CN102876217A - Antiseptic treatment liquid for online oxidized extruded aluminum pipes and preparation method of antiseptic treatment liquid - Google Patents

Antiseptic treatment liquid for online oxidized extruded aluminum pipes and preparation method of antiseptic treatment liquid Download PDF

Info

Publication number
CN102876217A
CN102876217A CN2012103774895A CN201210377489A CN102876217A CN 102876217 A CN102876217 A CN 102876217A CN 2012103774895 A CN2012103774895 A CN 2012103774895A CN 201210377489 A CN201210377489 A CN 201210377489A CN 102876217 A CN102876217 A CN 102876217A
Authority
CN
China
Prior art keywords
treatment liquid
antiseptic treatment
extruded aluminum
preparation
antiseptic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103774895A
Other languages
Chinese (zh)
Inventor
马功权
田四光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Great Wall Refrigeration Technology Co Ltd
Original Assignee
Hefei Great Wall Refrigeration Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Great Wall Refrigeration Technology Co Ltd filed Critical Hefei Great Wall Refrigeration Technology Co Ltd
Priority to CN2012103774895A priority Critical patent/CN102876217A/en
Publication of CN102876217A publication Critical patent/CN102876217A/en
Pending legal-status Critical Current

Abstract

The invention relates to the technical field of refrigerating processing, in particular to an antiseptic treatment liquid for online oxidized extruded aluminum pipes and a preparation method of the antiseptic treatment liquid. The antiseptic treatment liquid comprises, by weight, 350-450g of polyurethane, 350-400g of acrylic resin, 150-250g of diluents and 50-100g of curing agents. On the basis of a high-polymer material film formation mechanism, essential components of high-polymer materials and other diluents are screened and compounded, and an antiseptic treatment liquid product utilizing the high-polymer material as the essential film formation substance and containing no harmful substances such as aromatics is studied out. The antiseptic treatment liquid is used for antiseptic treatment for aluminum pipes, has high salt spray resistance and heat and humidity resistance, has antiseptic capacity much higher than that of other types of primers, and also has high seepage force so as to improve corrosion resistance of the surfaces of the aluminum pipes greatly.

