CN103129199A - Metal decorating machining technique - Google Patents
Metal decorating machining technique Download PDFInfo
- Publication number
- CN103129199A CN103129199A CN2013100825137A CN201310082513A CN103129199A CN 103129199 A CN103129199 A CN 103129199A CN 2013100825137 A CN2013100825137 A CN 2013100825137A CN 201310082513 A CN201310082513 A CN 201310082513A CN 103129199 A CN103129199 A CN 103129199A
- Authority
- CN
- China
- Prior art keywords
- drying
- tinplate
- processing
- drying room
- carried out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of ironwork printing, in particular to a metal decorating machining technique. The technique includes the following steps: cleaning tinplate with water, and then wiping the tinplate with organic solvent to remove dust; arranging bottoming coating material on the tinplate, and then treating the tinplate in a drying mode; and then respectively arranging white coating material on the tinplate and treating the tinplate in a drying mode, carrying out yellow printing ink printing operation and treating the tinplate in a drying mode, carrying out red printing ink prinking operation and treating the tinplate in a drying mode, carrying out blue printing ink prinking operation and treating the tinplate in a drying mode, carrying out black printing ink prinking operation, treating the tinplate in a drying and vanishing mode, and sending the tinplate into a drying room for drying treatment after the vanishing treatment. According to the metal decorating machining technique, not only can dust be effectively removed through cleaning, but also the organic solvent which is insoluble in water can be effectively cleaned up, the investment in equipment is effectively reduced, the coloring materials can not yellow, and the glossiness is better.
Description
Technical field
The present invention relates to the ironwork print field, specifically a kind of tin graphed sheet processing technology.
Background technology
Tin graphed sheet is exactly impressing pattern on tinplate, is mainly the physical characteristic of utilizing water, China ink to repel each other, by squeegee pressure, the forme pattern is printed onto on tinplate, belongs to the principle of offset lithographic.Development along with the epoch, growth in the living standard, use in the situation that food and beverage, technique pail pack are a large amount of, the tin graphed sheet coating process requirements at the higher level have been proposed, tradition tin graphed sheet processing technology comprises that dedusting-upper base oil-solidify-upper polychrome printing ink-curings-glazing wet goods step, traditional coating process exist that tinplate cleans not totally, use equipment is many, input cost is large, production site is large, the easy yellowing of coating, the bad shortcoming of glossiness.
Summary of the invention
For above-mentioned weak point of the prior art, the present invention aims to provide that a kind of cleaning is more clean, used device still less, the better tin graphed sheet processing technology of printing effect.
For solving the problems of the technologies described above, tin graphed sheet processing technology of the present invention comprises the steps:
(1) the tinplate water is cleaned, and then carry out the wiping dedusting with organic solvent;
(2) tinplate after adopting coating machine with wiping dedusting in step (1) carries out upper primer base operation, after upper complete primer base, tinplate is sent into drying room and carries out drying and processing, and the drying and processing time is 0.5h~1h;
(3) tinplate after drying and processing in step (2) is carried out upper whitewash operation by coating machine again; Gone up and tinplate has been sent into drying room after whitewash and carry out drying and processing, the drying and processing time is 0.5h~1h;
(4) tinplate after drying and processing in step (3) is carried out the Yellow ink printing operation by printing machine; After Yellow ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h;
(5) tinplate after drying and processing in step (4) is carried out the red ink printing operation by printing machine again; After red ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h;
(6) tinplate after drying and processing in step (5) is carried out the blue ink printing operation by printing machine again; After blue ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h;
(7) tinplate after drying and processing in step (6) is carried out the black ink printing operation by printing machine again; After black ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h;
(8) tinplate after drying and processing in step (7) is carried out Lacquer finish and process, after Lacquer finish is finished dealing with, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h.
Concrete, in described step (1), the temperature of water is between 25 ℃-40 ℃, the organic solvent temperature is between 15 ℃-25 ℃.
In described step (3), the dry film amount of whitewash is 10g/m
2-25g/m
2, viscosity is 80s-100s, the drying room temperature is 170 ℃-175 ℃.
In described step (4), the dry film amount of Yellow ink is 3g/m
2-5g/m
2, the drying room temperature is 165 ℃-170 ℃.
In described step (5), the dry film amount of red ink is 3g/m
2-5g/m
2, the drying room temperature is 160 ℃-165 ℃.
In described step (6), the dry film amount of blue ink is 3g/m
2-5g/m
2, the drying room temperature is 155 ℃-160 ℃.
