CN103114497A - Reel China paper for replication of artwork and producing process thereof - Google Patents

Reel China paper for replication of artwork and producing process thereof Download PDF

Info

Publication number
CN103114497A
CN103114497A CN 201210577467 CN201210577467A CN103114497A CN 103114497 A CN103114497 A CN 103114497A CN 201210577467 CN201210577467 CN 201210577467 CN 201210577467 A CN201210577467 A CN 201210577467A CN 103114497 A CN103114497 A CN 103114497A
Authority
CN
Grant status
Application
Patent type
Prior art keywords
coating
paper
china
rice paper
agent
Prior art date
Application number
CN 201210577467
Other languages
Chinese (zh)
Inventor
王桂云
吴振娟
姚薇
马少彬
Original Assignee
天津海华科技发展有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

The invention discloses special reel China paper for replication of an artwork, which has the advantages of advanced formula, reasonable and special process and high quality and high efficiency in production, and a producing process thereof. The technical scheme adopted by the invention is as follows: the special reel China paper comprises China paper base material and a coating, wherein the coating comprises the following components in percentage by weight: 35-50% of alcohol type solvent, 3-10% of pigment, 1-10% of color fixing agent, 1-8% of polyvinyl alcohol, 0.01-0.2% of cross-linking agent, 0.01-0.2% of leveling agent and the balance of water. The special reel China paper disclosed by the invention is particularly suitable for reproduction of traditional Chinese painting artworks and is used for producing museum pieces, indoor decoration, special art teaching materials and the like. The range of applications is wide, and the market prospects are very broad. The process disclosed by the invention is suitable for industrial flow type production of similar products.

Description

艺术品复制用卷轴宣纸及其制作工艺 Art reproduction with rice paper and reel production process

技术领域 FIELD

[0001] 本发明涉及一种宣纸及其制作工艺,特别涉及一种艺术品复制专用卷轴宣纸及其制作工艺。 [0001] The present invention relates to a rice paper and its production process, more particularly to a fine art and special rice paper reel production process.

背景技术 Background technique

[0002] 随着国民经济的不断发展及国民素质的不断提高,人们的文化品位也在不断提升。 [0002] With the increasing development of the national economy and national quality of people's cultural quality it is also rising. 艺术品收藏已进入千家万户,为了满足广大艺术品爱好者的需求和用于教学,进行传统艺术品复制产业将具有广阔的发展潜力;如用于复制名人国画的宣纸,市场需求巨大,但现有的宣纸用于艺术品复制难以达到预期的效果。 Art Collection has entered every household, in order to meet the needs of the majority of art lovers and for teaching, a traditional art reproduction industry will have broad potential for development; such as rice paper for the copy of famous painting, the huge market demand, but existing rice paper for fine art reproduction is difficult to achieve the desired results.

[0003] 目前,普通的宣纸仅仅用于画家的手工单独作画。 [0003] Currently, only ordinary rice paper for manual painter painting alone. 由于普通宣纸浸墨后会变软、变糙,柔韧性很差,不适合进行宣纸再处理,更谈不上进入机器拉抻加工,还易出现宣纸的卷、翘现象。 Since the ordinary become soft rice paper soaked ink becomes rough, poor flexibility, rice paper is not suitable for further processing, let alone into the machine pull stretch processing, is also prone to roll rice paper, Alice phenomenon. 现该领域技术人员也在摸索尝试制作适于艺术品复制用的宣纸,但由于宣纸基材涂层及制作工艺存在难以解决的问题,只可制成尺寸规格较小的单张、单片,同时简易地进行手工操作,作坊式加工,无法形成大规模产业化运行,制作费时、费力,制作成本高;且质量难以达到产业化进行艺术品复制的仿真要求,效果不佳。 The skilled person is now also suitable for the production trial and error fine art rice paper, but because of problems difficult to solve and rice paper coated substrate production process, only the dimensions can be made smaller single, monolithic, At the same time easily done manually, workshop-style processing, can not form a large-scale industrial operation, making time-consuming, laborious, production costs are high; and the quality is difficult to achieve the industrialization of fine art simulation requirements, ineffective. 如果能够通过工艺改进,提高涂层浆料的性能,保证本发明宣纸的再处理性和工业流程生产,无疑将会产生巨大的经济效益和社会效益。 If the process can be improved by improving the coating properties of the slurry, to ensure the flow of reprocessing industrial production of rice paper and the present invention will no doubt have a huge economic and social benefits.

