CN102976683A - Cement matrix wave-absorbing construction material - Google Patents
Cement matrix wave-absorbing construction material Download PDFInfo
- Publication number
- CN102976683A CN102976683A CN2012105264609A CN201210526460A CN102976683A CN 102976683 A CN102976683 A CN 102976683A CN 2012105264609 A CN2012105264609 A CN 2012105264609A CN 201210526460 A CN201210526460 A CN 201210526460A CN 102976683 A CN102976683 A CN 102976683A
- Authority
- CN
- China
- Prior art keywords
- wave
- absorbing agent
- cement matrix
- cement
- inhaled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cement matrix wave-absorbing construction material which is prepared by taking cement as a matrix and adding 55-65 parts of organic wave-transparent aggregate, 8-12 parts of dielectric loss wave-absorbing agent, 0.5-1 part of auxiliary enhancement wave-absorbing agent and 25-35 parts of electromagnetic loss wave-absorbing agent into every 100 parts of cement matrix. In such manner, the cement matrix wave-absorbing construction material disclosed by the invention can effectively shield the radiation of electromagnetic waves to a human body, achieves the purpose of purifying the environment polluted by electromagnetic waves, has favorable wave-absorbing property, stability quality and mechanical property, and is wide in frequency band and low in cost.
Description
Technical field
The present invention relates to the building decoration technology field, particularly relate to a kind of cement matrix and inhale the wave building material.
Background technology
Develop rapidly along with the hyundai electronics science and technology, electronics high frequency, digitizing, electromagnetic radiation etc. are when creating the wealth to the mankind, brought more and more serious harm also for equipment, system and ecotope, therefore, by internationally recognized for being the 4th large public hazards after topsoil, water pollution and sound pollution.In order to prevent outside electromagnetic interference and the leakage of electromagnetic signal, cut down hertzian wave to the injury of human body and the hertzian wave detectivity to buildings, the purifying electric magnetic radiation improves the space electromagnetic environment, eliminate electromagnetic pollution, need to carry out electromagnetic protection to buildings.
At present, mainly adopt wave-absorbing material applied to buildings effectively to realize the electromagnetic protection of buildings.Cement is for carrying and keeps building shape and use comparatively widely material of construction, but, plain cement does not have the shielding electromagnetic waves sorption, usually adopt electromagnetic shielding material to come filling concrete to make it can effectively suppress electromagnetic radiation and leakage, but this material just goes back reflection of electromagnetic wave usually, cause easily secondary pollution, and can not fundamentally weaken and eliminate hertzian wave.And existing absorbing material have frequency band narrow, absorb that usefulness is low, cost is high, the defective such as poor stability, environmental adaptation are poor.
Summary of the invention
The technical problem that the present invention mainly solves is: for the deficiencies in the prior art, provide a kind of cement matrix to inhale the wave building material, shielding electromagnetic wave is to the radiation of human body effectively, reach and purify by the purpose of the environment of Contamination of Electromagnetic Wave, have good absorbing property, stability and mechanical property, and bandwidth, cost are low.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of cement matrix to inhale the wave building material, it is take cement as base material that described cement matrix is inhaled the wave building material, adds organic wave transparent aggregate, the dielectric loss wave absorbing agent of 8-12 part, the auxiliary enhancing wave absorbing agent of 0.5-1 part and the electromagnetic consumable wave absorbing agent of 25-35 part of 55-65 part and make in per 100 parts of cement matrixs.
In a preferred embodiment of the present invention, described organic wave transparent aggregate is closed-cell expanded perlite.
In a preferred embodiment of the present invention, described dielectric loss wave absorbing agent is graphite microparticles.
In a preferred embodiment of the present invention, described auxiliary enhancing wave absorbing agent is continuous basalt fiber.
In a preferred embodiment of the present invention, described electromagnetic consumable wave absorbing agent is a kind of in polycrystalline iron fiber, steel fiber, carbon fiber or the ceramic fiber.
The invention has the beneficial effects as follows: by the organic wave transparent aggregate of reasonable selection, dielectric loss wave absorbing agent, auxiliary wave absorbing agent and the electromagnetic consumable wave absorbing agent of strengthening, adopt rational proportioning to make cement matrix and inhale the wave building material, shielding electromagnetic wave is to the radiation of human body effectively, reach and purify by the purpose of the environment of Contamination of Electromagnetic Wave, have good absorbing property, stability and mechanical property, and bandwidth, cost are low.
Embodiment
The below is described in detail preferred embodiment of the present invention, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
The embodiment of the invention comprises:
A kind of cement matrix is inhaled the wave building material, it is as base material take cement that described cement matrix is inhaled the wave building material, in per 100 parts of cement matrixs, add organic wave transparent aggregate of 55-65 part, be preferably 60 parts, the dielectric loss wave absorbing agent of 8-12 part, be preferably 10 parts, the auxiliary enhancing wave absorbing agent of 0.5-1 part, be preferably 0.5 part, and the electromagnetic consumable wave absorbing agent of 25-35 part, be preferably 25.5 parts, configuration forms in 8-18 GHz frequency range.
Wherein, described organic wave transparent aggregate is closed-cell expanded perlite, has guaranteed the high porosity of material, has reduced the convection current of air, has good electromagnetic consumable characteristic.
Described dielectric loss wave absorbing agent is graphite microparticles, its wide material sources, cheap, electroconductibility is good, good dispersity.
Described auxiliary enhancing wave absorbing agent is continuous basalt fiber, itself contains certain dielectric loss material, and the internal structure porous has certain suction wave energy, and good insulating has improved the thermal and insulating performance of material; Also have high chemical stability and thermostability, can suppress the expansion of tiny crack, play enhancing, toughness reinforcing effect.
Described electromagnetic consumable wave absorbing agent is a kind of in polycrystalline iron fiber, steel fiber, carbon fiber or the ceramic fiber, can improve dielectric material surface and inner to electromagnetic loss ability, the characteristics that have lightweight, enhancing and efficiently inhale ripple.
The present invention has disclosed a kind of cement matrix and has inhaled the wave building material, by the organic wave transparent aggregate of reasonable selection, dielectric loss wave absorbing agent, auxiliary wave absorbing agent and the electromagnetic consumable wave absorbing agent of strengthening, adopt rational proportioning to make cement matrix and inhale the wave building material, shielding electromagnetic wave is to the radiation of human body effectively, reach and purify by the purpose of the environment of Contamination of Electromagnetic Wave, have good absorbing property, stability and mechanical property, and bandwidth, cost are low.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (5)
1. a cement matrix is inhaled the wave building material, it is characterized in that, it is take cement as base material that described cement matrix is inhaled the wave building material, adds organic wave transparent aggregate, the dielectric loss wave absorbing agent of 8-12 part, the auxiliary enhancing wave absorbing agent of 0.5-1 part and the electromagnetic consumable wave absorbing agent of 25-35 part of 55-65 part and make in per 100 parts of cement matrixs.
2. cement matrix according to claim 1 is inhaled the wave building material, it is characterized in that described organic wave transparent aggregate is closed-cell expanded perlite.
3. cement matrix according to claim 1 is inhaled the wave building material, it is characterized in that described dielectric loss wave absorbing agent is graphite microparticles.
4. cement matrix according to claim 1 is inhaled the wave building material, it is characterized in that described auxiliary enhancing wave absorbing agent is continuous basalt fiber.
5. cement matrix according to claim 1 is inhaled the wave building material, it is characterized in that, described electromagnetic consumable wave absorbing agent is a kind of in polycrystalline iron fiber, steel fiber, carbon fiber or the ceramic fiber.