In described step (7), the dry film amount of black ink is 3g/m
2-5g/m
2, the drying room temperature is 150 ℃-155 ℃.
In described step (8), Lacquer finish processing employing dry film amount is 15g/m
2-20g/m
2, viscosity is the overprint coating of 60s-80s, the drying room temperature is 150 ℃-155 ℃.
Organic solvent described in described step (1) is absolute ethyl alcohol.
Described drying room is the tunnel type drying room, and the length of this tunnel type drying room is 20m-30m.
Tin graphed sheet processing technology of the present invention, owing to cleaning through water before using absolute ethyl alcohol to carry out wiping, not only effectively remove dust, and more water-fast organic solvent is cleaned up, owing to adopting same coating machine to carry out upper primer base, upper whitewash to tinplate; Adopt same printing machine to carry out Yellow ink printing, red ink printing, blue ink printing, blacking printing to tinplate, effectively reduced the input of equipment, and after ink printing is each time completed and tinplate is sent into drying room, the drying room temperature is suitably turned down 1 ℃-5 ℃, guarantee that not only preorder coating and printing ink can yellowing, and glossiness is better.
Description of drawings
In order to be illustrated more clearly in the embodiment of the present invention or technical scheme of the prior art, the below will do to introduce simply to the accompanying drawing of required use in embodiment or description of the Prior Art, apparently, accompanying drawing in the following describes is only some embodiments of the present invention, for those of ordinary skills, under the prerequisite of not paying creative work, can also obtain according to these accompanying drawings other accompanying drawing.
Fig. 1 is the flow chart of tin graphed sheet processing technology of the present invention.
The specific embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is only a part of embodiment of the present invention, rather than whole embodiment.Based on the embodiment in the present invention, those of ordinary skills belong to the scope of protection of the invention not making the every other embodiment that obtains under the creative work prerequisite.
As shown in Figure 1, tin graphed sheet processing technology of the present invention comprises the steps:
(1) the tinplate water is cleaned, and then carry out the wiping dedusting with organic solvent, described organic solvent is absolute ethyl alcohol;
(2) tinplate after adopting coating machine with wiping dedusting in step (1) carries out upper primer base operation, gone up and tinplate has been sent into drying room after primer base and carry out drying and processing, the drying and processing time is 0.5h~1h, and in concrete practice, the drying and processing time is 30 minutes, and primer base can be 25
#Primer, this coating is equipped with 214 by epoxy resin and amino resins
#Diluent forms, and this kind primer base can improve color coating to the adhesive force of tinplate, makes color coating incrust in the techniques such as rushing, press, draw, pull out of jug forming processed;
(3) tinplate after drying and processing in step (2) is carried out upper whitewash operation by coating machine again; Gone up and tinplate has been sent into drying room after whitewash and carry out drying and processing, the drying and processing time is 0.5h~1h; In concrete practice, the drying and processing time is 30 minutes; The dry film amount of whitewash is 10g/m
2-25g/m
2, viscosity is 80s-100s, and the drying room temperature is 170 ℃-175 ℃, and whitewash mainly is comprised of titanium dioxide, resin, three parts of solvent, if the whitewash form and aspect are not ideal enough, can add some toners, allocates different separately whitewashes;
(4) tinplate after drying and processing in step (3) is carried out the Yellow ink printing operation by printing machine; After Yellow ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h; In concrete practice, the drying and processing time is 30 minutes; The dry film amount of Yellow ink is 3g/m
2-5g/m
2, the drying room temperature is 165 ℃-170 ℃;
(5) tinplate after drying and processing in step (4) is carried out the red ink printing operation by printing machine again; After red ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h; In concrete practice, the drying and processing time is 30 minutes; The dry film amount of red ink is 3g/m
2-5g/m
2, the drying room temperature is 160 ℃-165 ℃;
(6) tinplate after drying and processing in step (5) is carried out the blue ink printing operation by printing machine again; After blue ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h; In concrete practice, the drying and processing time is 30 minutes; The dry film amount of blue ink is 3g/m
2-5g/m
2, the drying room temperature is 155 ℃-160 ℃;
(7) tinplate after drying and processing in step (6) is carried out the black ink printing operation by printing machine again; After black ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h; In concrete practice, the drying and processing time is 30 minutes; The dry film amount of black ink is 3g/m
2-5g/m
2, the drying room temperature is 150 ℃-155 ℃;
(8) tinplate after drying and processing in step (7) is carried out Lacquer finish and process, after Lacquer finish is finished dealing with, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h; In concrete practice, the drying and processing time is 30 minutes; The solids content of overprint coating is 40% left and right, can adopt the M81 overprint coating, also can adopt 348
#Overprint coating.The present invention not only effectively removes dust, and more water-fast organic solvent is cleaned up owing to cleaning through water before using absolute ethyl alcohol to carry out wiping, owing to adopting same coating machine to carry out upper primer base, upper whitewash to tinplate; Adopt same printing machine to carry out Yellow ink printing, red ink printing, blue ink printing, blacking printing to tinplate, effectively reduced the input of equipment, and after ink printing is each time completed and tinplate is sent into drying room, the drying room temperature is suitably turned down 1 ℃-5 ℃, guarantee that not only preorder coating and printing ink can yellowing, and glossiness is better.
