CN103131859B - Comprehensive recycling method for metals in superalloy scrap - Google Patents
Comprehensive recycling method for metals in superalloy scrap Download PDFInfo
- Publication number
- CN103131859B CN103131859B CN201310070067.8A CN201310070067A CN103131859B CN 103131859 B CN103131859 B CN 103131859B CN 201310070067 A CN201310070067 A CN 201310070067A CN 103131859 B CN103131859 B CN 103131859B
- Authority
- CN
- China
- Prior art keywords
- metal
- powder
- metals
- chlorine
- nitrogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a comprehensive recycling method for metals in superalloy scrap. The method comprises the following steps of: melting and atomizing nickel-based superalloy scrap into metal powder in certain particle size distribution by adopting a melting and atomizing process, constructing a metal powder bed layer by placing the metal powder in a fixed fluidized bed, placing the fixed fluidized bed in a tubular furnace, controlling the tubular furnace to be at a certain temperature, and enabling reactant gas with a certain pressure to pass through the metal powder bed layer from bottom to top, so that the reactant gas and nickel-based superalloy powder react at a certain reaction temperature to generate metallic oxides and metal chlorides; and separating different metals by utilizing that saturated vapor pressures of different metallic chlorides are different, then respectively treating the metals in a known manner, and recycling rare and precious metals, especially the metals such as rhenium, molybdenum and ruthenium. By adopting the comprehensive recycling method provided by the invention, the aim of comprehensively recycling valuable metals can be achieved, and the recycling efficiency of rare metals can be greatly improved; and the process is concise, the cost is low, and no pollution is produced.
Description
Technical field
The present invention relates to nickel base superalloy, particularly contain the comprehensive recovering process of the nickel base superalloy waste material of rare precious metal rhenium, ruthenium, tungsten, molybdenum, tantalum etc.
Background technology
Nickel base superalloy refers to taking nickel as base the austenitic alloy of (nickeliferous more than 50%).There is higher-strength, better anti-oxidant and corrosion resistance nature, the good over-all properties such as fatigue property, fracture toughness property 650～1100 DEG C of scopes.
Nickel-base alloy contains more than ten kind of alloying element, and wherein Cr mainly plays anti-oxidant and anticorrosive effect, and other elements mainly play strengthening effect.Can be divided into according to their strengthening effect mode: solution strengthening element, as tungsten, molybdenum, cobalt, chromium and vanadium etc.; Precipitation strength element, as aluminium, titanium, niobium and tantalum; Grain-boundary strengthening element, as boron, zirconium, magnesium and yttrium etc.
Nickel base superalloy is used for manufacturing aero-jet engine, the hot-end component of various industry gas turbine widely.Also can be used as the high-temperature component of rocket engine, nuclear reactor, petrochemical complex and Energy conversion equipment etc.At present, on advanced engine, nickelalloy has accounted for the half of gross weight, not only turbine blade and combustion chamber, and also even rear what compressor blade of the turbine disk is also brought into use nickelalloy.In present generation aircraft engine, turbine blade almost all adopts nickel-base alloy manufacture.Nickelalloy can become the leading of superalloy, its major cause, and the one, in nickel-base alloy, more alloying element can be dissolved, and good structure stability can be kept; The 2nd, can form compound g'[Ni3 (Al, Ti) between the orderly A3B shaped metal of coherence] as strengthening phase, alloy is effectively strengthened, obtain than iron-base superalloy and the higher hot strength of cobalt base superalloy; The 3rd, have than the better anti-oxidant and resistance to combustion gas corrosion ability of iron-base superalloy containing the nickel-base alloy of chromium.
Because the alloying element in nickel base superalloy is numerous, after its service hours finishes, carry out recycle applications more difficult, but its alloying element containing is the few strategic raw metal of nature reserves.Resource national conditions based on China, the scarcity of resources such as nickel, cobalt, rhenium, tantalum, tungsten, molybdenum, no matter from environmental benefit and economic benefit, are all very significant to the recycling of nickel base superalloy waste material.
The recovery of nickel base superalloy waste material mainly contains two kinds of pyrogenic process and hydrometallurgys, but due to multiple considerations such as the complex characteristics of its technique and economic evaluation, environmental evaluations, not yet has a kind of economically viable recovery process to be put into practice.The current feature for nickel base superalloy, as, complex chemical composition is changeable, and main flow process using wet processing carries out comprehensive reutilization, and its technique generally comprises the technological processs such as leaching, the pre-removal of impurities of chemistry, abstraction impurity removal, Separation of nickel and cobalt, but this technical process is long, energy consumption is high, acid consumption is large, and environmental protection treatment cost is high, and rare metal direct yield is low, easily loss on stream, economic benefit is not obvious.
