CN102787423A - Preparation method for heat-resisting pure-cotton clean wiping cloth - Google Patents
Preparation method for heat-resisting pure-cotton clean wiping cloth Download PDFInfo
- Publication number
- CN102787423A CN102787423A CN2012103042079A CN201210304207A CN102787423A CN 102787423 A CN102787423 A CN 102787423A CN 2012103042079 A CN2012103042079 A CN 2012103042079A CN 201210304207 A CN201210304207 A CN 201210304207A CN 102787423 A CN102787423 A CN 102787423A
- Authority
- CN
- China
- Prior art keywords
- cotton
- cloth
- preparation
- clean
- equipment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the technical field of a superfine textile material, and relates to a heat-resisting pure-cotton material dustless wiping cloth, and particularly relates to a preparation method for the pure-cotton clean wiping cloth for a high-temperature oven. The preparation method comprises the following steps of: preparing a cotton thread from a material cotton yarn, weaving into a greige cloth from the cotton yarn; punching and molding after dyeing and sizing, and obtaining the a finished product via a clean treatment inside a CLASS100-level purifying room, carrying out acceptance inspection and packaging. The heat-resisting clean wiping cloth prepared by the method disclosed by the invention can clean equipment when the equipment is not completely cooled, so that not only is valuable time for waiting cooling of the equipment saved, but also time for restarting the equipment to produce a heat engine is quickened. Therefore, original production efficiency is greatly improved, and loss of an energy source of the equipment is also reduced by addition of two aspects of the time.
Description
Technical field
The invention belongs to ultra-fine textile material technical field, relate to a kind of resistant to elevated temperatures textile material dust-free cleaning cloth, especially for the preparation method of the textile clean cleaning wiping cloth of high temperature oven.
Background technology
Existing former device of some high accuracy and optical flat show that all inevitably using baking oven that its parts are carried out heating, drying when producing handles; And drying plant also need regularly carry out clean; (temperature the during operation of these equipment basically all will between 120 ℃-150 ℃); All be to use the compound non-dust cloth of terylene or terylene to carry out cleaning operation in the past; But since its can not tolerate the residual high temperature of equipment (terylene or terylene composite material-feeding withstand high temperatures are 60 ℃--70 ℃; Will produce wire drawing or adhere to the situation on the equipment during high temperature wiping like this, have only by the time apparatus cools to get off and could clean, and device temperature drops to 60 ℃ from 150 ℃ and needs 15-30 minute basically rising) be great waste to production efficiency like this!
Summary of the invention
The objective of the invention is to above situation, and propose a kind of high temperature resistant, especially to the preparation method of the textile clean cleaning wiping cloth of high temperature oven.
Main technical schemes of the present invention: the preparation method of the clean cleaning wiping cloth of high temperature resistant cotton textiles; It is characterized in that may further comprise the steps: the raw material cotton yarn is processed cotton thread, and cotton thread is made into grey cloth, punching molding after dying boiling hot typing; Clean in the CLASS100 level purifies the room is is again checked and accepted, packing gets product.
Preparation method of the present invention, a kind of typical step is following:
1. raw material uses the smart yarn of 30x30 cotton to be made into 60 the smart line of cotton;
2. loom on the smart line of 60 cotton is woven to grey cloth, loom is set at twill, and on 22 times, 158 pieces/inch of warp-wises; 80 pieces/inch of broadwises;
3. grey cloth dyes through dye vat and scalds typing, and the door width of cloth is at 130mm-160mm, and density is 150--180 gram/square meter;
4. stamping machine carries out punching molding with cutting die on the cloth after the typing;
5. with the semi-finished product of punching molding,, the CLASS100 level carries out clean in purifying the room;
6. check and accept, pack.
Usually, in above-mentioned steps 4 punching molding, cloth is stacked as the 12-22 layer, cutter touch with cloth in angle of 45 degrees, the punching molding specification: 4 〞 x4 〞, 6 〞 x6 〞, 9 〞 x9 〞 etc. also can customize other specifications according to customer requirement; In the step 5, in the CLASS100 level purifies the room, carry out clean, comprise that mainly the pure water that uses 18.1 megaohms earlier cleans, and dries then, plates.
