CN102731857A - Abrasion resistance sole and production method thereof - Google Patents
Abrasion resistance sole and production method thereof Download PDFInfo
- Publication number
- CN102731857A CN102731857A CN2012102032313A CN201210203231A CN102731857A CN 102731857 A CN102731857 A CN 102731857A CN 2012102032313 A CN2012102032313 A CN 2012102032313A CN 201210203231 A CN201210203231 A CN 201210203231A CN 102731857 A CN102731857 A CN 102731857A
- Authority
- CN
- China
- Prior art keywords
- parts
- base
- rubber
- sole
- wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses an abrasion resistance sole and a production method thereof. The abrasion resistance sole comprises a base material, a vulcanizing agent S, an accelerator TS, an accelerator 2#-75, and an accelerator DM. The method of the present invention has characteristics of simple process and easy operation. The product of the present invention has excellent abrasion resistance, wherein the DIN abrasion resistance can be less than 50, and the AKRON abrasion resistance can be less than 0.02.
Description
Technical field
The present invention relates to a kind of wear-resisting sole and working method thereof.
Background technology
There is defective in existing sole at the wear-resisting aspect of performance that waits, and wear resisting property is undesirable.
Summary of the invention
The object of the present invention is to provide a kind of wear resisting property good wear-resisting sole and working method thereof.
Technical solution of the present invention is:
A kind of wear-resisting sole is characterized in that: the raw material by following weight part is formed:
Said base-material is made up of the raw material of following weight part:
Said rubber is the mixture of paracril of cis-1,4-polybutadiene rubber and 30% weight percent of 70% weight percent.
A kind of working method of wear-resisting sole; It is characterized in that: rubber is dropped into mixer mixing 120 "; add WHITE CARBON BLACK, Triple Pressed Stearic Acid, PEG4000, C 9 petroleum resin, antioxidant SP-P, silane coupling agent, paraffin, zinc carbonate mixing 300 then "; Mention the laggard one-step melting 300 of weight cleaning dust again ", discharging obtains base-material; Base-material was parked 8 ~ 12 hours, added sulphur again, and base-material adds promotor and vulcanizing agent in opening refining, and 160 ℃ of down sulfurations, curing time is a 1.1min/mm base-material thickness, parked then to carry out the sole mold pressing under 160 ℃ after 24 hours and obtain product.
Technology of the present invention is simple, easy to operate, and the product wear resisting property is excellent, and the DIN abrasion can reach 50 ↓, the AKRON abrasion can reach 0.02 ↓.
Below in conjunction with embodiment the present invention is described further.
Embodiment
Embodiment 1:
A kind of wear-resisting sole, form by the raw material of following weight part:
Said base-material is made up of the raw material of following weight part:
Said rubber is the mixture of paracril of cis-1,4-polybutadiene rubber and 30% weight percent of 70% weight percent.
During making; By said ratio rubber is dropped into mixer mixing 120 "; add WHITE CARBON BLACK, Triple Pressed Stearic Acid, PEG4000, C 9 petroleum resin, antioxidant SP-P, silane coupling agent, paraffin, zinc carbonate mixing 300 then "; Mention the laggard one-step melting 300 of weight cleaning dust again ", discharging obtains base-material; Base-material was parked 8 ~ 12 hours, added sulphur again, and base-material adds promotor and vulcanizing agent in opening refining, and 160 ℃ of down sulfurations, curing time is a 1.1min/mm base-material thickness, parked then to carry out the sole mold pressing under 160 ℃ after 24 hours and obtain product.
Product performance:
Embodiment 2:
A kind of wear-resisting sole, form by the raw material of following weight part:
Said base-material is made up of the raw material of following weight part:
Said rubber is the mixture of paracril of cis-1,4-polybutadiene rubber and 30% weight percent of 70% weight percent.
Working method is with embodiment 1.
Product DIN abrasion reach 50 ↓, the AKRON abrasion reach 0.02 ↓.
Embodiment 3:
A kind of wear-resisting sole is characterized in that: the raw material by following weight part is formed:
Said base-material is made up of the raw material of following weight part:
Said rubber is the mixture of paracril of cis-1,4-polybutadiene rubber and 30% weight percent of 70% weight percent.
Working method is with embodiment 1.
Product DIN abrasion reach 50 ↓, the AKRON abrasion reach 0.02 ↓.
Claims (2)
1. wear-resisting sole, it is characterized in that: the raw material by following weight part is formed:
20 parts of base-materials
0.2 part of vulcanizing agent S
0.02 ~ 0.03 part of promotor TS
0.08 ~ 0.16 part of promotor 2#-75
0.08 ~ 0.16 part of altax;
Said base-material is made up of the raw material of following weight part:
100 parts of rubber
45 ~ 50 parts of WHITE CARBON BLACKs
0.5 ~ 1 part of Triple Pressed Stearic Acid
4.0 ~ 4.5 parts of PEG4000
2.0 parts of C 9 petroleum resins
1.0 ~ 1.5 parts of antioxidant SP-P
3.0 parts of silane coupling agent SI-69
0.5 ~ 1.0 part in paraffin
4.0 ~ 4.5 parts of zinc carbonates;
Said rubber is the mixture of paracril of cis-1,4-polybutadiene rubber and 30% weight percent of 70% weight percent.
2. the working method of the described wear-resisting sole of claim 1; It is characterized in that: rubber is dropped into mixer mixing 120 "; add WHITE CARBON BLACK, Triple Pressed Stearic Acid, PEG4000, C 9 petroleum resin, antioxidant SP-P, silane coupling agent, paraffin, zinc carbonate mixing 300 then "; Mention the laggard one-step melting 300 of weight cleaning dust again ", discharging obtains base-material; Base-material was parked 8 ~ 12 hours, added sulphur again, and base-material adds promotor and vulcanizing agent in opening refining, and 160 ℃ of down sulfurations, curing time is a 1.1min/mm base-material thickness, parked then to carry out the sole mold pressing under 160 ℃ after 24 hours and obtain product.