Summary of the invention
For above problem, the object of the present invention is to provide a kind of economy, high-temperature alloy waste material metal efficient, environmental protection comprehensively to reclaim novel process, with simplification of flowsheet, reduce the energy consumption of whole operation, and the consumption of reduction mineral acid, reduce in environmental requirement, especially improve rare metal direct yield, reclaim to greatest extent high price rare metal, improve the economic benefit of whole technique.
The present invention realizes by following technical proposal: a kind of comprehensive method reclaiming of high-temperature alloy waste material metal, and the following each step of process:
Nickel base superalloy waste material cutting particle is become to 1～2cm, carry out again melting, and in aerosolization mode by its atomization as alloyed metal powder, by alloyed metal powder and particle diameter be 100～150 μ m silicon oxide powder by volume 1:1 mix, build metal-powder bed, then with the heat-up rate of 2～5 DEG C/min, metal-powder bed is warming up to 400～500 DEG C, pass into from bottom to up oxygen or pressurized air simultaneously, be incubated 1～3 hour, be cooled to subsequently 300～400 DEG C, and stop passing into oxygen or pressurized air, then pass into from bottom to up nitrogen and chlorine, at 300～400 DEG C, be incubated 1～3 hour, be warming up to 500～600 DEG C with 5～10 DEG C/min again, be incubated 1～3 hour, be cooled to subsequently below 200 DEG C, stop passing into nitrogen and chlorine, gas (the ReCl producing during this time
5, WCl
6, MoCl
5, TaCl
5and RuCl
3) collect and obtain solution A and (contain high rhenium acid group ion, tungstate ion, molybdenum acid ion and TaCl by water
5and RuCl
3the aqueous solution), and obtain rhenium, tungsten, molybdenum, tantalum, ruthenium through ordinary method separating-purifying, reaction residue B on metal-powder bed obtains solution C and filter residue D through washing, filter residue D being placed at 35～45 DEG C of temperature to mass concentration and being 10～30% hydrochloric acid soln soaks 1～3 hour, obtain after filtration again solution E and filter residue F, filter residue F is given up, and will after solution C and solution E merging, obtain nickel, cobalt, copper through ordinary method separating-purifying.
Described alloyed metal powder is that atomization is the alloyed metal powder of 10～50 μ m.
The thickness of described metal-powder bed is 2～10cm.
Describedly pass into oxygen or compressed-air actuated pressure is 1.5～2 normal atmosphere, air flow rate is 200～2000ml/ minute.
The described pressure that passes into nitrogen and chlorine is 1.2～2 normal atmosphere, and the flow of nitrogen is 200～2000ml/ minute, and the flow of chlorine is 100～1000ml/ minute, and nitrogen is controlled at 2～4:1 with chlorine flowrate ratio.
Describedly obtaining rhenium, tungsten, molybdenum, tantalum, ruthenium through ordinary method separating-purifying, is in solution A, to add ammoniacal liquor, obtains ammonium perrhenate precipitation, carries out solid-liquid separation, solid-state ammonium perrhenate again through repeatedly dissolve purify dry after logical hydrogen reduction can obtain rhenium metal; Other are the separation of purifying respectively of ripe and known road technology as the rare precious metals such as tungsten, molybdenum, tantalum, ruthenium all can adopt.
Describedly obtain nickel, cobalt, copper through ordinary method separating-purifying, the solution of nickelous chloride, cobalt chloride and cupric chloride is separated through extraction process, and the solution after separating is entered to electrolyzer, utilize known electrolysis process can obtain high-purity metallic nickel, cobalt, copper.
Know-why of the present invention is to adopt the metal-powder that atomized molten technique is certain grain size distribution by nickel base superalloy waste material atomized molten, and by metal-powder in the certain thickness metal-powder bed of fixed fluidized bed middle structure, the fixed fluidized bed tube furnace that is placed in, tube furnace is controlled to certain temperature, simultaneously by the reactant gases with certain pressure as oxygen, chlorine, from bottom to top by metal-powder bed, reactant gases and Ni-base Superalloy Powder are reacted under certain temperature of reaction, generate metal oxide and muriate, and utilize the muriatic saturated vapor pressure difference of different metal, different metal is separated, and will process respectively in known manner subsequently, reclaim rare precious metal, particularly rhenium metal, molybdenum, ruthenium.Adopt above processing step, nickel base superalloy waste material is obtained to the larger powdered alloy of specific surface area through atomized molten technique, be conducive to the contact area of augmenting response gas and alloy, improve speed of response and efficiency.At high temperature pass into oxygen or pressurized air, be conducive to the reactions such as active metal aluminium, titanium and first generate oxide compound, reduce chlorine consumption, reduce the subsequent technique content of active metal at a low price as far as possible, simple flow, enhances productivity, and increases economic efficiency simultaneously.
