CN102876258A - Preparation method of microcapsule elastic glue for carpet - Google Patents
Preparation method of microcapsule elastic glue for carpet Download PDFInfo
- Publication number
- CN102876258A CN102876258A CN2012103976153A CN201210397615A CN102876258A CN 102876258 A CN102876258 A CN 102876258A CN 2012103976153 A CN2012103976153 A CN 2012103976153A CN 201210397615 A CN201210397615 A CN 201210397615A CN 102876258 A CN102876258 A CN 102876258A
- Authority
- CN
- China
- Prior art keywords
- carpet
- air bag
- little air
- elastic plastic
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of microcapsule elastic glue for a carpet. The microcapsule elastic glue for the carpet comprises foaming solution and bonding agent substrates, wherein the foaming solution consists of 0.4 to 3.0 parts of foaming agents and 1.5 to 6.0 parts of solvents, the bonding agent substrates consist of 100 parts of carboxylic styrene butadiene emulsion, 0.1 to 0.75 parts of foaming auxiliary agents, 3.0 to 8.5 parts of thickening agents, 10 to 20 parts of filling materials, 0.5 to 2.5 parts of anti-aging agents, 1 to 2 parts of dispersing agents and 20 to 30 parts of water. According to the preparation method of the microcapsule elastic glue for the carpet, the foaming solution is added into the bonding agent substrates for preparing the microcapsule elastic bonding agents, after the microcapsule elastic bonding agents are uniformly coated onto the base cloth of the carpet, the microcapsule elastic bonding agents release gas in the heating curing process for forming microcapsule structures, and in addition, the controllability on the microcapsule structures is realized through controlling the foaming agent consumption, the foaming auxiliary agent types, the foaming temperature, the forming temperature, the foaming time and the forming time. The microcapsule elastic glue for the carpet has the advantages that the consumption of the carpet bonding agents is reduced, in addition, high elasticity performance and high flexibility are given to the carpet because the microcapsule structures have good elasticity modulus and compression modulus, the comfort of the carpet is greatly improved, and the production cost of enterprises is reduced.
Description
Technical field
The present invention relates to a kind of carpet with the preparation method of little air bag elastic plastic.
Background technology
Along with developing rapidly of carpet industry, kind constantly increases, needed tackiness agent consumption is huge, and carpet tamanori commonly used mainly contains oleic series emulsion, vinyl acetate latex, polyvinyl formal class, ethylene-vinyl acetate copolymer etc. in the market.But the problem that exists is:
1) the matrix price is high, and in order to reduce the production cost of carpet, the carpet adhesive filler content constantly increases, and this directly causes the mass penalty of carpet, and the feel hardening is easy to occur embrittlement.
2) cohesiveness of carpet adhesive is bad, makes blanket base and tackiness agent be easy to come off, and has reduced the work-ing life of carpet.
3) tackiness agent directly is bonded on the carpet, and its elasticity can decrease, comfort property do not reach people requirement.
4) comfort level and the elasticity in order to increase carpet, a lot of producers adopt increases the sponge backing between blanket base and tackiness agent.This just makes production process complicated, and labor cost strengthens greatly; And require stricter to the bonding between blanket base, backing, the tackiness agent three; The easy fold of sponge backing affects the carpet planarization simultaneously.
Based on the existing problem of above carpet adhesive, Japanese Patent JP3019980-A has announced a kind of carpet back coating and has sticked with glue agent, this tackiness agent is comprised of polymerized emulsion, whipping agent, mineral filler, thickening material, and its whipping agent is selected a kind of in sodium lauryl sulphate, trolamine, dodecyl sulfate, the Sodium dodecylbenzene sulfonate.Sodium lauryl sulphate, trolamine, dodecyl sulfate, Sodium dodecylbenzene sulfonate selected in this patent all belong to surfactant-based whipping agent.Tensio-active agent is during as whipping agent, and foam expansion can reach service requirements, but its little air bag aperture is uneven, the foam foam stability can be relatively poor; By adding suds-stabilizing agent, the foam foam stability can obtain corresponding improvement, but its foam expansion can reduce again, can't satisfy the elastomeric property of carpet, high suppleness and the strong requirement of wearing quality.Therefore in the urgent need to developing a kind of good springiness, snappiness is good, cohesive strength is high, wearing quality is strong carpet with little air bag elastic plastic.
