CN102942861A - Non-aromatic anti-corrosive paint coating scheme - Google Patents
Non-aromatic anti-corrosive paint coating scheme Download PDFInfo
- Publication number
- CN102942861A CN102942861A CN2012105396400A CN201210539640A CN102942861A CN 102942861 A CN102942861 A CN 102942861A CN 2012105396400 A CN2012105396400 A CN 2012105396400A CN 201210539640 A CN201210539640 A CN 201210539640A CN 102942861 A CN102942861 A CN 102942861A
- Authority
- CN
- China
- Prior art keywords
- aromatic hydrocarbons
- protective system
- coating scheme
- kind ofly
- system coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a non-aromatic anti-corrosive paint coating scheme which comprises the steps of: mixing the components such as siloxane, solvent, silica particles, rare earth compound, deionized water, catalyst, carbon fiber and polyimide, and then curing; filtering the cured mixture; and spraying, brushing or impregnating the filtered mixture on the surface of base material, wherein a coating is formed on the surface of the base material after deposition, thus realizing surface anti-corrosion treatment.
Description
Technical field
The present invention relates to a kind ofly without aromatic hydrocarbons protective system coating scheme, relate in particular to a kind of metal structure surface that is applicable to, have the coating method of the environmental protection coating material of excellent gloss and mechanical and physical performance and aromatic free solvent.
Background technology
In modern industry and daily life, corrosion of metal is seen everywhere, and the destruction of the forms such as crevice corrosion, stress corrosion and corrosion fatigue that especially occur in the storage vessel of a fuel oil dangerization product is caused great potential safety hazard for people's lives.
The metal protection method that adopts at present can roughly be divided three classes: a class is to carry out anodic oxidation treatment, namely form the anode oxide film of one deck tens micron thickness in the metallic surface, but because the anode oxidation process power consumption is large, and electrolyte solution is seriously polluted, be difficult to process, use its application to be restricted; Equations of The Second Kind is chemical conversion film, being about to metal parts is immersed in the solution of definite composition, rely at a certain temperature chemical reaction to form one deck chemical conversion film, now most widely used is the oxidation of chromic salt chemistry, but chromic salt is a kind of carcinogenic toxicant, and the world environments protective tissue has proposed restriction and used chromic salt and other to contain chromate compound; The 3rd class is organic coating, namely applies one deck organic coating in the metallic surface, with outward appearance and the physical and chemical performance that improves metal.People begin rare earth element is used in the aseptic technic of metallic surface in recent years.
The rare-earth conversion coatings film technique develops into today, and people have carried out a large amount of improvement to various film-forming process, and the performance of film also is improved.At present the rare-earth conversion coatings technology mainly is immersion treatment, and this technological operation is simple, be easy to safeguard; But its drawback is that the long period of soaking process treatment time is oversize, and formed rete is thinner and relatively poor with the sticking power of base material.Find through long-term exploratory development, add strong oxidizer in the soaking solution, such as H
2O
2, KMnO
4, (NH
4)
2S
2O
8Etc. strong oxide compound, rate of film build is improved greatly, the treatment time shortens dramatically, and the treatment soln temperature is not high yet simultaneously, can at room temperature use.But because the existence of strong oxidizer is so that the less stable for the treatment of process.
The problem that exists in order to solve the rare-earth conversion coatings treatment process, the present invention proposes a kind of improved a kind of without aromatic hydrocarbons protective system coating scheme.This method anticorrosion with low cost, remarkable in economical benefits can be carried out normal temperature and be spread, and coating processes is simple, and solution is environment friendly and pollution-free.
Summary of the invention
The objective of the invention is for the deficiencies in the prior art part, provide a kind of environmental protection a kind of without aromatic hydrocarbons protective system coating scheme, in order to solve the protection against corrosion difficult problem of the surfaces externally and internally applications such as steel, aluminium, especially aluminium alloy, and coating aromatic free solvent, do not contain strong oxidizer, without poisonous pigment, be fit to various constructional methods, application is not subject to seasonal restrictions, and construction technology is simple and convenient, and technical costs is cheap, good environmental protection.
The present invention is achieved by the following technical solutions:
(1) prepare following component (mass parts):
A vinyltriethoxysilane 1-10;
B propyl alcohol 40-60;
C SiO
2Particle 1-5;
The oxide compound 1-5 of d cerium;
E deionized water 5-25;
F acetic acid 4-6;
G carbon fiber 5-7;
H polyimide 1-3;
(2) with carrying out maturation process after the above component mixing, then spray, brush or be immersed in substrate surface, form coating at substrate surface after the deposition, realize the surface anticorrosion processing.
