CN103103705B - The production method of copper ammonia blend fabric - Google Patents
The production method of copper ammonia blend fabric Download PDFInfo
- Publication number
- CN103103705B CN103103705B CN201210446042.9A CN201210446042A CN103103705B CN 103103705 B CN103103705 B CN 103103705B CN 201210446042 A CN201210446042 A CN 201210446042A CN 103103705 B CN103103705 B CN 103103705B
- Authority
- CN
- China
- Prior art keywords
- copper ammonia
- fibre
- grey cloth
- concise
- adds
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of production method of copper ammonia blend fabric, it is characterized in that, comprise following processing step: copper ammonia fibre, spandex fibre and cotton fiber blending are obtained cuprammonium blending grey cloth by (1), the mass ratio of copper ammonia fibre, spandex fibre and cotton fiber is 40 ~ 60:3 ~ 10:30 ~ 57; (2) wash: cleaned in rinsing machine by cuprammonium blending grey cloth, bath raio is 1:30 ~ 50, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 3 ~ 5g, and water temperature is 60 ~ 65 DEG C; (3) concise: be immersed in water by the cuprammonium blending grey cloth after washing, bath raio is 1:25 ~ 30, and adds the NaOH of 10 ~ 20g/L, and process 0.5 ~ 1 hour, concise temperature is 65 ~ 70 DEG C; (4) dye; (5) rinsing, oven dry, obtain described copper ammonia blend fabric.The present invention adopts copper ammonia fibre, spandex fibre and cotton fiber blending to obtain, and can not destroy the anti-microbial property of copper ammonia fibre, have good snugness of fit simultaneously.
Description
Technical field
The present invention relates to a kind of fabric, especially a kind of production method of copper ammonia blend fabric, belongs to textile garment technical field.
Background technology
Copper ammonia fibre is a kind of regenerated celulose fibre, it is dissolved in the liquor ammoniae fortis of Kocide SD or alkaline cupric salt by natural cellulosic feedstocks such as cotton linters, be made into spinning solution, in coagulating bath, copper ammonia fibre element molecular compound disintegrating and regeneration goes out cellulose, and namely the hydrate cellulose of generation obtains copper ammonia fibre through aft-loaded airfoil.The cross section of copper ammonia fibre is rounded, and without skin-core structure, fiber can bear highly to carry to be stretched, and obtained monofilament is comparatively thin, so fabric is soft, gloss is soft, has silky touch.
Because the resistivity of copper ammonia fibre to the oxidant such as chlorine bleaches, hydrogen peroxide is poor, so the fabric of copper ammonia fibre and other fiber blends, in follow-up pre-treatment, dyeing and Final finishing process, there is certain difficulty.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, a kind of production method of copper ammonia blend fabric is provided, this copper ammonia blend fabric is obtained by copper ammonia fibre, spandex fibre and cotton fiber blending, can not destroy the anti-microbial property of copper ammonia fibre, has good wearability.
According to technical scheme provided by the invention, the production method of described copper ammonia blend fabric, is characterized in that, comprises following processing step:
(1) copper ammonia fibre, spandex fibre and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, spandex fibre and cotton fiber is 40 ~ 60:3 ~ 10:30 ~ 57;
(2) wash: cleaned in rinsing machine by cuprammonium blending grey cloth, bath raio is 1:30 ~ 50, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 3 ~ 5g, and water temperature is 60 ~ 65 DEG C, and washing time is 0.5 ~ 1 hour;
(3) concise: be immersed in water by the cuprammonium blending grey cloth after washing, bath raio is 1:25 ~ 30, and adds the NaOH of 10 ~ 20g/L, and process 0.5 ~ 1 hour, concise temperature is 65 ~ 70 DEG C;
(4) dye: the cuprammonium blending grey cloth after concise is put into dyeing machine, bath of dye liquor is than being 1:10 ~ 13, and every premium on currency adds 1 ~ 2g softener and 1 ~ 3g levelling agent, is warming up to 70 ~ 90 DEG C, is incubated 10 ~ 15 minutes; Be warming up to 110 ~ 120 DEG C again, be incubated 10 ~ 15 minutes; Be warming up to 120 ~ 130 DEG C again, be incubated 30 ~ 45 minutes; Cool to room temperature, discharge dye liquor;
(5) rinsing, oven dry, obtain described copper ammonia blend fabric.