Summary of the invention
In order to solve the problems such as the existing cohesive strength of above-mentioned existing carpet adhesive is poor, elasticity is low, the present invention proposes little air bag elastic plastic and preparation method thereof, and by the control to foaming agent consumption, frothing aid kind, blowing temperature, mold temperature, foamed time, molding time, the micropore of its elastic plastic is evenly distributed, its little air bag pore diameter range is realized little airbag structure controllability at 100-400 μ m.
A kind of carpet of the present invention is with the preparation method of little air bag elastic plastic, and described carpet is to add in the adhesive base under certain blowing temperature, time and mold temperature, time conditions frothing solution to the preparation carpet with little air bag elastic plastic with little air bag elastic plastic; Concrete steps are:
(1) it is for subsequent use first the adhesive base of little air bag elastic plastic and frothing solution all wt part to be taken by weighing materials;
(2) preparation adhesive base: the Carboxy emulsion is poured in the stainless steel vessel, stirred 10 minutes with decollator; Then add dispersion agent, stirred 5 minutes; Add entry and filler after being uniformly dispersed, stirred 15-20 minute; Add successively at last anti-aging agent, frothing aid, thickening material and fully stirred 10-15 minute, reach even without particle;
(3) preparation frothing solution: add whipping agent, solvent in container, its weight ratio is 0.4～3.0: 1.5～6.0, and fully stirring and dissolving is until yellowing solution namely is prepared into frothing solution;
(4) carpet of preparation is with little air bag elastic plastic: the frothing solution of step (3) preparation is added in the adhesive base that step (2) prepares, and constantly stirred 10-20 minute, namely get carpet after mixing with little air bag elastic plastic;
Described frothing solution forms: 1.5～6.0 parts of 0.4～3.0 part of whipping agent and solvents;
Described adhesive base forms: 20～30 parts in 100 parts of Carboxy emulsions, 0.1～0.75 part of frothing aid, 10～20 parts of fillers, thickening material 3.0-8.5 part, anti-aging agent 0.5-2.5 part, 1～2 part of dispersion agent and water;
Described blowing temperature is 90 degree～130 degree, and foamed time is 5～15 minutes;
Described mold temperature is 90 degree～120 degree, and molding time is 10～30 minutes;
Described whipping agent is Cellmic C 121, and described solvent is dithiocarbonic anhydride solution; Whipping agent and solvent are undertaken composite by 1: 2 weight ratio;
Described frothing aid is a kind of in zinc oxide, Zinic stearas and the urea, or the mixture of zinc oxide and Zinic stearas;
Described whipping agent and described frothing aid are undertaken composite by 1: 0.25 weight.
As preferred technical scheme:
Aforesaid a kind of carpet is a kind of of talcum powder, water-ground limestone, light calcium carbonate and potter's clay with the preparation method of little air bag elastic plastic, described filler.
Aforesaid a kind of carpet is a kind of of sodium polyacrylate, carboxymethyl cellulose with the preparation method of little air bag elastic plastic, described thickening material.
Aforesaid a kind of carpet is N-sec.-propyl-N '-diphenyl-para-phenylene diamine, N-(1,3-dimethylbutyl)-N '-diphenyl-para-phenylene diamine and N with the preparation method of little air bag elastic plastic, described anti-aging agent, and N '-diphenyl-para-phenylene diamine's is a kind of.
Aforesaid a kind of carpet is a kind of of Sodium dodecylbenzene sulfonate, ethyl cellulose and polyvinyl alcohol with the preparation method of little air bag elastic plastic, described dispersion agent.
A kind of carpet of the present invention, is realized little airbag structure controllability by the control to foaming agent consumption, frothing aid kind, blowing temperature, mold temperature, foamed time, molding time with the preparation method of little air bag elastic plastic.Temperature when blowing temperature refers to that little air bag elastic plastic forms little airbag structure.Mold temperature refers to the temperature of little air bag elastic plastic curing molding.Foamed time refers to that little air bag elastic plastic forms the needed time of little airbag structure.Molding time refers to little needed time of air bag elastic plastic curing molding.Foaming agent consumption is 0.4-3.0 part; Frothing aid is a kind of in zinc oxide, Zinic stearas, the urea, or the mixture of zinc oxide and Zinic stearas; Blowing temperature is 130 ± 5 ℃; Mold temperature is 105 ± 5 ℃; Foamed time is 10 ± 2min; Molding time is 24 ± 4min;
The present invention is prepared to be a kind of good springiness, cohesive strength are high, wearing quality is strong carpet with little air bag elastic plastic, and the technical scheme of optimum comprises following mass parts component:
(1) frothing solution forms: 1.6 parts of whipping agents, 3.2 parts of solvents.
