CN102746526A - Degradable porous film for wind prevention, ventilation and bacteriostasis - Google Patents
Degradable porous film for wind prevention, ventilation and bacteriostasis Download PDFInfo
- Publication number
- CN102746526A CN102746526A CN2012102391509A CN201210239150A CN102746526A CN 102746526 A CN102746526 A CN 102746526A CN 2012102391509 A CN2012102391509 A CN 2012102391509A CN 201210239150 A CN201210239150 A CN 201210239150A CN 102746526 A CN102746526 A CN 102746526A
- Authority
- CN
- China
- Prior art keywords
- resin solution
- under
- mixed resin
- apertured film
- main
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a degradable porous film for wind prevention, ventilation and bacteriostasis, which is prepared by the steps of: adjusting the liquid temperature of a reactor to 30 DEG C, and uniformly mixing butanone, dimethylformamide, toluene and polyurethane resin at the first stirring rate according to the mass ratio of 10:10:25:100 to form a first primary resin solution; slowly adding 1, 6-diisocyanate hexane into the first primary resin solution to form a first primary resin mixed solution; mixing the solvent which is formed by water and the butanone with the first primary resin solution to form the first primary resin mixed solution; mixing the regulated resin mixed solution with N-methylethanolamine; filtering the regulated first primary resin mixed solution by a nylon net of 100-200 meshes, so the filtered first primary resin mixed solution is obtained; and drying the macromolecular mixed resin which is scraped on the silicon oil release paper in a tensioning state by four stages. The porous film has uniform and dense micropores at a nanoscale of 50-200nm, has good wind prevention, moisture permeation, waterproofness, ventilation and excellent bacteriostasis, and is contributed to maintaining the long-term dryness of the film surface and wearing health when being used.
Description
Technical field
The present invention relates to a kind of windproof vapour bacteriostatic degradable apertured film that is used for, belong to the weaving face fabric technical field.
Background technology
Existing polyurethane film is that the multipolymer by one-component constitutes, and is alternately arranged along macromolecular chain by hard segment and soft chain segment.Hard segment is hydrophobic, and it can stop water droplet to pass through, and plays waterproof action; Soft chain segment is hydrophilic, it can with the water molecules effect, by hydrogen bond and other Intermolecular Forces,, be delivered to low humidity one side desorb, thereby reach the effect that wets through hydrophilic group on the macromolecular chain at high humidity one side absorbent moisture.Passing through wet process is " absorption-diffusion-desorb ".Its shortcoming is this kind nonporous moisture permeable film, and moisture permeable amount is very much limitedly can reach 5000g/m by ASTM E96BW
2/ D is difficult to satisfy people's rapid sweat vapour discharging needs that produce when vigorous exercise, is prone to let the wearer produce very heavy wet vexed sense.
Summary of the invention
The object of the invention provides a kind of antibacterial degradable apertured film of windproof vapour that is used for; This apertured film has the micropore of even compact nano level 50-200nm; Have good Wind-proof, moisture-permeability, water-proof air-permeable performance and excellent bacteriostatic action, the health of dry and comfortable and dress when keeping face long in helping to use.
