the spandex waste silk that part by weight is accounted for spandex waste silk to be added adds in three-necked bottle, then according to the parts by weight ratio range of default DeR with the raw material that uses in the shared DeR of the catalyzer stage, add the DeR catalyzer in three-necked bottle, then with agitator, the raw material that adds in three-necked bottle is carried out the DeR of constant temperature under stirring, add remaining spandex waste silk to be added in three-necked bottle in the DeR process in batches, the reaction solution viscosity that is accompanied by the dissolving of spandex waste silk like this when DeR and carries out DeR in three-necked bottle also increases, accelerate stirring reaction according to the increase of reaction solution viscosity by default speed, when the reaction solution hydroxyl value that stirring reaction forms through DeR after four hours and in three-necked bottle is stabilized in default scope, stop stirring reaction, reaction solution in three-necked bottle is cooled to after temperature range is 95 ℃-105 ℃, with 100 ~ 120 purpose filtering nets, the reaction solution in three-necked bottle is carried out filtered while hot, reaction solution after filtered while hot is cooled to the yellow thick liquid that obtains after normal temperature, be spandex waste silk degraded product dibasic alcohol, this DeR product is sealed save backup,
step 3: the synthesis phase of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, the raw material that uses at the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is vulcabond, the moisture curing catalysts, oxidation inhibitor, viscosity stabilizer, the spandex waste silk degraded product dibasic alcohol and the polyester polyol that obtain in step 2, polyether glycol, be about to polyester polyol, polyether glycol joins with the parts by weight ratio range of the raw material that uses in the synthesis phase of the spandex waste silk degraded product dibasic alcohol that obtains in step 2 by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives and forms mixture in flask, after this mixture is stirred with agitator, after mixture in this flask is warming up to temperature range and is 120-130 ℃, then this mixture was carried out vacuum hydro-extraction 2-3 hour, then the mixture after vacuum hydro-extraction being cooled to temperature range is 70 ℃-80 ℃, pass into nitrogen protection in flask, add vulcabond in the mixture of the parts by weight scope of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives simultaneously after the vacuum hydro-extraction, and the mixture that has added vulcabond is stirred according to default speed with agitator, carry out the building-up reactions of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives in whipping process, obtain the Primary product of building-up reactions after the lasting 2h of stirring, the parts by weight ratio range of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives adds the moisture curing catalysts, continue the involutory Primary product that becomes reaction after oxidation inhibitor and viscosity stabilizer and carry out the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives that obtains synthesizing after building-up reactions 20min, the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is poured out from flask and the bottle of the sealing of packing in standby.
Alcoholysis agent in described step 2 is the polyvalent alcohol of 2-10 carbon atom, the polyvalent alcohol that the alcoholysis agent used of described DeR is 2-10 carbon atom, the polyvalent alcohol of 2-10 carbon atom comprises ethylene glycol, propylene glycol, butyleneglycol, pentanediol, hexylene glycol, glycol ether, Triethylene glycol, tetraethylene-glycol, glycerol, low-molecular-weight polyethers or polyester polyol.
Described DeR used catalyst is zinc acetate, tin tetrachloride, stannous octoate, triethylamine or dibutyl tin laurate, also can adopt tin tetrachloride, stannous octoate, triethylamine, dibutyl tin laurate etc. to be combined with each other according to default ratio and form the DeR used catalyst.
The parts by weight proportioning of the raw material that the DeR of described step 2 used in the stage is: 16-33 part small molecules polyvalent alcohol, 33-80 part spandex waste silk and 0.2-0.5 part DeR catalyzer.
Polyvalent alcohol in described step 3 in the synthesis phase of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is the pure and mild polyether glycol of polyester polyols, and the molecular weight of the pure and mild polyether glycol of polyester polyols is in 1000～5000 scopes.
Described vulcabond comprises aromatic series, aliphatics and alicyclic diisocyanate, mainly be not limited to tolylene diisocyanate (TDI), diphenylmethanediisocyanate (MDI), the mixture of one or more in isophorone diisocyanate (IPDI), hexamethylene diisocyanate (HDI), xylylene diisocyanate (XDI).
Described moisture curing catalysts is one or more the composite use in organic tin, organo-bismuth class or amine.