(2) adhesive base forms: 100 parts of Carboxy emulsions, 0.4 part of frothing aid, 12 parts of fillers, 3.8 parts of thickening materials, 1.1 parts in anti-aging agent, 1.5 parts of dispersion agents, 24 parts in water.
Its preparation method is as follows:
(1) it is for subsequent use first the frothing solution of little air bag elastic plastic and adhesive base all wt part to be taken by weighing materials;
(2) preparation adhesive base: 100 parts of Carboxy emulsions are poured in the stainless steel vessel, stirred 10 minutes with decollator; Then add 1.5 parts of dispersion agents, stirred 5 minutes; Be uniformly dispersed 24 parts of water of rear adding and 12 parts of fillers stirred 15-20 minute; Add successively at last 1.1 parts of anti-aging agent, 0.4 part of frothing aid, 3.8 parts of thickening materials, fully stirred 10-15 minute, reach even without particle.
(3) preparation frothing solution: add whipping agent, solvent in container, its weight part ratio is 1.6: 3.2, and fully stirring and dissolving is until yellowing solution namely is prepared into frothing solution;
(4) the preparation carpet is with little air bag elastic plastic: the frothing solution of step (3) preparation is added in the adhesive base that step (2) prepares, and constantly stirred 10-20 minute, namely get carpet after mixing with little air bag elastic plastic.
(5) it is 1.6 parts by the regulation and control foaming agent consumption; Frothing aid is the mixture of zinc oxide and Zinic stearas; Blowing temperature is 130 ℃; Mold temperature is 105 ℃; Foamed time is 10min; Molding time is 26min, realizes little airbag structure controllability.
Utilizing the elasticity carpet of little air bag elastic plastic preparation of the present invention, is directly little air bag elastic plastic to be coated on the carpet backing fabric, and little air bag elastic plastic discharges gas and forms little airbag structure in the process that is heating and curing, be single stage method.And traditional elastic force carpet preparation process is by sticking with glue between the agent at carpet backing fabric and common carpet, adding spongy layer as the middle layer, to improve carpet elasticity, is two-step approach.Prepare the elasticity carpet with conventional two-step and compare, single stage method of the present invention prepares the elastic force carpet, and production technique is simplified, production cost reduces, and little airbag structure that little air bag elastic plastic of while has is a kind of local strengthening structure, a kind of utricule of sealing, its anti-impact force is strong, coefficient of elasticity is large, effectively absorbs the sole reactive force of advancing between activity, and can reply rapidly original shape, not yielding, and not absorbing smell, moisture, greasy dirt etc., easy cleaning, easy to use.And commonly used carpet foam-backing is a kind of open-celled structure on the market, and little air bag pore size is inhomogeneous, poor flexibility, and yielding, easy fold, and very easily absorbing smell, moisture, greasy dirt etc., easy cleaning has not limited use range and work-ing life greatly.
Advantage of the present invention is, utilizes the Carboxy emulsion as main raw material, has increased substantially cohesive strength and the elastomeric property of carpet with little air bag elastic plastic, and nontoxic, tasteless, environmental protection.
Another advantage of the present invention is, utilizes the AC whipping agent to form little airbag structure in heat-processed, and this little air bag is a kind of permanent and can reply structure, has greatly increased elasticity and the work-ing life of little air bag elastic plastic goods.
An again advantage of the present invention is, by the control to foaming agent consumption, frothing aid kind, storing temperature, storing time, realization is to the little airbag structure controllability of elastic plastic, its micropore can evenly distribute in the process that forms, its little air bag pore diameter range can be regulated and control the m at 100-400 μ, and good mechanical properties.
An again advantage of the present invention is, utilizes the elastic force carpet of little air bag elastic plastic preparation, and production technique is simplified, and can reduce the consumption of glue and veil, greatly reduces production cost.
An again advantage of the present invention is, utilizes the elastic force carpet of little air bag elastic plastic preparation, not absorbing smell, moisture, greasy dirt etc., and easy cleaning, easy to use.
