CN102766299A - Anti-impacting anti-ageing modified polypropylene material and preparation method thereof - Google Patents
Anti-impacting anti-ageing modified polypropylene material and preparation method thereof Download PDFInfo
- Publication number
- CN102766299A CN102766299A CN2012102697016A CN201210269701A CN102766299A CN 102766299 A CN102766299 A CN 102766299A CN 2012102697016 A CN2012102697016 A CN 2012102697016A CN 201210269701 A CN201210269701 A CN 201210269701A CN 102766299 A CN102766299 A CN 102766299A
- Authority
- CN
- China
- Prior art keywords
- shock resistance
- resistance according
- modified polypropene
- aging
- photostabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an anti-impacting anti-ageing modified polypropylene material and a preparation method thereof and aims at providing the anti-impacting anti-ageing modified polypropylene material which has basic physical characteristics of polypropylene and simultaneously has improved anti-impacting performance and good anti-ageing performance. The material comprises, by weight, 65-85% of polypropylene, 5-25% of inorganic fillers, 0.3-1.5% of antioxidant, 0.2-1.0% of light stabilizer, 0.2-1.0% of ultraviolet absorber, 5-15% of flexibilizer, 5-15% of compatilizer and 0.2-1.0% of coupling agent. Experiment results show that the material can achieve the purposes, and products can be widely applied to the fields such as electronics and electrics, automobile and household appliances, communication devices and building materials.
Description
Technical field
The present invention relates to plastics polymer modification technical field, specifically, relate to the preparation that a kind of novel anti is impacted the ageing resistance polypropylene material.
Background technology
Vestolen PP 7052 is a kind of thermoplastics, and density is little, and surface hardness is big, and thermotolerance, chemicalstability, insulativity are good, is widely used in producing, various fields of recent life.Especially use more extensive at automobile and building field.And virgin pp resin material shock resistance is poor, and especially low temperature impact properties is poorer.Owing to the tertiary carbon atom on the polypropylene molecular chain takes place to wear out easily, make that product surface be full of cracks, gloss are lost, shock strength in addition under the effect of ultraviolet ray, oxygen, light, heat, mechanical properties such as tensile strength reduce greatly.This makes PP be restricted in field sector applications such as electric, vehicle appliance, Communication Equipment, material of construction, in order to reach shock resistance and aging-resistant requirement, must carry out modification to the PP material.Through adding toughner and protective agent is the effective way that enlarges its range of application.
The present invention makes the polypropylene material mechanical property be able to improve greatly through interpolation talcum powder and POE toughner in the PP resin, and possesses good impact property.Utilize the effect of UV light absorber and photostabilizer simultaneously, assist, improved polyacrylic thermo-oxidative stability, make that the anti-aging of material is more lasting, better effects if with oxidation inhibitor.
Summary of the invention
The object of the present invention is to provide the anti-aging modified polypropylene material of a kind of shock resistance, when possessing the basic physical property of Vestolen PP 7052, both improved its shock resistance, possess excellent anti ageing property again.For reaching the object of the invention, realize through following scheme:
The anti-aging modified polypropene of a kind of shock resistance of the present invention, form by following materials of weight proportions:
Acrylic resin 65 ~ 85%
Mineral filler 5 ~ 25%
Oxidation inhibitor 0.3 ~ 1.5%
Photostabilizer 0.2 ~ 1.0%
UV light absorber 0.2 ~ 1.0%
Toughner 5 ~ 15%
Compatilizer 5 ~ 15%
Coupling agent 0.2 ~ 1.0%
Described acrylic resin is that an ancient unit of weight gathers or copolymerization PP, and melting index is 3 ~ 25.
Described mineral filler is a talcum powder, and its fineness is in 1200 ~ 3000 orders, whiteness>90.
Described oxidation inhibitor is at least a in phenolic antioxidant 1010 or the phosphite ester kind antioxidant 168.
Described photostabilizer is hydroxybenzotriazole class photostabilizer Tinuvin326, and Tinuvin 328, Hinered phenols photostabilizer Tinuvin 770, at least a among the Chimassorb 944.
Described UV light absorber is UV-531; UV-531.
Described toughner is octene and ethene polymers POE.
Described compatilizer is a maleic anhydride inoculated polypropylene.
Described coupling agent is a kind of in silane, titanic acid ester, the SULPHOSUCCINIC ACID ESTER.
The related anti-aging modified polypropene of a kind of shock resistance of the present invention is gathered by the following step and carries out:
1) 100 ℃ of-110 ℃ of dryings of mineral filler talcum powder preheating are added after 2 hours by the coupling agent of stipulating proportioning in mixing machine, after mixing, take out, it is for use to make the talcum powder compsn.
2) with acrylic resin, 75 ℃-85 ℃ dry 4-6 hour, adding the step then to scale gathers the 1 talcum powder compsn that makes; And oxidation inhibitor, photostabilizer, UV light absorber; Toughner; Compatilizer is put into twin screw extruder after in high-speed mixer, mixing, extrude, tie rod, air-cooled, pelletizing, be dried to the finished product.
3) described twin screw extruder screw slenderness ratio is that 35:1~40:1 extrusion temperature is 165 ℃~240 ℃, and screw speed is: 280-480 rev/min.
UV light absorber and photostabilizer are used and prevent the destruction of deleterious UV-light for color; Improve polyacrylic anti-ultraviolet ageing performance.The adding of POE has improved the shock strength of PP, has improved polyacrylic breakthrough fragile under low temperature and has fallen into.
6]The invention has the advantages that: make high impact properties ageing resistance polypropylene material through flow process method simple, continuous, high-efficiency and low-cost, make that polypropylene material physical and mechanical properties and the thermo-oxidative ageing property after the modification is greatly improved.Product can be widely used in fields such as car interior-exterior decorations, building, military project, Communication Equipment.
