CN102847672A - 转轮除湿机的吸附剂粘接方法 - Google Patents
转轮除湿机的吸附剂粘接方法 Download PDFInfo
- Publication number
- CN102847672A CN102847672A CN2012103613516A CN201210361351A CN102847672A CN 102847672 A CN102847672 A CN 102847672A CN 2012103613516 A CN2012103613516 A CN 2012103613516A CN 201210361351 A CN201210361351 A CN 201210361351A CN 102847672 A CN102847672 A CN 102847672A
- Authority
- CN
- China
- Prior art keywords
- adsorbent
- aluminum base
- base material
- rotary dehumidifier
- bonding method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种应用于转轮除湿机的吸附剂粘接方法，属于能源除湿技术领域。一种转轮除湿机的吸附剂粘接方法，将铝制基材在水玻璃中浸泡涂覆，干燥后，再将铝制基材在吸附剂中浸泡涂覆，在95℃下用烘箱干燥固化，实现吸附剂的物理吸附。在铝制基材上涂覆层的密度为0、9克/立方厘米～1.2克/立方厘米。本发明的吸附剂粘接方法应用于转轮，使之具有高吸湿量、再生温度低和稳定性高等优点，从而使转轮除湿机的除湿性能得到改善，增强市场竞争能力。
Description
技术领域；
本发明属于一种吸附剂粘接方法，尤其涉及一种应用于转轮除湿机的吸附剂粘接方法，属于能源除湿技术领域。
背景技术：
转轮除湿机属于空调领域的一个重要分支，是升温除湿的典型代表。目前，全世界转轮除湿机的主要产品是在美国、日本、瑞典和中国等地，中国的转轮除湿机也发展20多年，但核心技术仍掌握在美国、日本、瑞典等国的企业中，所以在市场的地位并不显著。作为转轮吸附式除湿机，其最主要的核心部件是除湿转轮，它是属高密集技术的特点。转轮的制造是以铝制基材或无机纤维基材经由成型机制成蜂巢状转轮后，涂覆吸附剂，并热处理，使吸附剂在转轮上沉积固化。这样，高效吸附剂加以转轮自身结构，不仅保证了转轮与空气接触的巨大面积，也提高转轮的吸湿效率，增加吸湿能力。目前，我国的生产企业基本是购买国外的除湿转轮，然后整机组装。
发明内容：
本发明的目的在于目前我国除湿转轮大部分是进口，提出一种转轮吸附剂粘接方法，使之具有高吸湿量、再生温度低、稳定性高、机械性能高，使我国企业可自行生产除湿转轮。
为了达到上述目的，本发明通过一定的技术方式将铝制基材浸泡在水玻璃中涂覆，干燥后，再将铝制基材浸泡在吸附剂中涂覆，然后固化，实现吸附剂的物理吸附。因此，本发明的主要内容是吸附剂的粘接方法，同时为了吸附剂有最大吸湿量，确定粘接剂及用量是技术的关键。具体配制方法如下：
1、首先，将铝制基材浸泡在水玻璃中涂覆，浸泡时间1～2小时，后取出，在室温下干燥5～10小时。
2、将吸附剂配制成粘稠的浆状物，用电磁搅拌机搅拌均匀，将所得浆状物浸泡涂覆第1步处理的铝制基材，浸泡时间1～2个小时。
3、将第2步处理铝制基材取出，热处理，在95℃下用烘箱干燥，吸附层在铝制基材上沉积固化。根据上述技术方式在铝制基材上涂覆层的密度为0.8克/立方厘米～1.2克/立方厘米。
上述所说的水玻璃模数为2.2～2.5，其浓度20～50％。
上述所说的吸附剂为4A分子筛，其浓度15～35％。
本发明的吸附剂粘接方法应用于转轮，使之具有高吸湿量、再生温度低、稳定性高及机械性能高等优点，从而使转轮除湿机的除湿性能得到改善，增强市场竞争能力。
具体实施方式：
实施例1：
1、首先，在烧杯中加入80克去离子水，然后加入模数为2.2的水玻璃20克，用电磁搅拌机搅拌均匀，将铝制基材浸泡涂覆，浸泡时间1～2小时，后取出，在室温下干燥5～10小时。
2、称取4A分子筛30克分散在150克去离子水中配制成粘稠的浆状物，用电磁搅拌机搅拌均匀，将所得浆状物浸泡涂覆第1步处理的铝制基材，浸泡时间1～2个小时。
3、将第2步处理铝制基材取出，热处理，在95℃下用烘箱干燥，吸附层在铝制基材上沉积固化。根据上述技术方式在铝制基材上涂覆层的密度为0.9克/立方厘米。空隙率为61％。
实施例2：
1、首先，在烧杯中加入70克去离子水，然后加入模数为2.2的水玻璃30克，用电磁搅拌机搅拌均匀，将铝制基材浸泡涂覆，浸泡时间1～2小时，后取出，在室温下干燥5～10小时。
2、称取4A分子筛30克分散在150克去离子水中配制成粘稠的浆状物，用电磁搅拌机搅拌均匀，将所得浆状物浸泡涂覆第1步处理的铝制基材，浸泡时间1～2个小时。
3、将第2步处理铝制基材取出，热处理，在95℃下用烘箱干燥，吸附层在铝制基材上沉积固化。根据上述技术方式在铝制基材上涂覆层的密度为1.0克/立方厘米。空隙率为59％
实施例3：
1、首先，在烧杯中加入60克去离子水，然后加入模数为2.2的水玻璃40克，用电磁搅拌机搅拌均匀，将铝制基材浸泡涂覆，浸泡时间1～2小时，后取出，在室温下干燥5～10小时。
2、称取4A分子筛30克分散在150克去离子水中配制成粘稠的浆状物，用电磁搅拌机搅拌均匀，将所得浆状物浸泡涂覆第1步处理的铝制基材，浸泡时间1～2个小时。
3、将第2步处理铝制基材取出，热处理，在95℃下用烘箱干燥，吸附层在铝制基材上沉积固化。根据上述技术方式在铝制基材上涂覆层的密度为1.1克/立方厘米。空隙率为57％。
Claims (3)
1.转轮除湿机的吸附剂粘接方法，其特征在于将铝制基材浸泡在水玻璃中涂覆，浸泡时间1～2小时后取出，在室温下干燥5～10小时，然后，将吸附剂配制成粘稠的浆状物，用电磁搅拌机搅拌均匀，将所得浆状物浸泡涂覆上面处理的铝制基材，浸泡时间1～2个小时后取出，热处理，在95℃下用烘箱干燥，吸附层在铝制基材上沉积固化，根据上述技术方式在铝制基材上涂覆层的密度为0.8克/立方厘米～1.2克/立方厘米。
2.根据权利要求1所述的转轮除湿机的吸附剂粘接方法，其特征在于水玻璃模数为2.2～2.5，其浓度20～50％。
3.根据权利要求1所述的转轮除湿机的吸附剂粘接方法，其特征在于吸附剂为4A分子筛，其浓度15～35％。