Advantage and effect that the present invention possesses are:
Utilize the different metal element reaction temperature of controlling in chlorine and nickel base superalloy, generate metal chloride, especially rare metal rhenium, molybdenum, the ruthenium with different saturation vapour pressures, its muriate is gaseous state, utilizes gas solid separation that metallic element is separated.Adopt this technique, compared with other method, strong oxidizer chlorine is easy to react with metallic element generation metal chloride under hot conditions, do not need to expend a large amount of mineral acids, utilize the different saturation vapour pressure feature of metal chloride simultaneously, make different metal element, especially yttrium just carries out effective gas solid separation with other metallic elements in reaction process, greatly shorten on the one hand technical process, simplify production process, do not need a large amount of mineral acids to carry out oxide treatment simultaneously, under environmental protection pressure, rare metal rhenium simultaneously, molybdenum, the metal chloride saturated vapo(u)r of ruthenium forces down, be easy to volatilization, so first the rare technology in nickel base superalloy waste material is separated in chloridization process from metallic matrix, reach the preliminary object of separating-purifying.The different mechanism at reactant aqueous solution according to different metal muriate are processed by known technique in subsequent technique simultaneously, reach the comprehensive object reclaiming of high-valency metal, can greatly improve the direct yield of rare metal simultaneously.Obtain larger economic benefit.Unreacted chlorine tail gas can adopt known maturation process to carry out harmless treatment, and therefore this technique is that a kind of technique is terse, cost is low, free of contamination comprehensive recycling process, there is not yet relevant report both at home and abroad.
Embodiment
Below by embodiment, the present invention will be further described.
Embodiment 1
Adopting certain model nickel base superalloy is raw material, and composition is as following table:
Above-mentioned 10kg nickel base superalloy waste material cutting particle is become to 1cm, in intermediate frequency (IF) smelting crucible, carry out again melting, and in aerosolization mode by its atomization the alloyed metal powder as 23 μ m, by alloyed metal powder and particle diameter be 100 μ m silicon oxide powder (purity is greater than 99%) by volume 1:1 mix, be placed on quartz sand sandwich layer, the metal-powder bed that structure thickness is 2cm, then with the heat-up rate of 2 DEG C/min, the metal-powder bed in tube furnace is warming up to 400 DEG C, pass into from bottom to up pressure is 1.5 normal atmosphere simultaneously, air flow rate is the oxygen of 200ml/ minute, be incubated 3 hours, be cooled to subsequently 300 DEG C, and stop passing into oxygen, then passing into from bottom to up pressure is 1.2 atmospheric nitrogen and chlorine, wherein the flow of nitrogen is 200ml/ minute, the flow of chlorine is 100ml/ minute (nitrogen is controlled at 2:1 with chlorine flowrate ratio), at 300 DEG C, be incubated 3 hours, be warming up to 500 DEG C with 5 DEG C/min again, be incubated 3 hours, be cooled to subsequently below 200 DEG C, stop passing into nitrogen and chlorine, gas (the ReCl producing during this time
5, WCl
6, MoCl
5, TaCl
5and RuCl
3) collect and obtain solution A and (contain high rhenium acid group ion, tungstate ion, molybdenum acid ion and TaCl by water
5and RuCl
3the aqueous solution), and obtain rhenium, tungsten, molybdenum, tantalum, ruthenium through ordinary method separating-purifying, reaction residue B on metal-powder bed obtains solution C and filter residue D through washing, filter residue D being placed at 35 DEG C of temperature to mass concentration and being 30% hydrochloric acid soln soaks 1 hour, obtain after filtration again solution E and filter residue F, filter residue F is given up, and will after solution C and solution E merging, obtain nickel, cobalt, copper through ordinary method separating-purifying.Finally obtain molybdenum powder 156g, cobalt powder 922g, electrolytic nickel 5122g.
