CN102850028A - Seawater-corrosion-resistant road surface material - Google Patents
Seawater-corrosion-resistant road surface material Download PDFInfo
- Publication number
- CN102850028A CN102850028A CN2012102923835A CN201210292383A CN102850028A CN 102850028 A CN102850028 A CN 102850028A CN 2012102923835 A CN2012102923835 A CN 2012102923835A CN 201210292383 A CN201210292383 A CN 201210292383A CN 102850028 A CN102850028 A CN 102850028A
- Authority
- CN
- China
- Prior art keywords
- surface material
- seawater
- road surface
- corrosion resistance
- ground surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a seawater-corrosion-resistant road surface material, belonging to the technical field of construction materials. The seawater-corrosion-resistant road surface material comprises the following components in percentage by weight: 20-30% of semi-hydrated gypsum, 40-50% of cement, 5-10% of quartz sand, 5-10% of aluminum oxide ceramic powder, 1-3% of carbon fiber, 1-3% of potassium titanate whisker, 5-10% of titanium white, 5-10% of fly ash and 1-3%. The material adopts fewer organic chemical reagents, has the advantages of strong seawater corrosion resistance and accessible components, and is suitable for road surface construction in coastal areas.
Description
Technical field
The invention provides a kind of ground surface material of seawater corrosion resistance, belong to building material technical field.
Background technology
Along with Global climate change, sea-level rise has become the event that the maritime nation pays close attention to.In addition, because unusual storm and precipitation that climate change causes also can increase the generation that the road surface, coastland suffers marine denudation.The buildings such as many sea port docks, oil drilling platform are because phenomenons such as significantly degrading only just appearred in the corrosion of seawater in several years, crackings.
At present, mainly be in material, to add corrosion resistant additive to finish for the method that improves the ground surface material anti-seawater corrosion.But this method need to consume too much chemical agent, and additive also can be aging gradually in seawater.
Summary of the invention
For above problem, the invention provides a kind of ground surface material of seawater corrosion resistance.
The technical scheme that adopts is:
A kind of ground surface material of seawater corrosion resistance, the composition that comprises following weight percent meter: semi-hydrated gypsum 20~30%, cement 40~50%, quartz sand 5~10%, alumina-ceramic powder 5~10%, carbon fiber 1~3%, potassium titanate crystal whisker 1~3%, titanium dioxide 5~10%, flyash 5~10%, mould inhibitor 1~3%.
The preparation method is:
(a) take by weighing gypsum, cement, quartz sand, carry out pre-dispersed.
(b) more above-mentioned gypsum, cement, quartz sand are mixed.
(c) take by weighing alumina-ceramic powder, carbon fiber, potassium titanate crystal whisker, titanium dioxide, flyash, mix.
(d) mixture and the mould inhibitor with step (b) and step (c) gained mixes, and gets finished product.
More preferably, above-mentioned alumina-ceramic powder is that particle size range is 0.2 μ m ~ 1 μ m.
Preferred, above-mentioned titanium dioxide particle size range is 0.15 ~ 0.3 μ m.
The preferred scheme of the present invention is to comprise following component by weight percentage: semi-hydrated gypsum 21%, cement 45%, quartz sand 6%, alumina-ceramic powder 5%, carbon fiber 1%, potassium titanate crystal whisker 1%, titanium dioxide 10%, flyash 10%, mould inhibitor 1%.Make the road surface that makes have the performance of better intensity and seawater corrosion resistance.
Owing to include median size different alumina-ceramic powder, titanium dioxide in the ground surface material of seawater corrosion resistance provided by the invention, they can take in the road surface that lays in mutual embedding, have improved the road surface degree of compactness, prevent that seawater from permeating in the road surface.In addition, because the chemical stability of alumina-ceramic powder and titanium dioxide is good, further strengthened the anti-sea-water corrosion performance on road surface.And, owing in ground surface material, include carbon fiber and potassium titanate crystal whisker, can the shape reticulated structure in the road surface, between granular powder, more firmly be combined, further strengthen degree of compactness and the anti-sea-water corrosion performance on road surface.