发明内容 SUMMARY

[0004] 本发明的目的在于克服上述不足之处,提供一种配方先进、工艺合理独特、优质高效生产的艺术品复制专用卷轴宣纸及其制作工艺。 [0004] The object of the present invention is to overcome the above disadvantages, to provide one kind of advanced formulation, reasonable unique technology, high quality and high copy artwork spool rice paper and special production process.

[0005] 为实现上述目的本发明所采用的技术方案是:一种艺术品复制专用卷轴喷墨打印宣纸,包括宣纸基材和涂层,其特征在于,所述涂层由下述组分按所述质量百分比组成:醇类溶剂=35-50% ;颜料:3-10% ;固色剂:1-10% ;聚乙烯醇:1_8% ;交联剂:0.01-0.2% ;流平剂:0.01-0.2%,余量为水。 [0005] To achieve the above object of the technical proposal of the present invention is: A special reel ink-jet printing art reproduction rice paper, rice paper comprising a substrate and a coating, wherein said coating consists of the following components in the mass percentage composition: solvent = 35-50% alcohol; pigment: 3-10%; fixing agent: 1-10%; polyvinyl alcohol: 1_8%; crosslinking agent: 0.01-0.2%; leveling agent : 0.01 to 0.2%, the balance being water.

[0006] 艺术品复制专用卷轴喷墨打印宣纸的制作工艺,其特征在于,按照下述步骤进行: [0006] The ink jet printing art reproduction dedicated spool rice paper production process, which is characterized by performing the following steps:

(1)涂布浆料的制备: (1) Preparation of coating slip:

组分配比如权利要求所述,先将醇类溶剂、水、交联剂、固色剂依次加入反应釜中,室温状态下高剪切5-25分钟,搅拌转数500-2000转/分;加入颜料高剪切分散20-120分钟,搅拌转数1000-10000转/分;加入胶黏剂、流平剂等高速搅拌10-60分钟,搅拌速度1000-2000转/分;在30-60°C恒温存放待用; Such as the group is assigned claim, first alcohol solvent, water, a crosslinking agent, fixing agent are sequentially added to the kettle, at a room temperature high shear 5-25 minutes, stirring 500-2000 rpm revolutions / min; high-shear dispersing pigment is added 20-120 minutes, with stirring revolutions 1000-10000 rev / min; adding adhesive, a leveling agent high speed stirring 10-60 minutes, stirring speed 1000-2000 rpm / min; 30-60 ° C temperature storage stand;

(2)涂布步骤: (2) Coating Step:

具体步骤分为:供片、在线附着、涂布、干燥、在线剥离和收卷;供片采用恒张力供片; Is divided into specific steps: for tablets, line attachment, coating, drying, peeling and winding line; sheet supply using constant tension film supply;

附着是将恒速运行的宣纸原纸附着在循环运行的引带基上;涂布采用气刀涂布方式涂布上述恒温存放的涂布浆料;干燥采用对流干燥方式,干燥温度控制在10-200°C,风速控制在2-30米/秒;剥离是将干燥好的宣纸从引带上剥离下来沿片路进入收片区;收卷采用锥度收卷实现大轴整齐收卷;收卷基准条件为;片路张力控制在5-40公斤.米,生产速度3-50米/分; The constant speed of the attachment is attached to the base paper rice paper circulation operation pulley group; coating a coating method using an air knife coating the coating slip storage temperature; drying convection drying mode, drying temperature was controlled at 10- 200 ° C, speed control in the 2-30 m / sec; peeling the dried rice paper is peeled from the lead tape along the sheet path into the closed Area; taper for rewinding large volume to achieve orderly winding shaft; reference winding conditions; sheet tension control path 5-40 kilograms of rice, production speed 3-50 m / min.;

(3)裁切获得成品。 (3) obtain a finished cut.