The parts by weight proportioning of the raw material that in described step 3, the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives uses is: 20-28 part spandex waste silk part degraded product dibasic alcohol, 18-34 part polyester polyol, 5-12 part high crystalline polyvalent alcohol, 30 ~ 45 parts of vulcabond, 0.1 ~ 0.15 part of moisture curing catalysts catalyzer, 0.1 ~ 0.15 portion of viscosity stabilizer and 0.1 ~ 0.5 part of oxidation inhibitor.
Method advantage of the present invention has overcome present polyurethane hot melt production cost and the prices of raw and semifnished materials are high, spandex waste silk is underused defective, adopting said method, degraded product need not separate and directly use, and the production cost that greatly reduces polyurethane hot melt can also be recycled a large amount of spandex waste silks.The adhesive for polyurethane of preparation can obtain good economic benefit and social benefit.
Embodiment
The present invention will be further described below by concrete embodiment:
Embodiment 1
Utilize spandex waste silk to prepare the method for the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, step is as follows:
Step 1: pretreatment stage, be about to spandex waste silk and be ground into the spandex waste silk of desired length through fiber pulverizer, the spandex waste silk of desired length is just spandex waste silk to be added like this;
step 2: DeR stage, the raw material that uses in stage in this DeR is the alcoholysis agent, DeR is with catalyzer and the spandex waste silk to be added that obtains in step 1, at first in the three-necked bottle that agitator and prolong are housed, first according to adding the alcoholysis agent in the default parts by weight ratio range dealing three-necked bottle of alcoholysis agent with spandex waste silk to be added, this alcoholysis agent is glycol ether, subsequently heat temperature raising is carried out in the alcoholysis agent in three-necked bottle, heat temperature raising is until temperature is 180 ℃, again in spandex waste silk to be added, 1/10 the spandex waste silk that part by weight is accounted for spandex waste silk to be added adds in three-necked bottle, then according to the parts by weight ratio range of default DeR with the raw material that uses in the shared DeR of the catalyzer stage, add the DeR catalyzer in three-necked bottle, described DeR catalyzer is tin tetrachloride, then with agitator, the raw material that adds in three-necked bottle is carried out the DeR of constant temperature under stirring, add remaining spandex waste silk to be added in three-necked bottle in the DeR process in batches, the reaction solution viscosity that is accompanied by the dissolving of spandex waste silk like this when DeR and carries out DeR in three-necked bottle also increases, accelerate stirring reaction according to the increase of reaction solution viscosity by default speed, when the reaction solution hydroxyl value that stirring reaction forms through DeR after four hours and in three-necked bottle is stabilized in default scope, stop stirring reaction, reaction solution in three-necked bottle is cooled to after temperature is 100 ℃, with 120 purpose filtering nets, the reaction solution in three-necked bottle is carried out filtered while hot, reaction solution after filtered while hot is cooled to the yellow thick liquid that obtains after normal temperature, be spandex waste silk degraded product dibasic alcohol, this DeR product is sealed save backup,
step 3: the synthesis phase of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, the raw material that uses at the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is vulcabond, the moisture curing catalysts, oxidation inhibitor, viscosity stabilizer, the spandex waste silk degraded product dibasic alcohol and the polyester polyol that obtain in step 2, polyether glycol, be about to polyester polyol, polyether glycol joins with the parts by weight ratio range of the raw material that uses in the synthesis phase of the spandex waste silk degraded product dibasic alcohol that obtains in step 2 by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives and forms mixture in flask, polyester polyol is that polyester polyol CMA-44 and poly-hexanodioic acid 1.4-butanediol ester glycol mix formation, after this mixture is stirred with agitator, after mixture in this flask is warming up to temperature and is 120 ℃, then this mixture was carried out vacuum hydro-extraction 2 hours, then the mixture after vacuum hydro-extraction being cooled to temperature is 80 ℃, pass into nitrogen protection in flask, add vulcabond in the mixture of the parts by weight scope of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives simultaneously after the vacuum hydro-extraction, this vulcabond is diphenylmethane isocyanate, and the mixture that has added vulcabond is stirred according to default speed with agitator, carry out the building-up reactions of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives in whipping process, obtain the Primary product of building-up reactions after the lasting 2h of stirring, the parts by weight ratio range of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives adds the moisture curing catalysts, continue the involutory Primary product that becomes reaction after oxidation inhibitor and viscosity stabilizer and carry out the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives that obtains synthesizing after building-up reactions 20min, this moisture curing catalysts is dibutyl tin laurate, the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is poured out from flask and the bottle of the sealing of packing in standby.
