CN102877557B - Wall heat preservation core plate and production method thereof - Google Patents
Wall heat preservation core plate and production method thereof Download PDFInfo
- Publication number
- CN102877557B CN102877557B CN201210187614.6A CN201210187614A CN102877557B CN 102877557 B CN102877557 B CN 102877557B CN 201210187614 A CN201210187614 A CN 201210187614A CN 102877557 B CN102877557 B CN 102877557B
- Authority
- CN
- China
- Prior art keywords
- central layer
- micron
- silicon dioxide
- zero
- incubated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a heat preservation core plate and a production method of the heat preservation core plate. The heat preservation core plate comprises the following components in percentage by weight: 28-90wt% of micro-silica powder, 0-35wt% of fumed silica, 0-30wt% of deposit silicon dioxide (white carbon black), 0-68wt% of superfine natural silicon dioxide powder, 1-18wt% of inorganic fiber, 0-3wt% of vacuum stabilizer and 0-3wt% of degasser. The preparation method of the heat preservation core plate comprises the following steps: (1) preparing materials, (2) drying, (3) molding core materials, (4) rolling and molding, (5) packaging and the like.
Description
Technical field
The present invention relates to production of construction materials technical field, relate in particular to a kind of wall thermal insulating central layer and production method thereof.
Background technology
Insulation central layer is the one in heat insulating material; be composited by filling core and vacuum protection top layer; the heat transmission that it avoids cross-ventilation to cause effectively; therefore coefficient of thermal conductivity significantly reduces; be less than 0.008w/m.K; and do not contain any ODS material, there is environmental protection and energy-efficient characteristic.Compared with traditional insulation materials, insulation central layer have layer thin, volume is little, lightweight, combustibility is the advantage of A level.
After the eighties in 20th century, world climate warms, and the energy is increasingly exhausted, under the dual-pressure of environmental protection and the energy, bring new requirement to exterior-wall heat insulation, should good heat insulating, anti-flammability is high again, and the external-wall heat-insulation material using is at present mainly the organic material such as polystyrene and polyurethane, these material heat-insulating properties and workability are all fine, cost is also relatively low, but the fatal shortcoming of these materials is easy firing, and combustibility is B2.Production of construction materials industry faces develops key subjects new, effectively insulating wall thermal insulating central layer.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is, a kind of method of utilizing the manufacture of materials such as silica and inorfil insulation central layer is provided, and the insulation central layer thermal conductivity of production is little, i.e. good heat insulating, and anti-flammability is high.
In order to realize foregoing invention object, the technical solution used in the present invention is: a kind of insulation central layer, it is characterized in that: contain SILICA FUME 28-90wt%, aerosil 0-35wt%, precipitated silica (White Carbon black) 0-30wt%, ultra-fine native silicon dioxide powder 0-68wt%, inorfil 1-18wt%, vacuum stabilizing agent 0-3wt%, getter 0-3wt%.。
Further, the bulk density of described SILICA FUME is 130-280kg/m
3, specific area is 15-29m
2/ g, average grain diameter is 0.1-2 micron; The bulk density of described aerosil is 60-100kg/m3, and average grain diameter is 0.3-5 micron, and the bulk density of described White Carbon black is 60-120kg/m3, and average grain diameter is 0.3-5 micron; The bulk density of described ultra-fine native silicon dioxide powder is 110-230kg/m
3, average grain diameter is 0.3-5 micron; Described vacuum stabilizing agent and getter are hollow sorbing material, and its mean inside diameter is 0.1-3 micron.
Further, described inorfil is one or more the mixture in glass chopped silk, super glass wool, flame cotton, aluminium silicate wool, ceramic fiber cotton, brucite fiber, foam, and length is 3-12mm, and diameter is 0.2-13 micron.
