CN102850860A - Building waterproof coating - Google Patents
Building waterproof coating Download PDFInfo
- Publication number
- CN102850860A CN102850860A CN 201210316214 CN201210316214A CN102850860A CN 102850860 A CN102850860 A CN 102850860A CN 201210316214 CN201210316214 CN 201210316214 CN 201210316214 A CN201210316214 A CN 201210316214A CN 102850860 A CN102850860 A CN 102850860A
- Authority
- CN
- China
- Prior art keywords
- parts
- building
- water
- waterproof coating
- proof paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a building waterproof coating which is characterized by being prepared from the following raw materials by weight: 20 to 40 parts of quartz powder, 3 to 7 parts of polypropylene short fibers, 3 to 10 parts of bentonite, 30 to 50 parts of styrene-acrylic emulsion, 15 to 25 parts of talcum powder, 10 to 20 parts of titanium dioxide, 5 to 10 parts of a thixotropic agent, 7 to 15 parts of a quick-drying agent and 15 to 35 parts of water. The waterproof coating used for building waterproofness provided by the invention has excellent aging resistance, strong bonding force, good material extensibility, good application performance and good comprehensive waterproofness and is green and environment-friendly.
Description
Technical field
The present invention relates to paint field, be specifically related to a kind of building water-proof paint.
Background technology
Mainly be divided into waterproof paint and protective system at architectural employed coating, have respectively waterproof, seepage control and rot-resistant function.In actual applications, often need simultaneously dope layer to have waterproof and rot-resistant function, for example the impact of acid rain is increasing, and the external coating of architectural needs is waterproof and acidproof simultaneously.Utilize prior art can only coat respectively waterproof paint and protective system formation waterproof and preservative coat.What in addition, existing waterproof paint had also has larger harm to human body and environment, such as solvent-type waterproofing paint and polyurethane water-proof paint etc.Existing waterproof paint and protective system much adopt oil to be prepared as raw material, in the situation that the petroleum resources growing tension causes the cost of waterproof paint constantly soaring inevitably.
Conventional waterproof coating is used for roof waterproof, easily cause aging, dry and cracked, be out of shape, fracture, the phenomenon such as layering, for complex-shaped place, constructional difficulties, and to Seepage, difficult quality guarantee, people will spend a large amount of funds and labor force and reprocess every several years.Not only upset people's orthobiosis, work and the production order, and affected the work-ing life of whole building buildings.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is, a kind of waterproof paint for building waterproof is provided, and this waterproof paint ageing-resistant performance is good, bonding force is strong, the material good-extensibility, application property is good, water tight integrity is good and the building water-proof paint of environmental protection.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of building water-proof paint, raw material by following parts by weight is made: silica powder 20-40 part, polypropene staple 3-7 part, wilkinite 3-10 part, phenylpropyl alcohol dairy industry 30-50 part, talcum powder 15-25 part, titanium dioxide 10-20 part, thixotropic agent 5-10 part, quick dry agent 7-15 part, water 15-35 part.
Above-mentioned building water-proof paint, described thixotropic agent are silicon-dioxide.
Above-mentioned building water-proof paint, described quick dry agent are propylene glycol.
Building water-proof paint advantage of the present invention is:
1, building water-proof paint of the present invention adopts stone flour as major ingredient, except the characteristics that keep styrene-acrylic coating, can so that after the coating film forming hardness high, anti humility performance is good.
2, building water-proof paint of the present invention, ageing-resistant performance is good, under the effects such as heat, light, long service life.
3, building water-proof paint of the present invention, bonding force is strong, the material good-extensibility, application property is good, and is non-foaming, and film-formation result is good, and is environment friendly and pollution-free.
Embodiment
The invention will be further described below in conjunction with embodiment.
Embodiment 1, and a kind of building water-proof paint is made by the raw material of following parts by weight: 20 parts of silica powders, 3 parts of polypropene staples, 3 parts of wilkinites, 30 parts of phenylpropyl alcohol dairy industries, 15 parts of talcum powder, 10 parts of titanium dioxides, 5 parts of thixotropic agent, 7 parts of quick dry agents, 15 parts in water.
Embodiment 2, and a kind of building water-proof paint is made by the raw material of following parts by weight: 30 parts of silica powders, 5 parts of polypropene staples, 8 parts of wilkinites, 40 parts of phenylpropyl alcohol dairy industries, 20 parts of talcum powder, 15 parts of titanium dioxides, 7 parts of thixotropic agent, 11 parts of quick dry agents, 28 parts in water.
Embodiment 3, and a kind of building water-proof paint is made by the raw material of following parts by weight: 40 parts of silica powders, 7 parts of polypropene staples, 10 parts of wilkinites, 50 parts of phenylpropyl alcohol dairy industries, 25 parts of talcum powder, 20 parts of titanium dioxides, 10 parts of thixotropic agent, 15 parts of quick dry agents, 35 parts in water.
Certainly, above-mentioned explanation is not to be limitation of the present invention, and the present invention also is not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, change, interpolation or replacement all should belong to protection scope of the present invention.
Claims (3)
1. building water-proof paint, it is characterized in that: the raw material by following parts by weight is made: silica powder 20-40 part, polypropene staple 3-7 part, wilkinite 3-10 part, phenylpropyl alcohol dairy industry 30-50 part, talcum powder 15-25 part, titanium dioxide 10-20 part, thixotropic agent 5-10 part, quick dry agent 7-15 part, water 15-35 part.
2. building water-proof paint according to claim 1, it is characterized in that: described thixotropic agent is silicon-dioxide.
3. building water-proof paint according to claim 1, it is characterized in that: described quick dry agent is propylene glycol.