CN103014908A - Process for producing bamboo charcoal polyester composite fibers - Google Patents
Process for producing bamboo charcoal polyester composite fibers Download PDFInfo
- Publication number
- CN103014908A CN103014908A CN2012104991409A CN201210499140A CN103014908A CN 103014908 A CN103014908 A CN 103014908A CN 2012104991409 A CN2012104991409 A CN 2012104991409A CN 201210499140 A CN201210499140 A CN 201210499140A CN 103014908 A CN103014908 A CN 103014908A
- Authority
- CN
- China
- Prior art keywords
- bamboo charcoal
- filtrate
- charcoal polyester
- polyester composite
- complex fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for producing bamboo charcoal polyester composite fibers. The process comprises the steps of adding terephthalic acid, glycol, an initiating agent, nano bamboo charcoal micro-powder and a solvent into a polymerization reactor made of stainless steel material; heating the polymerization reactor for continuous polymerization reaction to obtain a mixed stock solution; and filtering the mixed stock solution at the temperature between 50 and 70 DEG C, extruding the filtrate through spinneret orifices, drawing the filtrate in an air layer, and putting the filtrate into bath water to solidify the filtrate into threads, thus obtaining the bamboo charcoal polyester composite fibers. Therefore, by adopting the process for producing the bamboo charcoal polyester composite fibers, the prepared fibers has high extensibility, small difference of wet strength and dry strength, high strength, good shaping stability and capability of improving the durability of a fabric; the fabric has high sunlight resistance and high fluffiness, and the added bamboo charcoal has the functional characteristics of adsorbability, antibiosis and the like, so that the process is simple for preparation, reduces the production cost, and is suitable for large-scale batch industrialized production.
Description
Technical field
The present invention relates to the weaving face fabric field, particularly relate to a kind of production technology of bamboo charcoal polyester complex fiber.
Background technology
In modern society, people are more and more higher to the quality requirement of material life, and as the clothes of people's life necessity, having the ecology and the health that are beneficial to man has become a kind of prerequisite key element.Bamboo-carbon fibre is to get mao bamboon as raw material, adopt pure oxygen, high temperature and nitrogen to intercept the calcine technology of time-delay, refinement and honeycomb obtain bamboo charcoal micropowder more to make micropore that bamboo charcoal innately has, select nano level bamboo charcoal micropowder to mix with section or spinning solution by special processing technology, the conventional spinning technique of foundation spins has the new functional fiber product again.The fabric of making by bamboo-carbon fibre has effect and the functions such as bacteria mildew-proof, absorbing and deodorizing, emission far infrared, more and more is subject to people's favor.
The intensity of the viscose that adopts in the production of general bamboo-carbon fibre is lower, the percentage elongation of fiber is low, dried wet strength differs larger, the typing poor stability, application on fabric has very large limitation, and the durability of fabric reduces greatly, even add a large amount of dispersants in bamboo carbon dacron fiber or the bamboo carbon chinlon, the dispersing uniformity of bamboo charcoal in polymer matrix is difficult to solve, so the application of bamboo charcoal in fabric also has certain limitation.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of production technology of bamboo charcoal polyester complex fiber, and this technique can improve the fabric durability.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of production technology of bamboo charcoal polyester complex fiber is provided, comprises that step is:
(1) terephthalic acid (TPA), ethylene glycol, initator, bamboo charcoal nano micro mist and solvent are joined in the polymerization reaction kettle of the firm material of stainless steel, the continuous polymerization reaction occurs in heating, obtains the mixing stoste of polyester and bamboo charcoal micropowder after reaction finishes;
(2) described mixing stoste is kept 50-70 ℃ of lower the filtration, filtrate is extruded by spinneret orifice and is stretched in air layer, is frozen into silk in the bath water of going forward side by side, and obtains the bamboo charcoal polyester complex fiber.
In a preferred embodiment of the present invention, solvent comprises one or more in methyl alcohol, ethanol or the acetone described in the step (1).
In a preferred embodiment of the present invention, the polymerisation heating-up temperature is 180-210 ℃ described in the step (1).
In a preferred embodiment of the present invention, bath water is the mixed solution of second alcohol and water described in the step (2).
