CN103059705A - 一种发光涂料 - Google Patents

一种发光涂料 Download PDF

Info

Publication number
CN103059705A
CN103059705A CN 201210578129 CN201210578129A CN103059705A CN 103059705 A CN103059705 A CN 103059705A CN 201210578129 CN201210578129 CN 201210578129 CN 201210578129 A CN201210578129 A CN 201210578129A CN 103059705 A CN103059705 A CN 103059705A
Authority
CN
China
Prior art keywords
resin
luminescent
coating
luminescent coating
organic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201210578129
Other languages
English (en)
Inventor
杨相子
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dalian Jinjie Building Material Science & Technology Development Co Ltd
Original Assignee
Dalian Jinjie Building Material Science & Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dalian Jinjie Building Material Science & Technology Development Co Ltd filed Critical Dalian Jinjie Building Material Science & Technology Development Co Ltd
Priority to CN 201210578129 priority Critical patent/CN103059705A/zh
Publication of CN103059705A publication Critical patent/CN103059705A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种发光涂料，其组成以质量份数计为：有机树脂60-80份、发光颜料20-40份、防沉剂1-5份。所述防沉剂为气相二氧化硅。所述发光涂料的涂层厚度为50-100μｍ。所述有机树脂为聚氨酯树脂，丙烯酸树脂，环氧树脂，聚酯树脂，PVC树脂和聚乙烯醇缩丁醛树脂中的一种或多种。本发明的有益效果为：发光涂料是由发光颜料、有机树脂、有机溶剂、助剂组成，当其成膜后，吸光10—20分钟，可在黑暗处持续发光12小时，且吸光和发光过程可无限循环，具有优良的耐侯性、耐光性。

Description

一种发光涂料
技术领域
本发明涉及建筑涂料，具体是一种发光涂料。
背景技术
建筑涂料包括水性建筑涂料和溶剂型建筑涂料，溶剂型建筑涂料因其固化过程释放有毒溶剂，不符合环保要求而在建筑涂料中受到限制，但由于溶剂型涂料的高分子成膜物耐老化性强、附着力好、涂层光洁、耐沾污、耐磨性、耐酸碱、耐水性等优于一般水性涂料，在高层建筑的外墙装饰中仍在使用。从长远看，会被水性氟碳、硅丙等高性能涂料取代。
发明内容
本发明的目的是提供一种优良的耐侯性、耐光性的发光涂料。
本发明的技术方案是这样实现的：一种发光涂料，其特征在于，其组成以质量份数计为：有机树脂60-80份、发光颜料20-40份、防沉剂1-5份。所述防沉剂为气相二氧化硅。所述发光涂料的涂层厚度为50-100μｍ。所述有机树脂为聚氨酯树脂，丙烯酸树脂，环氧树脂，聚酯树脂，PVC树脂和聚乙烯醇缩丁醛树脂中的一种或多种。
本发明的有益效果为：发光涂料是由发光颜料、有机树脂、有机溶剂、助剂组成，当其成膜后，吸光10—20分钟，可在黑暗处持续发光12小时，且吸光和发光过程可无限循环，具有优良的耐侯性、耐光性。
具体实施方式
    种发光涂料，其组成以质量份数计为：有机树脂60-80份、发光颜料20-40份、防沉剂1-5份。所述防沉剂为气相二氧化硅。所述发光涂料的涂层厚度为50-100μｍ。所述有机树脂为聚氨酯树脂，丙烯酸树脂，环氧树脂，聚酯树脂，PVC树脂和聚乙烯醇缩丁醛树脂中的一种或多种。
    发光涂料的使用方法为：
1）可以使用发光涂料进行刷涂，滚涂，喷涂，刮涂，淋幕喷涂等工艺。
当发光涂层达到一定厚度时，才能获得较为理想的发光亮度，因此发光涂层最少应为50-100um。
2） 在发光涂层下面以白色底漆为底可提高发光亮度。
3） 在发光涂层上以清漆罩光可提高涂层的光泽度和耐候性。
4）可根据施工方法调整涂料的粘度，并在每次使用前把发光涂料搅拌均匀。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (4)

1. 一种发光涂料，其特征在于，其组成以质量份数计为：
有机树脂60-80份、发光颜料20-40份、防沉剂1-5份。
2.根据权利要求1所述的发光涂料，其特征在于，所述防沉剂为气相二氧化硅。
3.根据权利要求1所述的发光涂料，其特征在于，所述发光涂料的涂层厚度为50-100μｍ。
4.根据权利要求1所述的发光涂料，其特征在于，所述有机树脂为聚氨酯树脂，丙烯酸树脂，环氧树脂，聚酯树脂，PVC树脂和聚乙烯醇缩丁醛树脂中的一种或多种。
CN 201210578129 2012-12-27 2012-12-27 一种发光涂料 Pending CN103059705A (zh)