The parts by weight proportioning of the raw material that the DeR of described step 2 used in the stage is: 16 parts of alcoholysis agent, 48 parts of spandex waste silks and 0.16 part of DeR catalyzer.
The parts by weight proportioning of the raw material that in described step 3, the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives uses is: 20 parts of spandex waste silk part degraded product dibasic alcohol, 25 parts of polyester polyol CMA-44,8 parts of poly-hexanodioic acid 1.4-butanediol ester glycol, 39 parts of diphenylmethane isocyanate, 0.14 part of moisture curing catalytic reaction, 0.14 portion of viscosity stabilizer and 0.1 part of oxidation inhibitor.
Embodiment 2
Utilize spandex waste silk to prepare the method for the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, step is as follows:
Step 1: pretreatment stage, be about to spandex waste silk and be ground into the spandex waste silk of desired length through fiber pulverizer, the spandex waste silk of desired length is just spandex waste silk to be added like this;
step 2: DeR stage, the raw material that uses in stage in this DeR is the alcoholysis agent, DeR is with catalyzer and the spandex waste silk to be added that obtains in step 1, at first in the three-necked bottle that agitator and prolong are housed, first according to adding the alcoholysis agent in the default parts by weight ratio range dealing three-necked bottle of alcoholysis agent with spandex waste silk to be added, this alcoholysis agent is ethylene glycol, subsequently heat temperature raising is carried out in the alcoholysis agent in three-necked bottle, heat temperature raising is until temperature is 180 ℃, again in spandex waste silk to be added, 1/10 the spandex waste silk that part by weight is accounted for spandex waste silk to be added adds in three-necked bottle, then according to the parts by weight ratio range of default DeR with the raw material that uses in the shared DeR of the catalyzer stage, add the DeR catalyzer in three-necked bottle, described DeR catalyzer is zinc acetate, then with agitator, the raw material that adds in three-necked bottle is carried out the DeR of constant temperature under stirring, add remaining spandex waste silk to be added in three-necked bottle in the DeR process in batches, the reaction solution viscosity that is accompanied by the dissolving of spandex waste silk like this when DeR and carries out DeR in three-necked bottle also increases, accelerate stirring reaction according to the increase of reaction solution viscosity by default speed, when the reaction solution hydroxyl value that stirring reaction forms through DeR after four hours and in three-necked bottle is stabilized in default scope, stop stirring reaction, reaction solution in three-necked bottle is cooled to after temperature is 100 ℃, with 100 purpose filtering nets, the reaction solution in three-necked bottle is carried out filtered while hot, reaction solution after filtered while hot is cooled to the yellow thick liquid that obtains after normal temperature, be spandex waste silk degraded product dibasic alcohol, this DeR product is sealed save backup,
step 3: the synthesis phase of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, the raw material that uses at the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is vulcabond, the moisture curing catalysts, oxidation inhibitor, viscosity stabilizer, the spandex waste silk degraded product dibasic alcohol and the polyester polyol that obtain in step 2, polyether glycol, be about to polyester polyol, polyether glycol joins with the parts by weight ratio range of the raw material that uses in the synthesis phase of the spandex waste silk degraded product dibasic alcohol that obtains in step 2 by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives and forms mixture in flask, polyester polyol is that polyester polyol CMA-44 and poly-hexanodioic acid 1.4-butanediol ester glycol mix formation, after this mixture is stirred with agitator, after mixture in this flask is warming up to temperature and is 130 ℃, then this mixture was carried out vacuum hydro-extraction 3 hours, then the mixture after vacuum hydro-extraction being cooled to temperature is 80 ℃, pass into nitrogen protection in flask, add vulcabond in the mixture of the parts by weight scope of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives simultaneously after the vacuum hydro-extraction, this vulcabond is the terephthalylidene vulcabond, and the mixture that has added vulcabond is stirred according to default speed with agitator, carry out the building-up reactions of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives in whipping process, obtain the Primary product of building-up reactions after the lasting 2h of stirring, the parts by weight ratio range of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives adds the moisture curing catalysts, continue the involutory Primary product that becomes reaction after oxidation inhibitor and viscosity stabilizer and carry out the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives that obtains synthesizing after building-up reactions 20min, this moisture curing catalysts is dibutyl tin laurate, the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is poured out from flask and the bottle of the sealing of packing in standby.
