CN103102740A - Fluorescent ink and preparation method thereof - Google Patents
Fluorescent ink and preparation method thereof Download PDFInfo
- Publication number
- CN103102740A CN103102740A CN2012105354431A CN201210535443A CN103102740A CN 103102740 A CN103102740 A CN 103102740A CN 2012105354431 A CN2012105354431 A CN 2012105354431A CN 201210535443 A CN201210535443 A CN 201210535443A CN 103102740 A CN103102740 A CN 103102740A
- Authority
- CN
- China
- Prior art keywords
- parts
- vinyl chloride
- vinyl acetate
- propylene glycol
- glycol monomethyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses fluorescent ink, which comprises the components in pars by mass: 2-3 parts of styrene maleic anhydride modified vinyl chloride-acetate copolymer, 5-8 parts of vinyl chloride-acetate copolymer modified by chlorinated polypropylene, 3-4 parts of binary vinyl chloride-vinyl acetate copolymer CP-430, 55-70 parts of dipropylene glycol methyl ether, 30-35 parts of N, N-dimethyl formamide, 15-18 parts of ethyl acetate, 10-12 parts of methoxy-2-propyl propanoate, 5-8 parts of propylene glycol monomethyl ether, 5-7 parts of dye, 2-2.5 parts of hydrochloric acid dimethyl amine, 1.2-1.5 parts of adhesion promoter, 1.2-1.8 parts of mildew preventive, and 20-30 parts of organic fluorescent powder. By adopting the fluorescent ink disclosed by the invention, the filming quality, the rapid moisture-releasility and the environmental protection property of the ink are improved; the defects of poor solubility, overlarge ink viscosity and the like of a single solvent on different resin solutions are solved; and the fluorescent ink has the advantages of long alcohol tolerance time, good generality, high fluorescence intensity and the like.
Description
Technical field
The present invention relates to a kind of fluorescent ink, say more specifically a kind of fluorescent ink and preparation method thereof.
Background technology
Along with digital printed rise, the digital anti-counterfeiting technology is also in continuous development.The fluorescence jetted ink is the most extensive digital anti-counterfeiting technology of abroad using at present.It adds corresponding visible fluorescence compound and makes in jetted ink.Its printed matter can inspire fluorescence under action of ultraviolet radiation, have implement simple, cost is low, good concealment, the characteristics such as bright in luster, check is convenient.The fluorescence ink for ink-jet print of present domestic use almost all relies on import, and therefore, research and development fluorescence jetted ink is significant.
Summary of the invention
Technical problem to be solved by this invention is: a kind of environmental protection, the fluorescent ink that fluorescence intensity is high.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of fluorescent ink, and according to mass fraction, it consists of:
2 ~ 3 parts of the vinyl chloride-vinyl acetate resins of vinylbenzene cis-butenedioic anhydride modification;
5 ~ 8 parts of chlorinated polypropylene modified vinyl chloride-vinyl acetate resins;
3 ~ 4 parts of binary vinyl chloride-vinyl acetate resin CP-430;
55 ~ 70 parts of dipropylene glycol methyl ethers;
30 ~ 35 parts of DMFs;
15 ~ 18 parts of ethyl acetate;
10 ~ 12 parts of propylene glycol monomethyl ether acetates;
5 ~ 8 parts of propylene glycol monomethyl ethers;
5 ~ 7 parts of dyestuffs;
2 ~ 2.5 parts of hydrochloric acid dimethyl amines;
1.2 ~ 1.5 parts of adhesion promoters;
1.2 ~ 1.8 parts of mould inhibitors;
20 ~ 30 parts of organic fluorescent powders.
The vinyl chloride-vinyl acetate resin of described vinylbenzene cis-butenedioic anhydride modification (available from the vertical trade Co., Ltd that insults in: Guangzhou), outward appearance: pure white or band pale yellow powder, solids content 100%, cl content 30%, molecular weight approximately 38000.
Described chlorinated polypropylene modified vinyl chloride-vinyl acetate resin (available from: Guangzhou Lu Ou trade Co., Ltd), solid component (%): 75 ﹪, viscosity (KU): 50%(butanone, butyl ester 1:1 dissolving 800S(arrangement are measured) and TG:120 ℃ cl content (%): 30 molecular weight: approximately 38000 outward appearance range estimations: pure white or band pale yellow powder (faint yellow transparence after dissolving).
Described binary vinyl chloride-vinyl acetate resin CP-430(steps on chemical industry (China) company limited available from: height), the polymerization degree (JISK-6721): 450 ± 50, K value: 49.4 ~ 51.1, vinyl acetate content (%): 15.0 ± 1, apparent volume density (g/cc): 0.77 ± 0.07, volatile component (%):<4.0, intrinsic viscosity: 0.5308, second-order transition temperature (Tg, ℃): 63 ℃, granularity (%) (42 mesh sieve): 100.