Description

A kind of fungicidal wash for the on-line oxidation extruded aluminum tube and preparation method thereof
Technical field
The present invention relates to the processing technique field of freezing, specifically relate to a kind of fungicidal wash for the on-line oxidation extruded aluminum tube and preparation method thereof.
Background technology
In the refrigeration processing technique field, the rotproofing of extruded aluminum tube is the processing workshop section of outbalance, is the important factor that directly affects the moulding product quality.
Summary of the invention
In order to solve the technical problem that exists in the prior art, the object of the present invention is to provide the lower environmental friendly, anti-corrosive treatment solution of a kind of manufacturing cost, namely be used for fungicidal wash of on-line oxidation extruded aluminum tube and preparation method thereof.
The technical solution used in the present invention is as follows:
A kind of fungicidal wash for the on-line oxidation extruded aluminum tube is characterized in that, is comprised of the raw material of following weight proportion:
Figure BSA00000785614400011
Preferably, the raw material by following weight proportion forms:
Figure BSA00000785614400012
Figure BSA00000785614400021
Further, described thinner is lacquer thinner.
Be used for the preparation method of the fungicidal wash of on-line oxidation extruded aluminum tube, it is characterized in that step is as follows:
1., the part thinner is added in the urethane, be dispersing and mixing in the high speed dispersor of 1500~1800rpm at rotating speed;
2., will remain thinner and be added in the acrylic resin, be dispersing and mixing in the high speed dispersor of 1500~1800rpm at rotating speed;
3., mix 1. and 2., add simultaneously solidifying agent, be dispersing and mixing in the high speed dispersor of 1500~1800rpm at rotating speed, and get final product.
The present invention is used for fungicidal wash of on-line oxidation extruded aluminum tube and preparation method thereof, on the basis of macromolecular material membrane formation mechanism, by the major ingredient such as macromolecular material and other thinner screening and composite, work out the rotproofing liquid product take macromolecular material as main film forming substance, the objectionable impuritiess such as aromatic free class.Aluminum pipe is carried out rotproofing, have superpower salt spray resistance, wet-hot aging performance, its antiseptic power is also far above the priming paint of other types.Simultaneously, seepage force is higher, has greatly improved the erosion resistance of aluminum tube surfaces.
Embodiment
The present invention is further illustrated below in conjunction with embodiment.
Embodiment 1
The fungicidal wash that is used for the on-line oxidation extruded aluminum tube is comprised of the raw material of following weight proportion:
Figure BSA00000785614400022
Preparation method's step is as follows:
1., 90g lacquer thinner is added in the urethane, be dispersing and mixing in the high speed dispersor of 1500~1600rpm at rotating speed;
2., 90g lacquer thinner is added in the acrylic resin, be dispersing and mixing in the high speed dispersor of 1700~1750rpm at rotating speed;
3., mix 1. and 2., add simultaneously solidifying agent, be dispersing and mixing in the high speed dispersor of 1500~1600rpm at rotating speed, and get final product.
Embodiment 2
The fungicidal wash that is used for the on-line oxidation extruded aluminum tube is comprised of the raw material of following weight proportion:
Figure BSA00000785614400031
Preparation method's step is as follows:
1., 80g lacquer thinner is added in the urethane, be dispersing and mixing in the high speed dispersor of 1600~1650rpm at rotating speed;
2., 70g lacquer thinner is added in the acrylic resin, be dispersing and mixing in the high speed dispersor of 1600~1650rpm at rotating speed;
3., mix 1. and 2., add simultaneously solidifying agent, be dispersing and mixing in the high speed dispersor of 1700~1750rpm at rotating speed, and get final product.
Embodiment 3
The fungicidal wash that is used for the on-line oxidation extruded aluminum tube is comprised of the raw material of following weight proportion:
Figure BSA00000785614400041
Preparation method's step is as follows:
1., 110g lacquer thinner is added in the urethane, be dispersing and mixing in the high speed dispersor of 1650~1700rpm at rotating speed;
2., 90g lacquer thinner is added in the acrylic resin, be dispersing and mixing in the high speed dispersor of 1750~1800rpm at rotating speed;
3., mix 1. and 2., add simultaneously solidifying agent, be dispersing and mixing in the high speed dispersor of 1650~1700rpm at rotating speed, and get final product.
Embodiment 4
The fungicidal wash that is used for the on-line oxidation extruded aluminum tube is comprised of the raw material of following weight proportion:
Figure BSA00000785614400042
Preparation method's step is as follows:
1., 150g lacquer thinner is added in the urethane, be dispersing and mixing in the high speed dispersor of 1700~1750rpm at rotating speed;
2., 50g lacquer thinner is added in the acrylic resin, be dispersing and mixing in the high speed dispersor of 1500~1600rpm at rotating speed;
3., mix 1. and 2., add simultaneously solidifying agent, be dispersing and mixing in the high speed dispersor of 1750~1800rpm at rotating speed, and get final product.
Embodiment 5
The fungicidal wash that is used for the on-line oxidation extruded aluminum tube is comprised of the raw material of following weight proportion:
Preparation method's step is as follows:
1., 100g lacquer thinner is added in the urethane, be dispersing and mixing in the high speed dispersor of 1750~1800rpm at rotating speed;
2., 120g lacquer thinner is added in the acrylic resin, be dispersing and mixing in the high speed dispersor of 1650~1700rpm at rotating speed;
3., mix 1. and 2., add simultaneously solidifying agent, be dispersing and mixing in the high speed dispersor of 1600~1650rpm at rotating speed, and get final product.
Above content only is that the present invention is conceived example and explanation; under those skilled in the art described specific embodiment is made various modifications or replenish or adopt similar mode to substitute; only otherwise depart from the design of invention or surmount this scope as defined in the claims, all should belong to protection scope of the present invention.

Claims (4)

1. a fungicidal wash that is used for the on-line oxidation extruded aluminum tube is characterized in that, is comprised of the raw material of following weight proportion:
Figure FSA00000785614300011
2. a kind of fungicidal wash for the on-line oxidation extruded aluminum tube according to claim 1 is characterized in that, is comprised of the raw material of following weight proportion:
Figure FSA00000785614300012
3. a kind of fungicidal wash for the on-line oxidation extruded aluminum tube according to claim 1 and 2 is characterized in that, described thinner is lacquer thinner.
4. preparation is characterized in that such as the method for each described a kind of fungicidal wash for the on-line oxidation extruded aluminum tube of claim 1~3 step is as follows:
1., the part thinner is added in the urethane, be dispersing and mixing in the high speed dispersor of 1500~1800rpm at rotating speed;
2., will remain thinner and be added in the acrylic resin, be dispersing and mixing in the high speed dispersor of 1500~1800rpm at rotating speed;
3., mix 1. and 2., add simultaneously solidifying agent, be dispersing and mixing in the high speed dispersor of 1500~1800rpm at rotating speed, and get final product.
CN2012103774895A 2012-09-30 2012-09-30 Antiseptic treatment liquid for online oxidized extruded aluminum pipes and preparation method of antiseptic treatment liquid Pending CN102876217A (en)