The parts by weight proportioning of the raw material that the DeR of described step 2 used in the stage is: 16 parts of alcoholysis agent, 32 parts of spandex waste silks and 0.1 part of DeR catalyzer.
The parts by weight proportioning of the raw material that in described step 3, the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives uses is: 20 parts of spandex waste silk part degraded product dibasic alcohol, 30 parts of polyester polyol CMA-44,10 parts of poly-hexanodioic acid 1.4-butanediol ester glycol, 30 parts of terephthalylidene vulcabond, 0.13 part of moisture curing catalysts, 0.1 portion of viscosity stabilizer and 0.1 part of oxidation inhibitor.
Embodiment 3
Utilize spandex waste silk to prepare the method for the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, step is as follows:
Step 1: pretreatment stage, be about to spandex waste silk and be ground into the spandex waste silk of desired length through fiber pulverizer, the spandex waste silk of desired length is just spandex waste silk to be added like this;
step 2: DeR stage, the raw material that uses in stage in this DeR is the alcoholysis agent, DeR is with catalyzer and the spandex waste silk to be added that obtains in step 1, at first in the three-necked bottle that agitator and prolong are housed, first according to adding the alcoholysis agent in the default parts by weight ratio range dealing three-necked bottle of alcoholysis agent with spandex waste silk to be added, this alcoholysis agent is 1, the 4-butyleneglycol, subsequently heat temperature raising is carried out in the alcoholysis agent in three-necked bottle, heat temperature raising is until temperature is 180 ℃, again in spandex waste silk to be added, 1/10 the spandex waste silk that part by weight is accounted for spandex waste silk to be added adds in three-necked bottle, then according to the parts by weight ratio range of default DeR with the raw material that uses in the shared DeR of the catalyzer stage, add the DeR catalyzer in three-necked bottle, described DeR catalyzer is potassium acetate, then with agitator, the raw material that adds in three-necked bottle is carried out the DeR of constant temperature under stirring, add remaining spandex waste silk to be added in three-necked bottle in the DeR process in batches, the reaction solution viscosity that is accompanied by the dissolving of spandex waste silk like this when DeR and carries out DeR in three-necked bottle also increases, accelerate stirring reaction according to the increase of reaction solution viscosity by default speed, when the reaction solution hydroxyl value that stirring reaction forms through DeR after four hours and in three-necked bottle is stabilized in default scope, stop stirring reaction, reaction solution in three-necked bottle is cooled to after temperature is 100 ℃, with 100 purpose filtering nets, the reaction solution in three-necked bottle is carried out filtered while hot, reaction solution after filtered while hot is cooled to the yellow thick liquid that obtains after normal temperature, be spandex waste silk degraded product dibasic alcohol, this DeR product is sealed save backup,
step 3: the synthesis phase of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, the raw material that uses at the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is vulcabond, the moisture curing catalysts, oxidation inhibitor, viscosity stabilizer, the spandex waste silk degraded product dibasic alcohol and the polyester polyol that obtain in step 2, polyether glycol, be about to polyester polyol, polyether glycol joins with the parts by weight ratio range of the raw material that uses in the synthesis phase of the spandex waste silk degraded product dibasic alcohol that obtains in step 2 by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives and forms mixture in flask, polyester polyol is that the poly-hexanodioic acid 1.4-butanediol ester glycol of polyester polyol CMA-44 and 8g mixes formation, after this mixture is stirred with agitator, after mixture in this flask is warming up to temperature and is 130 ℃, then this mixture was carried out vacuum hydro-extraction 3 hours, then the mixture after vacuum hydro-extraction being cooled to temperature is 80 ℃, pass into nitrogen protection in flask, add vulcabond in the mixture of the parts by weight scope of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives simultaneously after the vacuum hydro-extraction, this vulcabond is diphenylmethanediisocyanate, and the mixture that has added vulcabond is stirred according to default speed with agitator, carry out the building-up reactions of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives in whipping process, obtain the Primary product of building-up reactions after the lasting 2h of stirring, the parts by weight ratio range of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives adds the moisture curing catalysts, continue the involutory Primary product that becomes reaction after oxidation inhibitor and viscosity stabilizer and carry out the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives that obtains synthesizing after building-up reactions 20min, this moisture curing catalysts is dibutyl tin laurate, the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is poured out from flask and the bottle of the sealing of packing in standby.
