CN102995121A - Nonlinear optical crystal vanadium thallium iodate - Google Patents
Nonlinear optical crystal vanadium thallium iodate Download PDFInfo
- Publication number
- CN102995121A CN102995121A CN2012105335854A CN201210533585A CN102995121A CN 102995121 A CN102995121 A CN 102995121A CN 2012105335854 A CN2012105335854 A CN 2012105335854A CN 201210533585 A CN201210533585 A CN 201210533585A CN 102995121 A CN102995121 A CN 102995121A
- Authority
- CN
- China
- Prior art keywords
- thallium
- iodate
- nonlinear optical
- vanadium
- optical crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a nonlinear optical crystal vanadium thallium iodate. The invention discloses a nonlinear optical crystal vanadium thallium iodate. The nonlinear optical crystal vanadium thallium iodate has a chemical formula of Tl (VO2) 2 (IO3) 3 and molecular weight of 894.97, belongs to orthorhombic system and space group Ima2, and has unit cell parameters as follows: a = 14.1143 (17), Angstrom, b=10.2116 (12), Angstrom, C=8.0319 (9), Angstrom, alpha=beta=gamma=90 DEG C, V=1157.6 (2), and Angstrom<3>, Z=4. The nonlinear optical crystal vanadium thallium iodate is prepared by a hydrothermal method. The vanadium thallium iodate [Tl(VO2)2(IO3)3] has excellent nonlinear optical performance, and SHG coefficient of a vanadium thallium iodate powder is similar to that of KTP.
Description
Technical field
The invention belongs to nonlinear optical material and synthetic.
Background technology
Non-linear optic crystal has frequency-doubled effect (SHG), and selling off the high-tech areas such as information processing at laser frequency conversion, Electro-optical Modulation, light has significant application value.Non-linear optic crystal has obtained paying close attention to widely with its good character.Nonlinear optical material is in modern science and technology, particularly in some military and civilian high-tech areas, such as the communication of submarine deep water, blinding laser weapons, the ocean locating fish, video disc recording, color laser printing, laser projection tv, photometry calculation and optical-fibre communications etc. has a series of important application.The non-linear optic crystal of at present practical application comprises KH
2PO
4(KDP), KTiOPO
4(KTP), LiNbO
3(LNO), BaTiO
3(BTO), α-LiIO
3, α-HIO
3, KIO
3Deng.Along with the development of laser technology and the appearance of tunable laser, the device for non-linear optical development is rapid, laser freuqency doubling, mixing, parametric oscillation and amplification; Electro-optical Modulation, deflection, Q-switch and optical dioptric device etc. occur in succession.Above these researchs and application have proposed more higher physics, the requirement of chemical property to nonlinear optical material, have also promoted developing rapidly of nonlinear optical material.
The key of design nonlinear optical material is how to induce the formation without core structure to reach the polarizability that how to increase compound, and this is nonlinear optical material design and a difficult problem of synthesizing.Think that at present the group that can produce without core structure mainly comprises B-O, P-O and Ge-O key, contain the ion of lone-pair electron such as I (V) such as IO
3 -, Se (IV), Bi (III), Pb (II), Te (IV) etc. and distorted octahedron coordination d
0The transition metal ion of electronic configuration such as Ti (IV), V (V), Nb (V), Ta (V), Mo (VI), W (VI) etc.The system that contains at present single nonlinear optical active group has been studied more detailed.Studies show that adopting compound method to be about to two or more nonlinear optical active groups is compound in the same compound, utilize its synergistic effect increase acquisition without the probability of core structure and improve the effective way that its nonlinear second-order optical susceptibility is a synthesizing new second-order non-linear optical materials.We are incorporated into V (V) positively charged ion of distorted octahedron coordination in the iodate compound of thallium, by IO
3And VO
6Thereby the collaborative polarized action of two kinds of polar groups has obtained the novel non-linearity optical material of superior performance.The research of relevant this respect there is no bibliographical information.
Summary of the invention
The object of the invention is to prepare a kind of non-linear optical crystal of iodic acid vanadium thallium.
Non-linear optical crystal of iodic acid vanadium thallium, its chemical formula are Tl (VO
2)
2(IO
3)
3, molecular weight is: 894.97, belong to rhombic system, and spacer Ima2, cell parameter are a=14.1143 (17), b=10.2116 (12), c=8.0319 (9), α=β=γ=90 °, V=1157.6 (2)
3, Z=4.The structure of acid iodide vanadium thallium is by VO
6Octahedra altogether summit interconnects the one-dimensional chain structure that forms, IO
3Group is attached to the both sides of one-dimensional chain, and Tl
+Ion then is embedded in the space of interchain.
Acid iodide vanadium thallium is synthetic with hydrothermal method: with TlI, and V
2O
3, I
2O
5And H
2O packs in the hydro-thermal reaction liner of 23 ml, the hydrothermal reaction kettle of packing into after the sealing.In chamber type electric resistance furnace in 200 ℃ the reaction a couple of days, can obtain the yellow transparent tabular crystal.
The nonlinear optics measurement shows, acid iodide vanadium thallium (Tl (VO
2)
2(IO
3)
3) have good non-linear optical property, under 2000 nm laser radiations, export the light of very strong wavelength 1000 nm, its powder SHG coefficient is suitable with KTP.Be expected at laser frequency conversion, Electro-optical Modulation, light is sold off the high-tech areas such as information processing that significant application value is arranged.This type of nonlinear optical material is in modern science and technology, particularly in some military and civilian high-tech areas, such as the communication of submarine deep water, blinding laser weapons, the ocean locating fish, video disc recording, color laser printing, laser projection tv, photometry calculation and optical-fibre communications etc. has a series of important application.
Embodiment
Example 1:TlI
(165.6 mg, 0.5 mmol), V
2O
3(18.7 mg, 0.125 mmol), I
2O
5(668 mg, 2 mmol) and H
2Mix in O (2 ml) hydrothermal reaction kettle of packing into, sealing places chamber type electric resistance furnace, is warmed up to 200 ℃ through 400 min from 30 ℃, and isothermal reaction four days per hour is down to 30 ℃ with 3 ℃ at last, can obtain the yellow transparent tabular crystal.
Claims (1)
1. non-linear optical crystal of iodic acid vanadium thallium, its chemical formula is Tl (VO
2)
2(IO
3)
3, molecular weight is: 894.97, belong to rhombic system, and spacer Ima2, cell parameter are a=14.1143 (17), b=10.2116 (12), c=8.0319 (9), α=β=γ=90 °, V=1157.6 (2)
3, Z=4.