CN103085432B - The preparation method of a kind of continuous heat posted set composite and continuously heat posted composite plate - Google Patents
The preparation method of a kind of continuous heat posted set composite and continuously heat posted composite plate Download PDFInfo
- Publication number
- CN103085432B CN103085432B CN201310044698.2A CN201310044698A CN103085432B CN 103085432 B CN103085432 B CN 103085432B CN 201310044698 A CN201310044698 A CN 201310044698A CN 103085432 B CN103085432 B CN 103085432B
- Authority
- CN
- China
- Prior art keywords
- machine
- heat posted
- volume
- hot
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the preparation method of a kind of continuous heat posted set composite and continuous heat posted composite plate thereof, it comprises material rolling device, heat posted device and transport tape (1), described transport tape (1) two ends are provided with at least one group of hot-pressing roller turbine (6), first volume aluminium machine (2), volume Two aluminium machine (3) and hot-pressing roller turbine (6) are set in parallel in transport tape (1) two ends, and described first heat posted machine (5) and second heat posted machine (6) one end are provided with hot melt polymeric membrane material rolling device.By hot-pressing roller, aluminium and hot melt polymeric membrane are fitted in advance, then by continuous print hot-pressing roller the sizing of A-level fireproof aluminum composite board continuous hot-press, complete the whole process of a set of A-level fireproof aluminum composite board continuous heat posted compound.Achieve continuous seepage, reach quantity-produced object, make speed of production fast, save time, and smooth by the product surface of this continuous heat posted set composite output, and after bonding, peel strength is evenly reliable.
Description
Technical field
The present invention relates to the continuous heat posted set composite of a kind of A-level fireproof aluminum composite board, refer more particularly to a kind of hot melt polymeric membrane that utilizes and aluminium sheet and inorganic core disposable thermal are pasted the continous way heat posted set composite be shaped, also relate to a kind of preparation method of continuous heat posted composite plate.
Background technology
What require the fire-protection rating of building and ornament materials along with country improves constantly, specify that more than three layers buildings must reach A level fire prevention index, B level fire prevention index can only be reached because conventional aluminium composite plate is the highest, aluminium-plastic panel cannot meet the burning behavior class of national compulsory architectural fire-protection methods code requirement using PE as core interlayer, so people's research adds fire proofing material to reach the highest fire-protection rating A level fire prevention index in aluminum composite plate, use this sheet material both to meet the aesthetic of general decoration, improve security performance simultaneously.
At present, A-level fireproof aluminum composite board set composite used on the market makes core with magnesium oxide plate, by inorganic central layer surface coating again upper and lower two layers of aluminium platen-press one by one or multi-disc overlap be deposited in extruded together, although this processing method reaches composite goal, but not only method speed is slow for this, loses time, nor can ensure the planarization in plate face, can not meet the need of market, can not promote the use.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of heat posted set composite continuously, additionally provide a kind of surface of aluminum plate by then first hot melt polymeric membrane being attached in advance heating to aluminium heating, then the preparation method of continuous heat posted composite plate by continuous roll extrusion mode output A-level fireproof aluminum composite board.
In order to solve the problems of the technologies described above, the invention provides a kind of heat posted set composite continuously, it comprises material rolling device, heat posted device and transport tape, described material rolling device comprises first volume aluminium machine and volume Two aluminium machine, this volume aluminium machine is provided with aluminium section bar, described heat posted device comprises the first heat posted machine and the second heat posted machine, described transport tape two ends are provided with at least one group of hot-pressing roller turbine, described first heat posted machine and the second heat posted machine are arranged at hot-pressing roller turbine side respectively, first volume aluminium machine, volume Two aluminium machine and hot-pressing roller turbine are set in parallel in transport tape two ends, described first heat posted machine and second heat posted machine one end are provided with hot melt polymeric membrane material rolling device, described hot melt polymeric membrane material rolling device comprises the first hot melt polymeric membrane volume machine and the second hot melt polymeric membrane volume, described hot melt polymeric membrane volume machine is provided with macromolecule felted-membrane material.Described transport tape arranges inorganic central layer.
Present invention also offers a kind of preparation method of continuous heat posted composite plate, according to following steps, compound carried out to composite plate:
Step one: aluminium section bar installed by first volume aluminium machine and volume Two aluminium machine, then hot melt polymeric membrane is arranged on respectively on the first hot melt polymeric membrane volume machine and the second hot melt polymeric membrane volume machine;
Step 2: respectively the first heat posted machine, the second heat posted machine and hot-pressing roller turbine are heated to 80 DEG C-180;
Step 3: aluminium core in macromolecule felted-membrane in the first hot melt polymeric membrane volume machine and first volume aluminium machine is fitted in advance by the first heat posted machine; By the second heat posted machine, aluminium core in macromolecule felted-membrane in the second hot melt polymeric membrane volume machine and first volume aluminium machine is fitted in advance;
Step 4: then inorganic central layer is bonded aluminium section bar by the hot pressing function of the first heat posted machine with the second heat posted machine together with macromolecule felted-membrane, then shaped by hot-pressing roller turbine continuous hot-press mode, finally arrange composition operation.
Compared with prior art, the present invention has following advantages.
Inorganic central layer is bonded aluminium section bar by the hot pressing function of the first heat posted machine with the second heat posted machine together with macromolecule felted-membrane, shaped by hot-pressing roller turbine continuous hot-press mode again, directly utilize hot melt polymeric membrane continuously shaped by hot pressing, achieve continuous seepage, reach quantity-produced object, make speed of production fast, save time, and smooth by the product surface of this continuous heat posted set composite output, after bonding, peel strength is evenly reliable.
Accompanying drawing explanation
Accompanying drawing 1 is the structural representation of the continuous heat posted set composite of the present invention.