Embodiment
The present invention relates to a kind of without aromatic hydrocarbons protective system coating scheme, after being mixed, the various components of protective system carry out maturation process, again the mixture after the slaking is filtered, then spray, brush or be immersed in substrate surface, form coating at substrate surface after the deposition, realize the surface anticorrosion processing.
Described SiO
2The particle diameter of particle is the 50-100 nanometer.
Described maturation process is to leave standstill at normal temperatures 50-60 hour.
Described base material is steel or aluminium, preferred aluminium alloy.
Heat in the deposition process after spraying, brushing or dipping, Heating temperature is to heat 1 minute to 1 hour under 50 ℃ to the 150 ℃ temperature.
The thickness of described coating is 1 micron to 10 microns, preferred 1 micron to 5 microns.The preferred method that adopts spraying or brush forms coating at substrate surface.
Disclosed by the invention a kind of simple, convenient, quick, reliable without aromatic hydrocarbons protective system coating scheme, and raw material is cheap, this method can be simply in conjunction with enter the existing pre-treatment that comprises coating and after in the conventional production line of other postprocessing working procedures of substrate material, substantially need not to carry out other adjustment on the equipment, is the Eco-power production technique of a kind of height.
The below elaborates with embodiment to the present invention, but protection scope of the present invention is not limited to following embodiment.
Embodiment 1
(1) prepare following component (mass parts):
A vinyltriethoxysilane 1;
B propyl alcohol 40;
C SiO
2Particle 1;
The oxide compound 1 of d cerium;
E deionized water 5;
F acetic acid 4;
G carbon fiber 5;
H polyimide 1;
(2) with carrying out maturation process after the above component mixing, then spray, brush or be immersed in substrate surface, form coating at substrate surface after the deposition, realize the surface anticorrosion processing.
Embodiment 2
(1) prepare following component (mass parts):
A vinyltriethoxysilane 10;
B propyl alcohol 60;
C SiO
2Particle 5;
The oxide compound 5 of d cerium;
E deionized water 25;
F acetic acid 6;
G carbon fiber 7;
H polyimide 3;
(2) with carrying out maturation process after the above component mixing, then spray, brush or be immersed in substrate surface, form coating at substrate surface after the deposition, realize the surface anticorrosion processing.
Embodiment 3
(1) prepare following component (mass parts):
A vinyltriethoxysilane 5;
B propyl alcohol 50;
C SiO
2Particle 3;
The oxide compound 3 of d cerium;
E deionized water 15;
F acetic acid 5;
G carbon fiber 6;
H polyimide 2;
(2) with carrying out maturation process after the above component mixing, then spray, brush or be immersed in substrate surface, form coating at substrate surface after the deposition, realize the surface anticorrosion processing.
Claims (9)
1. one kind without aromatic hydrocarbons protective system coating scheme, comprising:
(1) prepare following component (mass parts):
A vinyltriethoxysilane 1-10;
B propyl alcohol 40-60;
C SiO
2Particle 1-5;
The oxide compound 1-5 of d cerium;
E deionized water 5-25;
F acetic acid 4-6;
G carbon fiber 5-7;
H polyimide 1-3;
(2) with carrying out maturation process after the said components mixing, then spray, brush or be immersed in substrate surface, form coating at substrate surface after the deposition, realize the surface anticorrosion processing.
2. describedly according to claim 1 a kind ofly it is characterized in that described SiO without aromatic hydrocarbons protective system coating scheme
2The particle diameter of particle is the 50-100 nanometer.
3. describedly according to claim 1 a kind ofly it is characterized in that without aromatic hydrocarbons protective system coating scheme described maturation process is to leave standstill at normal temperatures 50-60 hour.
4. describedly according to claim 1 a kind ofly it is characterized in that without aromatic hydrocarbons protective system coating scheme described base material is steel or aluminium.
5. describedly according to claim 1 a kind ofly it is characterized in that without aromatic hydrocarbons protective system coating scheme described base material is aluminium alloy.
6. describedly according to claim 1 a kind ofly it is characterized in that without aromatic hydrocarbons protective system coating scheme heat, Heating temperature is 50 ℃ to 150 ℃, 1 minute to 1 hour heat-up time in described deposition process.
7. describedly according to claim 1 a kind ofly it is characterized in that without aromatic hydrocarbons protective system coating scheme described coat-thickness is 1 micron to 10 microns.
8. describedly according to claim 7 a kind ofly it is characterized in that without aromatic hydrocarbons protective system coating scheme described coat-thickness is 1 micron to 5 microns.
9. described a kind ofly it is characterized in that without aromatic hydrocarbons protective system coating scheme according to claim 1, adopt spraying in the described step (2) or the method for brushing forms coating at substrate surface.