[0007] 本发明的有益效果是:保持原有宣纸的纹路、改善固色性及色彩平衡并长久保持。 Advantageous Effects [0007] The present invention is: to maintain the original lines of rice paper, to improve the fixability and color balance and maintain long-term. 本发明可制成各种规格长度的轴状卷绕产品,制作工艺独特,实用效果显著,有效降低成本。 The present invention can be made into a variety of length of the winding shaft-like products, the production process is unique, the practical effect is significant, effectively reducing the cost. 本发明产品在保持原有宣纸的纹路,赋予其超强的固色性及耐光、耐候性。 Product of the invention maintained the original texture of rice paper, which gives superior light fastness properties and weather resistance. 在此前提下,使其保持基材状态平整、柔韧性良好;并便于喷墨打印机使用,有效降低成本。 In this context, the state of the base to keep it flat, good flexibility; and an ink jet printer easy to use, cost effective. 本发明之特别适于国画艺术品复制,用于珍藏品、室内装潢、特种艺术教材等的制作。 The present invention is particularly suitable for painting art reproduction, for the production of collectible items, upholstery, and other special materials arts. 应用范围广,市场前景非常广阔。 A wide range of applications, the market prospects are very bright. 本发明工艺适用于同类产品的工业流程式生产。 The process of the invention is applicable to similar products of industrial type production process.

[0008] 具体实施方式 [0008] DETAILED DESCRIPTION

以下结合较佳实施例,对依据本发明提供的具体实施方式、特征详述如下: The following in conjunction with preferred embodiments, specific embodiments according to the present invention provides, features detailed below:

宣纸基材的涂层涂料成分配比为:醇类溶剂:35-50% ;颜料:3-10% ;固色剂:1-10% ;聚乙烯醇:1-8% ;交联剂:0.01-0.2% ;流平剂:0.01-0.2% ;余量为水。 Rice paper base coat paint composition ratio of: an alcohol solvent: 35-50%; pigment: 3-10%; fixing agent: 1-10%; polyvinyl alcohol: 1-8%; crosslinking agent: 0.01-0.2%; leveling agent: 0.01-0.2%; the balance being water.

[0009] 颜料可采用微米级二氧化硅,二氧化钛,碳酸钙等;固色剂可使用阳离子型固色剂如双氰胺甲醛树脂水溶性初缩体、含铜双氰胺甲醛树脂水溶性初缩体等;交联剂可采用乙烯基三乙氧基硅烷,多元醇有机二元酸等;流平剂可采用,烷基酚聚氧乙烯醚、辛基酚聚氧乙烯醚等。 [0009] The pigment may be employed micron silica, titanium dioxide, calcium carbonate, and the like; fixing agent may be a cationic fixing agent such as dicyandiamide formaldehyde resin soluble early reduction, dicyandiamide-formaldehyde resin, a water-soluble copper First shrinking the like; vinyl triethoxysilane may be employed a crosslinking agent, a polyol organic dicarboxylic acid and the like; leveling agent may be employed, polyoxyethylene alkylphenol ether, polyoxyethylene octylphenol ether.

[0010] 实施例1 [0010] Example 1

醇类溶剂:35kg ;微米级二氧化硅:3kg ;双氰胺甲醛树脂水溶性初缩体:IOkg ;聚乙烯醇:8kg;乙烯基三乙氧基硅烷:0.2kg;烷基酚聚氧乙烯醚:0.2kg ;水43.6kg.实施例2 Alcohol solvents: 35kg; micron sized silica: 3kg; water soluble dicyandiamide-formaldehyde resins early reduction: IOkg; polyvinyl alcohol: 8kg; vinyltriethoxysilane: 0.2kg; alkylphenol ether:. 0.2kg; water 43.6kg Example 2