Embodiment 2
Adopting certain model nickel base superalloy is raw material, and composition is as following table:
Above 15kg nickel base superalloy waste material cutting particle is become to 1.5cm, in intermediate frequency (IF) smelting crucible, carry out again melting, and in aerosolization mode by its atomization the alloyed metal powder as 10 μ m, by alloyed metal powder and particle diameter be 150 μ m silicon oxide powder (purity is greater than 99%) by volume 1:1 mix, be placed on quartz sand sandwich layer, the metal-powder bed that structure thickness is 6cm, then with the heat-up rate of 5 DEG C/min, the metal-powder bed in tube furnace is warming up to 500 DEG C, pass into from bottom to up pressure is 2 normal atmosphere simultaneously, air flow rate is the oxygen of 2000ml/ minute, be incubated 2 hours, be cooled to subsequently 400 DEG C, and stop passing into oxygen, then passing into from bottom to up pressure is 2 atmospheric nitrogen and chlorine, wherein the flow of nitrogen is 2000ml/ minute, the flow of chlorine is 500ml/ minute (nitrogen is controlled at 4:1 with chlorine flowrate ratio), at 400 DEG C, be incubated 1 hour, be warming up to 600 DEG C with 10 DEG C/min again, be incubated 1 hour, be cooled to subsequently below 200 DEG C, stop passing into nitrogen and chlorine, gas (the ReCl producing during this time
5, WCl
6, MoCl
5, TaCl
5and RuCl
3) collect and obtain solution A and (contain high rhenium acid group ion, tungstate ion, molybdenum acid ion and TaCl by water
5and RuCl
3the aqueous solution), and obtain rhenium, tungsten, molybdenum, tantalum, ruthenium through ordinary method separating-purifying, reaction residue B on metal-powder bed obtains solution C and filter residue D through washing, filter residue D being placed at 40 DEG C of temperature to mass concentration and being 20% hydrochloric acid soln soaks 2 hours, obtain after filtration again solution E and filter residue F, filter residue F is given up, and will after solution C and solution E merging, obtain nickel, cobalt, copper through ordinary method separating-purifying.Finally obtain rhenium powder 401g, molybdenum powder 202g, cobalt powder 1057g, tantalum powder 932g, tungsten powder 667g, hafnium powder 19g, electrolytic nickel 8231g.
Embodiment 3
Adopting certain model nickel base superalloy is raw material, and composition is as following table:
Above 12kg nickel base superalloy waste material cutting particle is become to 2cm, in intermediate frequency (IF) smelting crucible, carry out again melting, and in aerosolization mode by its atomization the alloyed metal powder as 50 μ m, by alloyed metal powder and particle diameter be 110 μ m silicon oxide powder by volume 1:1 mix, be placed on quartz sand sandwich layer, the metal-powder bed that structure thickness is 10cm, then with the heat-up rate of 2.5 DEG C/min, the metal-powder bed in tube furnace is warming up to 450 DEG C, pass into from bottom to up pressure is 1.8 normal atmosphere simultaneously, air flow rate is the pressurized air of 1500ml/ minute, be incubated 1 hour, be cooled to subsequently 350 DEG C, and stop passing into pressurized air, then passing into from bottom to up pressure is 1.5 atmospheric nitrogen and chlorine, wherein the flow of nitrogen is 1500ml/ minute, the flow of chlorine is 500ml/ minute (nitrogen is controlled at 3:1 with chlorine flowrate ratio), at 350 DEG C, be incubated 2 hours, be warming up to 550 DEG C with 8 DEG C/min again, be incubated 2 hours, be cooled to subsequently below 200 DEG C, stop passing into nitrogen and chlorine, gas (the ReCl producing during this time
5, WCl
6, MoCl
5, TaCl
5and RuCl
3) collect and obtain solution A and (contain high rhenium acid group ion, tungstate ion, molybdenum acid ion and TaCl by water
5and RuCl
3the aqueous solution), and obtain rhenium, tungsten, molybdenum, tantalum, ruthenium through ordinary method separating-purifying, reaction residue B on metal-powder bed obtains solution C and filter residue D through washing, filter residue D being placed under temperature 45 C to mass concentration and being 10% hydrochloric acid soln soaks 3 hours, obtain after filtration again solution E and filter residue F, filter residue F is given up, and will after solution C and solution E merging, obtain nickel, cobalt, copper through ordinary method separating-purifying.Finally obtain molybdenum powder 192g, cobalt powder 1021g, tungsten powder 1058g, electrolytic nickel 9622g.