Described drying room is the tunnel type drying room, and the length of this tunnel type drying room is 20m-30m.In concrete practice, the length of tunnel type drying room is 27m.
The above is only preferred embodiment of the present invention, and is in order to limit the present invention, within the spirit and principles in the present invention not all, any modification of doing, is equal to replacement, improvement etc., within all should being included in protection scope of the present invention.
Claims (10)
1. a tin graphed sheet processing technology, is characterized in that, this technique comprises the steps:
(1) the tinplate water is cleaned, and then carry out the wiping dedusting with organic solvent;
(2) tinplate after adopting coating machine with wiping dedusting in step (1) carries out upper primer base operation, after upper complete primer base, tinplate is sent into drying room and carries out drying and processing, and the drying and processing time is 0.5h~1h;
(3) tinplate after drying and processing in step (2) is carried out upper whitewash operation by coating machine again; Gone up and tinplate has been sent into drying room after whitewash and carry out drying and processing, the drying and processing time is 0.5h~1h;
(4) tinplate after drying and processing in step (3) is carried out the Yellow ink printing operation by printing machine; After Yellow ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h;
(5) tinplate after drying and processing in step (4) is carried out the red ink printing operation by printing machine again; After red ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h;
(6) tinplate after drying and processing in step (5) is carried out the blue ink printing operation by printing machine again; After blue ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h;
(7) tinplate after drying and processing in step (6) is carried out the black ink printing operation by printing machine again; After black ink is completed for printing, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h;
(8) tinplate after drying and processing in step (7) is carried out Lacquer finish and process, after Lacquer finish is finished dealing with, tinplate is sent into drying room and carried out drying and processing, the drying and processing time is 0.5h~1h.
2. tin graphed sheet processing technology according to claim 1, it is characterized in that: in described step (1), the temperature of water is between 25 ℃-40 ℃, and the organic solvent temperature is between 15 ℃-25 ℃.
3. tin graphed sheet processing technology according to claim 1, it is characterized in that: in described step (3), the dry film amount of whitewash is 10g/m
2-25g/m
2, viscosity is 80s-100s, the drying room temperature is 170 ℃-175 ℃.
4. tin graphed sheet processing technology according to claim 1, it is characterized in that: in described step (4), the dry film amount of Yellow ink is 3g/m
2-5g/m
2, the drying room temperature is 165 ℃-170 ℃.
5. tin graphed sheet processing technology according to claim 1, it is characterized in that: in described step (5), the dry film amount of red ink is 3g/m
2-5g/m
2, the drying room temperature is 160 ℃-165 ℃.
6. tin graphed sheet processing technology according to claim 1, it is characterized in that: in described step (6), the dry film amount of blue ink is 3g/m
2-5g/m
2, the drying room temperature is 155 ℃-160 ℃.
7. tin graphed sheet processing technology according to claim 1, it is characterized in that: in described step (7), the dry film amount of black ink is 3g/m
2-5g/m
2, the drying room temperature is 150 ℃-155 ℃.
8. tin graphed sheet processing technology according to claim 1 is characterized in that: in described step (8), to process and adopt the dry film amount be 15g/m to Lacquer finish
2-20g/m
2, viscosity is the overprint coating of 60s-80s, the drying room temperature is 150 ℃-155 ℃.
9. tin graphed sheet processing technology according to claim 1, it is characterized in that: the organic solvent described in described step (1) is absolute ethyl alcohol.
10. according to claim 1-9 described tin graphed sheet processing technologys of any one, it is characterized in that: described drying room is the tunnel type drying room, the length of this tunnel type drying room is 20m-30m.