A kind of fluorescent ink, according to mass fraction, its preferred group becomes:
3 parts of the vinyl chloride-vinyl acetate resins of vinylbenzene cis-butenedioic anhydride modification;
6 parts of chlorinated polypropylene modified vinyl chloride-vinyl acetate resins;
3.5 parts of binary vinyl chloride-vinyl acetate resin CP-430;
60 parts of dipropylene glycol methyl ethers;
32 parts of DMFs;
16 parts of ethyl acetate;
11 parts of propylene glycol monomethyl ether acetates;
8 parts of propylene glycol monomethyl ethers;
5 parts of dyestuffs;
2 parts of hydrochloric acid dimethyl amines;
1.5 parts of adhesion promoters;
1.2 parts of mould inhibitors;
25 parts of organic fluorescent powders.
Described a kind of fluorescent ink, according to mass fraction, its preferred group becomes:
2.5 parts of the vinyl chloride-vinyl acetate resins of vinylbenzene cis-butenedioic anhydride modification;
8 parts of chlorinated polypropylene modified vinyl chloride-vinyl acetate resins;
4 parts of binary vinyl chloride-vinyl acetate resin CP-430;
65 parts of dipropylene glycol methyl ethers;
30 parts of DMFs;
18 parts of ethyl acetate;
12 parts of propylene glycol monomethyl ether acetates;
6 parts of propylene glycol monomethyl ethers;
6 parts of dyestuffs;
2.5 parts of hydrochloric acid dimethyl amines;
1.3 parts of adhesion promoters;
1.6 parts of mould inhibitors;
25 parts of organic fluorescent powders.
Described a kind of fluorescent ink is characterized in that: described dyestuff is a kind of in following substances: C.I. directly black 166, C.I. directly deceives directly black 168, C.I. acid yellow 23 of 19, C.I., C.I. Xylene Red 52, C.I. acid blue 9.
Described organic fluorescent powder is selected from a kind of in following substances: blue organic fluorescent powder, red organic fluorescent powder, yellow organic fluorescent powder, green organic fluorescent powder.
The second technical problem to be solved by this invention is: the preparation method that a kind of fluorescent ink is provided.
For solving second technical problem, the technical solution used in the present invention is: a kind of preparation method of fluorescent ink, its preparation process is: by described material rate, with the vinyl chloride-vinyl acetate resin of vinylbenzene cis-butenedioic anhydride modification, chlorinated polypropylene modified vinyl chloride-vinyl acetate resin and binary vinyl chloride-vinyl acetate resin CP-430, be dissolved in dipropylene glycol methyl ether, N, in the mixed solution that dinethylformamide, ethyl acetate, propylene glycol monomethyl ether acetate and propylene glycol monomethyl ether form, regulate 40 ~ 45 ℃ of temperature, stir 5~8h, dissolve fully to resin; Then be down to 20 ~ 25 ℃, add dyestuff, 4.5 ~ 5.5h is stirred in dissolving; Add again hydrochloric acid dimethyl amine, adhesion promoter, mould inhibitor, organic fluorescent powder, stir, filter and obtain fluorescent ink.
Beneficial effect of the present invention: fluorescent ink disclosed by the invention, improved quality of forming film, quick-drying, the feature of environmental protection of printing ink, solved the shortcomings such as single solvent is poorly soluble to different resins, ink viscosity is excessive; It is long that it has the ethanol-tolerant time, and versatility is good, the fluorescence intensity advantages of higher.
Embodiment
Embodiment 1
The vinyl chloride-vinyl acetate resin 3g of vinylbenzene cis-butenedioic anhydride modification;
Chlorinated polypropylene modified vinyl chloride-vinyl acetate resin 6g;
Binary vinyl chloride-vinyl acetate resin CP-430 3.5g;
Dipropylene glycol methyl ether 60g;
DMF 32g;
Ethyl acetate 16g;
Propylene glycol monomethyl ether acetate 11g;
Propylene glycol monomethyl ether 8g;
C.I. directly deceive 19 5g;
Hydrochloric acid dimethyl amine 2g;
Adhesion promoter 1.5g;
Mould inhibitor 1.2g;
Green organic fluorescent powder 25g.
Its preparation process: by above-mentioned mass ratio, with the vinyl chloride-vinyl acetate resin of vinylbenzene cis-butenedioic anhydride modification, chlorinated polypropylene modified vinyl chloride-vinyl acetate resin and binary vinyl chloride-vinyl acetate resin CP-430, be dissolved in dipropylene glycol methyl ether, N, in the mixed solution that dinethylformamide, ethyl acetate, propylene glycol monomethyl ether acetate and propylene glycol monomethyl ether form, regulate 40 ~ 45 ℃ of temperature, stir 8h, dissolve fully to resin; Then be down to 20 ~ 25 ℃, add dyestuff, 4.5h is stirred in dissolving; Add again hydrochloric acid dimethyl amine, adhesion promoter, mould inhibitor, organic fluorescent powder, stir, filter and obtain fluorescent ink.
The product performance test: ethanol-tolerant degree (t): 13s, viscosity (CP): 1.62, sticking power (N/mm
2): 0.23, luminous intensity: 490.367, time of drying (s): 456.
