CN102794959A - Anti-skidding composite material and preparation method thereof - Google Patents
Anti-skidding composite material and preparation method thereof Download PDFInfo
- Publication number
- CN102794959A CN102794959A CN2012102270260A CN201210227026A CN102794959A CN 102794959 A CN102794959 A CN 102794959A CN 2012102270260 A CN2012102270260 A CN 2012102270260A CN 201210227026 A CN201210227026 A CN 201210227026A CN 102794959 A CN102794959 A CN 102794959A
- Authority
- CN
- China
- Prior art keywords
- film
- ldpe
- skid
- skidding
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-skidding composite material which sequentially comprises a first anti-skidding membrane, a glue layer, an OPP (Oriented Polypropylene) printing membrane, an LDPE (Low-Density Polyethylene) membrane, non-woven fabrics and a second anti-skidding membrane from outside to inside. Compared with the prior art, the composite material has the following advantages of good anti-skidding property and double-sided anti-skidding effect, excellent temperature resisting property, and stable property at minus 50-300 DEG C; and the composite material is waterproof, anti-corrosion, thin and soft, easy to fold and convenient to carry; and the manufacturing method is simple, so that large-scale industrial production can be realized.
Description
Technical field
The present invention relates to a kind of composite, specifically relate to a kind of anti-skidding composite and preparation method thereof.
Background technology
Anti-slip material has been widely used, as is used to make carpet, ground cushion, slipmat etc.Classify by material, slipmat comprises rubber antiskid pad, PVC slipmat, PU slipmat, AB glue slipmat, silica gel slipmat, magic power glue slipmat etc.
It is strong that PVC has lightweight, heat insulation, insulation, moistureproof, fire-retardant, bending strength and impact flexibility; Characteristics such as higher, easy construction of ductility when breaking; Slipmat good stability with this manufacture of materials; Its shortcoming be viscosity a little less than, and for a long time the high temperature more than 80 degree itself fuel-displaced phenomenon can occur, causes oil stain can dye instrument desk.
It is viscosity with to attach power very strong that PU is applied to its advantage of slipmat, and shortcoming is dirty for being prone to, product is dull, under the above high temperature of 70 degree, itself can compatiblely with the leather that is all the PU material cause the instrument desk damage for a long time.
Magic power glue silica gel asepsis environment-protecting, free from extraneous odour, environmental-protecting performance obviously are superior to PVC and PU; Magic power glue silica gel strong adhesion is lower than PU in PVC, and toughness is better than PU, is lower than PVC, and elasticity is between also; Magic power glue silica gel heatproof degree is subzero 50 to spend to 200 degree, also is that the face heat resistance is best in the different materials, and its shortcoming is that manufacturing process is complicated, and cost is higher.
Summary of the invention
Goal of the invention: in order to solve the deficiency of prior art, the invention provides a kind of anti-skidding composite, the current material skid resistance is poor to overcome, instability, cost high, the shortcoming of complex manufacturing technology.
The present invention also provides the preparation method of above-mentioned anti-skidding composite.
Technical scheme: in order to realize above purpose, a kind of anti-skidding composite of the present invention, described composite is made up of first non-skid film, glue layer, OPP print film, LDPE film, nonwoven, second non-skid film from outside to inside successively.
Preferably, the mass ratio of the material of described first non-skid film and second non-skid film employing is: LDPE:EVA=6～8:1～3.
Further preferably, the quality proportioning of the glue of described glue layer employing is: AC blowing agent: methyl alcohol: isopropyl alcohol: water=1:25～35:10～20:5～15;
Further preferably, the thickness of described first non-skid film is 20 ~ 50um; The thickness of OPP print film is 12 ~ 30um; The thickness of LDPE film is that the thickness of 20 ~ 50um, nonwoven is 0.2 ~ 0.5mm; The thickness of second non-skid film is 20 ~ 50um.
A kind of method of making anti-skidding composite, the concrete steps of this preparation method are following:
A, pattern is printed on becomes the OPP print film on the OPP film;
B, LDPE is extruded under 320～350 ℃ of conditions, drench between the reverse side of OPP print film and nonwoven both are closed in pouring, form the LDPE film;
C, do multiple one deck glue layer in the front of OPP print film, the quality proportioning of this glue is: AC blowing agent: methyl alcohol: isopropyl alcohol: water=1:25～35:10～20:5～15;
D, treat that glue layer parches after, be under 320～350 ℃ of conditions in temperature, drench one deck non-skid film above that, the mass ratio of materials is LDPE:EVA=6～8:1～3, forms first non-skid film;
E, be under 320～350 ℃ of conditions in temperature, drench one deck non-skid film at the another side of nonwoven, the mass ratio of materials is LDPE:EVA=6～8:1～3, forms second non-skid film, is described anti-skidding composite.
