CN102877050A - Automobile part corrosion protection agent and corrosion prevention method - Google Patents
Automobile part corrosion protection agent and corrosion prevention method Download PDFInfo
- Publication number
- CN102877050A CN102877050A CN2012103582043A CN201210358204A CN102877050A CN 102877050 A CN102877050 A CN 102877050A CN 2012103582043 A CN2012103582043 A CN 2012103582043A CN 201210358204 A CN201210358204 A CN 201210358204A CN 102877050 A CN102877050 A CN 102877050A
- Authority
- CN
- China
- Prior art keywords
- auto parts
- protecting agent
- parts anti
- corrosive protecting
- agent according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an automobile part corrosion protection agent and a corrosion prevention method. The automobile part corrosion protection agent comprises 2-mercaptobenzothiazole (MBT), 2-mercapto benzimidazole (MBI), 2-mercaptobenzothiazole (MBO), benzotriazole (BTA), lubricant and surface active agent. The weight percentage ratio of 2-mercaptobenzothiazole (MBT) to 2-mercapto benzimidazole (MBI) to 2-mercaptobenzothiazole (MBO) to benzotriazole (BTA) is 0.5 : 3 : 0.5 : 1.
Description
Technical field
The invention belongs to the sanitas field, refer to especially a kind of auto parts surface anticorrosion protective material and anti-corrosion method.
Background technology
In automotive field, in order to reduce the deadweight of carwash, to reduce automobile to the consumption of basic energy, seeking lightweight always, the material that intensity is high substitutes the use of iron type materials, although existing had highstrenghtpiston's technology to be in the news, but because there is high temperature in some parts in the automobile, the reasons such as strong motion, this class material can not be used, and many auto parts come alternative metals iron with aluminium alloy now, and this is because some aluminum alloy materials have lightweight, the characteristics high temperature resistant, that intensity is high.But aluminium alloy is also the same with iron type materials, has etching problem.
Equipment and the product of aluminium and alloy thereof are widely used at each department of national economy, and especially in chemical industry and petrochemical industry, because aluminium alloy has the high excellent properties of light weight intensity, the in recent years application in aviation and navigation also order benefit is taken seriously simultaneously.
The corrosion that aluminium alloy occurs under various environmental activities spreads all over each department of national economy, brings about great losses, and has huge meaning for the research of metal protection.In the guard technology of various metallic corrosion, the inhibiter technology is simple owing to technique, suitability becomes by force one of effective and the most the most frequently used method.But the inhibiter technology has obvious limitation, and in the liquid phase medium that inhibiter is most widely used, inhibiter must have certain solubleness, and must reach certain concentration.Traditional inhibiter has caused pollution because toxicity is larger to environment; Simultaneously, because the inhibiter consumption is less, extraneous small variation will cause larger impact to system, and this has brought very large difficulty also for the research of inhibition mechanism, these effects limit further developing of inhibiter.
People study all the time and use various controls or prevent method and the technology of metallic corrosion.Use the method for maximum several control metallic corrosion to have in the practice: correct metallic substance and the appropriate design metal construction selected; Electro-chemical protection; Adopt protective coating; Change environment composition, add inhibiter; Self-assembled monolayer forms the inhibitor molecular protective membrane.
Summary of the invention
The objective of the invention is by the improvement to existing self-assembled monolayer technology, to improve auto parts a kind of anti-corrosive protecting agent of aluminum alloy surface rot-resistant and anti-corrosion method.
The present invention is achieved by the following technical solutions:
The auto parts anti-corrosive protecting agent, its composition comprises: 2-mercaptobenzothiazole MBT, 2-mercaptobenzimidazole MBI, 2-sulfydryl benzothiazole MBO, benzotriazole BTA, lubricant and tensio-active agent.
Be by weight percentage described 2-mercaptobenzothiazole MBT: 2-mercaptobenzimidazole MBI: 2-sulfydryl benzothiazole MBO: benzotriazole BTA is 0.5: 3: 0.5: 1.
