CN102993471A - Low water absorption rate rubber for rubber pipe for conveying food oil - Google Patents
Low water absorption rate rubber for rubber pipe for conveying food oil Download PDFInfo
- Publication number
- CN102993471A CN102993471A CN 201210502794 CN201210502794A CN102993471A CN 102993471 A CN102993471 A CN 102993471A CN 201210502794 CN201210502794 CN 201210502794 CN 201210502794 A CN201210502794 A CN 201210502794A CN 102993471 A CN102993471 A CN 102993471A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- raw materials
- water absorption
- aging agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to low water absorption rate rubber for a rubber pipe for conveying food oil. The rubber comprises the following components in parts by weight: 70-100 parts of 1#natural rubber, 30-50 parts of 9000 type butadiene rubber, 1-2 parts of sulphur, 3-5 parts of zinc oxide, 2-3 parts of anti-aging agent DTPD (domestic name: anti-aging agent 3100, Chinese name: N,N'-bis(methylphenyl)-p-phenylenediamine mixture), 2-4 parts of stearic acid, 2-3 parts of paraffin, 3-5 parts of vaseline, 70-90 parts of spraying carbon black, 50-80 parts of 600-mu calcium oxide and 1-2 parts of accelerant CZ with a molecular formula of C13H16N2S2 and a chemical name of N-cyclohexy1-2-benzothiazole sulfonamide. Water permeating through the rubber is absorbed through adding a modifying material, and therefore, the ageing of the main body material, caused by hydrolysis discoloring due to water absorption, is avoided.
Description
Technical field
The present invention relates to rubber materials, particularly relate to a kind of low water absorption and carry food oil with rubber hose rubber.
Background technology
Because absorbing water, the polar material in the rubber causes the variable color accelerated deterioration of rubber in the use procedure of long-term delivery food oil.
Summary of the invention
The purpose of this invention is to provide a kind of improve carry the alcohol environment with rubber product water-fast/water absorbing properties, the low water absorption that obviously improves the variable color problem of aging of product carries food oil with rubber hose rubber.
Technical scheme of the present invention is: low water absorption carries food oil with rubber hose rubber, it is characterized in that: its rubber raw materials component and raw material weight proportioning are chosen as 70~100 parts of 1# natural rubbers, 30~50 parts of 9000 type cis-1,4-polybutadiene rubbers, 1~2 part in sulphur, 3~5 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2~3 parts, the molecular formula C of 2~4 parts of stearic acid, 2~3 parts in paraffin, 3~5 parts in Vaseline, 70~90 parts of spray carbon blacks, 50~80 parts in 600 order calcium oxide, accelerant CZ
13H
16N
2S
21~2 part of chemical name N-cyclohexyl-2-benzothiazole sulfonamide.
Described low water absorption carries food oil with rubber hose rubber, it is characterized in that: its rubber raw materials component and raw material weight proportioning are 70 parts of 1# natural rubbers, 30 parts of 9000 type cis-1,4-polybutadiene rubbers, 1 part in sulphur, 3 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2 parts, the molecular formula C of 2 parts of stearic acid, accelerant CZ
13H
16N
2S
2Chemical name N-cyclohexyl-1 part of 2-benzothiazole sulfonamide, 2 parts in paraffin, 3 parts in Vaseline, 70 parts of spray carbon blacks, 50 parts in 600 order calcium oxide.
Described low water absorption carries food oil with rubber hose rubber, it is characterized in that: its rubber raw materials component and raw material weight proportioning are 80 parts of 1# natural rubbers, 40 parts of 9000 type cis-1,4-polybutadiene rubbers, 1.5 parts in sulphur, 3 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2.3 parts, the molecular formula C of 2 parts of stearic acid, 2.5 parts in paraffin, 4 parts in Vaseline, 85 parts of spray carbon blacks, 70 parts in 600 order calcium oxide, accelerant CZ
13H
16N
2S
21.5 parts of chemical name N-cyclohexyls-2-benzothiazole sulfonamide.
