CN1029914C - Catalyst for ethylene prodn. by oxidative coupling of methane - Google Patents
Catalyst for ethylene prodn. by oxidative coupling of methane Download PDFInfo
- Publication number
- CN1029914C CN1029914C CN91110922A CN91110922A CN1029914C CN 1029914 C CN1029914 C CN 1029914C CN 91110922 A CN91110922 A CN 91110922A CN 91110922 A CN91110922 A CN 91110922A CN 1029914 C CN1029914 C CN 1029914C
- Authority
- CN
- China
- Prior art keywords
- catalyst
- catalyzer
- methane
- content
- barium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a high-efficiency catalyst for preparing ethylene by oxidizing and coupling methane. The catalyst is composed of thorium oxide, lanthanum oxide and barium carbonate, wherein the thorium oxide content is from 26.0 to 59.0 wt%, the lanthanum oxide content is from 3.0 to 9.0 wt%, and the barium carbonate content is from 5.0 to 70.0 wt%. The catalyst provided by the present invention has high activity and high selectivity and particularly has good operational stability and high mechanical strength. The catalyst of the present invention has the advantages of simple preparation and good repetitiveness, and the comprehensive performance reaches the requirements of industrialization development.
Description
The technological development field of the methane oxidation coupling system of the invention belongs to ethene.
The invention relates to a kind of by Thorotrast (ThO
2), lanthanum trioxide (La
2O
3) and barium carbonate (BaCO
3) the high-efficiency methane oxidative coupling catalyst for making ethylene formed.
At present, very active to the research of methane oxidation coupling catalyst for making ethylene system, because it is significant to the development and use of the major ingredient methane in the Sweet natural gas.As can be seen, although the quite a lot of element in the periodictable is attempted, most of catalyzer only are applicable to laboratory study from the result of study of having reported, its C2 hydrocarbon yield (Yc
2) and the technical indicator of aspects such as space-time yield, operational stability, physical strength also have big gap from practical application in industry.
Du Bois people such as (J.L.Dubois) is at " applied catalysis " (App.Catal.67(1) 73,1990) reported a kind of dual-component catalyst of thoriated.They have prepared CaO-ThO with mechanically mixing thorium nitrate 99.99004323A8urity and alkine earth metal nitrate
2, SrO-ThO
2And BaO-ThO
2Catalyzer has prepared Ca/ThO with the nitrate solution oxide impregnation thorium of corresponding component
2, Sr/ThO
2, Ba/ThO
2And La, Sr/ThO
2Catalyzer has prepared Th/CaCO with thorium nitrate 99.99004323A8urity solution impregnation lime carbonate, Strontium carbonate powder, carbonic acid gas lanthanum
3, Th/SrCO
3And Th/La
2O
2CO
3Catalyzer.They are at methane CH
4: oxygen O
2=10: the 1(volume ratio), under the temperature of reaction T=880 ℃ of condition, estimated above-mentioned catalyzer, optimum is methane conversion XCH
4=15.1%, the selectivity Sc of C2 hydrocarbon and carbon two above hydrocarbon
+ 2=74.9%, the yield Yc of C2 hydrocarbon and carbon two above hydrocarbon
+ 2=11.3%.
The characteristics of oxidative coupling of methane have determined that in development of practical type catalyzer except that improving activity of such catalysts and selectivity, the operational stability of catalyzer and physical strength etc. also are the factors of very significant.
The present invention is intended to develop a kind of activity and selectivity height, operational stability and physical strength are good, the high-efficiency methane oxidative coupling catalyst that is made of Thorotrast, lanthanum trioxide and barium carbonate.
Detailed description of the invention
Catalyzer of the present invention contains ThO
2, La
2O
3And BaCO
3Three components, the weight percentage of each component (wt%) is:
ThO
2: 7.0-88.0wt%, preferably 15.0-70.0wt%, especially 26.0-59.0wt%.
La
2O
3: 1.0-27.0wt%, preferably 2.0-15.0wt%, especially 3.0-9.0wt%.
BaCO
3: 10.0-90.0wt%, preferably 30.0-80.0wt%, especially 35.0-70.0wt%.
Catalyzer adopts the coprecipitation method preparation.Th(NO with metering
3)
44H
2O(A.R.), La(NO
3)
36H
2O(A.R.) and Ba(NO
3)
2(A.R.) be dissolved in a certain amount of distilled water, make solution A.With the NH that equates with total metal ion equivalent number
4HCO
3(A.R.) be dissolved in a certain amount of aqueous solution, after treating to dissolve fully, add an amount of strong aqua (A.R.), make the solution B of PH=10.Under the condition of high degree of agitation, A is injected B, continue to stir after 2-5 minute, filter.Use the distilled water wash precipitation suitable three times one by one with the solution B volume.Dislocation is deposited in the baking oven, 140 ℃ dry 6-8 hour down, dislocation at 800-1000 ℃, preferably under 820-920 ℃, fused preferably 4-5 hour 3-6 hour in retort furnace thereafter.Grind again, sieve into the particle of required order number.
