CN103045093A - Spray paint for furniture - Google Patents
Spray paint for furniture Download PDFInfo
- Publication number
- CN103045093A CN103045093A CN2012105045739A CN201210504573A CN103045093A CN 103045093 A CN103045093 A CN 103045093A CN 2012105045739 A CN2012105045739 A CN 2012105045739A CN 201210504573 A CN201210504573 A CN 201210504573A CN 103045093 A CN103045093 A CN 103045093A
- Authority
- CN
- China
- Prior art keywords
- furniture
- spray paint
- dimethylbenzene
- bisphenol
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of coatings, and particularly relates to a spray paint for furniture. The spray paint for furniture is formed by mixing the following ingredients in percentage by weight: 30-40% of asphalt, 10-15% of titanium dioxide, 10-15% of mica powder, 1-5% of dimethylbenzene, 30-40% of poly divinyl acetylene, and 5-10% of bisphenol A-modified phenolic resin. The spray paint for furniture has ideal performances in the aspects of moist heat resistance, dry heat resistance, adhesion force and cold-heat temperature difference resistance.
Description
Technical field
The present invention relates to the furniture technical field of coatings, relate in particular to a kind of furniture spray paint.
Background technology
Along with socioeconomic development, upholstery develops like the mushrooms after rain, and the production level of furniture industry improves greatly.Furniture generally need to use coating, and coating is a kind of material, and this material can be coated in article surface with different construction technologies, form to adhere to firmly, has some strength, continuous solid film.The furniture lacquer energy is so that furniture is more attractive in appearance beautiful, improve furniture itself with harsh hand, make the not impact of climate and dried wet environment of furniture, play the effect of protection furniture.
Existing furniture coating also is not very desirable in the performance aspect wet-heat resisting, dry heat resistance, sticking power, the cold-hot temperature difference.
Summary of the invention
The object of the invention is to provides a kind of furniture spray paint for the deficiencies in the prior art, has the performance of desirable wet-heat resisting, dry heat resistance, sticking power, cold-hot temperature difference aspect.
For achieving the above object, the present invention adopts following technical scheme.
A kind of furniture spray paint, it is comprised of the composition mixing of following total amount per-cent:
Pitch 30% ~ 40%
Titanium dioxide 10% ~ 15%
Mica powder 10% ~ 15%
Dimethylbenzene 1% ~ 5%
Poly divinyl acetylene 30% ~ 40%
The resol 5% ~ 10% of bisphenol A-type modification.
Preferably, it is comprised of the composition mixing of following total amount per-cent:
Pitch 30%
Titanium dioxide 10%
Mica powder 15%
Dimethylbenzene 5%
Poly divinyl acetylene 30%
The resol 10% of bisphenol A-type modification.
Another is preferred, and it is comprised of the composition mixing of following total amount per-cent:
Pitch 35%
Titanium dioxide 15%
Mica powder 10%
Dimethylbenzene 2%
Poly divinyl acetylene 32%
The resol 6% of bisphenol A-type modification.
Another is preferred, and it is comprised of the composition mixing of following total amount per-cent:
Pitch 30%
Titanium dioxide 10%%
Mica powder 10%
Dimethylbenzene 3%
Poly divinyl acetylene 40%
The resol 7% of bisphenol A-type modification.
Another is preferred, and it is comprised of the composition mixing of following total amount per-cent:
Pitch 35%
Titanium dioxide 10%
Mica powder 10%
Dimethylbenzene 2%
Poly divinyl acetylene 35%
The resol 8% of bisphenol A-type modification.
Another is preferred, and it is comprised of the composition mixing of following total amount per-cent:
Pitch 32%
Titanium dioxide 12%
Mica powder 11%
Dimethylbenzene 1%
Poly divinyl acetylene 38%
The resol 6% of bisphenol A-type modification.
Beneficial effect of the present invention is: a kind of furniture spray paint of the present invention has the performance of desirable wet-heat resisting, dry heat resistance, sticking power, cold-hot temperature difference aspect.
Embodiment
The present invention is further illustrated below in conjunction with embodiment.
Embodiment one, a kind of furniture spray paint, and it is comprised of the composition mixing of following total amount per-cent:
Pitch 30% ~ 40%
Titanium dioxide 10% ~ 15%
Mica powder 10% ~ 15%
Dimethylbenzene 1% ~ 5%
Poly divinyl acetylene 30% ~ 40%
The resol 5% ~ 10% of bisphenol A-type modification.
