CN103102095A - Colored furan resin mortar - Google Patents
Colored furan resin mortar Download PDFInfo
- Publication number
- CN103102095A CN103102095A CN2012105329694A CN201210532969A CN103102095A CN 103102095 A CN103102095 A CN 103102095A CN 2012105329694 A CN2012105329694 A CN 2012105329694A CN 201210532969 A CN201210532969 A CN 201210532969A CN 103102095 A CN103102095 A CN 103102095A
- Authority
- CN
- China
- Prior art keywords
- furan resin
- colored
- color pigment
- resin mortar
- curing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to colored furan resin mortar which is applied to anticorrosion projects. The colored furan resin mortar is prepared through mixing acid-resisting filler, an activated curing agent, a ground color pigment and a main color pigment with the existing furfuralcohol/furfural furan resin, wherein the acid-resisting filler is a quartz or graphite material, the activated curing agent is a mixture of p-toluene sulfonyl chloride and aminosulfonic acid (the mass ratio of p-toluene sulfonyl chloride to aminosulfonic acid is 1: 1), the ground color pigment is titanium white, and the main color pigment is a mixture of chrome titanium brown and silver grey (the mass ratio of chrome titanium brown to silver grey is 1: 2). The dosage ratio of the furfuralcohol/furfural furan resin to the acid-resisting filler to the activated curing agent to the ground color pigment to the main color pigment is (9-66): (50-89): (1-17): (2-6): (1-5). According to the colored furan resin mortar disclosed by the invention, the color meets the requirements of users on color on the basis that the corrosion resistance and mechanical properties of furan resin mortar are not affected, so that the colored furan resin mortar can be widely applied to various anticorrosion projects.
Description
Technical field
The invention belongs to the corrosion resistant material technical field, particularly a kind of colored furane resin clay.
Background technology
Furane resin are take furfuryl alcohol, furfural as the synthetic superpolymer of raw material, mostly are used for the anticorrosion engineering of building trade.Furane resin can be mixed with clay by a certain percentage with acid-resistant powder, have good acidproof, alkaline-resisting, anti-solvent and resistance toheat after curing.But the furane resin clay is in building-up process, is exactly the finished product of black after liquid, solid two components are mixing cured according to a certain percentage.Because black is not attractive in appearance, many producers are unwilling to water with it smashes whole furans Concrete Anti corrosion ground, has greatly reduced the use range of furane resin clay.
Summary of the invention
The color that the objective of the invention is to exist for existing furfuryl alcohol furfurol furan resin clay is the inaesthetic problem of single black, and a kind of colored furane resin clay is provided.
Concrete scheme of the present invention is to add acid resistance filler, reactive curing agent, background color pigment and masstone pigment to mix in the furfuryl alcohol furfurol furan resin.Wherein acid resistance filler is quartzy class or graphite type material; Reactive curing agent is Tosyl chloride and thionamic acid mixture (both mass ratio is 1: 1); Background color pigment is titanium dioxide; Masstone pigment is titanium chromium palm fibre and silver grey mixture (titanium chromium palm fibre and silver grey mass ratio are 1: 2).Its amount ratio is to count in mass ratio: furfuryl alcohol furfurol furan resin 9-66 part, acid resistance filler 50-89 part, reactive curing agent 1-17 part, background color pigment 2-6 part, masstone pigment 1-5 part.
Utilize the prepared furane resin clay of the present invention on the basis that does not affect furane resin clay erosion resistance and mechanical property, color also can satisfy the user to the demand of color simultaneously, can be widely used in all kinds of antiseptic projects.
Embodiment
The invention provides a kind of colored furane resin clay.Following embodiment describes the present invention in detail, but should not be considered as the restriction of the scope of the invention.
Embodiment 1:
By following umber, each component is mixed, namely gets described colored furane resin clay:
10 parts of furfuryl alcohol furfurol furan resins
65 parts of 10-40 order silica powders
4 parts, Tosyl chloride and thionamic acid mixture (both mass ratio is 1: 1)
3 parts of titanium dioxides
1 part, the mixture that titanium chromium is brown and silver grey (titanium chromium palm fibre and silver grey mass ratio are 1: 2).
Embodiment 2:
By following umber, each component is mixed, namely gets described colored furane resin clay:
40 parts of furfuryl alcohol furfurol furan resins
50 parts of 50-100 order Graphite Powder 99s
2 parts, Tosyl chloride and thionamic acid mixture (both mass ratio is 1: 1)
2 parts of titanium dioxides
5 parts, the mixture that titanium chromium is brown and silver grey (titanium chromium palm fibre and silver grey mass ratio are 1: 2).
Embodiment 3:
By following umber, each component is mixed, namely gets described colored furane resin clay:
66 parts of furfuryl alcohol furfurol furan resins
89 parts of 5-40 order silica powders
17 parts, toluene sulfonyl chloride and thionamic acid mixture (both mass ratio is 1: 1)
6 parts of titanium dioxides
3 parts, the mixture that titanium chromium is brown and silver grey (titanium chromium palm fibre and silver grey mass ratio are 1: 2).
Claims (5)
1. a colored furane resin clay, is characterized in that, it is that mixed raw material by following parts by weight gets: furfuryl alcohol furfurol furan resin 9-66 part, acid resistance filler 50-89 part, reactive curing agent 1-17 part, background color pigment 2-6 part, masstone pigment 1-5 part.
2. a kind of colored furane resin clay as claimed in claim 1, is characterized in that, described acid resistance filler is quartzy class or graphite type material.
3. a kind of colored furane resin clay as claimed in claim 1, is characterized in that, described reactive curing agent is Tosyl chloride and thionamic acid mixture, and both mass ratio is 1: 1.
4. a kind of colored furane resin clay as claimed in claim 1, is characterized in that, described background color pigment is titanium dioxide.
5. a kind of colored furane resin clay as claimed in claim 1, is characterized in that, described masstone pigment is titanium chromium palm fibre and silver grey mixture (titanium chromium palm fibre and silver grey mass ratio are 1: 2).