醇类溶剂:45kg ;微米级二氧化钛:8kg ;双氰胺甲醒树脂水溶性初缩体:6kg ;聚乙烯醇:4kg ;多元醇有机二元酸:0.1kg ;烷基酚聚氧乙烯醚:0.1kg ;水36.8kg.实施例3 Alcohol solvents: 45kg; micron-sized titanium dioxide: 8kg; dicyandiamide A water-soluble resin wake early reduction: 6kg; polyvinyl alcohol: 4kg; organic dicarboxylic acid, polyhydric alcohol: 0.1kg; alkylphenol polyoxyethylene ethers: 0.1kg;. Example 3 water 36.8kg

醇类溶剂:50kg ;微米级碳酸钙:IOkg;含铜双氰胺甲醛树脂水溶性初缩体:1kg;聚乙烯醇:1kg ;乙烯基三乙氧基硅烷:0.0lkg ;辛基酚聚氧乙烯醚:0.0lkg ;水37.98.艺术品复制专用卷轴喷墨打印宣纸的制作工艺,按照下述步骤进行: Alcohol solvents: 50kg; micron calcium carbonate: IOkg; dicyandiamide-formaldehyde resin, a water-soluble copper early reduction: 1kg; polyvinyl alcohol: 1kg; vinyltriethoxysilane: 0.0lkg; polyoxyethylene octylphenol vinyl ethers: 0.0lkg; water 37.98 art reproduction dedicated inkjet printing roll rice paper production process, performed by the following steps:

(1)涂布浆料的制备: (1) Preparation of coating slip:

先将醇类溶剂、水、交联剂、固色剂依次加入反应釜中,室温状态下高剪切5-25分钟,搅拌转数500-2000转/分;加入颜料高剪切分散20-120分钟,搅拌转数1000-10000转/分;加入胶黏剂、流平剂等高速搅拌10-60分钟,搅拌速度1000-2000转/分;在30-60°C恒温存放待用; First an alcoholic solvent, water, a crosslinking agent, fixing agent are sequentially added to the kettle, high shear 5-25 minutes, stirring 500-2000 rpm revolutions / minute at room temperature; high shear pigment dispersion was added 20 for 120 minutes with stirring revolutions 1000-10000 rev / min; adding adhesive, a leveling agent high speed stirring 10-60 minutes, stirring speed 1000-2000 rpm / min; stored stand at 30-60 ° C temperature;

(2)涂布步骤: (2) Coating Step:

具体步骤分为:供片、在线附着、涂布、干燥、在线剥离和收卷;供片采用恒张力供片;附着是将恒速运行的宣纸原纸附着在循环运行的引带基上;涂布采用气刀涂布方式涂布上述恒温存放的涂布浆料;干燥采用对流干燥方式,干燥温度控制在10-200°C,风速控制在2-30米/秒;剥离是将干燥好的宣纸从引带上剥离下来沿片路进入收片区;收卷采用锥度收卷实现大轴整齐收卷;收卷基准条件为;片路张力控制在5-40牛顿,生产速度3-50米/分; Is divided into specific steps: for tablets, line attachment, coating, drying, peeling and winding line; sheet supply using constant tension film supply; is attached to the constant speed of the base paper attached to the rice paper circulation operation pulley group; coating cloth using air knife coating method coating the coating slip storage temperature; drying convection drying mode, drying temperature was controlled at 10-200 ° C, speed control in the 2-30 m / sec; is the dried peel rice paper tape peeled from the lead into the passage along the sheet receiving Area; taper for rewinding large volume to achieve orderly winding shaft; winding reference conditions; sheet tension control path 5-40 Newtons, production speed 3-50 m / Minute;

(3)裁切获得成品。 (3) obtain a finished cut.

[0011] 本发明之产品特别适于艺术品复制,制作名画、国画等,应用范围广,市场前景非常广阔;工艺方法适用于类似产品的工业流程式生产。 [0011] products of the present invention is particularly suitable for fine art reproduction, production paintings, painting, etc., a wide range of applications, the market prospects are very broad; process methods applicable to similar products of industrial processes Production.