Beneficial effect: the present invention compared with prior art has the following advantages: non-skid property is good, and two-sided anti-skidding; Heat resistance is excellent, at subzero 50 ℃ to 300 ℃, and stable performance; Have waterproof, anticorrosion, product is thin soft, is prone to foldingly, and advantage such as be easy to carry.Preparation method is simple, can realize large-scale industrialization production.
Description of drawings
Fig. 1 is a kind of structural representation of the present invention.
The specific embodiment
Below in conjunction with accompanying drawing and specific embodiment; Further illustrate the present invention; Should understand these embodiment only be used to the present invention is described and be not used in the restriction scope of the present invention; After having read the present invention, those skilled in the art all fall within the application's accompanying claims institute restricted portion to various equivalents of the present invention or modification.
Embodiment 1:
A kind of anti-skidding composite as shown in Figure 1; It is made up of first non-skid film 1, glue layer 2, OPP print film 3, LDPE film 4, nonwoven 5, second non-skid film 6 from outside to inside successively; Wherein, the mass ratio of the material of first non-skid film 1 and 6 employings of second non-skid film is: LDPE:EVA=7:2.
The quality proportioning of the glue that described glue layer 2 adopts is: AC blowing agent: methyl alcohol: isopropyl alcohol: water=1:20:15:10; The thickness of described first non-skid film 1 is 35um; The thickness of OPP print film 3 is 21um; The thickness of LDPE film 4 is that the thickness of 35um, nonwoven 5 is 0.3mm; The thickness of second non-skid film 6 is 35um.
Make the method for above-mentioned anti-skidding composite, the concrete steps of this preparation method are following:
A, pattern is printed on becomes OPP print film 3 on the OPP film;
B, LDPE is extruded under 320～350 ℃ of conditions, drench between the reverse side of OPP print film 3 and nonwoven 5 both are closed in pouring, form LDPE film 4;
C, do multiple one deck glue layer 2 in the front of OPP print film 3, the quality proportioning of this glue is: AC blowing agent: methyl alcohol: isopropyl alcohol: water=1:20:15:10;
D, treat that glue layer 2 parches after, be under 320～350 ℃ of conditions in temperature, drench one deck non-skid film above that, the mass ratio of materials is LDPE:EVA=7:2, forms first non-skid film 1;
E, be under 320～350 ℃ of conditions in temperature, drench one deck non-skid film at the another side of nonwoven 5, the mass ratio of materials is LDPE:EVA=7:2, forms second non-skid film 6, is described anti-skidding composite.
Embodiment 2:
A kind of anti-skidding composite as shown in Figure 1; It is made up of first non-skid film 1, glue layer 2, OPP print film 3, LDPE film 4, nonwoven 5, second non-skid film 6 from outside to inside successively; Wherein, the mass ratio of the material of first non-skid film, 1 employing is: LDPE:EVA=6:1; The mass ratio of the material that second non-skid film 6 adopts is: LDPE:EVA=8:3.
The quality proportioning of the glue that described glue layer 2 adopts is: AC blowing agent: methyl alcohol: isopropyl alcohol: water=1:25:10:5; The thickness of described first non-skid film 1 is 20um; The thickness of OPP print film 3 is 12um; The thickness of LDPE film 4 is that the thickness of 20um, nonwoven 5 is 0.2mm; The thickness of second non-skid film 6 is 20um.
Make the method for above-mentioned anti-skidding composite, the concrete steps of this preparation method are following:
A, pattern is printed on becomes OPP print film 3 on the OPP film;
B, LDPE is extruded under 320～350 ℃ of conditions, drench between the reverse side of OPP print film 3 and nonwoven 5 both are closed in pouring, form LDPE film 4;
C, do multiple one deck glue layer 2 in the front of OPP print film 3, the quality proportioning of this glue is: AC blowing agent: methyl alcohol: isopropyl alcohol: water=1:25:10:5;
D, treat that glue layer 2 parches after, be under 320～350 ℃ of conditions in temperature, drench one deck non-skid film above that, the mass ratio of materials is LDPE:EVA=6:1, forms first non-skid film 1;
E, be under 320～350 ℃ of conditions in temperature, drench one deck non-skid film at the another side of nonwoven 5, the mass ratio of materials is: LDPE:EVA=8:3, form second non-skid film 6, and be described anti-skidding composite.