Above-mentioned mould inhibitor can adopt the mould inhibitors commonly used such as common zinc sulfate, zinc oxide, borax, pentachlorophenol.
This material adopts less organic chemistry medicament, and seawater corrosion resistance can be strong, and each component easily obtains, and the pavement construction that is suitable for the coastland uses.
Embodiment
Below in conjunction with embodiment seawater corrosion resistance ground surface material provided by the invention is further described:
Take by weighing by weight following raw material:
Semi-hydrated gypsum (the grand foundation stone cream in Yingcheng City Products Co., Ltd)
Cement (Anhui Conch Cement limited-liability company, composite Portland cement P.C 32.5)
(stone quartz sand factory, particle size range 1 ~ 0.5mm) are good in the Lingshou County to quartz sand
Alumina-ceramic powder (the 0.2 μ m of Jing Dezhen Bai Te Weir novel material company limited ~ 1 μ m)
Carbon fiber (in multiple Condor carbon fiber limited liability company)
Potassium titanate crystal whisker (Dongying mountain letter type material company limited)
Titanium dioxide (Cang Zhouhai receive 0.15 ~ 0.3 μ m of chemical industry company limited)
Flyash (credit building materials company limited in the Chongqing)
Zinc sulfate (Ningbo City Gionee chemical industry company limited)
Be prepared in the steps below:
(a) take by weighing gypsum, cement, quartz sand, carry out pre-dispersed.
(b) more above-mentioned gypsum, cement, quartz sand are mixed.
(c) take by weighing alumina-ceramic powder, carbon fiber, potassium titanate crystal whisker, titanium dioxide, flyash, mix.
(d) mixture and the mould inhibitor with step (b) and step (c) gained mixes, and gets finished product.
The weight that each embodiment uses is as shown in table 1:
Each composition weight among table 1 embodiment 1~embodiment 2
Adopt following analysis test method to investigate the performance of this ground surface material seawater corrosion resistance:
With adding respectively 15kg water in the ground surface material of each embodiment, stir, make mortar, be prepared into again 200mm * 200mm * 5mm test block, test block is placed different solutions, changed a fresh solution in per 1 month, take out after 24 months.Ultimate compression strength, folding strength, weightlessness, surface finish (appearance method) to test block are investigated.Test-results such as table 2~table 4.
The sea water resistance testing data on the road surface of table 2 embodiment 1~4 (solution: true seawater)
Sea water resistance testing data (the solution: simulated seawater) on the road surface of table 3 embodiment 1~4
Sea water resistance testing data (the solution: brackish water) on the road surface of table 4 embodiment 1~4
Find out that from above experimental data ground surface material provided by the invention soaked after 24 months in testing liquid, still have higher intensity and less weightlessness, sea water corrosion resistant is good.
Claims (5)
1. the ground surface material of a seawater corrosion resistance, the composition that comprises following weight percent meter: semi-hydrated gypsum 20~30%, cement 40~50%, quartz sand 5~10%, alumina-ceramic powder 5~10%, carbon fiber 1~3%, potassium titanate crystal whisker 1~3%, titanium dioxide 5~10%, flyash 5~10%, mould inhibitor 1~3%.
2. the ground surface material of seawater corrosion resistance according to claim 1 is characterized in that: described mould inhibitor is a kind of in zinc sulfate, zinc oxide, borax, the pentachlorophenol.
3. the ground surface material of seawater corrosion resistance according to claim 1, it is characterized in that: the particle size range of described alumina-ceramic powder is 0.2 μ m~1 μ m.
4. the ground surface material of seawater corrosion resistance according to claim 1, it is characterized in that: described titanium dioxide particle size range is 0.15 ~ 0.3 μ m.
5. the ground surface material of seawater corrosion resistance according to claim 1, it is characterized in that: the following content by weight percentage of each component: semi-hydrated gypsum 21%, cement 45%, quartz sand 6%, alumina-ceramic powder 5%, carbon fiber 1%, potassium titanate crystal whisker 1%, titanium dioxide 10%, flyash 10%, mould inhibitor 1%.