Described low water absorption carries food oil with rubber hose rubber, it is characterized in that: its rubber raw materials component and raw material weight proportioning are 95 parts of 1# natural rubbers, 50 parts of 9000 type cis-1,4-polybutadiene rubbers, 2 parts in sulphur, 5 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 3 parts, the molecular formula C of 4 parts of stearic acid, 3 parts in paraffin, 5 parts in Vaseline, 90 parts of spray carbon blacks, 80 parts in 600 order calcium oxide, accelerant CZ
13H
16N
2S
22 parts of chemical name N-cyclohexyls-2-benzothiazole sulfonamide.
This low water absorption carries food oil to use the production method of rubber with rubber hose; Its step is by as follows; The concrete technology step:
Sizing material is produced
(1) according to the various batching of above-mentioned formula rate weighing; Its rubber raw materials component and raw material weight proportioning are chosen as 70~100 parts of 1# natural rubbers, 30~50 parts of 9000 type cis-1,4-polybutadiene rubbers, 1~2 part in sulphur, 3~5 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2~3 parts, 2~4 parts of stearic acid, 2~3 parts in paraffin, 3~5 parts in Vaseline, 70~90 parts of spray carbon blacks, 50~80 parts in 600 order calcium oxide, accelerant CZ molecular formula C
13H
16N
2S
21~2 part of chemical name N-cyclohexyl-2-benzothiazole sulfonamide, the weight unit that component is every part is fixed according to need of production, such as portion by 1 kilogram;
⑵ be added on the rubber mixing machine according to the rubber raw materials proportioning adding 1# natural rubber of step 1), mixing 1 minute rubber raw materials proportioning according to step 1) of roll spacing 4mm adds 9000 type cis-1,4-polybutadiene rubbers, then add successively sulphur, zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture), stearic acid, paraffin mixing, roll spacing is transferred to 5mm and is added Vaseline, spray carbon black and accelerant CZ molecular formula C according to the rubber raw materials proportioning of step 1)
13H
16N
2S
2Chemical name N-cyclohexyl-2-benzothiazole sulfonamide mixes, and the rubber raw materials proportioning according to step 1) adds 600 order calcium oxide at last;
⑶ rubber mixing machine roll spacing transfers to 2mm and makes repeatedly thin-pass 6 times of sizing material, clot 4 times, and eight cutter 4 times;
⑷ mixing even sizing material room temperature park 24 hours stand-by;
Products production
⑴ park on the rear sizing material rubber mixing machine with 4mm roll spacing heat refining 1 minute, rewinds 2 times;
⑵ sizing material cuts into pressurization 10MPa in 160 ℃ of moulds of suitable dimension film adding behind the heat refining, vulcanizes 15 minutes, and exhaust is 3 times when rising mould;
⑶ opening mold after sulfuration is finished takes out product.
The invention has the beneficial effects as follows: low water absorption provided by the invention carries food oil with rubber hose rubber, its rubber raw materials component and proportioning raw materials are chosen as 70~100 parts of 1# natural rubbers, 30~50 parts of 9000 type cis-1,4-polybutadiene rubbers, 1~2 part in sulphur, 3~5 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2~3 parts, the molecular formula C of 2~4 parts of stearic acid, 2~3 parts in paraffin, 3~5 parts in Vaseline, 70~90 parts of spray carbon blacks, 50~80 parts in 600 order calcium oxide, accelerant CZ
13H
16N
2S
21~2 part of chemical name N-cyclohexyl-2-benzothiazole sulfonamide.Infiltrate through moisture in the rubber by adding material modified absorption, thus avoid material of main part and cause because of the hydrolysis variable color that suction causes aging.
Embodiment
This low water absorption of embodiment carries food oil to be chosen as 70~100 parts of 1# natural rubbers, 30~50 parts of 9000 type cis-1,4-polybutadiene rubbers, 1~2 part in sulphur, 3~5 parts in zinc oxide, the domestic title of antioxidant D TPD(with rubber hose with rubber raw materials component and the proportioning of rubber: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2~3 parts, 2~4 parts of stearic acid, 2~3 parts in paraffin, 3~5 parts in Vaseline, 70~90 parts of spray carbon blacks, 50~80 parts in 600 order calcium oxide, accelerant CZ (molecular formula C
13H
16N
2S
2Chemical name N-cyclohexyl-2-benzothiazole sulfonamide) 1~2 part.