Embodiment 3:
A kind of anti-skidding composite as shown in Figure 1; It is made up of first non-skid film 1, glue layer 2, OPP print film 3, LDPE film 4, nonwoven 5, second non-skid film 6 from outside to inside successively; Wherein, the mass ratio of the material of first non-skid film, 1 employing is: LDPE:EVA=2:1; The mass ratio of the material that second non-skid film 6 adopts is: LDPE:EVA=8:1.
The quality proportioning of the glue that described glue layer 2 adopts is: AC blowing agent: methyl alcohol: isopropyl alcohol: water=1:35:20:15; The thickness of described first non-skid film 1 is 50um; The thickness of OPP print film 3 is 30um; The thickness of LDPE film 4 is that the thickness of 50um, nonwoven 5 is 0.5mm; The thickness of second non-skid film 6 is 50um.
Make the method for above-mentioned anti-skidding composite, the concrete steps of this preparation method are following:
A, pattern is printed on becomes OPP print film 3 on the OPP film;
B, LDPE is extruded under 320～350 ℃ of conditions, drench between the reverse side of OPP print film 3 and nonwoven 5 both are closed in pouring, form LDPE film 4;
C, do multiple one deck glue layer 2 in the front of OPP print film 3, the quality proportioning of this glue is: AC blowing agent: methyl alcohol: isopropyl alcohol: water=1:35:20:15;
D, treat that glue layer 2 parches after, be under 320～350 ℃ of conditions in temperature, drench one deck non-skid film above that, the mass ratio of materials is LDPE:EVA=2:1, forms first non-skid film 1;
E, be under 320～350 ℃ of conditions in temperature, drench one deck non-skid film at the another side of nonwoven 5, the mass ratio of materials is LDPE:EVA=8:1, forms second non-skid film 6, is described anti-skidding composite.
Claims (5)
1. anti-skidding composite, it is characterized in that: described composite is made up of first non-skid film (1), glue layer (2), OPP print film (3), LDPE film (4), nonwoven (5), second non-skid film (6) from outside to inside successively.
2. anti-skidding composite according to claim 1 is characterized in that: the mass ratio of the material that described first non-skid film (1) and second non-skid film (6) adopt is: LDPE:EVA=6～8:1～3.
3. anti-skidding composite according to claim 1 is characterized in that: the quality proportioning of the glue that described glue layer (2) adopts is: AC blowing agent: methyl alcohol: isopropyl alcohol: water=1:25～35:10～20:5～15.
4. anti-skidding composite according to claim 1 and 2 is characterized in that: the thickness of described first non-skid film (1) is 20 ~ 50um; The thickness of OPP print film (3) is 12 ~ 30um; The thickness of LDPE film (4) is that the thickness of 20 ~ 50um, nonwoven (5) is 0.2 ~ 0.5mm; The thickness of second non-skid film (6) is 20 ~ 50um.
5. method of making the described anti-skidding composite of claim 1, it is characterized in that: the concrete steps of this preparation method are following:
A, pattern is printed on becomes OPP print film (3) on the OPP film;
B, LDPE is extruded under 320～350 ℃ of conditions, drench between the reverse side of OPP print film (3) and nonwoven (5) both are closed in pouring, form LDPE film (4);
C, do multiple one deck glue layer (2) in the front of OPP print film (3), the quality proportioning of this glue is: AC blowing agent: methyl alcohol: isopropyl alcohol: water=1:25～35:10～20:5～15;
D, treat that glue layer (2) parches after, be under 320～350 ℃ of conditions in temperature, drench one deck non-skid film above that, the mass ratio of materials is LDPE:EVA=6～8:1～3, forms first non-skid film (1);
E, be under 320～350 ℃ of conditions in temperature, drench one deck non-skid film at the another side of nonwoven (5), the mass ratio of materials is LDPE:EVA=6～8:1～3, forms second non-skid film (6), is described anti-skidding composite.