CN102964086A - 混凝土养护剂 - Google Patents
混凝土养护剂 Download PDFInfo
- Publication number
- CN102964086A CN102964086A CN2012105490309A CN201210549030A CN102964086A CN 102964086 A CN102964086 A CN 102964086A CN 2012105490309 A CN2012105490309 A CN 2012105490309A CN 201210549030 A CN201210549030 A CN 201210549030A CN 102964086 A CN102964086 A CN 102964086A
- Authority
- CN
- China
- Prior art keywords
- cement concrete
- concrete
- building
- brush
- spray
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种混凝土养护剂是由石蜡,水,氢氧化钠,氧化剂,稳定剂,防腐剂组成,经过化工工序生产而成的材料和技术。用于新浇筑的水泥混凝土的养护,利用配方中的石蜡和淀粉为主要成膜物质在水泥混凝土表面形成一层致密的、憎水的、不透水的有机薄膜,使水泥混凝土不用外来水分补充的前提下,利用其自身含有的水分,充分参与水泥的水化反应,保障了水泥混凝土的抗压强度比的正常增长。
Description
技术领域
本发明是一种喷涂在混凝土表面形成致密的憎水的有机薄膜,有效防止混凝土内部水分蒸发,代替人工喷洒水养护混凝土的技术和材料。
技术背景
目前,用于混凝土养护的养护剂大致有以下几个种类:水玻璃(硅酸钠)类,石蜡乳液类,苯丙乳液类,氯乙烯类,氯丁胶乳液类,聚醋酸乙烯类等养护剂。以上的养护剂各有个的优点,但也存在本身的缺陷:
1.水玻璃类:该材料在混凝土在表面形成刚性的透明、光滑薄膜。具有成膜快,造价低廉,易保存,原材料易得的优点。该类的主要有效成分是So2(二氧化硅),与未凝固的混凝土的水化产物反应,生成的产物发生破坏性膨胀,降低混凝土表面的抗压强度,这是缺点之一;其二,由于该材料成膜1-2小时后,膜的强度大于未完全凝固混凝土的强度;随着混凝土强度的增长,混凝土本身的强度会大于水玻璃膜的强度,加上混凝土胶凝后的干缩因素的影响,该养护膜出现开裂、起皮、脱落的现象。这样既影响了混凝土制品外观,又影响了混凝土强度的增长。
2.石蜡乳液类:该材料在干燥的环境中在混凝土表面形成良好的憎水性薄膜,很好的封闭混凝土表面的毛细孔,达到养护的目的。但是,若在混凝土表面有自由水存在或在潮湿的环境中使用的情况下,石蜡乳液被稀释成低浓度的乳液后,会有以下缺点:其一,会形成一个个的麻点,影响它的成膜效果,导致养护膜封闭不严,保水率和养护效果就会降低;其二,稀释后的石蜡乳液会被混凝土表层吸收,使混凝土表面的水化反应不能彻底地反应完毕。影响了混凝土表面的抗压强度;其三,由于该材料的薄膜是憎水的,且化学性质稳定,其在混凝土表面不易清理,直接影响了二次粉刷工序的进行。
3.苯丙乳液、聚醋酸乙烯类:该类材料在混凝土表面干燥后,形成类似于塑料薄膜的柔性薄膜,封闭混凝土表面的毛细孔,降低混凝土内部的水分蒸发。但是,该类材料形成的薄膜是柔性的、强度低的,已损坏的。混凝土用该材料施工成膜后,工人接触或在其表面施工时,会损害该封闭薄膜的。这样,就会使混凝土内部的水分蒸发,直接影响了混凝土的抗压强度。其二,在该材料施工过的混凝土表面进行二次施工工序时,由于该表面有一层不溶于水的薄膜,使前后两次施工的结合部位粘接力降低,会造成脱落、空鼓的现象,严重影响了工程质量。
