CN102876120A - Silvery printing ink - Google Patents
Silvery printing ink Download PDFInfo
- Publication number
- CN102876120A CN102876120A CN2012103691430A CN201210369143A CN102876120A CN 102876120 A CN102876120 A CN 102876120A CN 2012103691430 A CN2012103691430 A CN 2012103691430A CN 201210369143 A CN201210369143 A CN 201210369143A CN 102876120 A CN102876120 A CN 102876120A
- Authority
- CN
- China
- Prior art keywords
- printing ink
- ink
- silvery
- black
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses silvery printing ink which comprises, by mass, 1-5g of transparent oil, 0.5-1.5g of 500# insulated silver powder and 1-4g of black printing ink. The transparent oil, the 500# insulated sliver powder and the black printing ink are baked at the temperature of 70 DEG C for 20 minutes. The silvery printing ink prepared by the method is high in adhesion, quick in drying, high in gloss and excellent in leveling property and is environment-friendly, cannot crack or spread or generate pinholes on materials, has strong enough strength and durability, and has no pollution.
Description
Technical field
The present invention relates to ink area, particularly relate to a kind of aluminium ink.
Background technology
Develop rapidly along with Chinese national economy, the prosperity of press-packaging industry has driven the manufacturing Fast Growth of printing ink, become one of world printing ink manufacturing big country so that China emerged rapidly between the nearest more than ten years, present domestic printing ink industry size just maintains sustained and rapid growth with the speed more than 10%.
The development in recent years of printing ink industry makes industry manifest one piece of prosperity, still, also should see the weak point in the industry development simultaneously, and scope of the enterprise is little, and individual enterprise's share of market is not high; Capacity for technological innovation is not strong; The printing ink feature of environmental protection of domestic production is not strong; Expensive goods is under-supply; The obstruction that ink technology talent shortage etc. are serious the development of printing ink industry, for this reason, industry has also taked a series of measure to strengthen consolidating the development of printing ink industry, as, strengthen the input in science and technology of industry, strengthen the exploitation of environment-friendly ink, the development of printing ink should be take autonomous innovation as main direction; Strengthen cultivation of printing ink theoretical investigation and skilled personnel etc., obtain good effect.
Printing ink is the important materials for the wrapping material printing, is a kind of gluing flowing material with certain color, and it is by printing on pattern, the present stock of literal table.Printing ink mainly forms uniform mixture by materials such as pigment, binder, stopping composition and auxiliary materials.
Because having become the human consumer, the design of the shell moulding of electronic product selects one of Consideration of product, manufacturers continues to release the electronic product of many different exterior design and appearance design, the shell shape-designing of modal electronic product namely is the visual pattern that presents multiple colour-change by the interpolation of colorant, so that the human consumer is when pursuing the electronic product of more fashion, how different style and features, and then improve more buying motive and desire.In addition, the shell of the electronic product products that adopt by the moulding of plastics institute to satisfy a large amount of the manufacturing and frivolous characteristic of carrying well more.Yet the shell of electronic product is when making, and its previous conventional process is sequentially injection molding manufacture procedure, color priming paint spraying processing procedure, pattern ink printing processing procedure, and the spraying processing procedure of ultraviolet ray (UV) clear lacquer is with the outward appearance hard formation as shell.Wherein spray paint and printing process in must use a large amount of organic solvents so that it is as follows to have the shortcoming that is difficult for overcoming in the use of plastic material and solvent.
In the time that plastics have high chemical transformation resistivity, some crystalline plastic can't be combined by the organic solvent in printing ink paint, the plastic casing surface of causing printing ink paint to be difficult for being attached to, the degree of difficulty that increasing sprays paint paints and easy depainting; Opposite, some amorphism plastics is because of low chemical resistance, and plastics can be corroded by organic solvent, and then produce be full of cracks and the structure deteriorate phenomenon on its plastic casing surface, cause high fraction defective.
Printing ink in the market exist long and the matt and good levelling property of poor adhesive force, time of drying printing ink, on material, chap easily, the problems such as ink diffusion and the inadequate environmental protection of insufficient, the easy contaminate environment of pin-hole phenomena, intensity and weather resistance.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of aluminium ink, can strong adhesion, fast drying and have high gloss and the printing ink of good levelling property, on material, do not chap, without ink diffusion and pin-hole phenomena, have sufficient intensity and weather resistance, pollution-free, environmental protection.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of aluminium ink is provided, it comprises clean oil, 500# type insulation silver powder and black ink, baking is 20 minutes under 70 ° temperature condition, and the mass parts ratio of described clean oil, 500# type insulation silver powder and black ink is 1g~5g, 0.5g~1.5g and 1g~4g.
Preferably, described clean oil is Halogen insulation transparent oil.
Preferably, described black ink is 201 type Halogen insulating black inks.
The invention has the beneficial effects as follows: a kind of aluminium ink of the present invention, can strong adhesion, fast drying and have high gloss and the printing ink of good levelling property, on material, do not chap, without ink diffusion and pin-hole phenomena, have sufficient intensity and weather resistance, pollution-free, environmental protection.
Embodiment
The below is described in detail preferred embodiment of the present invention, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
The embodiment of the invention comprises:
A kind of aluminium ink, it comprises Halogen insulation transparent oil, 500# type insulation silver powder and 201 type Halogen insulating black inks, baking is 20 minutes under 70 ° temperature condition, and the mass parts ratio of described Halogen insulation transparent oil, 500# type insulation silver powder and 201 type Halogen insulating black inks is 1g~5g, 0.5g~1.5g and 1g~4g.
Described a kind of aluminium ink, its white black difference are 77.86, the red green difference is 0.86, the champac value of chromatism is-0.17.
A kind of aluminium ink of the present invention, can strong adhesion, fast drying and have high gloss and the typing printing ink of good levelling property, on material, do not chap, without ink diffusion and pin-hole phenomena, have sufficient intensity and weather resistance, pollution-free, environmental protection.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (3)
1. aluminium ink, it is characterized in that: it comprises clean oil, 500# type insulation silver powder and black ink, baking is 20 minutes under 70 ° temperature condition, and the mass parts ratio of described clean oil, 500# type insulation silver powder and black ink is 1g~5g, 0.5g~1.5g and 1g~4g.
2. a kind of aluminium ink according to claim 1 is characterized in that: described clean oil is Halogen insulation transparent oil.
3. a kind of aluminium ink according to claim 1, it is characterized in that: described black ink is 201 type Halogen insulating black inks.