CN103102747A - Foaming type fireproof coating - Google Patents
Foaming type fireproof coating Download PDFInfo
- Publication number
- CN103102747A CN103102747A CN2012105267077A CN201210526707A CN103102747A CN 103102747 A CN103102747 A CN 103102747A CN 2012105267077 A CN2012105267077 A CN 2012105267077A CN 201210526707 A CN201210526707 A CN 201210526707A CN 103102747 A CN103102747 A CN 103102747A
- Authority
- CN
- China
- Prior art keywords
- parts
- grams
- intumescent coating
- fireproof coating
- foaming type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a foaming type fireproof coating. The foaming type fireproof coating comprises the following components in parts by weight: 7-12 parts of chloroprene rubber, 3-9 parts of methenamine, 6-14 parts of chlorinated rubber, 3-17 parts of triammonium phosphate, 6-8 parts of methyl triethoxysilane, 2-8 parts of mica, 3-5 parts of hydrochloric acid, 4-7 parts of butyl cellosolve, 2-5 parts of toluene and the balance of water. The foaming type fireproof coating disclosed by the invention is used for fire prevention of ships, trains, high-rise buildings, wires and cables, and can also be used for flame retardance of fiber, paper, textiles and the like and can be permeated into plastic, rubber and other products for realizing flame retardance.
Description
Technical field
The present invention is specifically related to a kind of intumescent coating.
Background technology
At present frie retardant coating roughly is divided into two kinds of intumescent coating and non-intumescent coatings.Intumescent coating fp principle is when contacting with heat-flash and flame when filming, and formation can expand into the 100-200 carburization zone that includes flame retardant resistance gas doubly, object and flame is separated, thereby play fireproofing function.But not intumescent coating is to produce fire-suppressant gas when utilizing coating to contact with flame to reach fire extinguishing function.
Summary of the invention
Goal of the invention: the invention provides a kind of intumescent coating, be used for the fire prevention of boats and ships, train, high-rise and electric wire.
Technical scheme: a kind of intumescent coating, described intumescent coating is comprised of according to parts by weight following component: chloroprene rubber 7-12 part, urotropine 3-9 part, chlorinated rubber 6-14 part, phosphoric acid triamine 3-17 part, Union carbide A-162 6-8 part, mica 2-8 part, hydrochloric acid 3-5 part, ethylene glycol butyl ether 4-7 part, toluene 2-5 part, surplus are water.
As preferably, described intumescent coating is comprised of according to parts by weight following component: 11 parts of chloroprene rubbers, 6 parts of urotropines, 12 parts of chlorinated rubbers, 15 parts of phosphoric acid triamines, 7 parts of Union carbide A-162s, 6 parts, mica, 4 parts of hydrochloric acid, 5 parts of ethylene glycol butyl ethers, 3 parts of toluene, surplus is water.
Beneficial effect: the present invention is used for the fire prevention of boats and ships, train, high-rise and electric wire, also can be used for the fire-retardant of fiber, paper, textiles etc., can infiltrate fire retardation in the goods such as plastics, rubber again.
Embodiment
The present invention will be described in detail below in conjunction with specific embodiment.
Specific embodiment 1:
A kind of intumescent coating, described intumescent coating is comprised of according to parts by weight following component: chloroprene rubber 7 grams, urotropine 3 grams, chlorinated rubber 6 grams, phosphoric acid triamine 3 grams, Union carbide A-162 6 grams, mica 2 grams, hydrochloric acid 3 grams, ethylene glycol butyl ether 4 grams, toluene 2 grams add water to 100 grams.
Specific embodiment 2:
A kind of intumescent coating, described intumescent coating is comprised of according to parts by weight following component: chloroprene rubber 12 grams, urotropine 9 grams, chlorinated rubber 14 grams, phosphoric acid triamine 17 grams, Union carbide A-162 8 grams, mica 8 grams, hydrochloric acid 5 grams, ethylene glycol butyl ether 7 grams, toluene 5 grams add water to 100 grams.
Specific embodiment 3:
A kind of intumescent coating, described intumescent coating is comprised of according to parts by weight following component: chloroprene rubber 11 grams, urotropine 6 grams, chlorinated rubber 12 grams, phosphoric acid triamine 15 grams, Union carbide A-162 7 grams, mica 6 grams, hydrochloric acid 4 grams, ethylene glycol butyl ether 5 grams, toluene 3 grams add water to 100 grams.
Claims (2)
1. intumescent coating, it is characterized in that: described intumescent coating is comprised of according to parts by weight following component: chloroprene rubber 7-12 part, urotropine 3-9 part, chlorinated rubber 6-14 part, phosphoric acid triamine 3-17 part, Union carbide A-162 6-8 part, mica 2-8 part, hydrochloric acid 3-5 part, ethylene glycol butyl ether 4-7 part, toluene 2-5 part, surplus are water.
2. intumescent coating as claimed in claim 1, it is characterized in that: described intumescent coating is comprised of according to parts by weight following component: 11 parts of chloroprene rubbers, 6 parts of urotropines, 12 parts of chlorinated rubbers, 15 parts of phosphoric acid triamines, 7 parts of Union carbide A-162s, 6 parts, mica, 4 parts of hydrochloric acid, 5 parts of ethylene glycol butyl ethers, 3 parts of toluene, surplus are water.