CN103087498A - Preparation method of polyphenyl ether flame-retardant material - Google Patents
Preparation method of polyphenyl ether flame-retardant material Download PDFInfo
- Publication number
- CN103087498A CN103087498A CN 201110344052 CN201110344052A CN103087498A CN 103087498 A CN103087498 A CN 103087498A CN 201110344052 CN201110344052 CN 201110344052 CN 201110344052 A CN201110344052 A CN 201110344052A CN 103087498 A CN103087498 A CN 103087498A
- Authority
- CN
- China
- Prior art keywords
- polyphenyl ether
- polyphenylene oxide
- retardant material
- flame
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of a polyphenyl ether flame-retardant material. The preparation method comprises the following steps of 1, taking 50 parts by weight of polyphenyl ether, and crushing the polyphenyl ether into polyphenyl ether particles having the diameter less than 5mm, 2, uniformly mixing the polyphenyl ether particles and 48 parts by weight of organic clay MMT, and adding 2 parts by weight of aluminum hydroxide into the mixture, and 3, heating the mixture obtained by the step 2 until partial fusion and cooling to obtain the polyphenyl ether flame-retardant material. Through utilization of organic clay MMT in polyphenyl ether, polyphenyl ether flame retardation is improved effectively. Through utilization of aluminum hydroxide, composite material flame retardation is not influenced and can be improved. The preparation method is simple. The polyphenyl ether flame-retardant material has a good flame retardation effect.
Description
Technical field
The present invention relates to a kind of preparation method of fire retardant material, particularly relate to a kind of method for preparing the polyphenylene oxide fire retardant material.
Background technology
In modern handle official bussiness and place, house, a lot of materials are all inflammable materials.Due to the uncertainty of fire, in the time of presence of fire, a lot of materials can burn, and produce a large amount of heats on the one hand, and main is that a lot of materials can send toxic gas and flue dust, thereby has increased the hazardness of fire.
In order to reduce the harm of fire, a lot of fire retardant materials are arranged in test or use, but a lot of fire retardant materials faces that cost is high, flame retardant effect is poor at present, low etc. the problem of physical strength, and the application of fire retardant material is restricted.
Summary of the invention
The object of the present invention is to provide a kind of good flame retardation effect, preparation simply prepares the method for polyphenylene oxide fire retardant material.
The present invention is achieved in that
A kind of method for preparing the polyphenylene oxide fire retardant material comprises the steps:
Step 1, get the polyphenylene oxide of 50 weight parts, make diameter less than the polyphenylene oxide particle of 5mm by crusher;
Step 2, the polyorganosilicate MMT of polyphenylene oxide particle and 48 weight parts is mixed after, add the aluminium hydroxide of 2 weight parts;
Step 3, miscellany is heated to partial melting after, the cooling polyphenylene oxide composite flame-proof material that namely makes.
Further scheme is: described aluminium hydroxide is that diameter is less than the pulvis of 1mm.
The present invention can effectively improve the flame retardant properties of polyphenylene oxide by add polyorganosilicate in polyphenylene oxide, and the aluminium hydroxide that adds in addition neither affects the flame retardant effect of matrix material, can improve flame retardant effect again.Has method simple, the advantages such as good flame retardation effect.
Embodiment
Embodiment one
A kind of method for preparing the polyphenylene oxide fire retardant material comprises the steps:
Step 1, get the polyphenylene oxide of 50 weight parts, make diameter less than the polyphenylene oxide particle of 5mm by crusher;
Step 2, the polyorganosilicate MMT of polyphenylene oxide particle and 48 weight parts is mixed after, add the diameter of 2 weight parts less than the aluminium hydroxide pulvis of 1mm;
Step 3, miscellany is heated to partial melting after, the cooling polyphenylene oxide composite flame-proof material that namely makes.
Claims (2)
1. a method for preparing the polyphenylene oxide fire retardant material, is characterized in that comprising the steps:
Step 1, get the polyphenylene oxide of 50 weight parts, make diameter less than the polyphenylene oxide particle of 5mm by crusher;
Step 2, the polyorganosilicate MMT of polyphenylene oxide particle and 48 weight parts is mixed after, add the aluminium hydroxide of 2 weight parts;
Step 3, miscellany is heated to partial melting after, the cooling polyphenylene oxide composite flame-proof material that namely makes.
2. method according to claim 1, it is characterized in that: described aluminium hydroxide is that diameter is less than the pulvis of 1mm.