Beneficial effect
Little air bag elastic plastic of the present invention and preparation method thereof is to add the little air bag elastic plastic stick of preparation in the adhesive base to by frothing solution, by after evenly applying on the carpet backing fabric, little air bag elastic plastic discharges gas and forms little airbag structure in the process that is heating and curing, this little airbag structure has been given carpet elastomeric property and high suppleness owing to have good elasticity modulus and compressive films amount.By the control to foaming agent consumption, frothing aid kind, storing temperature, storing time, realization is to the little airbag structure controllability of elastic plastic, its little air bag can evenly distribute in the process that forms, and its little air bag pore diameter range can be regulated and control the m at 100-400 μ, and good mechanical properties.Utilize the elasticity carpet of little air bag elastic plastic preparation of the present invention, can greatly increase the elasticity of carpet, but little airbag structure is a kind of permanent elasticity recovery for the elasticity carpet provides, prolonged the work-ing life of elasticity carpet, and little airbag structure has the not characteristics such as absorbing smell, moisture, greasy dirt, easy cleaning, easy to use.Can reduce simultaneously the consumption of glue and veil, greatly reduce production cost, simplify production technique, meet the requirement of national energy-saving consumption reduction.
Description of drawings
Fig. 1 is the carpet backing and installation system synoptic diagram that utilizes carpet of the present invention to prepare with little air bag elastic plastic
Among the figure, 1, little air bag elastic plastic; 2, main background fabric; 3, veil.
Fig. 2 is little airbag structure synoptic diagram of patent of the present invention.
Fig. 3 is that the foaming agent consumption of patent of the present invention is to the influence curve figure in little air bag aperture.
Fig. 4 is that the foaming agent consumption of patent of the present invention is to the influence curve figure of tensile strength.
Fig. 5 is little air bag aperture of patent of the present invention and the corresponding relation of tensile strength.
Fig. 6 is that the blowing temperature of patent of the present invention is to the influence curve figure in little air bag aperture.
Fig. 7 is that the mold temperature of patent of the present invention is to the influence curve figure of tensile strength.
Fig. 8 is that the foamed time of patent of the present invention is to the influence curve figure in little air bag aperture.
Fig. 9 is that the molding time of patent of the present invention is to the influence curve figure of tensile strength.
Embodiment
Below in conjunction with embodiment, further set forth the present invention.Should be understood that these embodiment only to be used for explanation the present invention and be not used in and limit the scope of the invention.Should be understood that in addition those skilled in the art can make various changes or modifications the present invention after the content of having read the present invention's instruction, these equivalent form of values fall within the application's appended claims limited range equally.
The preparation method of the little air bag elastic plastic that the present invention relates to, its concrete steps:
(1) it is for subsequent use first the frothing solution of little air bag elastic plastic and adhesive base all wt part to be taken by weighing materials;
(2) preparation adhesive base: 100 parts of Carboxy emulsions are poured in the stainless steel vessel, stirred 10 minutes with decollator; Then add 1.5 parts of dispersion agents, stirred 5 minutes; Be uniformly dispersed 24 parts of water of rear adding and 12 parts of fillers stirred 15-20 minute; Add successively at last 1.1 parts of anti-aging agent, 0.4 part of frothing aid, 3.8 parts of thickening materials, fully stirred 10-15 minute, reach even without particle.
(3) preparation frothing solution: add whipping agent, solvent in container, its weight part ratio is 1.6: 3.2, and fully stirring and dissolving is until yellowing solution namely is prepared into frothing solution;
(4) the preparation carpet is with little air bag elastic plastic: the frothing solution of step (3) preparation is added in the adhesive base that step (2) prepares, and constantly stirred 10-20 minute, namely get carpet after mixing with little air bag elastic plastic, as shown in Figure 1.
(5) it is 1.6 parts by the regulation and control foaming agent consumption; Frothing aid is the mixture of zinc oxide and Zinic stearas; Blowing temperature is 130 ℃; Mold temperature is 105 ℃; Foamed time is 10min; Molding time is 26min, realizes little airbag structure controllability.
