CN103146092A - Blended, easily tearable wire and cable material and production method thereof - Google Patents
Blended, easily tearable wire and cable material and production method thereof Download PDFInfo
- Publication number
- CN103146092A CN103146092A CN2011103990052A CN201110399005A CN103146092A CN 103146092 A CN103146092 A CN 103146092A CN 2011103990052 A CN2011103990052 A CN 2011103990052A CN 201110399005 A CN201110399005 A CN 201110399005A CN 103146092 A CN103146092 A CN 103146092A
- Authority
- CN
- China
- Prior art keywords
- parts
- cable material
- wire
- product
- blended
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a blended, easily tearable wire and cable material. The wire and cable material comprises the following components, by mass, 100 parts of resin, 60-90 parts of dioctyl phthalate, 60 parts of chlorinated polyethylene, 60 parts of calcium carbonate, 0.8 parts of polyethylene wax, 10 parts of Ca-Zn composite stabilizer and a toner added in according to the color needed by a user. The material provided by the invention increases the toughness of a product; the product is torn in one direction without deviation when being torn in a longitudinal direction, has good transverse toughness, is not easy to crack, and improves the product safety performance.
Description
Technical field:
The present invention relates to the wire cable material field, be specifically related to a kind of blend and easily tear wire cable material and preparation method.
Background technology:
Electric wire is widely used in the transmission of energy and information at present, the electric wire coating material made from traditional macromolecular material (PVC), when the electric wire that applies to require easily tear, what general PVC material easily tore the material employing is to increase the intensity that the way of filling reduces the PVC wire cable material, this method causes electric wire there is no toughness, easily ftracture in production and use procedure, too many owing to filling, product surface is rough.
Summary of the invention:
The purpose of this invention is to provide a kind of blend and easily tear wire cable material and preparation method, can increase the toughness of product, tear according to a direction when longitudinal direction tears, do not depart from, transverse toughness is good, is not easy cracking, improves the safety performance of product.
The object of the present invention is achieved like this, and wire cable material is easily torn in a kind of blend, it is characterized in that: each main auxiliary material composition by mass fraction is:
Resin: 100 parts
O-phthalic acid dibutyl ester: 60-90 part
Chlorinatedpolyethylene: 60 parts
Calcium carbonate: 60 parts
Polyethylene wax: 0.8 part
Calcium-zinc composite stabilizing agent: 10 parts
Toner: join according to user's needs color.
The present invention includes following steps: batching → stirrer stirs → internal mixer internally mix → twin-screw extrusion → single Screw Extrusion → pelletizing → cooling → packing.
The present invention has increased the toughness of product, tears according to a direction when longitudinal direction tears, does not depart from, and transverse toughness is good, is not easy cracking, has improved the safety performance of product.
Embodiment:
Wire cable material is easily torn in a kind of blend, it is characterized in that: each main auxiliary material composition by mass fraction is:
Resin: 100 parts
O-phthalic acid dibutyl ester: 60-90 part
Chlorinatedpolyethylene: 60 parts
Calcium carbonate: 60 parts
Polyethylene wax: 0.8 part
Calcium-zinc composite stabilizing agent: 10 parts
Toner: join according to user's needs color.
The present invention includes following steps: batching → stirrer stirs → internal mixer internally mix → twin-screw extrusion → single Screw Extrusion → pelletizing → cooling → packing.During concrete enforcement, accurately take various raw materials according to formula, put into 500 liters of stirrers, high-speed stirring 0.5 minute; The material that stirs is dropped into internal mixer intensification degree to 130 ℃, the twin screw extruder extruding pelletization, temperature is controlled between 120-130 ℃, then the single screw extrusion machine extruding pelletization, is controlled between 100-120 ℃ pelletizing, cooling, packing.
Claims (2)
1. wire cable material is easily torn in a blend, it is characterized in that: each main auxiliary material composition by mass fraction is:
Resin: 100 parts
O-phthalic acid dibutyl ester: 60-90 part
Chlorinatedpolyethylene: 60 parts
Calcium carbonate: 60 parts
Polyethylene wax: 0.8 part
Calcium-zinc composite stabilizing agent: 10 parts
Toner: join according to user's needs color.
2. a kind of blend according to claim 1 preparation method of easily tearing wire cable material, it is characterized in that: comprise the following steps: batching → stirrer stirs → internal mixer internally mix → twin-screw extrusion → single Screw Extrusion → pelletizing → cooling → packing.