Embodiment two, a kind of furniture spray paint, and it is comprised of the composition mixing of following total amount per-cent:
Pitch 30%
Titanium dioxide 10%
Mica powder 15%
Dimethylbenzene 5%
Poly divinyl acetylene 30%
The resol 10% of bisphenol A-type modification.
Embodiment three, a kind of furniture spray paint, and it is comprised of the composition mixing of following total amount per-cent:
Pitch 35%
Titanium dioxide 15%
Mica powder 10%
Dimethylbenzene 2%
Poly divinyl acetylene 32%
The resol 6% of bisphenol A-type modification.
Embodiment four, a kind of furniture spray paint, and it is comprised of the composition mixing of following total amount per-cent:
Pitch 30%
Titanium dioxide 10%%
Mica powder 10%
Dimethylbenzene 3%
Poly divinyl acetylene 40%
The resol 7% of bisphenol A-type modification.
Embodiment five, a kind of furniture spray paint, and it is comprised of the composition mixing of following total amount per-cent:
Pitch 35%
Titanium dioxide 10%
Mica powder 10%
Dimethylbenzene 2%
Poly divinyl acetylene 35%
The resol 8% of bisphenol A-type modification.
Embodiment six, a kind of furniture spray paint, and it is comprised of the composition mixing of following total amount per-cent:
Pitch 32%
Titanium dioxide 12%
Mica powder 11%
Dimethylbenzene 1%
Poly divinyl acetylene 38%
The resol 6% of bisphenol A-type modification.
Above-described embodiment one to six described furniture spray paint, its performance test results sees the following form.
| Interventions Requested | Standard-required | Experimental result |
| Wet-heat resisting | A level: 80 ° of C secondarys; | A level: 80 ° of C one-levels; |
| Dry heat resistance | A level: 85 ° of C secondarys; | A level: 85 ° of C one-levels; |
| Sticking power | A level: secondary | A level: one-level |
| The cold-hot temperature difference | Test temperature (40 ± 2) ° C and (20 ± 2) ° C, 3 cycles, without bubbling, leakless and obvious loss of gloss | Qualified |
As can be seen from the above table, above-described embodiment one to six described furniture spray paint, its performance test results all is better than standard-required or symbol standard-required, has the performance of desirable wet-heat resisting, dry heat resistance, sticking power, cold-hot temperature difference aspect.
The above only is better embodiment of the present invention, therefore all equivalences of doing according to the described structure of patent claim of the present invention, feature and principle change or modify, is included in the patent claim of the present invention.
Claims (6)
1. furniture spray paint is characterized in that: it is mixed by the composition of following total amount per-cent and forms:
Pitch 30% ~ 40%
Titanium dioxide 10% ~ 15%
Mica powder 10% ~ 15%
Dimethylbenzene 1% ~ 5%
Poly divinyl acetylene 30% ~ 40%
The resol 5% ~ 10% of bisphenol A-type modification.
2. a kind of furniture spray paint according to claim 1 is characterized in that: it is mixed by the composition of following total amount per-cent and forms:
Pitch 30%
Titanium dioxide 10%
Mica powder 15%
Dimethylbenzene 5%
Poly divinyl acetylene 30%
The resol 10% of bisphenol A-type modification.
3. a kind of furniture spray paint according to claim 1 is characterized in that: it is mixed by the composition of following total amount per-cent and forms:
Pitch 35%
Titanium dioxide 15%
Mica powder 10%
Dimethylbenzene 2%
Poly divinyl acetylene 32%
The resol 6% of bisphenol A-type modification.
4. a kind of furniture spray paint according to claim 1 is characterized in that: it is mixed by the composition of following total amount per-cent and forms:
Pitch 30%
Titanium dioxide 10%%
Mica powder 10%
Dimethylbenzene 3%
Poly divinyl acetylene 40%
The resol 7% of bisphenol A-type modification.
5. a kind of furniture spray paint according to claim 1 is characterized in that: it is mixed by the composition of following total amount per-cent and forms:
Pitch 35%
Titanium dioxide 10%
Mica powder 10%
Dimethylbenzene 2%
Poly divinyl acetylene 35%
The resol 8% of bisphenol A-type modification.
6. a kind of furniture spray paint according to claim 1 is characterized in that: it is mixed by the composition of following total amount per-cent and forms:
Pitch 32%
Titanium dioxide 12%
Mica powder 11%
Dimethylbenzene 1%
Poly divinyl acetylene 38%
The resol 6% of bisphenol A-type modification.