Further, described vacuum stabilizing agent is carborundum or superfine fibre active carbon material or the mixture of the two, and it mainly absorbs the light such as IR, far-infrared light frequency range, can absorb again the gas that the core material such as water vapour, nitrogen slowly discharges simultaneously.
Further, described getter is one or more the mixture in active carbon, barium lithium alloy activator, calcium oxide, magnesia, silica gel, is mainly to absorb the gas that the core materials such as water vapour, nitrogen, oxygen slowly discharge
Further, described ultra-fine native silicon dioxide powder is one or more the mixture in silica flour, silicon ash, pozzolan, SiO 2 powder, perlite powder.
The present invention further provides the preparation method of above-mentioned insulation central layer, described method comprises the steps:
(1) batching: the SILICA FUME of described formula, aerosil, White Carbon black, ultra-fine native silicon dioxide powder, inorfil, vacuum stabilizing agent, getter are dropped into mixer and fully mix;
(2) dry: the compound stirring is dried, and bake out temperature is controlled at 100-120 DEG C, in drying course, measured the moisture content of mixed once material every 8 minutes, until the moisture content of compound reaches below 0.5%, stop drying;
(3) core material moulding: the material of drying is dropped in mould, and surface strikes off;
(4) compressing: mould is put into press compressing, the decrease speed control of press is 3-7 cm/s, and pressure control is 20-280T/m
2;
(5) parcel: compressing central layer is taken out from mould, and in the periphery of central layer parcel layer of non-woven fabric, obtain being incubated central layer.
Further, the drying course of preparation method's step (2) of described insulation central layer also can carry out in the process of step (1) simultaneously; In step (5), nonwoven used is flame-retardant non-woven, and mass area ratio is 35-100g/m
2.
Application the inventive method is produced insulation central layer, technique is simple, there is no three waste discharge, the insulation central layer of producing is easily constructed as wall heat insulation material, fire prevention, can be good at playing insulation, heat-blocking action, combustibility is A level, and insulation thickness is generally at 10-15mm, and lightweight, the weather-proof time is long, and can reach more than 30 years application life.
Raw material involved in the present invention is the usual commercially available technical pure commodity raw material using of the industry.
The present invention does not relate to special equipment, and related detection method is industry customary way.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in detail.
Embodiment 1
(1) batching: by SILICA FUME 28wt%, ultra-fine native silicon dioxide powder 68wt%, inorfil 3wt%, vacuum stabilizing agent 0.5wt%, getter 0.5% drops into mixer fully to be mixed;
(2) dry: the compound stirring is dried, and bake out temperature is controlled at 110 DEG C, in drying course, measured the moisture content of mixed once material every 8 minutes, until the moisture content of compound reaches below 0.5%, stop drying;
(3) core material moulding: the material of drying is dropped in mould, and surface strikes off;
(4) compressing: mould is put into press compressing, the decrease speed control of press is 4cm/s, and pressure control is 30T/m
2;
(5) parcel: compressing central layer is taken out from mould, and in the periphery of central layer parcel layer of non-woven fabric, obtain being incubated central layer.
Embodiment 2
(1) batching: by SILICA FUME 90wt%, aerosil 1wt%, inorfil 8wt%, vacuum stabilizing agent 1wt% drops into mixer fully to be mixed;
(2) dry: the compound stirring is dried, and bake out temperature is controlled at 120 DEG C, in drying course, measured the moisture content of mixed once material every 8 minutes, until the moisture content of compound reaches below 0.5%, stop drying;
(3) core material moulding: the material of drying is dropped in mould, and surface strikes off;
(4) compressing: mould is put into press compressing, the decrease speed control of press is 7cm/s, and pressure control is 80T/m
2;
(5) parcel: compressing central layer is taken out from mould, and in the periphery of central layer parcel layer of non-woven fabric, obtain being incubated central layer.