4.氯乙烯类、氯丁胶乳液类:该材料在混凝土表面成膜后,形成高弹性的、强度较高的、封闭的,不透水的、柔性薄膜。其能很好地保护混凝土内部水分的蒸发,使混凝土的水泥“水化反应”反应充分,能很好保护混凝土的胶凝,使混凝土的抗压强度数据达到最大化的优点。但是该类材料也是有缺陷的:
其一,该类材料含有大量的有机挥发性溶剂,对人体有害;其二,造价高昂,限制了该类材料在市场上的份额;其三,该材料在混凝土表面形成高弹性的薄膜后,在二次施工工序前清理该材料困难,同样也会造成前后两次施工的结合部位粘接力降低,会造成脱落、空鼓的现象,严重影响了工程质量,留下了安全的隐患。
以上就是对目前养护剂在市场的反馈,它们既有优点,也有缺点。该申请的专利技术保留了以上材料的优点,避免了以上材料的缺点。
该申请的混凝土养护剂的专利技术在混凝土表面形成一层致密的、憎水的、易粉化的有机薄膜。使混凝土与空气隔绝,极大限度地降低水分从混凝土表面蒸发,使混凝土利用自身的水分,充分地完成水泥的水化反应。该专利技术在混凝土表面形成的薄膜会在20天以后,短时间内逐步地、彻底地粉化,不影响二次施工工序的进行。具备了混凝土强度不降低,检测结果是,7d的抗压强度比100%,28d的抗压强度比99%,保水率高,成本低,易施工,无毒,无害的优点。以下是经“国家建筑材料测试中心”利用该申报专利技术生产的材料进行了检测,检测报告如下(见下一页):
国家建筑材料测试中心
检测报告
发明内容
经过对混凝土养护剂进行长时间的观察及研究。经过反复地调整配方,反复地实地应用,综合考虑各方的建议,发明了该技术。
该发明采取的技术配方为:
本发明的生产工序是:
1:制取A组份:
a.按照配方称取A组份的质量数;
b.石蜡和乳化剂加热融化备用;
c.把水在反应釜中加热到85℃-90℃,把加热融化的石蜡和乳化剂,徐徐加入到反应釜中,边加边搅拌,静止反应0.5小时;
d.静止反应后的溶液,迅速冷却至30℃以下,包装入库。
2.a.按照配方称取B组份的质量数;
b.把配方中的水倒入防腐容器中;
c.再把制取的A组份(按B组份总质量的5%)加入,搅拌均匀;
d.依次加入防腐剂,淀粉,氢氧化钠,边加边搅拌,得到乳白色的粘稠胶状液体,静止反应1小时;
e.1小时后,依次加入防腐剂、氧化剂、稳定剂,搅拌0.5小时,包装入库,即得或品。
Claims (8)
1.一种混凝土养护剂是由石蜡,水,氢氧化钠,乳化剂,淀粉,氧化剂,稳定剂,防腐剂组成,经过化工工序生产而成的技术和材料。
2.根据权利要求1所述,其特征是:用于水泥混凝土在浇筑后,喷、涂、刷在新浇筑的水泥混凝土表面,防止混凝土内部水分蒸发,保障混凝土内部的水分彻底地、充分地参与水泥混凝土的水化反应。
3.根据权利要求1所述,其特征是:用于水泥混凝土在浇筑后,喷、涂、刷在该水泥混凝土表面,与人工喷洒水或湿物覆盖的养护方式一样,保障混凝土的抗压强度比正常的增长。
4.根据权利要求1所述,其特征是:用于水泥混凝土在浇筑后,喷、涂、刷在该水泥混凝土表面,形成不透水的薄膜。
5.根据权利要求1所述,其特征是:用于水泥混凝土在浇筑后,喷、涂、刷在该水泥混凝土表面,形成憎水的有机薄膜。
6.根据权利要求1所述,其特征是:用于水泥混凝土在浇筑后,喷、涂、刷在该水泥混凝土表面,水泥混凝土不用外来水分补充的前提下,保障水泥混凝土的抗压强度比的正常增长。
7.根据权利要求1所述,其特征是:用于水泥混凝土在浇筑后,是用水稀释并搅拌均匀,喷、涂、刷在该水泥混凝土表面。
8.根据权利要求1所述,其特征是:用于水泥混凝土在浇筑后,喷、涂、刷在该水泥混凝土表面,利用淀粉和石蜡为主要成膜的材料。