Embodiment 2
The vinyl chloride-vinyl acetate resin 2.5g of vinylbenzene cis-butenedioic anhydride modification;
Chlorinated polypropylene modified vinyl chloride-vinyl acetate resin 8g;
Binary vinyl chloride-vinyl acetate resin CP-430 4g;
Dipropylene glycol methyl ether 65g;
DMF 30g;
Ethyl acetate 18g;
Propylene glycol monomethyl ether acetate 12g;
Propylene glycol monomethyl ether 6g;
C.I. directly deceive 168 6g;
Hydrochloric acid dimethyl amine 2.5g;
Adhesion promoter 1.3g;
Mould inhibitor 1.6g;
Blue organic fluorescent powder 25g.
Its preparation method is identical with embodiment 1.
The product performance test: ethanol-tolerant degree (t): 13.2s, viscosity (CP): 1.61, sticking power (N/mm
2): 0.24, luminous intensity: 492.153, time of drying (s): 452.
Claims (6)
1. fluorescent ink, according to mass fraction, it consists of:
2 ~ 3 parts of the vinyl chloride-vinyl acetate resins of vinylbenzene cis-butenedioic anhydride modification;
5 ~ 8 parts of chlorinated polypropylene modified vinyl chloride-vinyl acetate resins;
3 ~ 4 parts of binary vinyl chloride-vinyl acetate resin CP-430;
55 ~ 70 parts of dipropylene glycol methyl ethers;
30 ~ 35 parts of DMFs;
15 ~ 18 parts of ethyl acetate;
10 ~ 12 parts of propylene glycol monomethyl ether acetates;
5 ~ 8 parts of propylene glycol monomethyl ethers;
5 ~ 7 parts of dyestuffs;
2 ~ 2.5 parts of hydrochloric acid dimethyl amines;
1.2 ~ 1.5 parts of adhesion promoters;
1.2 ~ 1.8 parts of mould inhibitors;
20 ~ 30 parts of organic fluorescent powders.
2. a kind of fluorescent ink according to claim 1, is characterized in that, according to mass fraction, it consists of:
3 parts of the vinyl chloride-vinyl acetate resins of vinylbenzene cis-butenedioic anhydride modification;
6 parts of chlorinated polypropylene modified vinyl chloride-vinyl acetate resins;
3.5 parts of binary vinyl chloride-vinyl acetate resin CP-430;
60 parts of dipropylene glycol methyl ethers;
32 parts of DMFs;
16 parts of ethyl acetate;
11 parts of propylene glycol monomethyl ether acetates;
8 parts of propylene glycol monomethyl ethers;
5 parts of dyestuffs;
2 parts of hydrochloric acid dimethyl amines;
1.5 parts of adhesion promoters;
1.2 parts of mould inhibitors;
25 parts of organic fluorescent powders.
3. a kind of fluorescent ink according to claim 1, is characterized in that, according to mass fraction, it consists of:
2.5 parts of the vinyl chloride-vinyl acetate resins of vinylbenzene cis-butenedioic anhydride modification;
8 parts of chlorinated polypropylene modified vinyl chloride-vinyl acetate resins;
4 parts of binary vinyl chloride-vinyl acetate resin CP-430;
65 parts of dipropylene glycol methyl ethers;
30 parts of DMFs;
18 parts of ethyl acetate;
12 parts of propylene glycol monomethyl ether acetates;
6 parts of propylene glycol monomethyl ethers;
6 parts of dyestuffs;
2.5 parts of hydrochloric acid dimethyl amines;
1.3 parts of adhesion promoters;
1.6 parts of mould inhibitors;
25 parts of organic fluorescent powders.
4. according to claim 1-3 described a kind of fluorescent inks of arbitrary claim, it is characterized in that: described dyestuff is a kind of in following substances: C.I. is black 166, C.I. directly black 19 directly, C.I. directly deceive 168, C.I. acid yellow 23, C.I. Xylene Red 52, C.I. acid blue 9.
5. according to claim 1-3 described a kind of fluorescent inks of arbitrary claim is characterized in that: described organic fluorescent powder is selected from a kind of in following substances: blue organic fluorescent powder, red organic fluorescent powder, yellow organic fluorescent powder, green organic fluorescent powder.
6. the preparation method of the described a kind of fluorescent ink of the arbitrary claim of claims 1 to 3, its preparation process is: by described material rate, with the vinyl chloride-vinyl acetate resin of vinylbenzene cis-butenedioic anhydride modification, chlorinated polypropylene modified vinyl chloride-vinyl acetate resin and binary vinyl chloride-vinyl acetate resin CP-430, be dissolved in dipropylene glycol methyl ether, N, in the mixed solution that dinethylformamide, ethyl acetate, propylene glycol monomethyl ether acetate and propylene glycol monomethyl ether form, regulate 40 ~ 45 ℃ of temperature, stir 5~8h, dissolve fully to resin; Then be down to 20 ~ 25 ℃, add dyestuff, 4.5 ~ 5.5h is stirred in dissolving; Add again hydrochloric acid dimethyl amine, adhesion promoter, mould inhibitor, organic fluorescent powder, stir, filter and obtain fluorescent ink.