CN102839538A - Method for manufacturing anti-static cashmere overcoat - Google Patents
Method for manufacturing anti-static cashmere overcoat Download PDFInfo
- Publication number
- CN102839538A CN102839538A CN2012103489307A CN201210348930A CN102839538A CN 102839538 A CN102839538 A CN 102839538A CN 2012103489307 A CN2012103489307 A CN 2012103489307A CN 201210348930 A CN201210348930 A CN 201210348930A CN 102839538 A CN102839538 A CN 102839538A
- Authority
- CN
- China
- Prior art keywords
- static
- overcoat
- cashmere
- cashmere overcoat
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing an anti-static cashmere overcoat. The method comprises the following steps of: putting a cashmere overcoat into water containing a washing agent for soaking; adding a fulling agent, soaking, flushing with hot water, dehydrating, drying, and removing stain spots on the surface of the overcoat; putting the treated cashmere overcoat on a pulling-shearing combination machine for pulling and shearing repeatedly, and smoothening cashmere through a teaseling machine; and soaking the cashmere overcoat in a soaking liquid containing an anti-static finishing agent, drying, and preserving heat at the temperature of 115-150 DEG C for 0.5-2 hours. In the method, a compound anti-static finishing agent is adopted for performing anti-static finishing on the cashmere overcoat, so that the anti-static cashmere overcoat has a superior anti-static effect; and moreover, the compound anti-static finishing agent is firmly combined with cloth fiber, and has high durability.
Description
Technical field
The present invention relates to a kind of manufacturing approach of anti-static cashmere overcoat.
Background technology
The static that the clothes of different materials produce can make clothes tangle each other, dress inconvenience.Dress material and skin electric charge can adsorb each other and " skirt is embraced leg " phenomenon occur not simultaneously, make people's dysbasia.The chemical fibre clothes is because of serious static, and the special dirt particle that is prone to band heterocharge in the absorbed air is prone to make clothes to stain; The chemical fibre clothes also is prone to the adsorption head scurf especially.Wear next to the skin the chemical fibre underwear, skin can produce prodding and itching feeling, and snugness of fit descends.Wear the chemical fibre clothes, because triboelectrification, the electrostatic pressure of generation is very high, but when touching conducting objects such as metal objects or shaking hands with the people, just can discharge, and produces electric-shock feeling and makes us uncomfortable.
Wear the chemical fibre clothes, the electrostatic charge of gathering can puncture the little gap of air and produce spark, and the flammable explosive gas around the energy of spark is enough to make catches fire even explodes.When the human body direct-to-ground capacitance was 200 μ F, the human body electrified voltage reached 2000V, and carried charge is 0.4mJ, and this primer limit value (0.2mJ) than gasoline and air mixture exceeds one times.Ignite petrol drum, the etherization chamber of hospital, the dust of factory because of wearing the chemical fibre clothes, static makes the parachute accidents such as causing casualties of not opening that generation all arranged.
Static is still indeterminate to the mechanism of action of human body.The somebody thinks that static can make elevation of blood pressure; The somebody thinks that static can make the calcium loss in the blood; Also the somebody to think that static can cause allergic or the like.But have a bit very clear and definite, people are when the research man-made organ, and the electrostatic problem of the selection of material cause people's generally attention possibly for the influence of human body.
Antistatic clothing adopts method for sorting usually, and antistatic additive is compounded in fabric face, but often durability is relatively poor, through repeatedly losing efficacy seriously after the washing, influences its effect.
Summary of the invention
The technical problem that the present invention will solve provides a kind of manufacturing approach of anti-static cashmere overcoat, to overcome the above-mentioned defective that prior art exists.
For solving the problems of the technologies described above, the manufacturing approach of anti-static cashmere overcoat of the present invention comprises the steps:
1) place 35-40 ℃ the water that contains washing agent to soak 30 minutes in the cashmere overcoat;
2) add fulling agent, continue to soak after 30 minutes dewatered drying after 30 minutes, remove the surperficial fault of overcoat with 60-65 ℃ of hot water injection;
3) the processed cashmere coat combined tension and shear machine placed in tension and shear 25-30 times repeatedly, and then through thorn fruit machine obedient fluff;
4) the cashmere overcoat is padded processing in containing the maceration extract of antistatic finishing agent, pressure 2-2.5kg/cm
2, liquid carrying rate 75-80%;
5) oven dry is handled, between 115-150 ℃ constant temperature 0.5-2 hour then.
As preferably, said antistatic finishing agent is made up of the component of following weight portion:
Sulfatobetaine 60-65 part;
Polyoxyethylene alkyl ether 20-30 part;
Magnesium chloride 2-5 part;
Silane coupler 1-5 part;
Sodium Polyacrylate dispersant 0.5-1.0 part.
As preferably, said Sodium Polyacrylate dispersant preferred viscosities 200-300mPas.
As preferably; Antistatic finishing agent can adopt general mixed method; The following method preparation of preferred employing: sulfatobetaine, polyoxyethylene alkyl ether and magnesium chloride are mixed; Slowly add silane coupler and Sodium Polyacrylate dispersant then simultaneously, feeding intake in 1 hour finishes, and continues to mix 20-30 minute.
As preferably, add water after each component of antistatic finishing agent is mixed and be made into mass content and be not less than 15% maceration extract; Preferably be made into the maceration extract of mass content 35-50%.
As preferably, used washing agent, fulling agent etc. all adopt conventional commercially available prod.
The present invention will adopt the composite anti-static finishing agent that the cashmere overcoat is carried out antistatic finish, have good antistatic property, and with the clothes fiber strong bonded, durability is strong.