The production method of copper ammonia blend fabric of the present invention, adopts copper ammonia fibre, spandex fibre and cotton fiber blending to obtain, can not destroy the anti-microbial property of copper ammonia fibre, have good snugness of fit simultaneously.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment one: a kind of production method of copper ammonia blend fabric, is characterized in that, comprises following processing step:
(1) copper ammonia fibre, spandex fibre and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, spandex fibre and cotton fiber is 40:3:57;
(2) wash: cleaned in rinsing machine by cuprammonium blending grey cloth, bath raio is 1:30, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 3g, and water temperature is 60 DEG C, and washing time is 1 hour;
(3) concise: be immersed in water by the cuprammonium blending grey cloth after washing, bath raio is 1:25, and adds the NaOH of 10g/L, and process 0.5 hour, concise temperature is 70 DEG C;
(4) dye: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor ratio is 1:, every premium on currency adds 1g softener and 1g levelling agent, is warming up to 70 DEG C, is incubated 15 minutes; Be warming up to 110 DEG C again, be incubated 15 minutes; Be warming up to 120 DEG C again, be incubated 45 minutes; Cool to room temperature, discharge dye liquor;
(5) rinsing, oven dry, obtain described copper ammonia blend fabric.
Embodiment two: a kind of production method of copper ammonia blend fabric, is characterized in that, comprises following processing step:
(1) copper ammonia fibre, spandex fibre and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, spandex fibre and cotton fiber is 60:10:30;
(2) wash: cleaned in rinsing machine by cuprammonium blending grey cloth, bath raio is 1:50, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 5g, and water temperature is 65 DEG C, and washing time is 0.5 hour;
(3) concise: be immersed in water by the cuprammonium blending grey cloth after washing, bath raio is 1:30, and adds the NaOH of 20g/L, and process 1 hour, concise temperature is 70 DEG C;
(4) dye: the cuprammonium blending grey cloth after concise is put into dyeing machine, bath of dye liquor is than being 1:13, and every premium on currency adds 2g softener and 3g levelling agent, is warming up to 90 DEG C, is incubated 15 minutes; Be warming up to 120 DEG C again, be incubated 15 minutes; Be warming up to 130 DEG C again, be incubated 45 minutes; Cool to room temperature, discharge dye liquor;
(5) rinsing, oven dry, obtain described copper ammonia blend fabric.
Embodiment three: a kind of production method of copper ammonia blend fabric, is characterized in that, comprises following processing step:
(1) copper ammonia fibre, spandex fibre and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, spandex fibre and cotton fiber is 50:5:45;
(2) wash: cleaned in rinsing machine by cuprammonium blending grey cloth, bath raio is 1:40, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 4g, and water temperature is 62 DEG C, and washing time is 0.6 hour;
(3) concise: be immersed in water by the cuprammonium blending grey cloth after washing, bath raio is 1:26, and adds the NaOH of 15g/L, and process 0.6 hour, concise temperature is 66 DEG C;
(4) dye: the cuprammonium blending grey cloth after concise is put into dyeing machine, bath of dye liquor is than being 1:12, and every premium on currency adds 1.5g softener and 2g levelling agent, is warming up to 80 DEG C, is incubated 12 minutes; Be warming up to 115 DEG C again, be incubated 12 minutes; Be warming up to 125 DEG C again, be incubated 40 minutes; Cool to room temperature, discharge dye liquor;
(5) rinsing, oven dry, obtain described copper ammonia blend fabric.
Copper ammonia fibre in copper ammonia blend fabric of the present invention touch fungi, bacterium and virus time can play protective effect immediately, and its antibacterial action can not disappear because of the washing in production technology or dyeing etc.
Claims (1)
1. a production method for copper ammonia blend fabric, is characterized in that, comprises following processing step:
(1) copper ammonia fibre, spandex fibre and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, spandex fibre and cotton fiber is 40 ~ 60:3 ~ 10:30 ~ 57;
(2) wash: cleaned in rinsing machine by cuprammonium blending grey cloth, bath raio is 1:30 ~ 50, and adds mild detergent, and the consumption of mild detergent is every premium on currency 3 ~ 5g, and water temperature is 60 ~ 65 DEG C, and washing time is 0.5 ~ 1 hour;
(3) concise: be immersed in water by the cuprammonium blending grey cloth after washing, bath raio is 1:25 ~ 30, and adds the NaOH of 10 ~ 20g/L, and process 0.5 ~ 1 hour, concise temperature is 65 ~ 70 DEG C;
(4) dye: the cuprammonium blending grey cloth after concise is put into dyeing machine, bath of dye liquor is than being 1:10 ~ 13, and every premium on currency adds 1 ~ 2g softener and 1 ~ 3g levelling agent, is warming up to 70 ~ 90 DEG C, is incubated 10 ~ 15 minutes; Be warming up to 110 ~ 120 DEG C again, be incubated 10 ~ 15 minutes; Be warming up to 120 ~ 130 DEG C again, be incubated 30 ~ 45 minutes; Cool to room temperature, discharge dye liquor;
(5) rinsing, oven dry, obtain described copper ammonia blend fabric.