CN102990249A - High carbon ferro-chrome welding stick - Google Patents
High carbon ferro-chrome welding stick Download PDFInfo
- Publication number
- CN102990249A CN102990249A CN2012104202484A CN201210420248A CN102990249A CN 102990249 A CN102990249 A CN 102990249A CN 2012104202484 A CN2012104202484 A CN 2012104202484A CN 201210420248 A CN201210420248 A CN 201210420248A CN 102990249 A CN102990249 A CN 102990249A
- Authority
- CN
- China
- Prior art keywords
- high carbon
- chrome
- carbon ferro
- ferro
- weld wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high carbon ferro-chrome welding stick, which comprises the following components by weight percent: 68-72% of chromium, 7.5-9.5% of carbon, 1-3% of silicon, 0.01-0.04% of sulphur, 0.01-0.04% of phosphorus, and 10-30% of iron. The high carbon ferro-chrome welding stick has the advantages of high hardness, high temperature resistance, corrosion resistance, and wear resistance.
Description
Technical field
The present invention relates to a kind of welding wire, relate in particular to a kind of high carbon ferro-chrome welding wire.
Background technology
In welding wire when welding, is as filling metal or simultaneously as the welded wire material of conduction usefulness.When gas welding and shielded arc welding of tungsten electrode gas, welding wire is as filling metal.High carbon ferro-chrome is widely used in metallurgy, electric power, machinery, the fields such as chemical industry because it has hardness height, high temperature resistant, corrosion-resistant, abrasion resistance properties.Therefore, need to provide a kind of new technical scheme to solve the problems referred to above.
Summary of the invention
The purpose of this invention is to provide a kind of anti abrasive high carbon ferro-chrome welding wire.
The technical solution used in the present invention:
The high carbon ferro-chrome welding wire, this high carbon ferro-chrome component of weld wire is by weight percentage:
Chromium 68-72%;
Carbon 7.5-9.5%;
Silicon 1-3%;
Sulphur 0.01-0.04%;
Phosphorus 0.01-0.04%;
Iron 10-30%.
Chromium in the described high carbon ferro-chrome component of weld wire was the chromium powder of 30-50 mesh sieve.
Carbon in the described high carbon ferro-chrome component of weld wire was the carbon dust of 90-110 mesh sieve.
Silicon in the described high carbon ferro-chrome component of weld wire was the silica flour of 180-220 mesh sieve.
Sulphur in the described high carbon ferro-chrome component of weld wire was the sulphur powder of 300-350 mesh sieve.
Phosphorus in the described high carbon ferro-chrome component of weld wire was the phosphorus powder of 300-350 mesh sieve.
Iron in the described high carbon ferro-chrome component of weld wire was the iron powder of 280-320 mesh sieve.
Advantage of the present invention is: the welding wire that high carbon ferro-chrome is made has and has that hardness is high, high temperature resistant, corrosion-resistant, abrasion resistance properties.
The specific embodiment
Following embodiment only is used for explanation the present invention, but can not limit protection scope of the present invention.
Embodiment 1
The high carbon ferro-chrome welding wire, this high carbon ferro-chrome component of weld wire is by weight percentage:
Chromium 68%;
Carbon 7.5%;
Silicon 1.5%;
Sulphur 0.01%;
Phosphorus 0.04%;
Iron 22.95%.
Chromium in the high carbon ferro-chrome component of weld wire was the chromium powder of 30 mesh sieves, carbon in the high carbon ferro-chrome component of weld wire was the carbon dust of 90 mesh sieves, silicon in the high carbon ferro-chrome component of weld wire was the silica flour of 180 mesh sieves, sulphur in the high carbon ferro-chrome component of weld wire was the sulphur powder of 300 mesh sieves, phosphorus in the high carbon ferro-chrome component of weld wire was the phosphorus powder of 300 mesh sieves, and the iron in the high carbon ferro-chrome component of weld wire was the iron powder of 280 mesh sieves.
Embodiment 2
The high carbon ferro-chrome welding wire, this high carbon ferro-chrome component of weld wire is by weight percentage:
Chromium 70%;
Carbon 8%;
Silicon 2%;
Sulphur 0.02%;
Phosphorus 0.02%;
Iron 19.96%.
Chromium in the high carbon ferro-chrome component of weld wire was the chromium powder of 40 mesh sieves, carbon in the high carbon ferro-chrome component of weld wire was the carbon dust of 100 mesh sieves, silicon in the high carbon ferro-chrome component of weld wire was the silica flour of 200 mesh sieves, sulphur in the high carbon ferro-chrome component of weld wire was the sulphur powder of 325 mesh sieves, phosphorus in the high carbon ferro-chrome component of weld wire was the phosphorus powder of 325 mesh sieves, and the iron in the high carbon ferro-chrome component of weld wire was the iron powder of 300 mesh sieves.
Embodiment 3
The high carbon ferro-chrome welding wire, this high carbon ferro-chrome component of weld wire is by weight percentage:
Chromium 72%;
Carbon 9.5%;
Silicon 3%;
Sulphur 0.04%;
Phosphorus 0.04%;
Iron 15.42%.
Chromium in the high carbon ferro-chrome component of weld wire was the chromium powder of 50 mesh sieves, carbon in the high carbon ferro-chrome component of weld wire was the carbon dust of 110 mesh sieves, silicon in the high carbon ferro-chrome component of weld wire was the silica flour of 220 mesh sieves, sulphur in the high carbon ferro-chrome component of weld wire was the sulphur powder of 350 mesh sieves, phosphorus in the high carbon ferro-chrome component of weld wire was the phosphorus powder of 350 mesh sieves, and the iron in the high carbon ferro-chrome component of weld wire was the iron powder of 320 mesh sieves.
The welding wire that high carbon ferro-chrome is made has and has that hardness is high, high temperature resistant, corrosion-resistant, abrasion resistance properties.
Claims (7)
1. high carbon ferro-chrome welding wire, it is characterized in that: this high carbon ferro-chrome component of weld wire is by weight percentage:
Chromium 68-72%;
Carbon 7.5-9.5%;
Silicon 1-3%;
Sulphur 0.01-0.04%;
Phosphorus 0.01-0.04%;
Iron 10-30%.
2. high carbon ferro-chrome welding wire according to claim 1, it is characterized in that: the chromium in the described high carbon ferro-chrome component of weld wire was the chromium powder of 30-50 mesh sieve.
3. high carbon ferro-chrome welding wire according to claim 1, it is characterized in that: the carbon in the described high carbon ferro-chrome component of weld wire was the carbon dust of 90-110 mesh sieve.
4. high carbon ferro-chrome welding wire according to claim 1, it is characterized in that: the silicon in the described high carbon ferro-chrome component of weld wire was the silica flour of 180-220 mesh sieve.
5. high carbon ferro-chrome welding wire according to claim 1, it is characterized in that: the sulphur in the described high carbon ferro-chrome component of weld wire was the sulphur powder of 300-350 mesh sieve.
6. high carbon ferro-chrome welding wire according to claim 1, it is characterized in that: the phosphorus in the described high carbon ferro-chrome component of weld wire was the phosphorus powder of 300-350 mesh sieve.
7. high carbon ferro-chrome welding wire according to claim 1, it is characterized in that: the iron in the described high carbon ferro-chrome component of weld wire was the iron powder of 280-320 mesh sieve.