CN102934860A - Anti-radiation shoe insole material - Google Patents
Anti-radiation shoe insole material Download PDFInfo
- Publication number
- CN102934860A CN102934860A CN2012104181882A CN201210418188A CN102934860A CN 102934860 A CN102934860 A CN 102934860A CN 2012104181882 A CN2012104181882 A CN 2012104181882A CN 201210418188 A CN201210418188 A CN 201210418188A CN 102934860 A CN102934860 A CN 102934860A
- Authority
- CN
- China
- Prior art keywords
- parts
- radiation
- nonwoven
- nano
- medium bottom
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an anti-radiation shoe insole material and belongs to the field of preparation of shoe materials. The anti-radiation shoe insole material is prepared through the following steps of: dipping a non-woven fabric in a dip material and drying the non-woven fabric, wherein the non-woven fabric is made of polyester staple fibers and Fe-Cr-Al alloy fibers through a needle punching technology in a mass ratio of 20:1, and the dip material is prepared from the following raw materials in parts by weight: 5-15 parts of nanometer copper powder, 4-10 parts of nanometer nickel powder, 4-12 parts of nanometer silver power and 100-500 parts of styrene-acrylic emulation. Compared with the prior art, the anti-radiation shoe insole material provided by the invention has the advantages that the shoe insole material with the anti-radiation function is prepared by adding an anti-radiation material to an insole material, can be used for effectively preventing the harm of external radiation to the feet of a human body, and has an anti-microbial deodorization function while the original function of the shoe insole is reserved.
Description
Technical field
The present invention relates to the preparation field of footwear material, specifically a kind of radiation proof medium bottom shoes material.
Background technology
Radiation refers to that energy is with electromagnetic wave or particle, such as the form of α particle, β particle etc. to external diffusion, modal electromagnetic radiation, the fourth-largest pollution sources after water pollution, atmosphere pollution, noise pollution have been become, such as the radio frequency induction dielectric heating equipment that continues, radio frequency and microwave medical equipment etc.When these radiation surpass national standard, will produce negative effect, cause human body pathology and harm in various degree.In order to reduce and to prevent that radiation, people from having invented multiple radiation-resistant clothes, but has radiation proof function in the footwear materials seldom.
Summary of the invention
Technical assignment of the present invention provides a kind of radiation proof medium bottom shoes material.
Technical assignment of the present invention realizes that in the following manner this medium bottom shoes material soaks material by nonwoven, makes after the oven dry;
Described nonwoven is with terylene short fiber peacekeeping iron-chromium-aluminum, presses the mass ratio of 20:1, the nonwoven of making through needling process;
The described raw material of expecting by following weight portion proportioning that soaks is prepared from:
5~15 parts of copper nanoparticles; 4~10 parts of nano-nickel powders; 4~12 parts of nano-silver powders; 100~500 parts of benzene emulsions.
Thick 1~the 4mm of described nonwoven.
The processing method of described radiation proof medium bottom shoes material is as follows:
Copper nanoparticle, nano-nickel powder, the nano-silver powder of formula ratio are mixed in powder stirring machine, stirred 10~20 minutes, go to reactor; Add the benzene emulsion of formula ratio in the reactor, stirred 10~20 minutes, make to soak and expect and pack into and soak hopper;
With terylene short fiber peacekeeping iron-chromium-aluminum, press the mass ratio of 20:1, the nonwoven immersion of making through needling process fills the hopper that soaks that soaks material, pushes laggard baking oven through many group light surface rollers simultaneously; At baking oven 100~120
0After the C drying 5~10 minutes, namely get radiation proof medium bottom shoes material.
A kind of radiation proof medium bottom shoes material of the present invention is compared with existing technology, radiation proof material is added in the middle bottom material, making has the medium bottom shoes material of radiation proof function, can effectively prevent the harm of external Radiation On Human body foot, when having kept the original function of medium bottom shoes material, also have the antibacterial and deodouring function.