Embodiment 1 concrete production stage is as follows:
Sizing material is produced
(1) according to the various batching of above-mentioned formula rate weighing; Its rubber raw materials component and raw material weight proportioning are 70 parts of 1# natural rubbers, 30 parts of 9000 type cis-1,4-polybutadiene rubbers, 1 part in sulphur, 3 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2~3 parts, 2 parts of stearic acid, accelerant CZ (molecular formula C
13H
16N
2S
2Chemical name N-cyclohexyl-2-benzothiazole sulfonamide) 1 part, 2 parts in paraffin, 3 parts in Vaseline, 70 parts of spray carbon blacks, 50 parts in 600 order calcium oxide.Every part weight unit is fixed according to need of production in the component, such as every part by 1 kilogram.
⑵ be added on the rubber mixing machine according to the rubber raw materials proportioning adding 1# natural rubber of step 1), mixing 1 minute rubber raw materials proportioning according to step 1) of roll spacing 4mm adds 9000 type cis-1,4-polybutadiene rubbers, then add successively sulphur, zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture), stearic acid, paraffin mixing, roll spacing is transferred to 5mm and is added Vaseline, spray carbon black and accelerant CZ (molecular formula C according to the rubber raw materials proportioning of step 1)
13H
16N
2S
2Chemical name N-cyclohexyl-2-benzothiazole sulfonamide) mix, the rubber raw materials proportioning according to (1) adds 600 order calcium oxide at last.
⑶ rubber mixing machine roll spacing transfers to 2mm and makes repeatedly thin-pass 6 times of sizing material, clot 4 times, and eight cutter 4 times.
⑷ mixing even sizing material room temperature park 24 hours stand-by.
Products production
⑴ park on the rear sizing material rubber mixing machine with 4mm roll spacing heat refining 1 minute, rewinds 2 times;
⑵ sizing material cuts into pressurization 10MPa in 160 ℃ of moulds of suitable dimension film adding behind the heat refining, vulcanizes 15 minutes, and exhaust is 3 times when rising mould;
⑶ opening mold after sulfuration is finished takes out product.
It is duplicate with industry standard and known technology that present embodiment does not have the part of narration, so be not described in detail.
Embodiment 2 production processes are identical with embodiment 1, difference is that rubber mass component ratio is different, the component meter is as follows by weight for the rubber mass composition of embodiment 2: 80 parts of 1# natural rubbers, 40 parts of 9000 type cis-1,4-polybutadiene rubbers, 1.5 parts in sulphur, 3 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2~3 parts, 2.3 parts of stearic acid, 2.5 parts in paraffin, 4 parts in Vaseline, 85 parts of spray carbon blacks, 70 parts in 600 order calcium oxide, accelerant CZ (molecular formula C
13H
16N
2S
2Chemical name N-cyclohexyl-2-benzothiazole sulfonamide) 1.5 part.
Embodiment 3 production processes are identical with embodiment 1, difference is that rubber mass component ratio is different, the component meter is as follows by weight for the rubber mass composition of embodiment 3: 95 parts of 1# natural rubbers, 50 parts of 9000 type cis-1,4-polybutadiene rubbers, 2 parts in sulphur, 5 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 3 parts, 4 parts of stearic acid, 3 parts in paraffin, 5 parts in Vaseline, 90 parts of spray carbon blacks, 80 parts in 600 order calcium oxide, accelerant CZ (molecular formula C
13H
16N
2S
2Chemical name N-cyclohexyl-2-benzothiazole sulfonamide) 2 part.
Three kinds of embodiment performance comparison
Embodiment 2 prescriptions and the contrast of existing market product
Claims (5)
1. low water absorption carries food oil with rubber hose rubber, it is characterized in that: its rubber raw materials component and raw material weight proportioning are chosen as 70~100 parts of 1# natural rubbers, 30~50 parts of 9000 type cis-1,4-polybutadiene rubbers, 1~2 part in sulphur, 3~5 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2~3 parts, the molecular formula C of 2~4 parts of stearic acid, 2~3 parts in paraffin, 3~5 parts in Vaseline, 70~90 parts of spray carbon blacks, 50~80 parts in 600 order calcium oxide, accelerant CZ
13H
16N
2S
21~2 part of chemical name N-cyclohexyl-2-benzothiazole sulfonamide.