Described lubricant is one or both combinations in stearic acid, butyl stearate or the oleylamide.
Described tensio-active agent is one or both combinations in Nonyl pheno, aliphatic acid polyethenoxy ether sodium sulfate or the aliphatic acid polyethenoxy ether ammonium sulfate.
The protectant preparation method of described auto parts surface anticorrosion; with the 2-mercaptobenzothiazole MBT that forms in proportion; 2-mercaptobenzimidazole MBI; 2-sulfydryl benzothiazole MBO and benzotriazole BTA join in the sealed vessel that organic solvent is housed; heating in water bath stirs and makes the complexing agent dissolving; being mixed with is 1.0% solution by weight percentage, then adds the lubricant and above-mentioned four kinds of tensio-active agents that the material gross weight is identical of 1/2 above-mentioned four kinds of material gross weights.
Described organic solvent is one or more combinations in ethylene dichloride, trichloroethane, trichloromethane, ethanol, acetone or the epoxy chloropropane.
Described auto parts surface anticorrosion method, its step is to comprise:
1), be coated with pre-treatment: with machinery, chemical or electrochemical method depositing dust goes out degreasing and various erosion, is coated with pre-treatment if the rear aluminium alloy of plating needn't be done;
2), phosphatization: preparation NaH
2PO
4-H
3PO
4Solution is as phosphorization agent;
3) clean: use first the dehydrated alcohol degreasing, with distilled water workpiece is cleaned, clean surface makes its surface for neutral;
4) drying: Al alloy parts must be dry before the coating, and protective material contacts with water when avoiding applying, impact effect, constant weight in loft drier;
5), coating: the Al alloy parts after the clean dried is applied with anti-corrosive protecting agent;
6), dry: under ventilation condition, placed 1-2 minute.
Described phosphating time is 3min.
Described coating is immersion plating, brushing, spraying or showering.
The described immersion plating time is 15-20min.
The invention has the beneficial effects as follows:
By using above anti-corrosive protecting agent to utilize benzotriazole to form the conjugation complex compound with the aluminum alloy surface metal of auto parts, this complex compound is insoluble to the solution such as acid, alkali, can be good at playing a protective role.
Embodiment
Below describe technical scheme of the present invention in detail by specific embodiment, these embodiment only are used for explanation of the invention and explanation and can not be interpreted as it is limitation of the present invention.
Auto parts surface anticorrosion protective material, its composition comprises: 2-mercaptobenzothiazole MBT, 2-mercaptobenzimidazole MBI, 2-sulfydryl benzothiazole MBO, benzotriazole BTA, lubricant and tensio-active agent.Be by weight percentage described 2-mercaptobenzothiazole MBT: 2-mercaptobenzimidazole MBI: 2-sulfydryl benzothiazole MBO: benzotriazole BTA is 0.5: 3: 0.5: 1.Described lubricant is one or both combinations in stearic acid, butyl stearate or the oleylamide.
Described tensio-active agent is one or both combinations in Nonyl pheno, aliphatic acid polyethenoxy ether sodium sulfate or the aliphatic acid polyethenoxy ether ammonium sulfate.
The preparation method of described auto parts anti-corrosive protecting agent is; with the 2-mercaptobenzothiazole MBT that forms in proportion; 2-mercaptobenzimidazole MBI; 2-sulfydryl benzothiazole MBO and benzotriazole BTA join in the sealed vessel that organic solvent is housed; heating in water bath stirs and makes the complexing agent dissolving; described bath temperature is 30-60 ℃; optimal selection is 30-40 ℃; being mixed with is 1.0% solution by weight percentage, then adds the lubricant and above-mentioned four kinds of tensio-active agents that the material gross weight is identical of 1/2 above-mentioned four kinds of material gross weights.
Described organic solvent is one or more combinations in ethylene dichloride, trichloroethane, trichloromethane, ethanol, acetone or the epoxy chloropropane.
