CN102922858A - Compounding method for electrospinning nanometer composite nonwoven fabric - Google Patents
Compounding method for electrospinning nanometer composite nonwoven fabric Download PDFInfo
- Publication number
- CN102922858A CN102922858A CN2012102000238A CN201210200023A CN102922858A CN 102922858 A CN102922858 A CN 102922858A CN 2012102000238 A CN2012102000238 A CN 2012102000238A CN 201210200023 A CN201210200023 A CN 201210200023A CN 102922858 A CN102922858 A CN 102922858A
- Authority
- CN
- China
- Prior art keywords
- cloth
- nonwoven fabric
- nano
- nanometer
- stick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a compounding method for an electrospinning nanometer composite nonwoven fabric. The compounding method comprises the following steps that: (1) nanometer cloth is produced, a layer of bottom cloth receives the nanometer cloth, and the nanometer cloth is compounded on the bottom cloth; (2) a spare first anti-stick nonwoven fabric is subjected to unwinding, and a glue is sprayed on one surface of the spare first anti-stick nonwoven fabric; (3) the nanometer cloth and the original bottom cloth are subjected to unwinding, the nanometer cloth is covered on the spare first anti-stick nonwoven fabric surface sprayed with the glue, and pressing rolling adhesion is performed; (4) the original bottom cloth is striped from the nanometer cloth; (5) a spare second anti-stick nonwoven fabric is subjected to unwinding, and the glue is sprayed on one surface of the spare second anti-stick nonwoven fabric; (6) the spare second anti-stick nonwoven fabric surface sprayed with the glue is paved and covered on the nanometer cloth surface striped from the original bottom cloth, and pressing rolling adhesion is performed; and (7) the nanometer composite nonwoven fabric having a first anti-stick nonwoven fabric-nanometer cloth-second anti-stick nonwoven fabric layer structure is prepared. With the technical scheme, the compounding method has the following beneficial effects that: nanometer composite nonwoven fabric production is solved, such that the manometer cloth can be applied in nonwoven fabric industry, and the nonwoven fabric can be applicable for occasions having special requirements.
Description
Technical field:
The present invention relates to a kind of complex method of electrostatic spinning nano compound nonwoven cloth.
Background technology:
Current nanometer technology is used very extensive, materialogy aspect particularly, because the existence of nanometer technology, can produce the material with particular physical characteristics aspect the materialogy field, nano-cloth for example, nano-cloth can be applicable to the technical of medical protection, battery production, and nano-cloth has small-size effect, get final product blowing air, obstructed liquid and bacterium.But nano-cloth is because can be with very strong static, and be difficult to independently exist, must carry out compound could the use with other cloth, during production, the nano-cloth of producing is received by the original base fabric of one deck, nano-cloth just is combined with each other with original base fabric, but the characteristic of original base fabric might not satisfy instructions for use, obtain having the nano combined nonwoven of nano-cloth characteristic, must be in the both sides of nano-cloth compound layer of non-woven fabric all, but also with regard to how nano-cloth being carried out secondary do not peel off at present, again it is compounded in two production methods between the nonwoven.
Summary of the invention:
The objective of the invention is in order to overcome the shortcoming of above-mentioned prior art, a kind of complex method of the electrostatic spinning nano compound nonwoven cloth at nano-cloth two sides compound nonwoven cloth is provided.
Goal of the invention of the present invention can realize by following technical scheme: the complex method of electrostatic spinning nano compound nonwoven cloth, its step is as follows: 1. produce nano-cloth and received by one deck base fabric, nano-cloth is compounded on the base fabric, 2. the first anti-bonded non-woven fabrics debatching for subsequent use, and toward its surperficial glue spraying wherein, 3. nano-cloth and original base fabric debatching, nano-cloth is covered on the side surface that the first antiseized nonwoven is sprayed with glue, pressure roller is bonding, 4. original base fabric is peeled off from nano-cloth, 5. for subsequent use second anti-bonded non-woven fabrics debatching, an and past wherein surperficial glue spraying, 6. with on the side surface of a side bedding after nano-cloth is peeled off original base fabric of the second antiseized nonwoven with glue, then pressure roller is bonding, and 7. making layer structure is the nano combined nonwoven of the anti-bonded non-woven fabrics of first anti-bonded non-woven fabrics-nano-cloth-second.
After adopting the technical program, the invention has the beneficial effects as follows: solved the production of nano combined nonwoven, order may be used on the nonwoven industry to nano-cloth, makes nonwoven adapt to some occasions that specific (special) requirements is arranged and uses.
Description of drawings:
Fig. 1 is the combination process flow chart of electrostatic spinning nano compound nonwoven cloth of the present invention.
The specific embodiment:
Below in conjunction with accompanying drawing present technique is described further.
The complex method of the electrostatic spinning nano compound nonwoven cloth of present embodiment, its step is as follows: 1. produce nano-cloth and received by one deck base fabric, nano-cloth is compounded on the base fabric, 2. the first anti-bonded non-woven fabrics debatching for subsequent use, and toward its surperficial glue spraying wherein, 3. nano-cloth and original base fabric debatching, nano-cloth is covered on the side surface that the first antiseized nonwoven is sprayed with glue, pressure roller is bonding, 4. original base fabric is peeled off from nano-cloth, 5. for subsequent use second anti-bonded non-woven fabrics debatching, an and past wherein surperficial glue spraying, 6. with on the side surface of a side bedding after nano-cloth is peeled off original base fabric of the second antiseized nonwoven with glue, then pressure roller is bonding, and 7. making layer structure is the nano combined nonwoven of the anti-bonded non-woven fabrics of first anti-bonded non-woven fabrics-nano-cloth-second.
The combination process flow chart as shown in Figure 1.
The above only is preferred embodiment of the present invention, is not the present invention is done any pro forma restriction.Any those of ordinary skill in the art, do not breaking away from the technical solution of the present invention scope situation, all can utilize method and the technology contents of above-mentioned announcement that technical solution of the present invention is made many possible changes and modification, or be revised as the equivalent embodiment of equivalent variations.So every content that does not break away from technical solution of the present invention, the equivalence of doing according to the present invention's shape, structure and principle changes, and all should be covered by in protection scope of the present invention.
Claims (1)
1. the complex method of electrostatic spinning nano compound nonwoven cloth, its step is as follows: 1. produce nano-cloth and received by one deck base fabric, nano-cloth is compounded on the base fabric, 2. the first anti-bonded non-woven fabrics debatching for subsequent use, and toward its surperficial glue spraying wherein, 3. nano-cloth and original base fabric debatching, nano-cloth is covered on the side surface that the first antiseized nonwoven is sprayed with glue, pressure roller is bonding, 4. original base fabric is peeled off from nano-cloth, 5. for subsequent use second anti-bonded non-woven fabrics debatching, an and past wherein surperficial glue spraying, 6. with on the side surface of a side bedding after nano-cloth is peeled off original base fabric of the second antiseized nonwoven with glue, then pressure roller is bonding, and 7. making layer structure is the nano combined nonwoven of the anti-bonded non-woven fabrics of first anti-bonded non-woven fabrics-nano-cloth-second.