The specific embodiment
Embodiment 1
The preparation of antistatic finishing agent:
65 parts of sulfatobetaines;
20 parts of polyoxyethylene alkyl ethers;
5 parts in magnesium chloride;
1 part of silane coupler;
0.5 part of Sodium Polyacrylate dispersant.
Sulfatobetaine, polyoxyethylene alkyl ether and magnesium chloride are mixed in proportion, slowly add silane coupler and Sodium Polyacrylate dispersant then simultaneously, feeding intake in 1 hour finishes, and continues to mix 30 minutes.Adding water then, to be mixed with the quality solid content be 40% maceration extract.
The manufacturing of anti-static cashmere overcoat:
1) place 40 ℃ the water that contains washing agent to soak 30 minutes in the cashmere overcoat;
2) add fulling agent, continue to soak after 30 minutes dewatered drying after 30 minutes, remove the surperficial fault of overcoat with 65 ℃ of hot water injections;
3) the processed cashmere coat is placed repeatedly on the tensile shear tensile shear combined machine 30 times, and then through the thorn fruit machines obedient fluff;
4) the cashmere overcoat is padded processing in containing the maceration extract of antistatic finishing agent, pressure 2.5kg/cm
2, liquid carrying rate 80%;
5) oven dry is handled, then constant temperature 0.5 hour between 150 ℃.
Embodiment 2
The preparation of antistatic finishing agent:
60 parts of sulfatobetaines;
30 parts of polyoxyethylene alkyl ethers;
2 parts in magnesium chloride;
5 parts of silane couplers;
1.0 parts of Sodium Polyacrylate dispersants.
Sulfatobetaine, polyoxyethylene alkyl ether and magnesium chloride are mixed in proportion, slowly add silane coupler and Sodium Polyacrylate dispersant then simultaneously, feeding intake in 1 hour finishes, and continues to mix 20 minutes.Adding water then, to be mixed with the quality solid content be 20% maceration extract.
The manufacturing of anti-static cashmere overcoat:
1) place 35 ℃ the water that contains washing agent to soak 30 minutes in the cashmere overcoat;
2) add fulling agent, continue to soak after 30 minutes dewatered drying after 30 minutes, remove the surperficial fault of overcoat with 60 ℃ of hot water injections;
3) the processed cashmere coat is placed repeatedly on the tensile shear tensile shear combined machine 25 times, and then through the thorn fruit machines obedient fluff;
4) the cashmere overcoat is padded processing in containing the maceration extract of antistatic finishing agent, pressure 2kg/cm
2, liquid carrying rate 75%;
5) oven dry is handled, then constant temperature 2 hours between 115 ℃.
The application implementation example
Antistatic property
According to national standard GB 12703.4-2010 " evaluation the 4th part of textiles antistatic property: resistivity "; Measure the antistatic property of cashmere overcoat under different wash conditions with the method for GBT 12703.5-2010 " evaluation the 5th part of textiles antistatic property: frictional electrification voltage ", the result is following:
Antistatic property behind the different washing times of table 1
A representes that b representes to wash 5 times without the clothing of washing in the table, and c representes to wash 30 times.
It is thus clear that the antistatic effect of the anti-static cashmere overcoat that the present invention makes is excellent, and has good wash durability, through repeatedly still having good antistatic performance after the washing.
Claims (6)
1. the manufacturing approach of anti-static cashmere overcoat is characterized in that, comprises the steps:
1) place 35-40 ℃ the water that contains washing agent to soak 30 minutes in the cashmere overcoat;
2) add fulling agent, continue to soak after 30 minutes dewatered drying after 30 minutes, remove the surperficial fault of overcoat with 60-65 ℃ of hot water injection;
3) the processed cashmere coat combined tension and shear machine placed in tension and shear 25-30 times repeatedly, and then through thorn fruit machine obedient fluff;
4) the cashmere overcoat is padded processing in containing the maceration extract of antistatic finishing agent, pressure 2-2.5kg/cm
2, liquid carrying rate 75-80%;
5) oven dry is handled, and between 115-150 ℃, keeps constant temperature 0.5-2 hour.
2. the manufacturing approach of anti-static cashmere overcoat according to claim 1 is characterized in that, said antistatic finishing agent is made up of the component of following weight portion:
Sulfatobetaine 60-65 part;
Polyoxyethylene alkyl ether 20-30 part;
Magnesium chloride 2-5 part;
Silane coupler 1-5 part;
Sodium Polyacrylate dispersant 0.5-1.0 part.
3. the manufacturing approach of anti-static cashmere overcoat according to claim 2 is characterized in that, the viscosity of said Sodium Polyacrylate dispersant is 200-300mPas.
4. the manufacturing approach of anti-static cashmere overcoat according to claim 2; It is characterized in that; Said antistatic finishing agent adopts following method preparation: sulfatobetaine, polyoxyethylene alkyl ether and magnesium chloride are mixed; Slowly add silane coupler and Sodium Polyacrylate dispersant then simultaneously, feeding intake in 1 hour finishes, and continues to mix 20-30 minute.
5. the manufacturing approach of anti-static cashmere overcoat according to claim 4 is characterized in that, adds water after antistatic finishing agent preparation is accomplished and is made into mass content and is not less than 15% maceration extract.
6. the manufacturing approach of anti-static cashmere overcoat according to claim 5 is characterized in that, adds the maceration extract that water is made into mass content 35-50% after the antistatic finishing agent preparation is accomplished.