The invention has the beneficial effects as follows: the production technology of bamboo charcoal polyester complex fiber of the present invention, the elongate fiber rate that makes is high, and dried wet strength differs little, and intensity is high, the typing good stability, can improve the durability of fabric, the fabric sunlight resistance is good, and bulkiness is good, the bamboo charcoal that adds simultaneously also has absorption, the functional characteristic such as antibiotic, preparation is simple, has reduced manufacturing cost, is suitable for large-scale in batches suitability for industrialized production.
The specific embodiment
The below is described in detail preferred embodiment of the present invention, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
Embodiment one:
(1) 100g terephthalic acid (TPA), 50g ethylene glycol, 5g initator, 10g bamboo charcoal nano micro mist and 10L ethanol are joined in the polymerization reaction kettle of the firm material of stainless steel, 180 ℃ of lower heating the continuous polymerization reaction occuring, obtains the mixing stoste of polyester and bamboo charcoal micropowder after reaction finishes;
(2) described mixing stoste is kept 50-70 ℃ of lower the filtration, filtrate is extruded by spinneret orifice and is stretched in air layer, and enters in the mixed solution of ethanol and water and be frozen into silk, obtains the bamboo charcoal polyester complex fiber.
Embodiment two:
(1) 210g terephthalic acid (TPA), 105g ethylene glycol, 7g initator, 22g bamboo charcoal nano micro mist and 20L methyl alcohol are joined in the polymerization reaction kettle of the firm material of stainless steel, 210 ℃ of lower heating the continuous polymerization reaction occuring, obtains the mixing stoste of polyester and bamboo charcoal micropowder after reaction finishes;
(2) described mixing stoste is kept 50-70 ℃ of lower the filtration, filtrate is extruded by spinneret orifice and is stretched in air layer, and enters in the mixed solution of ethanol and water and be frozen into silk, obtains the bamboo charcoal polyester complex fiber.
Embodiment three:
(1) 53g terephthalic acid (TPA), 25g ethylene glycol, 2g initator, 6g bamboo charcoal nano micro mist and 8L acetone are joined in the polymerization reaction kettle of the firm material of stainless steel, 200 ℃ of lower heating the continuous polymerization reaction occuring, obtains the mixing stoste of polyester and bamboo charcoal micropowder after reaction finishes;
(2) described mixing stoste is kept 50-70 ℃ of lower the filtration, filtrate is extruded by spinneret orifice and is stretched in air layer, and enters in the mixed solution of ethanol and water and be frozen into silk, obtains the bamboo charcoal polyester complex fiber.
The production technology of the bamboo charcoal polyester complex fiber that the present invention discloses, the elongate fiber rate that makes is high, and dried wet strength differs little, and intensity is high, the typing good stability, can improve the durability of fabric, the fabric sunlight resistance is good, and bulkiness is good, the bamboo charcoal that adds simultaneously also has absorption, the functional characteristic such as antibiotic, preparation is simple, has reduced manufacturing cost, is suitable for large-scale in batches suitability for industrialized production.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (4)
1. the production technology of a bamboo charcoal polyester complex fiber is characterized in that, comprises that step is:
(1) terephthalic acid (TPA), ethylene glycol, initator, bamboo charcoal nano micro mist and solvent are joined in the polymerization reaction kettle of the firm material of stainless steel, the continuous polymerization reaction occurs in heating, obtains the mixing stoste of polyester and bamboo charcoal micropowder after reaction finishes;
(2) described mixing stoste is kept 50-70 ℃ of lower the filtration, filtrate is extruded by spinneret orifice and is stretched in air layer, is frozen into silk in the bath water of going forward side by side, and obtains the bamboo charcoal polyester complex fiber.
2. the production technology of bamboo charcoal polyester complex fiber according to claim 1 is characterized in that, solvent comprises one or more in methyl alcohol, ethanol or the acetone described in the step (1).
3. the production technology of bamboo charcoal polyester complex fiber according to claim 1 is characterized in that, the polymerisation heating-up temperature is 180-210 ℃ described in the step (1).
4. the production technology of bamboo charcoal polyester complex fiber according to claim 1 is characterized in that, bath water is the mixed solution of second alcohol and water described in the step (2).