Embodiment 4
Adopting certain model nickel base superalloy is raw material, and composition is as following table:
Above 15kg nickel base superalloy waste material cutting particle is become to 1.5cm, in intermediate frequency (IF) smelting crucible, carry out again melting, and in aerosolization mode by its atomization the alloyed metal powder as 10 μ m, by alloyed metal powder and particle diameter be 150 μ m silicon oxide powder (purity is greater than 99%) by volume 1:1 mix, be placed on quartz sand sandwich layer, the metal-powder bed that structure thickness is 6cm, then with the heat-up rate of 5 DEG C/min, the metal-powder bed in tube furnace is warming up to 500 DEG C, pass into from bottom to up pressure is 2 normal atmosphere simultaneously, air flow rate is the oxygen of 2000ml/ minute, be incubated 2 hours, be cooled to subsequently 400 DEG C, and stop passing into oxygen, then passing into from bottom to up pressure is 2 atmospheric nitrogen and chlorine, wherein the flow of nitrogen is 2000ml/ minute, the flow of chlorine is 1000ml/ minute (nitrogen is controlled at 2:1 with chlorine flowrate ratio), at 400 DEG C, be incubated 1 hour, be warming up to 600 DEG C with 10 DEG C/min again, be incubated 1 hour, be cooled to subsequently below 200 DEG C, stop passing into nitrogen and chlorine, gas (the ReCl producing during this time
5, WCl
6, MoCl
5, TaCl
5and RuCl
3) collect and obtain solution A and (contain high rhenium acid group ion, tungstate ion, molybdenum acid ion and TaCl by water
5and RuCl
3the aqueous solution), and obtain rhenium, tungsten, molybdenum, tantalum, ruthenium through ordinary method separating-purifying, reaction residue B on metal-powder bed obtains solution C and filter residue D through washing, filter residue D being placed at 40 DEG C of temperature to mass concentration and being 20% hydrochloric acid soln soaks 2 hours, obtain after filtration again solution E and filter residue F, filter residue F is given up, and will after solution C and solution E merging, obtain nickel, cobalt, copper through ordinary method separating-purifying.Finally obtain rhenium powder 401g, molybdenum powder 202g, cobalt powder 1057g, tantalum powder 932g, tungsten powder 667g, hafnium powder 19g, electrolytic nickel 8231g.
Claims (4)
1. the comprehensive method reclaiming of high-temperature alloy waste material metal, is characterized in that through following each step:
Nickel base superalloy waste material cutting particle is become to 1～2cm, carry out again melting, and in aerosolization mode by its atomization as alloyed metal powder, by alloyed metal powder and particle diameter be 100～150 μ m silicon oxide powder by volume 1:1 mix, build metal-powder bed, then with the heat-up rate of 2～5 DEG C/min, metal-powder bed is warming up to 400～500 DEG C, pass into from bottom to up oxygen or pressurized air simultaneously, be incubated 1～3 hour, be cooled to subsequently 300～400 DEG C, and stop passing into oxygen or pressurized air, then pass into from bottom to up nitrogen and chlorine, at 300～400 DEG C, be incubated 1～3 hour, the pressure that wherein passes into nitrogen and chlorine is 1.2～2 normal atmosphere, the flow of nitrogen is 200～2000ml/ minute, the flow of chlorine is 100～1000ml/ minute, nitrogen is controlled at 2～4:1 with chlorine flowrate ratio, be warming up to 500～600 DEG C with 5～10 DEG C/min again, be incubated 1～3 hour, be cooled to subsequently below 200 DEG C, stop passing into nitrogen and chlorine, the gas producing is during this time collected and is obtained solution A by water, and obtain rhenium, tungsten, molybdenum, tantalum, ruthenium through ordinary method separating-purifying, reaction residue B on metal-powder bed obtains solution C and filter residue D through washing, filter residue D being placed at 35～45 DEG C of temperature to mass concentration and being 10～30% hydrochloric acid soln soaks 1～3 hour, obtain after filtration again solution E and filter residue F, filter residue F is given up, and will after solution C and solution E merging, obtain nickel, cobalt, copper through ordinary method separating-purifying.
2. the comprehensive method reclaiming of high-temperature alloy waste material metal according to claim 1, is characterized in that: described alloyed metal powder is that atomization is the alloyed metal powder of 10～50 μ m.
3. the comprehensive method reclaiming of high-temperature alloy waste material metal according to claim 1, is characterized in that: the thickness of described metal-powder bed is 2～10cm.
4. the comprehensive method reclaiming of high-temperature alloy waste material metal according to claim 1, is characterized in that: described in pass into oxygen or compressed-air actuated pressure is 1.5～2 normal atmosphere, air flow rate is 200～2000ml/ minute.