Evaluating catalyst carries out in atmospheric fixed bed flowing reactive system.The main C of reaction product by analysis
2H
4, C
2H
6, CO
2, CO, H
2O, H
2With a small amount of high-carbon hydrocarbon.At CH
4: O
2=10: the 1(volume ratio), under the temperature of reaction T=780 ℃ of condition, methane conversion XCH
4=17.0%, the selectivity Sc of C2 hydrocarbon
2=78.3%, the yield Yc of C2 hydrocarbon
2=13.3%.And at CH
4: O
2: N
2=4: 1: the 9(volume ratio), temperature of reaction T=780-900 ℃, air speed GHSV=1.0 * 10
4-1.2 * 10
5Hr
1Down, XCH
4Can reach 30.7%, Yc
2Can reach 19.4%.Under reaction conditions, carry out operational stability test in 1000 hours, whole experimental session XCH
4, Sc
2And Yc
2Quite stable.The fluid catalyst polishing machine is measured and is shown, the intensity of catalyzer can satisfy the requirement that fluidized-bed uses.
The invention provides a kind of activity and the good high-efficiency methane oxidative coupling catalyst of selectivity height, operational stability and physical strength.Catalyzer of the present invention is made simple, good reproducibility.
Accompanying drawing is a catalyzer operational stability test-results.
The present invention is further illustrated by embodiment below:
Embodiment 1.
With 7.65g Th(NO
3)
44H
2O(A.R.), 0.90g La(NO
3)
36H
2O(A.R.) and 7.95gBa(NO
3)
2(A.R.) be dissolved in the 100ml distilled water and make solution A, 4.84g NH
4HCO
3(A.R.) be dissolved in the 90ml distilled water, treat to dissolve fully the back and add strong aqua (A.R.) adjustment solution pH value, make the solution B of PH=10 at last.Under high degree of agitation, A is injected B, continue to stir after 2 minutes, filter.Precipitate three times with the 100ml distilled water wash one by one.Be deposited in the baking oven 140 ℃ dry 8 hours down, thereafter 900 ℃ of following roastings of retort furnace 4 hours.Abrasive catalyst sieves into 30-60 order particle.Evaluating catalyst carries out reaction conditions and evaluation result such as table one in atmospheric fixed bed flowing reactive system.
Table one
CH
4∶O
2∶N
2T(℃) GHSV(h
-1) XCH
4Sc
2Yc
2
4∶1∶9 780 6×10
430.7 63.3 19.4
4∶1∶9 680 6×10
428.2 65.0 18.3
4∶1∶9 820 6×10
464.0 19.2
4∶1∶9 780 1×10
430.2 62.7 19.0
4∶1∶9 780 1.2×10
529.8 64.4 19.2
Embodiment 2.
With 7.88g Th(NO
3)
44H
2O(A.R.), 1.24gLa(NO
3)
36H
2O(A.R.) and 7.95gBa(NO
3)
2(A.R.) be dissolved in the 100ml distilled water and make solution A.With 4.60g NH
4HCO
3(A.R.) be dissolved in the 90ml distilled water, treat to dissolve fully the back and add strong aqua (A.R.) adjustment solution pH value, make the solution B of PH=10 at last.Under high degree of agitation, A is injected B, continue to stir after 4 minutes, filter.Precipitate three times with the 100ml distilled water wash one by one.Be deposited in the baking oven 140 ℃ dry 8 hours down, thereafter 850 ℃ of following roastings of retort furnace 4 hours.Abrasive catalyst sieves into 30-60 order particle.Evaluating catalyst carries out reaction conditions and evaluation result such as table two in atmospheric fixed bed flowing reactive system.
Table two
CH
4∶O
2∶N
2T(℃) GHSV(h
-1) XCH
4Sc
2Yc
2
4∶1∶9 780 6×10
430.4 63.2 19.2
Embodiment 3.
The catalyzer method for making changes Preparation of Catalyst raw material input amount and is respectively: Th(NO with example 1
3)
44H
2O(A.R.) 9.58g, La(NO
3)
36H
2O(A.R.) 1.12g, Ba(NO
3)
2(A.R.) 6.63g and NH
4HCO
3(A.R.) 5.05g.
At CH
4: O
2: N
2=4: 1: 9, T=780 ℃, GHSV=6X10
4h
-1Carry out 1000 hours stable operation experiment under the condition, the results are shown in accompanying drawing.
Claims (7)
1, a kind of methane oxidation coupling catalyst for making ethylene, it is characterized in that said catalyzer is by Thorotrast, lanthanum trioxide and barium carbonate are formed, and Thorotrast content is 7.0~88.0wt% in the said catalyzer, lanthanum trioxide content is 1.0~27.0wt%, and barium carbonate content is 10.0~90.0wt%.
2,, it is characterized in that Thorotrast content is 15.0~70.0wt% according to the said catalyzer of claim 1.
3,, it is characterized in that Thorotrast content is 26.0~59.0wt% according to claim 1 and 2 said catalyzer.
4,, it is characterized in that lanthanum trioxide content is 2.0~15.0wt% according to the said catalyzer of claim 1.
5,, it is characterized in that lanthanum trioxide content is 3.0~9.0wt% according to claim 1 and 4 said catalyzer.
6,, it is characterized in that barium carbonate content is 30.0~80.0wt% according to the said catalyzer of claim 1.
7,, it is characterized in that barium carbonate content is 35.0~70.0wt% according to claim 1 and 6 said catalyzer.