CN102827558A - Adhesive used for tailoring - Google Patents
Adhesive used for tailoring Download PDFInfo
- Publication number
- CN102827558A CN102827558A CN 201210327265 CN201210327265A CN102827558A CN 102827558 A CN102827558 A CN 102827558A CN 201210327265 CN201210327265 CN 201210327265 CN 201210327265 A CN201210327265 A CN 201210327265A CN 102827558 A CN102827558 A CN 102827558A
- Authority
- CN
- China
- Prior art keywords
- parts
- ethanol
- starch
- deionized water
- ammonium chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an adhesive for tailoring. The adhesive comprises the following components in parts by weight: 10-20 parts of vinyl acetate, 5-8 parts of ethanol, 20-30 parts of methyl acrylate, 8-10 parts of polyvinyl alcohol, 1-2 parts of hydrogen peroxide, 1-2 parts of tartaric acid, 5-8 parts of dibutyl phthalate, 5-10 parts of starch, 1-2 parts of ammonium chloride, 1-2 parts of hydroxymethyl cellulose and 50-80 parts of deionized water. In comparison with the prior art, the adhesive, provided by the invention has the advantages of good adhesive property, quick curing speed, no any chemical residues and the like.
Description
Technical field
The invention belongs to the textile product technical field, more specifically relate to a kind of clothes processing and stick with glue agent.
Background technology
In the clothes processing industry, need some patterns, stamp etc. be pasted on the clothing usually, therefore, tackiness agent also is widely used on this industry.
At present, the tackiness agent that on apparel industry, uses all exists such as viscosity not strong, and curing performance is bad, has the deficiency of aspects such as chemical residual, thereby makes its use receive certain limitation.
Summary of the invention
The objective of the invention is to overcome the deficiency that prior art exists, provide that a kind of viscosity is good, curing speed fast, the clothes of no any chemical residual are processed and sticked with glue agent.
For achieving the above object, the present invention has taked following technical scheme:
A kind of clothes processing sticks with glue agent, and is in weight part, composed of the following components:
Vinyl-acetic ester: 10～20, ethanol: 5～8, methyl acrylate: 20～30,
Z 150PH: 8～10, ydrogen peroxide 50: 1～2, tartrate: 1～2,
The neck phthalic acid dibutyl ester: 5～8, starch: 5～10, ammonium chloride: 1～2,
Walocel MT 20.000PV: 1～2, deionized water: 50～80.
In the technique scheme, the preparation technology that described clothes processing sticks with glue agent is following:
(1) in reactor drum, add deionized water, ethanol and Z 150PH, be warming up to 80～90 ℃, keep this temperature, it is back for use that Z 150PH is all dissolved;
(2) be cooled to 70～80 ℃ after, add ydrogen peroxide 50, tartrate, vinyl-acetic ester, methyl acrylate after, stir, make it to react completely;
(3) be cooled to 40～50 ℃, after adding ammonium chloride and leading phthalic acid dibutyl ester, react 4～5 hours to complete;
(4) be cooled to 30～40 ℃, add starch and Walocel MT 20.000PV, after mixing, be cooled to room temperature and promptly get product.
Compared with prior art, the present invention has beneficial effects such as cementability is good, curing speed fast, no any chemical residual.
Embodiment
Come the present invention is further described below in conjunction with specific embodiment, but the present invention's scope required for protection is not limited to the scope that embodiment describes.
Embodiment 1
A kind of clothes processing sticks with glue agent, and is in weight part, composed of the following components:
Vinyl-acetic ester: 10, ethanol: 5, methyl acrylate: 20,
Z 150PH: 8, ydrogen peroxide 50: 1, tartrate: 1,
The neck phthalic acid dibutyl ester: 5, starch: 5, ammonium chloride: 1,
Walocel MT 20.000PV: 1, deionized water: 50.
The preparation technology that described clothes processing sticks with glue agent is following:
(1) in reactor drum, add deionized water, ethanol and Z 150PH, be warming up to 80～90 ℃, keep this temperature, it is back for use that Z 150PH is all dissolved;
(2) be cooled to 70～80 ℃ after, add ydrogen peroxide 50, tartrate, vinyl-acetic ester, methyl acrylate after, stir, make it to react completely;
(3) be cooled to 40～50 ℃, after adding ammonium chloride and leading phthalic acid dibutyl ester, react 4～5 hours to complete;
(4) be cooled to 30～40 ℃, add starch and Walocel MT 20.000PV, after mixing, be cooled to room temperature and promptly get product.
Embodiment 2
A kind of clothes processing sticks with glue agent, and is in weight part, composed of the following components:
Vinyl-acetic ester: 20, ethanol: 8, methyl acrylate: 30,
Z 150PH: 10, ydrogen peroxide 50: 2, tartrate: 2,
The neck phthalic acid dibutyl ester: 8, starch: 10, ammonium chloride: 2,
Walocel MT 20.000PV: 2, deionized water: 80.
Preparation technology is with embodiment 1.
Embodiment 3
A kind of clothes processing sticks with glue agent, and is in weight part, composed of the following components:
Vinyl-acetic ester: 15, ethanol: 6, methyl acrylate: 25,
Z 150PH: 9, ydrogen peroxide 50: 1, tartrate: 2,
The neck phthalic acid dibutyl ester: 7, starch: 8, ammonium chloride: 2,
Walocel MT 20.000PV: 2, deionized water: 60.
Preparation technology is with embodiment 1.
Claims (4)
1. a clothes processing sticks with glue agent, it is characterized in that, and is in weight part, composed of the following components:
Vinyl-acetic ester: 10～20, ethanol: 5～8, methyl acrylate: 20～30,
Z 150PH: 8～10, ydrogen peroxide 50: 1～2, tartrate: 1～2,
The neck phthalic acid dibutyl ester: 5～8, starch: 5～10, ammonium chloride: 1～2,
Walocel MT 20.000PV: 1～2, deionized water: 50～80.
2. a kind of clothes processing according to claim 1 sticks with glue agent, it is characterized in that, and is in weight part, composed of the following components:
Vinyl-acetic ester: 10, ethanol: 5, methyl acrylate: 20,
Z 150PH: 8, ydrogen peroxide 50: 1, tartrate: 1,
The neck phthalic acid dibutyl ester: 5, starch: 5, ammonium chloride: 1,
Walocel MT 20.000PV: 1, deionized water: 50.
3. a kind of clothes processing according to claim 1 sticks with glue agent, it is characterized in that, and is in weight part, composed of the following components:
Vinyl-acetic ester: 20, ethanol: 8, methyl acrylate: 30,
Z 150PH: 10, ydrogen peroxide 50: 2, tartrate: 2,
The neck phthalic acid dibutyl ester: 8, starch: 10, ammonium chloride: 2,
Walocel MT 20.000PV: 2, deionized water: 80.
4. a kind of clothes processing according to claim 1 sticks with glue agent, it is characterized in that, and is in weight part, composed of the following components:
Vinyl-acetic ester: 15, ethanol: 6, methyl acrylate: 25,
Z 150PH: 9, ydrogen peroxide 50: 1, tartrate: 2,
The neck phthalic acid dibutyl ester: 7, starch: 8, ammonium chloride: 2,
Walocel MT 20.000PV: 2, deionized water: 60.