The parts by weight proportioning of the raw material that the DeR of described step 2 used in the stage is: 16 parts of alcoholysis agent, 48 parts of spandex waste silks and 0.3 part of DeR catalyzer.
The parts by weight proportioning of the raw material that in described step 3, the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives uses is: 20 parts of spandex waste silk part degraded product dibasic alcohol, 30 parts of CMA-44 and 10 parts of poly-hexanodioic acid 1.4-butanediol ester glycol, 33 parts of diphenylmethanediisocyanates, 0.14 part of moisture curing catalysts, 0.14 portion of viscosity stabilizer and 0.1 part of oxidation inhibitor.
Embodiment 4
Utilize spandex waste silk to prepare the method for the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, step is as follows:
Step 1: pretreatment stage, be about to spandex waste silk and be ground into the spandex waste silk of desired length through fiber pulverizer, the spandex waste silk of desired length is just spandex waste silk to be added like this;
step 2: DeR stage, the raw material that uses in stage in this DeR is the alcoholysis agent, DeR is with catalyzer and the spandex waste silk to be added that obtains in step 1, at first in the three-necked bottle that agitator and prolong are housed, first according to adding the alcoholysis agent in the default parts by weight ratio range dealing three-necked bottle of alcoholysis agent with spandex waste silk to be added, this alcoholysis agent is the 1.3-propylene glycol, subsequently heat temperature raising is carried out in the alcoholysis agent in three-necked bottle, heat temperature raising is until temperature is 180 ℃, again in spandex waste silk to be added, 1/10 the spandex waste silk that part by weight is accounted for spandex waste silk to be added adds in three-necked bottle, then according to the parts by weight ratio range of default DeR with the raw material that uses in the shared DeR of the catalyzer stage, add the DeR catalyzer in three-necked bottle, described DeR catalyzer is potassium acetate, then with agitator, the raw material that adds in three-necked bottle is carried out the DeR of constant temperature under stirring, add remaining spandex waste silk to be added in three-necked bottle in the DeR process in batches, the reaction solution viscosity that is accompanied by the dissolving of spandex waste silk like this when DeR and carries out DeR in three-necked bottle also increases, accelerate stirring reaction according to the increase of reaction solution viscosity by default speed, when the reaction solution hydroxyl value that stirring reaction forms through DeR after four hours and in three-necked bottle is stabilized in default scope, stop stirring reaction, reaction solution in three-necked bottle is cooled to after temperature is 100 ℃, with 100 purpose filtering nets, the reaction solution in three-necked bottle is carried out filtered while hot, reaction solution after filtered while hot is cooled to the yellow thick liquid that obtains after normal temperature, be spandex waste silk degraded product dibasic alcohol, this DeR product is sealed save backup,
step 3: the synthesis phase of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, the raw material that uses at the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is vulcabond, the moisture curing catalysts, oxidation inhibitor, viscosity stabilizer, the spandex waste silk degraded product dibasic alcohol and the polyester polyol that obtain in step 2, polyether glycol, be about to polyester polyol, polyether glycol joins with the parts by weight ratio range of the raw material that uses in the synthesis phase of the spandex waste silk degraded product dibasic alcohol that obtains in step 2 by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives and forms mixture in flask, polyester polyol is that polyester polyol CMA-44 and poly-hexanodioic acid 1.4-butanediol ester glycol mix formation, after this mixture is stirred with agitator, after mixture in this flask is warming up to temperature and is 130 ℃, then this mixture was carried out vacuum hydro-extraction 3 hours, then the mixture after vacuum hydro-extraction being cooled to temperature is 80 ℃, pass into nitrogen protection in flask, add vulcabond in the mixture of the parts by weight scope of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives simultaneously after the vacuum hydro-extraction, this vulcabond is diphenylmethanediisocyanate, and the mixture that has added vulcabond is stirred according to default speed with agitator, carry out the building-up reactions of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives in whipping process, obtain the Primary product of building-up reactions after the lasting 2h of stirring, the parts by weight ratio range of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives adds the moisture curing catalysts, continue the involutory Primary product that becomes reaction after oxidation inhibitor and viscosity stabilizer and carry out the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives that obtains synthesizing after building-up reactions 20min, this moisture curing catalysts is dibutyl tin laurate, the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is poured out from flask and the bottle of the sealing of packing in standby.
