CN102907386B - Multi-section movably-connected artificial bait - Google Patents
Multi-section movably-connected artificial bait Download PDFInfo
- Publication number
- CN102907386B CN102907386B CN201210361114.XA CN201210361114A CN102907386B CN 102907386 B CN102907386 B CN 102907386B CN 201210361114 A CN201210361114 A CN 201210361114A CN 102907386 B CN102907386 B CN 102907386B
- Authority
- CN
- China
- Prior art keywords
- powder
- housing
- bentonite
- weight
- fish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a multi-section movably-connected artificial bait which comprises multiple sections of shells. 8-shaped rings connected with fishhooks are mounted on the multiple sections of shells, and the multiple sections of shells are connected to form an integrated fish-shaped shell structure by means of coordination of sleeving rings and plug pins. A hologram paper layer is adhered on the surface of the fish-shaped shell, a hollow cavity is arranged in each of the multiple sections of shells, a lead block is arranged at the inner bottom of each hollow cavity, and a plurality of glass beads are further arranged in one of the hollow cavities and collide with one another. The multi-section movably-connected artificial bait is simple in structure, can swing freely by a movable connection mode and splashes water to attract fish, and floating water level requirement is met by increasing the weight, so that fishing efficiency is improved.
Description
Technical field
The present invention relates to fishing gear, is mainly the synthetic bait that a kind of multi-segment activity connects.
background technology
Along with social development, synthetic bait application is more and more extensive, and the synthetic bait of selling on market is mostly comprised of independent plastic casing and fish hook, and its structure is single, form is not true to nature, because plastics are low weight, be floating state in water, its location comparison on the upper side simultaneously, prey seldom, therefore fishing effect is low, can not meet fisherman's requirement, has affected the use value of synthetic bait.
Summary of the invention
Technical problem to be solved by this invention is to provide the synthetic bait that a kind of multi-segment activity connects, and it is simple in structure, and the mode of flexible connection can make it freely swing, produce spray, attract prey, and by gaining in weight to meet floating water level requirement, improve fishing effect.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
The synthetic bait that a kind of multi-segment activity connects, include multistage housing, on multistage housing, be provided with a plurality of for connecting the Eight characters circle of fish hook, it is characterized in that: described multistage housing is by the group all-in-one-piece fish shape shell structure that is connected of the collar and latch, described fish shape surface of shell posts one deck laser paper, in described multistage housing, is respectively equipped with cavity, and cavity inner bottom part has lead, in one of them cavity, be also provided with a plurality of beades, a plurality of beades are piled up.
Housing is that the raw material granulation by following weight parts makes: nylon PA6 70-75, ABS high glue powder 10-15, poly--4-methyl-1-pentene 5-10, polycaprolactone 1-2, silane coupler KH570 0.5-1, irgasfos 168 0.4-0.6, anti ultraviolet agent 0.1-0.3, Tissuemat E 1-2, calcium stearate 1-1.5, modified Nano celestite powder 2-4, modified alta-mud 3-6;
Described method for preparing modified bentonite is:
(1) acetic acid solution that is 10-15% by bentonite by concentration soaks 3-4 hour, deionized water washing, then the sodium hydroxide solution that is 10-12% by concentration immersion 3-4 hour, more extremely neutral with deionized water washing, dry, obtain treated bentonite standby;
(2) sodium phosphate trimer that is equivalent to bentonite weight 2-3% is dissolved in deionized water, add again the lauric monoglyceride of bentonite weight 2-3%, the polyoxyethylene nonylphenol ether of the fatty glyceride of 1-2%, 2-3%, 3-5% aluminium oxide, under 1200-1500 rev/min, stir 4-8 minute, obtain dispersion liquid;
(3) the treated bentonite of step (1) gained and step (2) gained dispersion liquid are stirred to 10-15 minute under 1500-1800 rev/min, dry, be ground into powder, cross 100-200 mesh sieve and get final product;
Described modified Nano celestite powder is prepared by the following method: by celestite powder scaling loss 4-5 hour at 600-700 ℃, after grind to form nanometer powder, admix and be equivalent to the diisooctyl phthalate of powder weight 1-2%, the epoxidized soybean oil agitating of 1-2% is even, dry, be ground into powder, obtain;
According to weight portion, its each raw material is placed in to high-speed mixer and mixing 3-5min, the mixture obtaining adds in double screw extruder through main spout, controlled working temperature is at 250-270 ℃, and screw speed is at 300-600rpm, and after melting, extruding pelletization obtains described housing raw material.
On a piece housing of described fish shape housing, there is birdeye, on described birdeye, be coated with one golden layer pigment.
The mode that synthetic bait of the present invention connects by multi-segment activity can freely swing it in water, and rotary water current produces spray, attracts prey; Simultaneously surface of shell has laser paper, and it is luminous in water to scribble the birdeye of golden color, attracts prey.
In the present invention, by setting up lead, increase weight, in use, can meet floating water level requirement; Between a plurality of beades of enclosure interior, can mutually clash in addition, in water, produce the sound, attract fish.
Advantage of the present invention is:
The present invention is simple in structure, and the mode of flexible connection can make it freely swing, and produces spray, attracts prey, and by gaining in weight to meet floating water level requirement, improves fishing effect.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention.