For achieving the above object, the technical scheme that the present invention adopts is: this apertured film is obtained by the centrifugal paper film of silicone oil stripping technique:
Step 1-1, adjustment reaction kettle liquid temperature to 30 ℃ with butanone, N, toluene and urethane resin according to 10: 10: 25: 100 mass ratio is uniformly mixed to form the first main resin solution under first stir speed (S.S.);
30 ℃ of step 1-2, maintenance liquid temperature; With 1; The 6-diisocyanato-Hexane slowly drops into (SD-27M can express better through main ingredient) and under second stir speed (S.S.), is uniformly mixed to form the first main mixed resin solution with the said first main resin solution according to 3: 100 mass ratios;
Step 1-3, keep 30 ℃ of liquid temperature, water and butanone are mixed the formation solvent according to 9: 1 mass ratio, this solvent and the said first main mixed resin solution mix the first main mixed resin solution after the formation adjusting according to 30: 100 mass ratios;
Step 1-4, keep 30 ℃ of liquid temperature, mixed resin solution and the ratio of N-Mono Methyl Ethanol Amine by 100: 1 with step 1-3 regulates slowly drop into (CL-15 can pass through the main ingredient expression better)
Step 1-5, the first main mixed resin solution after the first main mixed resin solution after the said adjusting filtered through 100~200 purpose nylon net filters;
Step 1-6, the first main mixed resin solution standing and defoaming after the said filtration is handled;
Step 1-7, the thickness that said polymer hybrid resin is pressed 0.005-0.05mm apply and the centrifugal paper of silicone oil top layer;
Step 1-8, said blade coating had under the tension state in the polymer hybrid resin of silicone oil separate-type paper drying, drying time is 2-3 minute, and divides the four-stage fs: under 60 ℃ condition, and under swiftly flowing air atmosphere, carry out; Subordinate phase: under 90 ℃ condition, and under low speed mobile air atmosphere, carry out; Phase III: under 120 ℃ condition, and under swiftly flowing air atmosphere, carry out; Stage: under 140 ℃ condition, and under swiftly flowing air atmosphere, carry out;
Step 1-9, with said through the oven dry film carry out the refrigerated separation bundling;
Further improved technical scheme is following in the technique scheme:
Utilized the different boiling of different solvents butanone, N, toluene and water can do stage volatilization system as preferred step 1-1 and 1-3.
Accelerate stirring velocity as the said stirring velocity of optimized technical scheme with the addition of solvent, and keep at the uniform velocity more than 5 minutes of the highest 2000 commentaries on classics;
Be 2 hours as the standing and defoaming treatment time among the preferred said step 1-6;
As the centrifugal paper film of the silicone oil stripping technique described in preferred said step 1-7,1-8 and the 1-9;
Because the technique scheme utilization, the present invention compared with prior art has advantage and effect:
1, the object of the invention provides a kind of antibacterial degradable apertured film of windproof vapour that is used for; This apertured film has the micropore of even compact nano level 50-200nm; Have good Wind-proof, moisture-permeability, water-proof air-permeable performance and excellent bacteriostatic action, the health of dry and comfortable and dress when keeping face long in helping to use.
When 2, apertured film of the present invention is burnt by simple (carbon C, hydrogen H, oxygen O, the nitrogen N) incinerator of structure, do not have empty dirty problem, material receives humidity and microbial process when soil is buried, and the 3-5 natural decomposition belongs to ep-type material; Secondly; Be used for the antibacterial degradable apertured film of windproof vapour have outstanding tear, wear-resisting, warping strength performance is used for the antibacterial degradable apertured film of windproof vapour and has outstanding water-fast and anti-electric bacterinertness; This porose moisture permeable membrane has the water vapour permeability of high target, the highlyest can reach 30000g/m2*24h, is equivalent to can discharge 30 kg of water every square metre of every day; Be the TPU film, the common PU film in market is with originally being beyond one's reach; Secondly, apertured film film water pressure resistance of the present invention is up to 10000mmH
2O is equivalent to film body and bears 10 meters high water columns, can not seep water.
Description of drawings
Accompanying drawing 1 is used for the antibacterial degradable apertured film of windproof vapour process flow sheet for the present invention.
