CN103014448B - 改进型6061铝合金冰箱发泡模铸件的加工工艺 - Google Patents
改进型6061铝合金冰箱发泡模铸件的加工工艺 Download PDFInfo
- Publication number
- CN103014448B CN103014448B CN201210503597.2A CN201210503597A CN103014448B CN 103014448 B CN103014448 B CN 103014448B CN 201210503597 A CN201210503597 A CN 201210503597A CN 103014448 B CN103014448 B CN 103014448B
- Authority
- CN
- China
- Prior art keywords
- good
- aluminium
- hour
- improved
- aluminum alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种改进型6061铝合金冰箱发泡模铸件的加工工艺,其包括配料、熔炼、浇铸、热处理四个步骤。本发明改进型6061铝合金中添加了适量的稀土元素Nd、Ce、Sc,显著减少共晶相的尺寸,均匀细化合金的铸态组织并提高合金的强度和耐腐蚀耐磨性。本发明加工出来的铝合金冰箱发泡模铸件具有良好的机械性能、强度高,耐热性好、可使用性好,内部组织致密性好,不存在气孔和起皮缺陷,耐磨性好,抗腐蚀性能、抗氧化性好,膨胀系数小等优点。
Description
技术领域
本发明涉及一种改进型6061铝合金冰箱发泡模铸件的加工工艺,属于铝合金材料加工技术领域。
背景技术
冰箱发泡模作为冰箱生产的制造的一个重要模具,其加工制造的好坏,将直接关系到整个产品的优劣,甚至会影响整个产品制造的成败。目前可作为冰箱发泡模的材料有金属和非金属两类,采用金属制做的发泡模无疑能运用于大批量及高速生产中,发泡模金属材料有铝、铜、低熔点合金、镍、铁、锌合金等。其中铝合金制做的发泡模应用最广泛,其具有导热性能好、容易调节模具温度,不易生锈和被腐蚀,容易维修、保管、造价低廉、制做时间段等优点。但是铝合金发泡模还存在着质软、强度低、内部组织致密性差等缺点,因此,急需研发一种高性能的铝合金冰箱发泡模。
发明内容
本发明的目的在于针对现有技术的不足,提供一种高性能的改进型6061铝合金冰箱发泡模铸件的加工工艺,提高铝合金冰箱发泡模的综合性能。
改进型6061铝合金冰箱发泡模铸件的加工工艺,包括以下步骤:
(1)配料
按照元素质量百分数满足如下要求:Si 0.40-0.8%、Fe≤0.7%、Cu 0.15-0.40%、Mn≤0.15%、Mg 0.8-1.2%、Cr 0.04-0.35%、Zn≤0.25%、Ti≤0.15%、 Nd 0.04-0.06%、Ce 0.03-0.05%、Sc 0.02-0.04%,其他杂质元素合计≤0.15%、其余为Al,进行配料;
(2)熔炼
将配料依次投入熔炼炉中进行熔炼,炉内控制在730-750℃,投料40-50min后,待炉内出现铝水时,加入覆盖剂进行覆盖,开始搅拌,调整成分后,加入精炼剂经过精炼、扒渣得到合格成分后,将铝液从熔炼炉注入保温炉,炉温在720-740℃条件下静置保持20-30min,然后利用氩气将铝液中的氢及细小杂质带到表面,从而降低铝液中的氢含量;
(3)浇铸
铝液通过熔炼炉的放水孔经铝槽进入结晶器,铸造出所需要的铸件,铸造温度控制在680-720℃,铸造速度控制30-42mm/min,冷却水流量控制在1150-1250 l/min;
(4)热处理
对铸件进行表面处理后,进行均匀化退火处理,具体过程如下:先升温至320-330℃下,保温2-3h,每小时70-90℃升温加热至530-550℃下保温6-8h,然后空气冷却,再每小时60-80℃升温加热至360-380℃,并保温度5-6h;再降温至150-180℃下保温3-4h,空冷至室温即可。
所述的覆盖剂为40-50%的玻璃和50-60%的苏打组成的混合物;所述的精炼剂由下列重量份原料制得:氯化钾5-8、氟化钙3-5、硝酸钠3-5、石墨粉5-8、氟硅酸钠8-10、氯化铝5-8、海泡石8-10、树木灰 5-8、Na2TiF6 8-10、NaF 5-8;
所述的精炼剂制备方法如下:
a、将上述重量份的海泡石用10-15%盐酸浸泡3-4小时,去离子水洗涤,再用10-12%氢氧化钠溶液浸泡3-4小时,再用去离子水洗涤至中性,然后在500-530℃下煅烧2-3小时,粉碎成纳米粉末;
b、将海泡石以外的各原料加热熔融后,澄清1-2小时,将上面的澄清液倒入水中冷淬,得到破碎的颗粒;
c、将步骤a、b得到的物料混合搅拌即得所述精炼剂。
本发明的有益效果:
本发明改进型6061铝合金中添加了适量的稀土元素Nd、Ce、Sc,显著减少共晶相的尺寸,均匀细化合金的铸态组织并提高合金的强度和耐腐蚀耐磨性。本发明加工出来的铝合金冰箱发泡模铸件具有良好的机械性能、强度高,耐热性好、可使用性好,内部组织致密性好,不存在气孔和起皮缺陷,耐磨性好,抗腐蚀性能、抗氧化性好,膨胀系数小等优点。
具体实施方式
改进型6061铝合金冰箱发泡模铸件的加工工艺,包括以下步骤:
(1)配料
按照元素质量百分数满足如下要求:Si 0.40-0.8%、Fe≤0.7%、Cu 0.15-0.40%、Mn≤0.15%、Mg 0.8-1.2%、Cr 0.04-0.35%、Zn≤0.25%、Ti≤0.15%、 Nd 0.04-0.06%、Ce 0.03-0.05%、Sc 0.02-0.04%,其他杂质元素合计≤0.15%、其余为Al,进行配料;
(2)熔炼
将配料依次投入熔炼炉中进行熔炼,炉内控制在750℃,投料40min后,待炉内出现铝水时,加入覆盖剂进行覆盖,开始搅拌,调整成分后,加入精炼剂经过精炼、扒渣得到合格成分后,将铝液从熔炼炉注入保温炉,炉温在730℃条件下静置保持25min,然后利用氩气将铝液中的氢及细小杂质带到表面,从而降低铝液中的氢含量;
(3)浇铸
铝液通过熔炼炉的放水孔经铝槽进入结晶器,铸造出所需要的铸件,铸造温度控制在705℃,铸造速度控制36mm/min,冷却水流量控制在1200 l/min;
(4)热处理
对铸件进行表面处理后,进行均匀化退火处理,具体过程如下:先升温至330℃下,保温2h,每小时90℃升温加热至540℃下保温7h,然后空气冷却,再每小时80℃升温加热至380℃,并保温度5h;再降温至160℃下保温4h,空冷至室温即可。
其中,所述的覆盖剂为50%的玻璃和50%的苏打组成的混合物;所述的精炼剂由下列重量份原料制得:氯化钾8份、氟化钙4份、硝酸钠3份、石墨粉6份、氟硅酸钠9份、氯化铝8份、海泡石8份、树木灰 6份、Na2TiF6 10份、NaF 5份;
所述的精炼剂制备方法如下:
a、将上述重量份的海泡石用15%盐酸浸泡3小时,去离子水洗涤,再用12%氢氧化钠溶液浸泡4小时,再用去离子水洗涤至中性,然后在530℃下煅烧2小时,粉碎成纳米粉末;
b、将海泡石以外的各原料加热熔融后,澄清2小时,将上面的澄清液倒入水中冷淬,得到破碎的颗粒;
c、将步骤a、b得到的物料混合搅拌即得所述精炼剂。
经检验,产物化学成分为:Si 0.674%、Fe 0.592%、Cu 0.276%、Mn 0.113%、Mg 1.006%、Cr 0.224%、Zn 0.138%、Ti 0.088%、Nd 0.048%、Ce 0.042%、Sc 0.036%,其他杂质元素合计0.103%、其余为Al;力学性能为:抗拉强度387Mpa,0.2%屈服强度305Mpa,伸长率10%,弹性模量56Gpa。
Claims (1)
1.改进型6061铝合金冰箱发泡模铸件的加工工艺,其特征在于包括以下步骤:
(1)配料
按照元素质量百分数满足如下要求:Si 0.40-0.8%、Fe≤0.7%、Cu 0.15-0.40%、Mn≤0.15%、Mg 0.8-1.2%、Cr 0.04-0.35%、Zn≤0.25%、Ti≤0.15%、 Nd 0.04-0.06%、Ce 0.03-0.05%、Sc 0.02-0.04%,其他杂质元素合计≤0.15%、其余为Al,进行配料;
(2)熔炼
将配料依次投入熔炼炉中进行熔炼,炉内控制在730-750℃,投料40-50min后,待炉内出现铝水时,加入覆盖剂进行覆盖,开始搅拌,调整成分后,加入精炼剂经过精炼、扒渣得到合格成分后,将铝液从熔炼炉注入保温炉,炉温在720-740℃条件下静置保持20-30min,然后利用氩气将铝液中的氢及细小杂质带到表面,从而降低铝液中的氢含量;
(3)浇铸
铝液通过保温炉的放水孔经铝槽进入结晶器,铸造出所需要的铸件,铸造温度控制在680-720℃,铸造速度控制30-42mm/min,冷却水流量控制在1150-1250 L/min;
(4)热处理
对铸件进行表面处理后,进行均匀化退火处理,具体过程如下:先升温至320-330℃下,保温2-3h,每小时70-90℃升温加热至530-550℃下保温6-8h,然后空气冷却,再每小时60-80℃升温加热至360-380℃,并保温度5-6h;再降温至150-180℃下保温3-4h,空冷至室温即可;
所述的覆盖剂为40-50%的玻璃和50-60%的苏打组成的混合物;
所述的精炼剂由下列重量份原料制得:氯化钾5-8、氟化钙3-5、硝酸钠3-5、石墨粉5-8、氟硅酸钠8-10、氯化铝5-8、海泡石8-10、树木灰 5-8、Na2TiF6 8-10、NaF 5-8;
所述的精炼剂制备方法如下:
a、将上述重量份的海泡石用10-15%盐酸浸泡3-4小时,去离子水洗涤,再用10-12%氢氧化钠溶液浸泡3-4小时,再用去离子水洗涤至中性,然后在500-530℃下煅烧2-3小时,粉碎成纳米粉末;
b、将海泡石以外的各原料加热熔融后,澄清1-2小时,将上面的澄清液倒入水中冷淬,得到破碎的颗粒;
c、将步骤a、b得到的物料混合搅拌即得所述精炼剂。