The parts by weight proportioning of the raw material that the DeR of described step 2 used in the stage is: 16 parts of alcoholysis agent, 64 parts of spandex waste silks and 0.48 part of DeR catalyzer.
The parts by weight proportioning of the raw material that in described step 3, the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives uses is: 25 parts of spandex waste silk part degraded product dibasic alcohol, 30 parts of polyester polyol CMA-44,8 parts of poly-hexanodioic acid 1.4-butanediol ester glycol, 45 parts of diphenylmethanediisocyanates, 0.13 part of moisture curing catalysts, 0.13 portion of viscosity stabilizer and 0.1 part of oxidation inhibitor.
Claims (8)
1. a method of utilizing spandex waste silk to prepare the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, is characterized in that, step is as follows:
Step 1: pretreatment stage, be about to spandex waste silk and be ground into the spandex waste silk of desired length through fiber pulverizer, the spandex waste silk of desired length is just spandex waste silk to be added like this;
step 2: DeR stage, the raw material that uses in stage in this DeR is the alcoholysis agent, DeR is with catalyzer and the spandex waste silk that obtains in step 1, at first in the three-necked bottle that agitator and prolong are housed, first according to the parts by weight proportioning of default alcoholysis agent with spandex waste silk to be added, add the alcoholysis agent in the dealing three-necked bottle, subsequently heat temperature raising is carried out in the alcoholysis agent in three-necked bottle, heat temperature raising is until temperature is 180-200 ℃, again in spandex waste silk to be added, 1/10 the spandex waste silk that part by weight is accounted for spandex waste silk to be added adds in three-necked bottle, then according to the parts by weight ratio range of default DeR with the raw material that uses in the shared DeR of the catalyzer stage, add the DeR catalyzer in three-necked bottle, then with agitator, the raw material that adds in three-necked bottle is carried out the DeR of constant temperature under stirring, add remaining spandex waste silk to be added in three-necked bottle in the DeR process in batches, the reaction solution viscosity that is accompanied by the dissolving of spandex waste silk like this when DeR and carries out DeR in three-necked bottle also increases, accelerate stirring reaction according to the increase of reaction solution viscosity by default speed, when the reaction solution hydroxyl value that stirring reaction forms through DeR after four hours and in three-necked bottle is stabilized in default scope, stop stirring reaction, reaction solution in three-necked bottle is cooled to after temperature range is 95 ℃-105 ℃, with 100 ~ 120 purpose filtering nets, the reaction solution in three-necked bottle is carried out filtered while hot, reaction solution after filtered while hot is cooled to the yellow thick liquid that obtains after normal temperature, be spandex waste silk degraded product dibasic alcohol, this DeR product is sealed save backup,
step 3: the synthesis phase of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives, the raw material that uses at the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is vulcabond, the moisture curing catalysts, oxidation inhibitor, viscosity stabilizer, the spandex waste silk degraded product dibasic alcohol and the polyester polyol that obtain in step 2, polyether glycol, be about to polyester polyol, polyether glycol joins with the parts by weight proportioning of the raw material that uses in the synthesis phase of the spandex waste silk degraded product dibasic alcohol that obtains in step 2 by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives and forms mixture in flask, after this mixture is stirred with agitator, after mixture in this flask is warming up to temperature range and is 120 ~ 130 ℃, then this mixture was carried out vacuum hydro-extraction 2-3 hour, then the mixture after vacuum hydro-extraction being cooled to temperature range is 70-80 ℃, pass into nitrogen protection in flask, add vulcabond in the mixture of the parts by weight scope of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives simultaneously after the vacuum hydro-extraction, and the mixture that has added vulcabond is stirred according to default speed with agitator, carry out the building-up reactions of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives in whipping process, obtain the Primary product of building-up reactions after the lasting 2h of stirring, the parts by weight ratio range of the raw material that uses in the synthesis phase by the glutinous agent of default shared One-Component Moisture-Curable Polyurethane Hot Melt Adhesives adds the moisture curing catalysts, continue the involutory Primary product that becomes reaction after oxidation inhibitor and viscosity stabilizer and carry out the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives that obtains synthesizing after building-up reactions 20min, the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives is poured out from flask and the bottle of the sealing of packing in standby.
