CN102837158A - Manufacturing technique of front fork steel tube of electrombile - Google Patents
Manufacturing technique of front fork steel tube of electrombile Download PDFInfo
- Publication number
- CN102837158A CN102837158A CN2011101699931A CN201110169993A CN102837158A CN 102837158 A CN102837158 A CN 102837158A CN 2011101699931 A CN2011101699931 A CN 2011101699931A CN 201110169993 A CN201110169993 A CN 201110169993A CN 102837158 A CN102837158 A CN 102837158A
- Authority
- CN
- China
- Prior art keywords
- round steel
- baking
- pickling
- curing
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of a production method of a stainless steel section, and particularly relates to a manufacturing technique of a front fork steel tube of an electrombile. The method orderly comprises the steps of: cogging through a steel ingot, roughing a billet into a round billet, rolling the round billet into a round pipe billet, rolling the round pipe billet into the round billet, slotting and sizing a round steel, and pressing the round steel into teeth-shaped and the like to produce a stainless steel tube. The manufacturing technique has the advantages of being simple in method, high in production efficiency, and low in production cost, and mass production can be achieved.
Description
Technical field
The invention belongs to the field of production of bar section of stainless steel, especially a kind of production technology of electric motor car front fork steel pipe.
Background technology
Now along with science and technology development; The application of steel is more and more widely all used steel in many technical fields, need connect with the C shaped steel of band round steel such as glass curtain wall; The also required round steel that is used for iron core in the motor; In the metallurgical and biological field of configuration, round steel also all has a very wide range of applications, but these round steel are produced and all can't be applied on the electric motor car front fork; The electric motor car front fork in use need be adjusted the height of electric motor car front fork according to different people's demand, and common steel pipe rust easily is dead.
Goal of the invention
The present invention is directed to the problem that needs to solve stainless steel round steel on the production electric motor car front fork in the above-mentioned technology, a kind of production technology of electric motor car front fork steel pipe is provided, the stainless steel with round steel that utilizes this method to produce can be used for the electric motor car front fork.
The technical scheme that realizes the object of the invention is following:
The production technology of electric motor car front fork steel pipe, the step of this production method is following,
A, steel ingot is heated after annealing handle, form round steel through roughing then, after the annealed processing of round steel, carry out pickling, roasting baking successively, go up oil-bound distemper, baking-curing is handled;
B, the round steel that obtains in a step is rolled obtains circular pipe blank; Circular pipe blank is annealed successively, pickling, roasting baking, go up oil-bound distemper, baking-curing is handled; Then in that to carry out the second time rolling, then carry out pickling, roasting baking once more, go up oil-bound distemper, baking-curing is handled, and then carry out temper;
C, the circular pipe blank that makes in b step is rolled obtains round steel billet; Round steel billet is annealed successively, pickling, roasting baking, go up oil-bound distemper, baking-curing and handle after, obtain exquisite round steel billet, this exquisiteness round steel billet carries out pickling; After pickling, dry, anneal after drying, temper;
D, the round steel billet that c was made in the step carry out obtaining round steel behind the pumping slot, and the round steel behind the pumping slot carries out annealing in process, and notch is finalized the design; Then the round steel alignment is finalized the design; Pass through baking-curing behind the oil-bound distemper again, then round steel is carried out kerve, behind the kerve round steel is carried out annealing in process; Alignment round steel after the annealing in process, the alignment round steel is carrying out temper;
E, with the round steel compacting tooth form that obtains in d step, anneal successively then, pickling, roasting baking, go up oil-bound distemper, baking-curing and handle after, after typing, carry out alignment, the stainless steel that pickling obtains having round steel is carried out in finishing after the correction then.
F, the stainless steel that obtains in the e step is carried out the metallized aluminum alloy and is rolled, annealed then, pickling, roasting baking, go up oil-bound distemper, baking-curing obtains the final products round steel after handling.
Advantage of the present invention is that this method is simple, and production efficiency is high, and production cost is low, can become to produce in enormous quantities.
The specific embodiment
The production technology of electric motor car front fork steel pipe, the step of this production method is following,
A, steel ingot is heated after annealing handle, form round steel through roughing then, after the annealed processing of round steel, carry out pickling, roasting baking successively, go up oil-bound distemper, baking-curing is handled;
B, the round steel that obtains in a step is rolled obtains circular pipe blank; Circular pipe blank is annealed successively, pickling, roasting baking, go up oil-bound distemper, baking-curing is handled; Then in that to carry out the second time rolling, then carry out pickling, roasting baking once more, go up oil-bound distemper, baking-curing is handled, and then carry out temper;
C, the circular pipe blank that makes in b step is rolled obtains round steel billet; Round steel billet is annealed successively, pickling, roasting baking, go up oil-bound distemper, baking-curing and handle after, obtain exquisite round steel billet, this exquisiteness round steel billet carries out pickling; After pickling, dry, anneal after drying, temper;
D, the round steel billet that c was made in the step carry out obtaining round steel behind the pumping slot, and the round steel behind the pumping slot carries out annealing in process, and notch is finalized the design; Then the round steel alignment is finalized the design; Pass through baking-curing behind the oil-bound distemper again, then round steel is carried out kerve, behind the kerve round steel is carried out annealing in process; Alignment round steel after the annealing in process, the alignment round steel is carrying out temper;
E, with the round steel compacting tooth form that obtains in d step, anneal successively then, pickling, roasting baking, go up oil-bound distemper, baking-curing and handle after, after typing, carry out alignment, the stainless steel that pickling obtains having round steel is carried out in finishing after the correction then.
F, the stainless steel that obtains in the e step is carried out the metallized aluminum alloy and is rolled, annealed then, pickling, roasting baking, go up oil-bound distemper, baking-curing obtains the final products round steel after handling.
Claims (1)
1. the production technology of electric motor car front fork steel pipe, the step of this production method is following,
A, steel ingot is heated after annealing handle, form round steel through roughing then, after the annealed processing of round steel, carry out pickling, roasting baking successively, go up oil-bound distemper, baking-curing is handled;
B, the round steel that obtains in a step is rolled obtains circular pipe blank; Circular pipe blank is annealed successively, pickling, roasting baking, go up oil-bound distemper, baking-curing is handled; Then in that to carry out the second time rolling, then carry out pickling, roasting baking once more, go up oil-bound distemper, baking-curing is handled, and then carry out temper;
C, the circular pipe blank that makes in b step is rolled obtains round steel billet; Round steel billet is annealed successively, pickling, roasting baking, go up oil-bound distemper, baking-curing and handle after, obtain exquisite round steel billet, this exquisiteness round steel billet carries out pickling; After pickling, dry, anneal after drying, temper;
D, the round steel billet that c was made in the step carry out obtaining round steel behind the pumping slot, and the round steel behind the pumping slot carries out annealing in process, and notch is finalized the design; Then the round steel alignment is finalized the design; Pass through baking-curing behind the oil-bound distemper again, then round steel is carried out kerve, behind the kerve round steel is carried out annealing in process; Alignment round steel after the annealing in process, the alignment round steel is carrying out temper;
E, with the round steel compacting tooth form that obtains in d step, anneal successively then, pickling, roasting baking, go up oil-bound distemper, baking-curing and handle after, after typing, carry out alignment, the stainless steel that pickling obtains having round steel is carried out in finishing after the correction then.
F, the stainless steel that obtains in the e step is carried out the metallized aluminum alloy and is rolled, annealed then, pickling, roasting baking, go up oil-bound distemper, baking-curing obtains the final products round steel after handling.