Embodiment
For a better understanding of the present invention, enumerate the embodiment detailed description.
Shown in table one, the acrylic resin that adopts in the present embodiment is that Daqing petrochemical T30S an ancient unit of weight of 3 gathers Vestolen PP 7052 for molten the finger, and talcum powder is 1600 commercially available order talcum powder, and the coupling agent KH792 that adds by the regulation proportioning after 2 hours through 100 ℃ of-110 ℃ of dryings obtains.Oxidation inhibitor is lrganox1010, and photostabilizer is that Tinuvin 770, UV light absorber are UV-531, and toughner is that LG-DOW POE8150, compatilizer are commercially available toxilic acid bar grafting PP.
With acrylic resin, 75 ℃-85 ℃ dry 4-6 hour, add talcum powder, antioxidant 1010, Tinuvin 770 in table just like the regulation ratio then; UV-531; POE Tao Shi 8150, raw materials such as maleic anhydride graft PP mix after 10 minutes in high-speed mixer; Put into twin screw extruder, extrude, tie rod, air-cooled, pelletizing, be dried to the finished product.
Said forcing machine is a twin screw extruder, and its length-to-diameter ratio is 38:1, and each temperature of screw rod is: 165 ℃, 170 ℃, 180 ℃, 185 ℃, 190 ℃, 195 ℃, 195 ℃, 195 ℃.Screw speed is 400rpm.
Performance index such as the table two of embodiment
Table one
Material name | Embodiment 1 | Embodiment 2 | Embodiment 3 |
Vestolen PP 7052 | 65 | 70 | 75 |
Talcum powder | 15 | 12 | 10 |
Antioxidant 1010 | 0.2 | 0.2 | 0.2 |
Tinuvin 770 | 0.5 | 0.5 | 0.5 |
UV-531 | 0.5 | 0.5 | 0.5 |
POE Tao Shi 8150 | 10 | 10 | 7 |
Maleic anhydride graft PP (commercially available) | 8.5 | 6.5 | 6.5 |
KH792 | 0.3 | 0.3 | 0.3 |
Table two
Relevant testing standard and method:
GB/T3682: the molten testing standard that refers to.
GB/1040: tensile strength testing standard.
GB/T9341: flexural strength testing standard.
GB/1843: notched Izod impact strength testing standard.
GB/1643: heat-drawn wire testing standard.
GB/7141: anti-aging testing standard.
Can find out that through last table the anti-aging modified polypropene of shock resistance of the present invention possesses good shock resistance, ageing resistance is also very excellent simultaneously.
The above only is a preferred embodiments of the present invention, is not to be the restriction of the present invention being made other form, and any professional and technical personnel of being familiar with possibly utilize the technology contents of above-mentioned prompting to change or be modified as the actual effect instance of equivalent variations.This description should not be construed as limitation of the present invention.
Claims (9)
1. the anti-aging modified polypropylene material of shock resistance is characterized in that, is made up of following materials of weight proportions:
?
Acrylic resin 65 ~ 85%
Mineral filler 5 ~ 25%
Oxidation inhibitor 0.3 ~ 1.5%
Photostabilizer 0.2 ~ 1.0%
UV light absorber 0.2 ~ 1.0%
Toughner 5 ~ 15%
Compatilizer 5 ~ 15%
Coupling agent 0.2 ~ 1.0%.
2. the anti-aging modified polypropene of shock resistance according to claim 1 is characterized in that, and is described
Acrylic resin is that an ancient unit of weight gathers or copolymerization PP, and melting index is 3 ~ 25.
3. the anti-aging modified polypropene of shock resistance according to claim 1 is characterized in that described mineral filler is a talcum powder, and its fineness is in 1200 ~ 3000 orders, whiteness>90.
4. the anti-aging modified polypropene of shock resistance according to claim 1 is characterized in that, described oxidation inhibitor is at least a in phenolic antioxidant 1010 or the phosphite ester kind antioxidant 168.
5. the anti-aging modified polypropene of shock resistance according to claim 1; It is characterized in that described photostabilizer is hydroxybenzotriazole class photostabilizer Tinuvin326, Tinuvin 328; Hinered phenols photostabilizer Tinuvin 770, at least a among the Chimassorb 944.
6. the anti-aging modified polypropene of shock resistance according to claim 1 is characterized in that described UV light absorber is UV-531; UV-531.
The anti-aging modified polypropene of shock resistance according to claim 1 is characterized in that, described toughner is octene and ethene polymers POE.
7. the anti-aging modified polypropene of shock resistance according to claim 1 is characterized in that described compatilizer is a maleic anhydride inoculated polypropylene.
8. the anti-aging modified polypropene of shock resistance according to claim 1 is characterized in that, described coupling agent is a kind of in silane, titanic acid ester, the SULPHOSUCCINIC ACID ESTER.
9. anti-aging preparation method of modified polypropylene of shock resistance according to claim 1 is characterized in that comprising that the following step gathers:
100 ℃ of-110 ℃ of dryings of mineral filler talcum powder preheating are added after 2 hours by the coupling agent of stipulating proportioning in mixing machine, after mixing, take out, it is for use to make the talcum powder compsn.
With acrylic resin, 75 ℃-85 ℃ dry 4-6 hour, adding the step then to scale gathers the 1 talcum powder compsn that makes; And oxidation inhibitor, photostabilizer, UV light absorber; Toughner; Compatilizer is put into twin screw extruder after in high-speed mixer, mixing, extrude, tie rod, air-cooled, pelletizing, be dried to the finished product.
Described twin screw extruder screw slenderness ratio is that 35:1~40:1 extrusion temperature is 165 ℃~240 ℃, and screw speed is: 280-480 rev/min.