Embodiment 3
(1) batching: by SILICA FUME 50wt%, aerosil 10wt%, White Carbon black 10wt%, ultra-fine native silicon dioxide powder 10wt%, inorfil 18wt%, getter 2wt% drops into mixer fully to be mixed;
(2) dry: the compound stirring is dried, and bake out temperature is controlled at 100 DEG C, in drying course, measured the moisture content of mixed once material every 8 minutes, until the moisture content of compound reaches below 0.5%, stop drying;
(3) core material moulding: the material of drying is dropped in mould, and surface strikes off;
(4) compressing: mould is put into press compressing, the decrease speed control of press is 5cm/s, and pressure control is 280T/m
2;
(5) parcel: compressing central layer is taken out from mould, and in the periphery of central layer parcel layer of non-woven fabric, obtain being incubated central layer.
The present invention is incubated core plate applications in wall heat insulation material by gained, and high insulating effect can effectively reduce the energy consumption of its application scenario, has accomplished energy-conserving and environment-protective.
Claims (6)
1. an insulation central layer, it is characterized in that: contain SILICA FUME 28-90wt%, aerosil is greater than zero and be less than or equal to 35wt%, White Carbon black is greater than zero and be less than or equal to 30wt%, ultra-fine native silicon dioxide powder is greater than zero and be less than or equal to 68wt%, inorfil 1-18wt%, vacuum stabilizing agent is greater than zero and be less than or equal to 3wt%, and getter is greater than zero and be less than or equal to 3wt%; The bulk density of described SILICA FUME is 130-280kg/m
3, specific area is 15-29m
2/ g, average grain diameter is 0.1-2 micron; The bulk density of described aerosil is 60-100kg/m
3, average grain diameter is 0.3-5 micron, the bulk density of described White Carbon black is 60-120kg/m
3, average grain diameter is 0.3-5 micron; The bulk density of described ultra-fine native silicon dioxide powder is 110-230kg/m
3, average grain diameter is 0.3-5 micron; Described vacuum stabilizing agent is hollow sorbing material, and its mean inside diameter is 0.1-3 micron; Described getter is one or more the mixture in active carbon, barium lithium alloy activator, calcium oxide, magnesia, silica gel.
2. be incubated according to claim 1 central layer, it is characterized in that: described inorfil is one or more the mixture in glass chopped silk, super glass wool, flame cotton, aluminium silicate wool, ceramic fiber cotton, brucite fiber, foam, length is 3-12mm, and diameter is 0.2-13 micron.
3. be incubated according to claim 1 central layer, it is characterized in that: described vacuum stabilizing agent is carborundum or superfine fibre active carbon material or the mixture of the two.
4. be incubated according to claim 1 central layer, it is characterized in that: described ultra-fine native silicon dioxide powder is one or more the mixture in silica flour, silicon ash, pozzolan, SiO 2 powder, perlite powder.
5. according to the preparation method who is incubated central layer described in any one in claim 1-4, it is characterized in that described method comprises the steps:
(1) batching: the SILICA FUME of described formula, aerosil, White Carbon black, ultra-fine native silicon dioxide powder, inorfil, vacuum stabilizing agent, getter are dropped into mixer and fully mix;
(2) dry: the compound stirring is dried, and bake out temperature is controlled at 100-120 DEG C, in drying course, measured the moisture content of mixed once material every 8 minutes, until the moisture content of compound reaches below 0.5%, stop drying;
(3) core material moulding: the material of drying is dropped in mould, and surface strikes off;
(4) compressing: mould is put into press compressing, the decrease speed control of press is 3-7 cm/s, and pressure control is 20-280T/m
2;
(5) parcel: compressing central layer is taken out from mould, and in the periphery of central layer parcel layer of non-woven fabric, obtain being incubated central layer.
6. the preparation method who is incubated according to claim 5 central layer, is characterized in that: the drying course of step (2) carries out in the process of step (1) simultaneously; In step (5), nonwoven used is flame-retardant non-woven, and mass area ratio is 35-100g/m
2.