In order to obtain best foaming agent consumption, frothing aid, blowing temperature, mold temperature, foamed time, molding time, the present invention has done the impact test of foaming agent consumption on little air bag aperture, foaming agent consumption is on the impact test of tensile strength, the corresponding test of little air bag aperture and tensile strength, blowing temperature is on the impact test in little air bag aperture, mold temperature is on the impact test of tensile strength, foamed time is on the impact test in little air bag aperture, and molding time is on the impact test of tensile strength.Because carpet directly can draw by its little air bag aperture and tensile strength with the elastic effect of little air bag elastic plastic, so this test has recorded the impact of foaming agent consumption on little air bag aperture, foaming agent consumption is on the impact of tensile strength, the relation of little air bag aperture and tensile strength, blowing temperature is on the impact in little air bag aperture, mold temperature is on the impact of tensile strength, and foamed time is on the impact in little air bag aperture, and molding time is on the impact of tensile strength.The result is shown in Fig. 3-9, and Fig. 2 is little airbag structure synoptic diagram of patent of the present invention.。
Can find out from Fig. 3,4,5: the invention foaming agent consumption is 0.4-3.0 part, the little air bag that plays little air bag power glue is evenly distributed, little air bag pore size, little airbag structure, mechanical property are better, little air bag pore diameter range can be controlled in 100-400 μ m, tensile strength can be controlled in 2.5-4.0MPa, realizes the little airbag structure controllability of elastic plastic.When being in particular 1.6 parts, the little air bag of little air bag aperture is at 300-400 μ m, and tensile strength is 4MPa, and it is optimum that the mechanical property of little air bag elastic plastic and little airbag structure reach.Foaming agent consumption is not enough to form enough little airbag structures very little, can not obtain good mechanical property.When foaming agent consumption was too large, the too much and little air bag of the little air bag number aperture of generation was larger, even can't form little airbag structure, when only having foaming agent consumption moderate, could form little airbag structure, and the performance carpet is with the effectiveness of little air bag elastic plastic.
Frothing aid can effectively reduce the decomposition temperature of whipping agent, also is of value to the decomposition rate of regulating whipping agent simultaneously.The frothing aid that the AC whipping agent is commonly used has stearic acid, stearate, urea, zinc oxide etc.Carpet selects zinc oxide and Zinic stearas mixture excellent as the frothing aid effect with little air bag elastic plastic.Zinc oxide and Zinic stearas mixture can not only reduce the decomposition temperature of AC whipping agent, increase the gas forming amount of AC whipping agent, reduce the consumption of AC whipping agent, reduce cost, improve foam performance.Simultaneous oxidation zinc also is the activator of natural rubber, synthetic rubber and latex, promotes sulfuration, activation and reinforcement, the anti-aging effect of rubber, can strengthen sulfidation, improves rubber item resistance to tearing, wear resistance.Again with AC during by 0.25: 1, the micropore of elastic plastic is evenly distributed after zinc oxide and Zinic stearas are compound with 5: 1, and its little air bag pore diameter range can be controlled in 100-400 μ m, and the resistance to tearing of little air bag elastic plastic goods, wear resistance, ageing-resistant performance are optimum.
As can be seen from Figure 6: the blowing temperature of little air bag elastic plastic is 128 ± 7 ℃.In this blowing temperature scope, the AC whipping agent can decompose fully, and gas forming amount is 250-300ml/g, and little air bag is evenly distributed, and its little air bag pore diameter range can be controlled in 100-400 μ m.When being in particular 130 ℃, it is optimum that little air bag pore size of little air bag elastic plastic, mechanical property all reach.Blowing temperature is too low, can not reach the temperature that whipping agent decomposes fully, causes the whipping agent decomposition amount very little, is not enough to form enough little airbag structures.Blowing temperature is too high, and little air bag aperture is excessive, causes the microvoid structure of micropore elastic plastic goods inhomogeneous, loses little air bag effectiveness.When only having blowing temperature moderate, could form little airbag structure, the performance carpet is with the effectiveness of little air bag elastic plastic.
As can be seen from Figure 7: the mold temperature of little air bag elastic plastic is 105 ± 5 ℃.In this mold temperature scope, be conducive to the formation of little airbag structure, improve the elastomeric property of little air bag elastic plastic goods, effectively shorten storing time, reduce production costs, when being in particular 105 ℃, the complete curing molding of little air bag elastic plastic goods, and mechanical property is optimum.When mold temperature was too low, the moisture in the micropore elastic plastic was difficult for fast volatilization, and storing time prolongs, and caused production cost increase, production efficiency to descend, and cause easily microvoid structure to subside.When mold temperature is too high, cause easily micropore elastic plastic goods aging, lose elastomeric property.When only having mold temperature moderate, just can make the complete curing molding of little air bag elastic plastic, the performance carpet is with the effectiveness of little air bag elastic plastic.
As can be seen from Figure 8: the foamed time of little air bag elastic plastic is that foamed time is 10 ± 3min.In this foamed time scope, the AC whipping agent can decompose fully, and little airbag structure is evenly distributed, and little air bag aperture can be controlled in 100-400 μ m.When being in particular 10min, the little air bag of little air bag aperture is at 300-400 μ m, and it is optimum that mechanical property all reaches.Foamed time is too short, and little airbag structure of micropore elastic plastic goods is not obvious, and this is because the AC whipping agent does not decompose fully.Foamed time is oversize, and little air bag aperture is excessive, very easily subside, and loses little air bag effectiveness.When only having foamed time moderate, could form be evenly distributed, little airbag structure that the aperture is moderate, the competence exertion carpet is with the effectiveness of little air bag elastic plastic.