Embodiment
Below in conjunction with embodiment the present invention is further described:
Embodiment: a kind of antibacterial degradable apertured film of windproof vapour that is used for is characterized in that: this apertured film is obtained by the centrifugal paper film of silicone oil stripping technique; Said coating obtains through following technology oven dry:
Step 1-1, adjustment reaction kettle liquid temperature to 30 ℃ with butanone, N, toluene and urethane resin according to 10: 10: 25: 100 mass ratio is uniformly mixed to form the first main resin solution under first stir speed (S.S.);
30 ℃ of step 1-2, maintenance liquid temperature; With 1; The 6-diisocyanato-Hexane slowly drops into (SD-27M can express better through main ingredient) and under second stir speed (S.S.), is uniformly mixed to form the first main mixed resin solution with the said first main resin solution according to 3: 100 mass ratios;
Step 1-3, keep 30 ℃ of liquid temperature, water and butanone are mixed the formation solvent according to 9: 1 mass ratio, this solvent and the said first main mixed resin solution mix the first main mixed resin solution after the formation adjusting according to 30: 100 mass ratios;
Step 1-4, keep 30 ℃ of liquid temperature, mixed resin solution and the ratio of N-Mono Methyl Ethanol Amine by 100: 1 with step 1-3 regulates slowly drop into (CL-15 can pass through the main ingredient expression better)
Step 1-5, the first main mixed resin solution after the first main mixed resin solution after the said adjusting filtered through 100~200 purpose nylon net filters;
Step 1-6, the first main mixed resin solution standing and defoaming after the said filtration is handled the back oven dry obtain said undercoat;
Step 1-7, the thickness that said polymer hybrid resin is pressed 0.005-0.05mm apply and the centrifugal paper of silicone oil top layer;
Step 1-8, said blade coating had under the tension state in the polymer hybrid resin of silicone oil separate-type paper drying, drying time is 2-3 minute, and divides the four-stage fs: under 60 ℃ condition, and under swiftly flowing air atmosphere, carry out; Subordinate phase: under 90 ℃ condition, and under low speed mobile air atmosphere, carry out; Phase III: under 120 ℃ condition, and under swiftly flowing air atmosphere, carry out; Stage: under 140 ℃ condition, and under swiftly flowing air atmosphere, carry out;
Step 1-9, with said through the oven dry film carry out the refrigerated separation bundling;
Above-mentioned steps 1-1, be to adjust reaction kettle liquid temperature to 30 ℃ with butanone, N, toluene and urethane resin according to 10: 10: 25: 100 mix
Above-mentioned steps 1-2, be to keep 30 ℃ of liquid temperature, with 1, the 6-diisocyanato-Hexane slowly drops into and mixes according to 3: 100 with the said first main resin solution
Above-mentioned steps 1-3, be to keep 30 ℃ of liquid temperature; Water and butanone are mixed the formation solvent according to 9: 1 mass ratio, and this solvent and the said first main mixed resin solution mix the first main mixed resin solution that forms after regulating according to 30: 100 mass ratios;
Above-mentioned steps 1-4, be to keep 30 ℃ of liquid temperature, with the mixed resin solution and the ratio of N-Mono Methyl Ethanol Amine that step 1-3 regulates, slow input by 100: 1
Above-mentioned steps 1-5, the first main mixed resin solution after being the first main mixed resin solution after the said adjusting filtered through 100~200 purpose nylon net filters;
Above-mentioned steps 1-6, be the first main mixed resin solution standing and defoaming after the said filtration is handled
Above-mentioned steps 1-7, be said polymer hybrid resin is applied and the centrifugal paper of silicone oil top layer by the thickness of 0.005-0.05mm;
Above-mentioned steps 1-8, be said blade coating had under the tension state in the polymer hybrid resin of silicone oil separate-type paper and dry; Drying time is 2-3 minute; And divide the four-stage fs: under 60 ℃ condition, and under swiftly flowing air atmosphere, carry out; Subordinate phase: under 90 ℃ condition, and under low speed mobile air atmosphere, carry out; Phase III: under 120 ℃ condition, and under swiftly flowing air atmosphere, carry out; Stage: under 140 ℃ condition, and under swiftly flowing air atmosphere, carry out;
Above-mentioned steps 1-9, be with said through the oven dry film carry out the refrigerated separation bundling;
Adopt above-mentionedly when being used for the antibacterial degradable apertured film of windproof vapour,, have good Wind-proof, moisture-permeability, waterproof and breathable performance, and face is dry and comfortable owing to adopt the microporous membrane of special process made to have the little porous of even compact; Secondly, when being used for the antibacterial degradable apertured film of windproof vapour by simple (carbon C, hydrogen H, oxygen O, nitrogen N) incinerator burning of structure, do not have empty dirty problem, material receives humidity and microbial process when soil is buried, 3-5 natural decomposition, genus ep-type material; Once more; Be used for the antibacterial degradable apertured film of windproof vapour have outstanding tear, wear-resisting, warping strength performance is used for the antibacterial degradable apertured film of windproof vapour and has outstanding water-fast and anti-electric bacterinertness; Be used for the water vapour permeability that the antibacterial degradable apertured film of windproof vapour has high target, generally can reach 9000-10000g/m2*24h (JIS 1099 A1), be equivalent to discharge 10 kg of water every square metre of every day; Be the TPU film, the PU film is with originally being beyond one's reach; Secondly, the present invention is used for the antibacterial degradable apertured film of windproof vapour water pressure resistance and can reaches 6000mmH
2O is equivalent to film body and bears 6 meters high water columns, can not seep water.