[0012] 上述参照实施例对该艺术品复制用卷轴宣纸及其制作工艺进行的详细描述,是说明性的而不是限定性的,因此在不脱离本发明总体构思下的变化和修改,应属本发明的保护范围之内。 DETAILED DESCRIPTION [0012] Referring to the above-described embodiment the spool with rice paper copy of the art technology for its production, and is illustrative rather than limiting, and therefore variations and modifications without departing from the general concept of the present invention, should be within the scope of the present invention.

Claims (2)

  1. 1.一种艺术品复制专用卷轴喷墨打印宣纸,包括宣纸基材和涂层,其特征在于,所述涂层由下述组分按所述质量百分比组成:醇类溶剂:35-50% ;颜料:3-10% ;固色剂:1-10% ;聚乙烯醇:1-8% ;交联剂:0.01-0.2% ;流平剂:0.01-0.2%,余量为水。 An ink jet printing art reproduction dedicated spool rice paper, rice paper comprising a substrate and a coating, wherein said coating consists of the following components in the mass percentage composition: alcohol solvents: 35-50% ; pigment: 3-10%; fixing agent: 1-10%; polyvinyl alcohol: 1-8%; crosslinking agent: 0.01-0.2%; leveling agent: 0.01 to 0.2%, the balance being water.
  2. 2.一种根据权利要求1所述的艺术品复制专用卷轴喷墨打印宣纸的制作工艺,其特征在于,按照下述步骤进行: (1)涂布浆料的制备: 组分配比如权利要求所述,先将醇类溶剂、水、交联剂、固色剂依次加入反应釜中,室温状态下高剪切5-25分钟,搅拌转数500-2000转/分;加入颜料高剪切分散20-120分钟,搅拌转数1000-10000转/分;加入胶黏剂、流平剂等高速搅拌10-60分钟,搅拌速度1000-2000转/分;在30-60°C恒温存放待用; (2)涂布步骤: 具体步骤分为:供片、在线附着、涂布、干燥、在线剥离和收卷;供片采用恒张力供片;附着是将恒速运行的宣纸原纸附着在循环运行的引带基上;涂布采用气刀涂布方式涂布上述恒温存放的涂布浆料;干燥采用对流干燥方式,干燥温度控制在10-200°C,风速控制在2-30米/秒;剥离是将干燥好的宣纸从引带上剥离下来沿片路进入收片区; A work of art according to a production process according to claim special copy rice paper reel ink-jet printing, characterized in that, in accordance with the following steps: preparing a coating slurry (1): group allocation such claims described later, the first alcohol solvent, water, a crosslinking agent, fixing agent are sequentially added to the kettle, high shear 5-25 minutes, stirring 500-2000 rpm revolutions / minute at room temperature; high shear pigment dispersion was added 20-120 minutes, with stirring revolutions 1000-10000 rev / min; adding adhesive, a leveling agent high speed stirring 10-60 minutes, stirring speed 1000-2000 rpm / min; stored stand at 30-60 ° C temperature ; (2) coating step: divided into specific steps: for tablets, line attachment, coating, drying, peeling and winding line; sheet supply using constant tension film supply; is attached to the constant operation cycle adheres to the rice paper base paper running on pulley group; coating a coating method using an air knife coating the coating slip storage temperature; drying convection drying mode, drying temperature was controlled at 10-200 ° C, speed control in the 2-30 m / sec; peeling the dried rice paper is peeled from the lead tape along the sheet path into the closed Area; 卷采用锥度收卷实现大轴整齐收卷;收卷基准条件为;片路张力控制在5-40牛顿,生产速度3-50米/分; (3)裁切获得成品。 Volume rewinding achieved using a large taper neat winding shaft; winding reference conditions; sheet tension control path 5-40 Newtons, production speed 3-50 m / min; (3) cut to obtain the finished product.
CN 201210577467 2012-12-27 2012-12-27 Reel China paper for replication of artwork and producing process thereof CN103114497A (en)