The specific embodiment
Embodiment 1:
5kg copper nanoparticle, 4kg nano-nickel powder, 4kg nano-silver powder are mixed in powder stirring machine, stirred 10 minutes, go to reactor; Add the 100kg benzene emulsion in the reactor, stirred 10 minutes, make to soak and expect and pack into and soak hopper;
With terylene short fiber peacekeeping iron-chromium-aluminum, press the mass ratio of 20:1, make the thick nonwoven immersion of 1mm through needling process and fill the hopper that soaks that soaks material, push laggard baking oven through many group light surface rollers simultaneously; At baking oven 100
0Behind dry 5 minutes of the C, namely get radiation proof medium bottom shoes material.
Embodiment 2:
15kg copper nanoparticle, 10kg nano-nickel powder, 12kg nano-silver powder are mixed in powder stirring machine, stirred 20 minutes, go to reactor; Add the 500kg benzene emulsion in the reactor, stirred 20 minutes, make to soak and expect and pack into and soak hopper;
With terylene short fiber peacekeeping iron-chromium-aluminum, press the mass ratio of 20:1, make the thick nonwoven immersion of 4mm through needling process and fill the hopper that soaks that soaks material, push laggard baking oven through many group light surface rollers simultaneously; At baking oven 120
0Behind dry 10 minutes of the C, namely get radiation proof medium bottom shoes material.
Embodiment 3:
10kg copper nanoparticle, 7kg nano-nickel powder, 8kg nano-silver powder are mixed in powder stirring machine, stirred 15 minutes, go to reactor; Add the 300kg benzene emulsion in the reactor, stirred 15 minutes, make to soak and expect and pack into and soak hopper;
With terylene short fiber peacekeeping iron-chromium-aluminum, press the mass ratio of 20:1, make the thick nonwoven immersion of 2.5mm through needling process and fill the hopper that soaks that soaks material, push laggard baking oven through many group light surface rollers simultaneously; At baking oven 110
0Behind dry 8 minutes of the C, namely get radiation proof medium bottom shoes material.
The above-mentioned material explanation:
Copper nanoparticle: 30-50nm is purchased from: Deco island, Beijing gold Science and Technology Ltd.;
Nano-silver powder: 50nm is purchased from: Deco island, Beijing gold Science and Technology Ltd.;
Nano-nickel powder: 50nm is purchased from: Deco island, Beijing gold Science and Technology Ltd.;
Benzene emulsion: solid content 48%,, be purchased from: chemical industry firm converges in Jinan City's Licheng District sea.
Claims (3)
1. radiation proof medium bottom shoes material, it is characterized in that: described medium bottom shoes material soaks material by nonwoven, makes after the oven dry;
Described nonwoven is with terylene short fiber peacekeeping iron-chromium-aluminum, presses the mass ratio of 20:1, the nonwoven of making through needling process;
The described raw material of expecting by following weight portion proportioning that soaks is prepared from:
5~15 parts of copper nanoparticles; 4~10 parts of nano-nickel powders; 4~12 parts of nano-silver powders; 100~500 parts of benzene emulsions.
2. radiation proof medium bottom shoes material according to claim 1 is characterized in that: the thick 1~4mm of described nonwoven.
3. radiation proof medium bottom shoes material according to claim 1, it is characterized in that: the processing method of described radiation proof medium bottom shoes material is as follows:
Copper nanoparticle, nano-nickel powder, the nano-silver powder of formula ratio are mixed in powder stirring machine, stirred 10~20 minutes, go to reactor; Add the benzene emulsion of formula ratio in the reactor, stirred 10~20 minutes, make to soak and expect and pack into and soak hopper;
With terylene short fiber peacekeeping iron-chromium-aluminum, press the mass ratio of 20:1, the nonwoven immersion of making through needling process fills the hopper that soaks that soaks material, pushes laggard baking oven through many group light surface rollers simultaneously; At baking oven 100~120
0After the C drying 5~10 minutes, namely get radiation proof medium bottom shoes material.