2. the spandex waste silk that utilizes according to claim 1 prepares the method that One-Component Moisture-Curable Polyurethane Hot Melt Adhesives sticks agent, it is characterized in that, alcoholysis agent in described step 2 is the polyvalent alcohol of 2-10 carbon atom, the polyvalent alcohol that the alcoholysis agent used of described DeR is 2-10 carbon atom, the polyvalent alcohol of 2-10 carbon atom comprises ethylene glycol, propylene glycol, butyleneglycol, pentanediol, hexylene glycol, glycol ether, Triethylene glycol, tetraethylene-glycol, glycerol, low-molecular-weight polyethers or polyester polyol.
3. according to claim 1 or the method for utilizing spandex waste silk to prepare the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives claimed in claim 2, it is characterized in that, described DeR used catalyst is zinc acetate, tin tetrachloride, stannous octoate, triethylamine or dibutyl tin laurate, also can adopt tin tetrachloride, stannous octoate, triethylamine, dibutyl tin laurate to be combined with each other according to default ratio and form the DeR used catalyst.
4. the parts by weight proportioning that according to claim 1 or the method for utilizing spandex waste silk to prepare the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives claimed in claim 2, it is characterized in that the raw material that the DeR of described step 2 used in the stage is: 16-33 part small molecules polyvalent alcohol, 33-80 part spandex waste silk and 0.2-0.5 part DeR catalyzer.
5. according to claim 1 or the method for utilizing spandex waste silk to prepare the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives claimed in claim 2, it is characterized in that the polyvalent alcohol in the synthesis phase of the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives in described step 3 is the pure and mild polyether glycol of polyester polyols, the molecular weight of the pure and mild polyether glycol of polyester polyols is in 1000～5000 scopes.
6. according to claim 1 or the method for utilizing spandex waste silk to prepare the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives claimed in claim 2, it is characterized in that described vulcabond comprises aromatic series, aliphatics and alicyclic diisocyanate, but be not limited to tolylene diisocyanate (TDI), diphenylmethanediisocyanate (MDI), the mixture of one or more in isophorone diisocyanate (IPDI), hexamethylene diisocyanate (HDI), xylylene diisocyanate (XDI).
7. according to claim 1 or the method for utilizing spandex waste silk to prepare the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives claimed in claim 2, it is characterized in that described moisture curing catalysts is one or more the composite uses in organic tin, organo-bismuth class or amine.
8. the parts by weight proportioning that according to claim 1 or the method for utilizing spandex waste silk to prepare the glutinous agent of One-Component Moisture-Curable Polyurethane Hot Melt Adhesives claimed in claim 2, it is characterized in that the raw material that the synthesis phase of the glutinous agent of this One-Component Moisture-Curable Polyurethane Hot Melt Adhesives in described step 3 uses is: 20-28 part spandex waste silk part degraded product dibasic alcohol, 18-34 part polyester polyol, 5-12 part high crystalline polyvalent alcohol, 30 ~ 45 parts of vulcabond, 0.1 ~ 0.15 part of moisture curing catalysts catalyzer, 0.1 ~ 0.15 portion of viscosity stabilizer and 0.1 ~ 0.5 part of oxidation inhibitor.