Described auto parts anti-corrosion method, its step is to comprise:
1), be coated with pre-treatment: with machinery, chemical or electrochemical method depositing dust goes out degreasing and various erosion, is coated with pre-treatment if the rear aluminium alloy of plating needn't be done;
2), phosphatization: preparation NaH
2PO
4-H
3PO
4Solution is as phosphorization agent; Described phosphating time is 3min.
3) clean: use first the dehydrated alcohol degreasing, with distilled water workpiece is cleaned, clean surface makes its surface for neutral;
4) drying: Al alloy parts must be dry before the coating, and protective material contacts with water when avoiding applying, impact effect, constant weight in loft drier;
5), coating: the Al alloy parts after the clean dried is applied with anti-corrosive protecting agent; Described coating can be selected the methods such as immersion plating, brushing, spraying or showering.If selecting the described immersion plating time of immersion plating mode is 15-20min.
6), dry: under ventilation condition, placed 1-2 minute.
Claims (10)
1. auto parts anti-corrosive protecting agent, it is characterized in that: its composition includes 2-mercaptobenzothiazole MBT, 2-mercaptobenzimidazole MBI, 2-sulfydryl benzothiazole MBO, benzotriazole BTA, lubricant and tensio-active agent.
2. auto parts anti-corrosive protecting agent according to claim 1, it is characterized in that: be by weight percentage described 2-mercaptobenzothiazole MBT: 2-mercaptobenzimidazole MBI: 2-sulfydryl benzothiazole MBO: benzotriazole BTA is 0.5: 3: 0.5: 1.
3. auto parts anti-corrosive protecting agent according to claim 1, it is characterized in that: described lubricant is one or both combinations in stearic acid, butyl stearate or the oleylamide.
4. auto parts anti-corrosive protecting agent according to claim 1, it is characterized in that: described tensio-active agent is one or both combinations in Nonyl pheno, aliphatic acid polyethenoxy ether sodium sulfate or the aliphatic acid polyethenoxy ether ammonium sulfate.
5. auto parts anti-corrosive protecting agent according to claim 2; it is characterized in that: the 2-mercaptobenzothiazole MBT that will form in proportion; 2-mercaptobenzimidazole MBI; 2-sulfydryl benzothiazole MBO and benzotriazole BTA join in the sealed vessel that organic solvent is housed; heating in water bath stirs and makes the complexing agent dissolving; being mixed with is 1.0% solution by weight percentage, then adds the lubricant and above-mentioned four kinds of tensio-active agents that the material gross weight is identical of 1/2 above-mentioned four kinds of material gross weights.
6. auto parts anti-corrosive protecting agent according to claim 5, it is characterized in that: described organic solvent is one or more combinations in ethylene dichloride, trichloroethane, trichloromethane, ethanol, acetone or the epoxy chloropropane.
7. auto parts anti-corrosive protecting agent according to claim 5, it is characterized in that: described bath temperature is 30-60 ℃, is preferably 30-40 ℃.
8. described auto parts anti-corrosion method is characterized in that: may further comprise the steps:
1), be coated with pre-treatment: with machinery, chemical or electrochemical method depositing dust goes out degreasing and various erosion, is coated with pre-treatment if the rear aluminium alloy of plating needn't be done;
2), phosphatization: preparation NaH
2PO
4-H
3PO
4Solution is as phosphorization agent;
3) clean: use first the dehydrated alcohol degreasing, with distilled water workpiece is cleaned, clean surface makes its surface for neutral;
4) drying: Al alloy parts must be dry before the coating, and protective material contacts with water when avoiding applying, impact effect, constant weight in loft drier;
5), coating: the Al alloy parts after the clean dried is applied with anti-corrosive protecting agent;
6), dry: under ventilation condition, placed 1-2 minute.
9. auto parts surface anticorrosion method according to claim 8, it is characterized in that: described phosphating time is 3min.
10. auto parts anti-corrosion method according to claim 8, it is characterized in that: described coating is immersion plating, brushing, spraying or showering; The described immersion plating time is 15-20min.