Embodiment
Referring to Fig. 1, the synthetic bait that a kind of multi-segment activity connects, include multistage housing 1, 2, 3, 4, 5, multistage housing 1, 2, 3, 4, on 5, be provided with a plurality of for connecting the Eight characters circle 12 of fish hook, described multistage housing 1, 2, 3, 4, 5 by the group all-in-one-piece fish shape shell structure that is connected of the collar 6 and latch 7, described fish shape surface of shell posts one deck laser paper, described multistage housing 1, 2, 3, 4, in 5, be respectively equipped with cavity 8, cavity 8 inner bottom parts have lead 9, in the cavity of one of them housing 3, be also provided with a plurality of beades 10, a plurality of beades 10 are piled up.
On a piece housing of described fish shape housing, there is birdeye 11, on described birdeye 11, be coated with one golden layer pigment.
Housing is that the raw material granulation by following weight parts (kg) makes: nylon PA6 70, ABS high glue powder 10, poly--4-methyl-1-pentene 10, polycaprolactone 1, silane coupler KH570 0.5, irgasfos 168 0.6, anti ultraviolet agent 0.3, Tissuemat E 2, calcium stearate 1.5, modified Nano celestite powder 4, modified alta-mud 6;
Described method for preparing modified bentonite is:
(1) acetic acid solution that is 15% by bentonite by concentration soaks 4 hours, deionized water washing, then the sodium hydroxide solution that is 12% with concentration soaks 4 hours, then with deionized water washing to neutral, oven dry, obtains treated bentonite standby;
(2) sodium phosphate trimer that is equivalent to bentonite weight 3% is dissolved in deionized water, add again the lauric monoglyceride of bentonite weight 3%, 2% fatty glyceride, 3% polyoxyethylene nonylphenol ether, 3% aluminium oxide, under 1500 revs/min, stir 4-8 minute, obtain dispersion liquid;
(3) the treated bentonite of step (1) gained and step (2) gained dispersion liquid are stirred 10 minutes under 1500 revs/min, dry, be ground into powder, cross 200 mesh sieves and get final product;
Described modified Nano celestite powder is prepared by the following method: by celestite powder scaling loss 5 hours at 700 ℃, after grind to form nanometer powder, admix that to be equivalent to diisooctyl phthalate, 2% the epoxidized soybean oil agitating of powder weight 2% even, dry, be ground into powder, obtain.
Described a kind of nylon material that contains modified alta-mud, manufacture method is: according to weight portion, its each raw material is placed in to high-speed mixer and mixing 5min, the mixture obtaining adds in double screw extruder through main spout, controlled working temperature is at 270 ℃, screw speed is at 500rpm, and after melting, extruding pelletization obtains product.
The Performance Detection of the present embodiment:
Claims (2)
1. the synthetic bait that a multi-segment activity connects, include multistage housing, on multistage housing, be provided with a plurality of for connecting the Eight characters circle of fish hook, it is characterized in that: described multistage housing is by the group all-in-one-piece fish shape shell structure that is connected of the collar and latch, described fish shape surface of shell posts one deck laser paper, in described multistage housing, is respectively equipped with cavity, and cavity inner bottom part has lead, in one of them cavity, be also provided with a plurality of beades, a plurality of beades are piled up;
The granulation of manufacturing described housing is that the raw material by following weight parts makes: nylon PA6 70-75, ABS high glue powder 10-15, poly--4-methyl-1-pentene 5-10, polycaprolactone 1-2, silane coupler KH570 0.5-1, irgasfos 168 0.4-0.6, anti ultraviolet agent 0.1-0.3, Tissuemat E 1-2, calcium stearate 1-1.5, modified Nano celestite powder 2-4, modified alta-mud 3-6;
Described method for preparing modified bentonite is:
(1) acetic acid solution that is 10-15% by bentonite by concentration soaks 3-4 hour, deionized water washing, then the sodium hydroxide solution that is 10-12% by concentration immersion 3-4 hour, more extremely neutral with deionized water washing, dry, obtain treated bentonite standby;
(2) sodium phosphate trimer that is equivalent to bentonite weight 2-3% is dissolved in deionized water, add again the lauric monoglyceride of bentonite weight 2-3%, the polyoxyethylene nonylphenol ether of the fatty glyceride of 1-2%, 2-3%, 3-5% aluminium oxide, under 1200-1500 rev/min, stir 4-8 minute, obtain dispersion liquid;
(3) the treated bentonite of step (1) gained and step (2) gained dispersion liquid are stirred to 10-15 minute under 1500-1800 rev/min, dry, be ground into powder, cross 100-200 mesh sieve and get final product;
Described modified Nano celestite powder is prepared by the following method: by celestite powder scaling loss 4-5 hour at 600-700 ℃, after grind to form nanometer powder, admix and be equivalent to the diisooctyl phthalate of powder weight 1-2%, the epoxidized soybean oil agitating of 1-2% is even, dry, be ground into powder, obtain;
According to weight portion, its each raw material is placed in to high-speed mixer and mixing 3-5min, the mixture obtaining adds in double screw extruder through main spout, controlled working temperature is at 250-270 ℃, and screw speed is at 300-600rpm, and after melting, extruding pelletization obtains manufacturing the granulation of described housing.
2. the synthetic bait that a kind of multi-segment activity according to claim 1 connects, is characterized in that: on a piece housing of described fish shape housing, have birdeye, be coated with one golden layer pigment on described birdeye.