As can be seen from Figure 9: the molding time of little air bag elastic plastic is that foamed time is 25 ± 3min.In this molding time scope, the moisture in the micropore elastic plastic can volatilize fast, little air bag elastic plastic can solidify fully and mechanical property better.When being in particular 26min, little air bag of little air bag elastic rubber distributes optimum, and tensile strength is maximum.Molding time is too short, and micropore elastic plastic goods are curing molding fully, and microvoid structure very easily subsides.Molding time is oversize, and production cost is increased greatly, causes the wasting of resources, and causes easily micropore elastic plastic goods to wear out, lose elastomeric property.When only having molding time moderate, just can make the complete curing molding of little air bag elastic plastic, save production cost, the performance carpet is with the effectiveness of little air bag elastic plastic.
The above only is preferred embodiment of the present invention, be not the present invention is done any pro forma restriction, every foundation technical spirit of the present invention, to above embodiment do any simple modification, equivalent variations, all fall within protection scope of the present invention.
Claims (5)
1. a carpet is characterized in that with the preparation method of little air bag elastic plastic: described carpet is to add in the adhesive base under certain blowing temperature, time and mold temperature, time conditions frothing solution to the preparation carpet with little air bag elastic plastic with little air bag elastic plastic; Concrete steps are:
(1) it is for subsequent use first the adhesive base of little air bag elastic plastic and frothing solution all wt part to be taken by weighing materials;
(2) preparation adhesive base: the Carboxy emulsion is poured in the stainless steel vessel, stirred 10 minutes with decollator; Then add dispersion agent, stirred 5 minutes; Add entry and filler after being uniformly dispersed, stirred 15-20 minute; Add successively at last anti-aging agent, frothing aid, thickening material and fully stirred 10-15 minute, reach even without particle;
(3) preparation frothing solution: add whipping agent, solvent in container, its weight ratio is 0.4～3.0:1.5～6.0, and fully stirring and dissolving is until yellowing solution namely is prepared into frothing solution;
(4) carpet of preparation is with little air bag elastic plastic: the frothing solution of step (3) preparation is added in the adhesive base that step (2) prepares, and constantly stirred 10-20 minute, namely get carpet after mixing with little air bag elastic plastic;
Described frothing solution forms: 1.5～6.0 parts of 0.4～3.0 part of whipping agent and solvents;
Described adhesive base forms: 20～30 parts in 100 parts of Carboxy emulsions, 0.1～0.75 part of frothing aid, 10～20 parts of fillers, thickening material 3.0-8.5 part, anti-aging agent 0.5-2.5 part, 1～2 part of dispersion agent and water;
Described blowing temperature is 90 degree～130 degree, and foamed time is 5～15 minutes;
Described mold temperature is 90 degree～120 degree, and molding time is 10～30 minutes;
Described whipping agent is Cellmic C 121, and described solvent is dithiocarbonic anhydride solution; Whipping agent and solvent are undertaken composite by 1: 2 weight ratio;
Described frothing aid is a kind of in zinc oxide, Zinic stearas and the urea, or the mixture of zinc oxide and Zinic stearas;
Described whipping agent and described frothing aid are undertaken composite by 1: 0.25 weight.
2. a kind of carpet according to claim 1 is characterized in that with the preparation method of little air bag elastic plastic, and described filler is a kind of of talcum powder, water-ground limestone, light calcium carbonate and potter's clay.
3. a kind of carpet according to claim 1 is characterized in that with the preparation method of little air bag elastic plastic, and described thickening material is a kind of of sodium polyacrylate, carboxymethyl cellulose.
4. a kind of carpet according to claim 1 is with the preparation method of little air bag elastic plastic, it is characterized in that, described anti-aging agent is N-sec.-propyl-N '-diphenyl-para-phenylene diamine, N-(1,3-dimethylbutyl)-N '-diphenyl-para-phenylene diamine and N, and N '-diphenyl-para-phenylene diamine's is a kind of.
5. a kind of carpet according to claim 1 is characterized in that with the preparation method of little air bag elastic plastic, and described dispersion agent is a kind of of Sodium dodecylbenzene sulfonate, ethyl cellulose and polyvinyl alcohol.