Wherein 1-transport tape, 2-first volume aluminium machine, 3-volume Two aluminium machine, 4-first heat posted machine, 5-second heat posted machine, 6-hot-pressing roller turbine, the inorganic central layer of 7-, 8-first hot melt polymeric membrane volume machine, 9-second hot melt polymeric membrane volume machine.
Detailed description of the invention
Below in conjunction with drawings and Examples, the present invention is further described.
As shown in Figure 1, a kind of heat posted set composite continuously, it comprises material rolling device, heat posted device and transport tape 1, described transport tape 1 arranges inorganic central layer 7, described material rolling device comprises first volume aluminium machine 2 and volume Two aluminium machine 3, described heat posted device comprises the first heat posted machine 4 and the second heat posted machine 5, described transport tape 1 two ends are provided with at least one group of hot-pressing roller turbine 6, described first heat posted machine 5 and the second heat posted machine 6 are arranged at hot-pressing roller turbine 6 side respectively, first volume aluminium machine 2, volume Two aluminium machine 3 and hot-pressing roller turbine 6 are set in parallel in transport tape 1 two ends, described first heat posted machine 5 and second heat posted machine 6 one end are provided with hot melt polymeric membrane material rolling device.
Aluminium section bar installed by first volume aluminium machine 2 and volume Two aluminium machine 3, described hot melt polymeric membrane material rolling device comprises the first hot melt polymeric membrane volume machine 8 and the second hot melt polymeric membrane volume machine 9, then is arranged on by hot melt macromolecule felted-membrane on the first hot melt polymeric membrane volume machine 8 and the second hot melt polymeric membrane volume machine 9 respectively; Running roller is installed in first hot melt polymeric membrane volume machine 8 and the second hot melt polymeric membrane volume machine 9 side, by running roller, macromolecule felted-membrane is transferred to the first heat posted machine 4 and the second heat posted machine 5, running roller is installed in first volume aluminium machine 2 and volume Two aluminium machine 3 side, by running roller, aluminium section bar is transferred to the first heat posted machine 4 and the second heat posted machine 5.
Respectively the first heat posted machine 4, second heat posted machine 5 and four groups of hot-pressing roller turbines 6 are heated to 80 DEG C-180 DEG C.
By the first heat posted machine 4, aluminium core in macromolecule felted-membrane in first hot melt polymeric membrane volume machine 8 and first volume aluminium machine 2 is fitted in advance; By the second heat posted machine 5, aluminium core in macromolecule felted-membrane in second hot melt polymeric membrane volume machine 9 and first volume aluminium machine 3 is fitted in advance.
In laminating process, inorganic central layer 7 is delivered between the first heat posted machine 4 and the second heat posted machine 5 by transport tape 1, then inorganic central layer 7 is bonded aluminium section bar by the hot pressing function of the first heat posted machine 4 with the second heat posted machine 5 together with macromolecule felted-membrane, successively through the continuous multiple tracks roll extrusion sizing of three groups of hot-pressing roller turbines, 6 pairs of refractory compound aluminium plates, shaping rear central layer posts aluminium up and down, centre is provided with macromolecule felted-membrane material, and after bonding, peel strength has evenly reliably finally arranged composition operation.
Teachings herein is example of the present invention and explanation; but do not mean that the obtainable advantage of the present invention is so limited, may to wherein one or more of the advantage realized in the simple transformation of structure and/or some embodiments all in the protection domain of the application in every practice process of the present invention.
Claims (3)
1. a continuous heat posted set composite, it comprises material rolling device, heat posted device and transport tape (1), described material rolling device comprises first volume aluminium machine (2) and volume Two aluminium machine (3), described heat posted device comprises the first heat posted machine (4) and the second heat posted machine (5), it is characterized in that: described transport tape (1) two ends are provided with at least one group of hot-pressing roller turbine (6), described first heat posted machine (4) and the second heat posted machine (5) are arranged at hot-pressing roller turbine (6) side respectively, first volume aluminium machine (2), volume Two aluminium machine (3) and hot-pressing roller turbine (6) are set in parallel in transport tape (1) two ends, described first heat posted machine (4) and second heat posted machine (5) one end are provided with hot melt polymeric membrane material rolling device
,described hot melt polymeric membrane material rolling device comprises the first hot melt polymeric membrane volume machine (8) and the second hot melt polymeric membrane volume machine (9).
2. the continuous heat posted set composite of one according to claim 1, is characterized in that: described transport tape (1) is arranged inorganic central layer (7).
3. a preparation method for continuous heat posted composite plate, is characterized in that: carry out compound according to following steps to composite plate:
Step one: aluminium section bar installed by first volume aluminium machine (2) and volume Two aluminium machine (3), then hot melt polymeric membrane is arranged on respectively on the first hot melt polymeric membrane volume machine (8) and the second hot melt polymeric membrane volume machine (9);
Step 2: respectively the first heat posted machine (4), the second heat posted machine (5) and hot-pressing roller turbine (6) are heated to 80 DEG C-180 DEG C;
Step 3: aluminium core in macromolecule felted-membrane in the first hot melt polymeric membrane volume machine (8) and first volume aluminium machine (2) is fitted in advance by the first heat posted machine (4); By the second heat posted machine (5), aluminium core in macromolecule felted-membrane in the second hot melt polymeric membrane volume machine (9) and volume Two aluminium machine (3) is fitted in advance;
Step 4: then the hot pressing function of inorganic central layer (7) by the first heat posted machine (4) and the second heat posted machine (5) is bonded aluminium section bar together with macromolecule felted-membrane, shaped by hot-pressing roller turbine (6) continuous hot-press mode again, finally arranged composition operation.