CN102993599A - Low-smoke halogen-free environment-friendly cable material - Google Patents
Low-smoke halogen-free environment-friendly cable material Download PDFInfo
- Publication number
- CN102993599A CN102993599A CN 201210415306 CN201210415306A CN102993599A CN 102993599 A CN102993599 A CN 102993599A CN 201210415306 CN201210415306 CN 201210415306 CN 201210415306 A CN201210415306 A CN 201210415306A CN 102993599 A CN102993599 A CN 102993599A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- wire material
- cable wire
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a low-smoke halogen-free environment-friendly cable material. The low-smoke halogen-free environment-friendly cable material comprises the following ingredients in parts by weight: 20 to 80 parts of vinyl acetate-chloroethylene polymer resin, 10 to 50 parts of urea resin, 15 to 60 parts of polrvinyl chloride resin, 5 to 10 parts of environment-friendly stabilizer, 2 to 15 parts of electrical property modifier, 1 to 10 parts of brightener, 5 to 15 parts of rheological agent, 3 to 8 parts of inorganic filler and 4 to 20 parts of flame retardant. The low-smoke halogen-free environment-friendly cable material can reduce damage to a human body and environmental pollution and is environment-friendly and safe.
Description
Technical field
The present invention relates to cable material field, particularly relate to a kind of low smoke and zero halogen environmental protection cable wire material.
Background technology
The electric wire of anti-the combustion is mainly used in the aspects such as signal transmission cable, electric power and data transmission cable and control cable at present.Guarantee that key facility can work in the specified time under hot conditions in case on fire, for personnel's escape offers an opportunity, the while also is conducive to the firefighter to controlling control and the putting out fire of fire scope.Space relative closures such as Highrise buildings, public venue and subway tunnel particularly, in the place and buildings that personnel are intensive, must guarantee some Key Circuit in fire according to different requirements, normally do not doing down in the equal time, generally little etc. from 30 minutes to 3 hours, the personal security in the above-mentioned building of guarantee.Simultaneously original polyvinyl chloride etc. has the halogen material can produce a large amount of irritant gass and black smoke, tends to forbid in above-mentioned building.As everyone knows, because original PVC and magnalium halogen-free flame-retardant polymer material do not have effect of heat insulation, must adopt resistant to elevated temperatures refractory materials, imprison this insulation system and generally adopt mica method wrapped and mineral insulation to make fire-resistant wire and cable.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of low smoke and zero halogen environmental protection cable wire material, can reduce human body infringement and environmental pollution, Environmental Safety.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of low smoke and zero halogen environmental protection cable wire material is provided, comprises: vinyl acetate-chloroethylene polymerization resin 20-80 part, urea-formaldehyde resin 10-50 part, polyvinyl chloride (PVC) RESINS 15-60 part environmental protection stablizer 5-10 part, electrical modifying agent 2-15 part, brightening agent 1-10 part, rheological agent 5-15 part, mineral filler 3-8 part, fire retardant 4-20 part.
In a preferred embodiment of the present invention, described releasing agent is one or more the mixture in siloxanes, metallic stearate, low molecular weight polyethylene, fluorine-containing oligomer and the polyolefine.
In a preferred embodiment of the present invention, described rheological agent is fluorine-containing rheological agent or ATL-95 resin, and described environmental protection stablizer is calcium zinc class one package stabilizer or polyalcohols one package stabilizer.
In a preferred embodiment of the present invention, described mineral filler is one or more the mixture in titanium dioxide, calcium carbonate, talcum powder, the kaolin.
In a preferred embodiment of the present invention, described electrical modifying agent is calcinated argil, and described fire retardant is the mixture of magnesium hydroxide and aluminium hydroxide.
The invention has the beneficial effects as follows: low smoke and zero halogen environmental protection cable wire material of the present invention can reduce human body infringement and environmental pollution, Environmental Safety.
Embodiment
The below is described in detail preferred embodiment of the present invention, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
A kind of low smoke and zero halogen environmental protection cable wire material comprises: vinyl acetate-chloroethylene polymerization resin 20-80 part, urea-formaldehyde resin 10-50 part, polyvinyl chloride (PVC) RESINS 15-60 part environmental protection stablizer 5-10 part, electrical modifying agent 2-15 part, brightening agent 1-10 part, rheological agent 5-15 part, mineral filler 3-8 part, fire retardant 4-20 part.
In addition, the mixture of one or more in metallic stearate, low molecular weight polyethylene, fluorine-containing oligomer and the polyolefine.
In addition, described rheological agent is fluorine-containing rheological agent or ATL-95 resin, and described environmental protection stablizer is calcium zinc class one package stabilizer or polyalcohols one package stabilizer.
In addition, described mineral filler is one or more the mixture in titanium dioxide, calcium carbonate, talcum powder, the kaolin.
In addition, described electrical modifying agent is calcinated argil, and described fire retardant is the mixture of magnesium hydroxide and aluminium hydroxide.
Embodiment 1: vinyl acetate-20 parts of chloroethylene polymerization resins, 10 parts of urea-formaldehyde resins, 5 parts of 15 parts of environmental protection stablizers of polyvinyl chloride (PVC) RESINS, 2 parts of electrical modifying agents, 1 part of brightening agent, 5 parts of rheological agents, 3 parts of mineral fillers, 4 parts of fire retardants.
Embodiment 2: vinyl acetate-80 parts of chloroethylene polymerization resins, 50 parts of urea-formaldehyde resins, 10 parts of 60 parts of environmental protection stablizers of polyvinyl chloride (PVC) RESINS, 15 parts of electrical modifying agents, 10 parts of brightening agents, 15 parts of rheological agents, 8 parts of mineral fillers, 20 parts of fire retardants.
Embodiment 3: vinyl acetate-50 parts of chloroethylene polymerization resins, 30 parts of urea-formaldehyde resins, 8 parts of 40 parts of environmental protection stablizers of polyvinyl chloride (PVC) RESINS, 10 parts of electrical modifying agents, 8 parts of brightening agents, 10 parts of rheological agents, 6 parts of mineral fillers, 10 parts of fire retardants.
Be different from prior art, low smoke and zero halogen environmental protection cable wire material of the present invention can reduce human body infringement and environmental pollution, Environmental Safety.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes specification sheets of the present invention to do, or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (5)
1. low smoke and zero halogen environmental protection cable wire material, it is characterized in that, comprising: vinyl acetate-chloroethylene polymerization resin 20-80 part, urea-formaldehyde resin 10-50 part, polyvinyl chloride (PVC) RESINS 15-60 part environmental protection stablizer 5-10 part, electrical modifying agent 2-15 part, brightening agent 1-10 part, rheological agent 5-15 part, mineral filler 3-8 part, fire retardant 4-20 part.
2. low smoke and zero halogen environmental protection cable wire material according to claim 1 is characterized in that, described releasing agent is one or more the mixture in siloxanes, metallic stearate, low molecular weight polyethylene, fluorine-containing oligomer and the polyolefine.
3. low smoke and zero halogen environmental protection cable wire material according to claim 1 is characterized in that, described rheological agent is fluorine-containing rheological agent or ATL-95 resin, and described environmental protection stablizer is calcium zinc class one package stabilizer or polyalcohols one package stabilizer.
4. low smoke and zero halogen environmental protection cable wire material according to claim 1 is characterized in that, described mineral filler is one or more the mixture in titanium dioxide, calcium carbonate, talcum powder, the kaolin.
5. low smoke and zero halogen environmental protection cable wire material according to claim 1 is characterized in that, described electrical modifying agent is calcinated argil, and described fire retardant is the mixture of magnesium hydroxide and aluminium hydroxide.