The foregoing description only is explanation technical conceive of the present invention and characteristics, and its purpose is to let the personage who is familiar with this technology can understand content of the present invention and enforcement according to this, can not limit protection scope of the present invention with this.All equivalences that spirit is done according to the present invention change or modify, and all should be encompassed within protection scope of the present invention.
Claims (7)
1. one kind is used for windproof vapour bacteriostatic degradable apertured film, it is characterized in that: this apertured film is obtained by the centrifugal paper film of silicone oil stripping technique; Said coating obtains through following technology:
Step 1-1, adjustment reaction kettle liquid temperature to 30 ℃ with butanone, N, toluene and urethane resin according to 10: 10: 25: 100 mass ratio is uniformly mixed to form the first main resin solution under first stir speed (S.S.);
30 ℃ of step 1-2, maintenance liquid temperature, with 1, the 6-diisocyanato-Hexane slowly drops into the said first main resin solution and under second stir speed (S.S.), is uniformly mixed to form the first main mixed resin solution according to 3: 100 mass ratios;
Step 1-3, keep 30 ℃ of liquid temperature, water and butanone are mixed the formation solvent according to 9: 1 mass ratio, this solvent and the said first main mixed resin solution mix the first main mixed resin solution after the formation adjusting according to 30: 100 mass ratios;
Step 1-4, keep 30 ℃ of liquid temperature, the mixed resin solution of step 1-3 adjusting and N-Mono Methyl Ethanol Amine are slowly dropped in 100: 1 ratio mix;
Step 1-5, the first main mixed resin solution after the first main mixed resin solution after the said adjusting filtered through 100~200 purpose nylon net filters;
Step 1-6, the first main mixed resin solution after the said filtration is left standstill deaeration in 2 hours handle;
Step 1-7, to be the polymer hybrid resin with the said first main mixed resin solution apply and the centrifugal paper of silicone oil top layer by the thickness of 0.005-0.05mm;
Step 1-8, said blade coating had under the tension state in the polymer hybrid resin of silicone oil separate-type paper drying, drying time is 23 minutes, and divides the four-stage fs: under 60 ℃ condition, and under swiftly flowing air atmosphere, carry out; Subordinate phase: under 90 ℃ condition, and under low speed mobile air atmosphere, carry out; Phase III: under 120 ℃ condition, and under swiftly flowing air atmosphere, carry out; Stage: under 140 ℃ condition, and under swiftly flowing air atmosphere, carry out;
Step 1-9, with said through the oven dry film carry out the refrigerated separation bundling.
2. apertured film according to claim 1 is characterized in that: utilized the different boiling of different solvents butanone, N, toluene and water can do stage volatilization system.
3. apertured film according to claim 1 is characterized in that: solvent is divided at least six times and drops into the said first main mixed resin solution and the second main mixed resin solution among the said step 1-3.
4. apertured film according to claim 1 is characterized in that: said stirring velocity is accelerated stirring velocity with the addition of solvent.
5. apertured film according to claim 1 is characterized in that: at the uniform velocity more than 5 minutes of said maintenance 2000 commentaries on classics.
6. apertured film according to claim 1 is characterized in that: the standing and defoaming treatment time is 2 hours among the said step 1-6.
7. apertured film according to claim 1 is characterized in that: this apertured film is obtained by the centrifugal paper film of silicone oil stripping technique.