The high temperature resistant clean cleaning wiping cloth of the inventive method preparation; Can, equipment just carry out clean when not lowering the temperature fully to it; Not only saved the quality time of device wait cooling, also accelerated equipment and restarted the time that hot machine is produced, two aspects of time are closed and are added like this; Improve original production efficiency greatly, also reduced the loss of the equipment energy simultaneously.
Description of drawings
Fig. 1 is for dying the actual lines figure of cotton that scalds after finalizing the design in the embodiment of the invention method; Fig. 2 is for dying the 120 times of enlarged drawings of cotton lines that scald after finalizing the design in the embodiment method; Fig. 3 is cotton edge effect figure after the punching molding in the embodiment of the invention method; Fig. 4 is cotton edge effect figure after the punching molding in the Comparative Examples.
The specific embodiment
Below in conjunction with embodiment and accompanying drawing the inventive method is described in detail.
Embodiment: the preparation method of the clean cleaning wiping cloth of high temperature resistant cotton textiles mainly comprises following processing step:
1. raw material uses the smart yarn of 30x30 cotton to be made into 60 the smart line of cotton;
2. loom on the smart line of 60 cotton is woven to grey cloth, loom is set at twill, and on 22 times, 158 pieces/inch of warp-wises; 80 pieces/inch of broadwises;
3. grey cloth dyes through dye vat and scalds typing, and the door width of cloth is at 130mm-160mm, and density is 150--180 gram/square meter, and the cotton lines after the typing is as attaching shown in Fig. 1 and 2;
4. stamping machine carries out punching molding with cutting die on the cloth after the typing, and the cotton edge effect after the punching molding is shown in accompanying drawing 3;
5. with the semi-finished product of punching molding,, the CLASS100 level carries out clean in purifying the room;
6. check and accept, pack, get product.
In embodiment step 4 punching molding, cloth is stacked as 12 layers, cutter touch with cloth in angle of 45 degrees, the punching molding specification can be 4 〞 x4 〞, 6 〞 x6 〞, 9 〞 x9 〞 etc., also can customize other specifications according to customer requirement; In the step 5, in the CLASS100 level purifies the room, carry out clean, comprise that mainly the pure water that uses 18.1 megaohms earlier cleans, and dries then, plates.
Comparative Examples: other steps are identical with embodiment, and just in step 4, cutting die becomes 90 degree angles with cloth, and the effect at cotton edge is shown in accompanying drawing 4 after the punching molding.
Can find out from the contrast of Fig. 3 and Fig. 4, adopt the punching molding method of present embodiment, phenomenon is fallen to consider to be worth doing in the limit that can not occur loosing.
Claims (4)
1. the preparation method of the clean cleaning wiping cloth of high temperature resistant cotton textiles is characterized in that may further comprise the steps: the raw material cotton yarn is processed cotton thread, and cotton thread is made into grey cloth, scalds typing back punching molding through dying, and clean in the CLASS100 level purifies the room is is again checked and accepted, packed and get product.
2. preparation method as claimed in claim 1 is characterized in that step is following:
A. raw material uses the smart yarn of 30x30 cotton to be made into 60 the smart line of cotton;
B. loom on the smart line of 60 cotton is woven to grey cloth, loom is set at twill, and on 22 times, 158 pieces/inch of warp-wises; 80 pieces/inch of broadwises;
C. grey cloth dyes through dye vat and scalds typing, and the door width of cloth is at 130mm-160mm, and density is 150--180 gram/square meter;
D. stamping machine carries out punching molding with cutting die on the cloth after the typing;
E. with the semi-finished product of punching molding,, the CLASS100 level carries out clean in purifying the room;
F. check and accept, pack.
3. preparation method as claimed in claim 2 is characterized in that in the steps d punching molding cloth being stacked as the 12-22 layer, cutter touch with cloth in angle of 45 degrees.
4. preparation method as claimed in claim 2 is characterized in that among the step e, in the CLASS100 level purifies the room, carries out clean, comprises that the pure water that uses 18.1 megaohms earlier cleans, and dries then, plates.