2. low water absorption according to claim 1 carries food oil with rubber hose rubber, it is characterized in that: its rubber raw materials component and raw material weight proportioning are 70 parts of 1# natural rubbers, 30 parts of 9000 type cis-1,4-polybutadiene rubbers, 1 part in sulphur, 3 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2 parts, the molecular formula C of 2 parts of stearic acid, accelerant CZ
13H
16N
2S
2Chemical name N-cyclohexyl-1 part of 2-benzothiazole sulfonamide, 2 parts in paraffin, 3 parts in Vaseline, 70 parts of spray carbon blacks, 50 parts in 600 order calcium oxide.
3. low water absorption according to claim 1 carries food oil with rubber hose rubber, it is characterized in that: its rubber raw materials component and raw material weight proportioning are 80 parts of 1# natural rubbers, 40 parts of 9000 type cis-1,4-polybutadiene rubbers, 1.5 parts in sulphur, 3 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2.3 parts, the molecular formula C of 2 parts of stearic acid, 2.5 parts in paraffin, 4 parts in Vaseline, 85 parts of spray carbon blacks, 70 parts in 600 order calcium oxide, accelerant CZ
13H
16N
2S
21.5 parts of chemical name N-cyclohexyls-2-benzothiazole sulfonamide.
4. low water absorption according to claim 1 carries food oil with rubber hose rubber, it is characterized in that: its rubber raw materials component and raw material weight proportioning are 95 parts of 1# natural rubbers, 50 parts of 9000 type cis-1,4-polybutadiene rubbers, 2 parts in sulphur, 5 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 3 parts, the molecular formula C of 4 parts of stearic acid, 3 parts in paraffin, 5 parts in Vaseline, 90 parts of spray carbon blacks, 80 parts in 600 order calcium oxide, accelerant CZ
13H
16N
2S
22 parts of chemical name N-cyclohexyls-2-benzothiazole sulfonamide.
5. this low water absorption carries food oil to use the production method of rubber with rubber hose; Its step is by as follows; The concrete technology step:
Sizing material is produced
(1) according to the various batching of above-mentioned formula rate weighing; Its rubber raw materials component and raw material weight proportioning are chosen as 70~100 parts of 1# natural rubbers, 30~50 parts of 9000 type cis-1,4-polybutadiene rubbers, 1~2 part in sulphur, 3~5 parts in zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture) 2~3 parts, 2~4 parts of stearic acid, 2~3 parts in paraffin, 3~5 parts in Vaseline, 70~90 parts of spray carbon blacks, 50~80 parts in 600 order calcium oxide, accelerant CZ molecular formula C
13H
16N
2S
21~2 part of chemical name N-cyclohexyl-2-benzothiazole sulfonamide, the weight unit that component is every part is fixed according to need of production, such as portion by 1 kilogram;
⑵ be added on the rubber mixing machine according to the rubber raw materials proportioning adding 1# natural rubber of step 1), mixing 1 minute rubber raw materials proportioning according to step 1) of roll spacing 4mm adds 9000 type cis-1,4-polybutadiene rubbers, then add successively sulphur, zinc oxide, the domestic title of antioxidant D TPD(: anti-aging agent 3100, Chinese: N, N '-di tolyl p phenylenediamine mixture), stearic acid, paraffin mixing, roll spacing is transferred to 5mm and is added Vaseline, spray carbon black and accelerant CZ molecular formula C according to the rubber raw materials proportioning of step 1)
13H
16N
2S
2Chemical name N-cyclohexyl-2-benzothiazole sulfonamide mixes, and the rubber raw materials proportioning according to step 1) adds 600 order calcium oxide at last;
⑶ rubber mixing machine roll spacing transfers to 2mm and makes repeatedly thin-pass 6 times of sizing material, clot 4 times, and eight cutter 4 times;
⑷ mixing even sizing material room temperature park 24 hours stand-by;
Products production
⑴ park on the rear sizing material rubber mixing machine with 4mm roll spacing heat refining 1 minute, rewinds 2 times;
⑵ sizing material cuts into pressurization 10MPa in 160 ℃ of moulds of suitable dimension film adding behind the heat refining, vulcanizes 15 minutes, and exhaust is 3 times when rising mould;
⑶ opening mold after sulfuration is finished takes out product.